CN110808169A - 一种450-500v铝电解电容器用电解液及其制备方法 - Google Patents
一种450-500v铝电解电容器用电解液及其制备方法 Download PDFInfo
- Publication number
- CN110808169A CN110808169A CN201911197028.8A CN201911197028A CN110808169A CN 110808169 A CN110808169 A CN 110808169A CN 201911197028 A CN201911197028 A CN 201911197028A CN 110808169 A CN110808169 A CN 110808169A
- Authority
- CN
- China
- Prior art keywords
- electrolyte
- aluminum electrolytic
- electrolytic capacitor
- solute
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种450‑500V铝电解电容器用电解液及其制备方法，所述450‑500V铝电解电容器用电解液包括溶质、主溶剂、辅助溶剂及其他添加剂，其中，所述溶质为2‑己基己二酸铵或2‑己基己二酸与其铵盐的组合；所述溶质、主溶剂、辅助溶剂及其他添加剂的质量百分比为：溶质1‑30%；主溶剂40‑60%；辅助溶剂10‑30%；添加剂0.3‑10%。利用本发明提供的铝电解电容器用电解液可以制备450‑500V的铝电解电容器，且闪火电压稳定，满足市场需求。
Description
技术领域
本发明属于铝电解电容器用电解液技术领域，具体涉及一种450-500V铝电解电容器用电解液及其制备方法。
背景技术
铝电解电容器在滤波、旁路、耦合、谐振、移相和储能等领域有着广泛的运用。随着电子元器件集成化和高速处理化技术的高速发展，具有“耐高压、耐高温、长寿命、耐高频波纹电流、低阻抗和低漏电流”的优点的铝电解电容器是目前的发展趋势。
铝电解电容器的典型结构是由铝圆筒做负极，里面装有液体电解质***一片弯曲的铝带做正极。它的芯子是由阳极铝箔、浸有电解液的衬垫板、阴极铝箔、天然氧化膜等重叠卷绕而成的，芯子浸电解液后用铝壳和胶盖密闭起来就构成一个电解电容器。
在铝电解电容器中，电解液对电容器的高温寿命、耐高压、阻抗和损耗因子等性能有着极其重要的影响。电解液主要由溶质、溶剂和添加剂构成，其中，溶质的高温性能和闪火电压直接影响着电容器的高温寿命和耐高压性能。很多设备需要用到450-500V铝电解电容器，因此需要提供一种450-500V铝电解电容器用电解液，以将铝电解电容器的闪火电压稳定在450-500V，满足市场需求。
发明内容
本发明的发明目的是提供450-500V铝电解电容器用电解液及其制备方法，以将铝电解电容器的闪火电压稳定在450-500V，满足市场需求。
为解决上述技术问题，本发明的实施例提供一种450-500V铝电解电容器用电解液，包括溶质、主溶剂、辅助溶剂及其他添加剂，其中，所述溶质为2-己基己二酸铵或2-己基己二酸与其铵盐的组合；
所述溶质、主溶剂、辅助溶剂及其他添加剂的质量百分比为：
溶质 1-30%；
主溶剂 40-60%；
辅助溶剂 10-30%；
添加剂 0.3-10%。
其中，所述主溶剂为醇类溶剂。
优选的，所述主溶剂为乙二醇、二甘醇、丙三醇中的一种或多种；
所述辅助溶剂为乙二醇、乙二醇单丁醚、二甘醇、丙二醇、丙三醇、正丁醇、正辛醇、二甘醇单丁醚、二甘醇二丁醚、二甘醇单甲醚、二甘醇二甲醚、二甘醇二***、γ-丁内酯、聚乙二醇和醋酸丁酯中的一种或多种。
其中，所述添加剂包括消氢添加剂、防水合添加剂和闪火电压提升剂；其中，
所述消氢添加剂选自间苯二酚、对硝基苯甲酸、对硝基苯甲醇、间硝基乙酰苯、对硝基苯酚、邻硝基苯甲醚和对苯醌中的一种或多种；
所述防水合添加剂选自磷酸、磷酸铵盐、亚磷酸及其铵盐、次亚磷酸及其铵盐和硅酸化合物或其铝盐的一种或多种；
所述闪火电压提升剂选自聚乙二醇400-20000、聚丙二醇、聚丙烯醇、聚合脂肪酸、聚合脂肪酸铵和纳米无机氧化物的一种或多种。
其中，所述电解液中各成分的质量百分比为：
2-己基己二酸铵 10%；
乙二醇 50%；
乙二醇单丁醚 30%；
对硝基苯甲酸 3%；
亚磷酸铵盐 2%；
聚丙二醇 5%。
所述电解液中各成分的质量百分比还可以采用如下组合：
2-己基己二酸与其铵盐的组合 25%；
丙三醇 56.5%；
二甘醇单丁醚 15%；
对硝基苯酚 1%；
次亚磷酸铵盐 0.5%；
聚乙二醇1000 2%。
本发明还提供一种铝电解电容器用电解液的制备方法，包括如下步骤：
（1）提供1-30份溶质、40-60份主溶剂、10-30份辅助溶剂和0.3-10份添加剂，其中，所述溶质为2-己基己二酸铵或2-己基己二酸与其铵盐的组合，所述主溶剂为醇类溶剂；
（2）混合主溶剂和辅助溶质，加热至50-80℃，加入溶质，搅拌至混合均匀，得到混合液A；
（3）将混合液A继续加热至95-120℃，保温60-90min，保温过程中，加入添加剂，缓慢搅拌至混合均匀，然后自然冷却至室温，即可得到铝电解电容器用电解液。
本发明还提供一种铝电解电容器，包括铝电解电容器用电解液，所述铝电解电容器用电解液由上述的制备方法制备得到。
本发明的上述技术方案的有益效果如下：利用本发明提供的铝电解电容器用电解液可以制备450-500V的铝电解电容器，且闪火电压稳定，满足市场需求。
具体实施方式
为使本发明要解决的技术问题、技术方案和优点更加清楚，下面将结合具体实施例进行详细描述。
本发明提供了一种450-500V铝电解电容器用电解液，包括溶质、主溶剂、辅助溶剂及其他添加剂，其中，所述溶质为2-己基己二酸铵或2-己基己二酸与其铵盐的组合；
所述溶质、主溶剂、辅助溶剂及其他添加剂的质量百分比为：
溶质 1-30%；
主溶剂 40-60%；
辅助溶剂 10-30%；
添加剂 0.3-10%。
所述主溶剂为醇类溶剂。优选的，所述主溶剂为乙二醇、二甘醇、丙三醇中的一种或多种；所述辅助溶剂为乙二醇、乙二醇单丁醚、二甘醇、丙二醇、丙三醇、正丁醇、正辛醇、二甘醇单丁醚、二甘醇二丁醚、二甘醇单甲醚、二甘醇二甲醚、二甘醇二***、γ-丁内酯、聚乙二醇和醋酸丁酯中的一种或多种。
所述添加剂包括消氢添加剂、防水合添加剂和闪火电压提升剂；其中，所述消氢添加剂选自间苯二酚、对硝基苯甲酸、对硝基苯甲醇、间硝基乙酰苯、对硝基苯酚、邻硝基苯甲醚和对苯醌中的一种或多种；所述防水合添加剂选自磷酸、磷酸铵盐、亚磷酸及其铵盐、次亚磷酸及其铵盐和硅酸化合物或其铝盐的一种或多种；所述闪火电压提升剂选自聚乙二醇400-20000、聚丙二醇、聚丙烯醇、聚合脂肪酸、聚合脂肪酸铵和纳米无机氧化物的一种或多种。
本发明还提供一种铝电解电容器用电解液的制备方法，包括如下步骤：
（1）提供1-30份溶质、40-60份主溶剂、10-30份辅助溶剂和0.3-10份添加剂，其中，所述溶质为2-己基己二酸铵或2-己基己二酸与其铵盐的组合，所述主溶剂为醇类溶剂；
（2）混合主溶剂和辅助溶质，加热至50-80℃，加入溶质，搅拌至混合均匀，得到混合液A；
（3）将混合液A继续加热至95-120℃，保温60-90min，保温过程中，加入添加剂，缓慢搅拌至混合均匀，然后自然冷却至室温，即可得到铝电解电容器用电解液。
本发明还提供一种铝电解电容器，包括铝电解电容器用电解液，所述铝电解电容器用电解液由上述的制备方法制备得到。
下面结合2个具体实施例进一步阐述本发明的技术方案。
实施例1
所述电解液中各成分的质量百分比为：
2-己基己二酸铵 10%；
乙二醇 50%；
乙二醇单丁醚 30%；
对硝基苯甲酸 3%；
亚磷酸铵盐 2%；
聚丙二醇 5%。
铝电解电容器用电解液的制备方法为：
（1-1）称量10份2-己基己二酸铵、50份乙二醇、30份乙二醇单丁醚、3份对硝基苯甲酸、2份亚磷酸铵盐和5份聚丙二醇。
（1-2）50份乙二醇和30份乙二醇单丁醚混合后加热至70℃，加入10份2-己基己二酸铵，搅拌至混合均匀，得到混合液A1。
（1-3）将上面得到的混合液A1继续加热至110℃，保温90min，保温过程中，加入3份对硝基苯甲酸、2份亚磷酸铵盐和5份聚丙二醇，缓慢搅拌至混合均匀，然后自然冷却至室温，即可得到450-500V铝电解电容器用电解液。
实施例2
所述电解液中各成分的质量百分比为：
2-己基己二酸与其铵盐的组合物 25%；
丙三醇 56.5%；
二甘醇单丁醚 15%；
对硝基苯酚 1%；
次亚磷酸铵盐 0.5%；
聚乙二醇1000 2%。
铝电解电容器用电解液的制备方法为：
（1-1）称量25份2-己基己二酸与其铵盐的组合物、56.5份丙三醇、15份二甘醇单丁醚、1份对硝基苯酚、0.5份次亚磷酸铵盐和2份聚乙二醇1000。
（1-2）56.5份丙三醇和15份二甘醇单丁醚混合后加热至65℃，加入25份2-己基己二酸与其铵盐的组合物，搅拌至混合均匀，得到混合液A2。
（1-3）将上面得到的混合液A2继续加热至120℃，保温90min，保温过程中，加入1份对硝基苯酚、0.5份次亚磷酸铵盐和2份聚乙二醇1000，缓慢搅拌至混合均匀，然后自然冷却至室温，即可得到450-500V铝电解电容器用电解液。
将上述实施例得到的铝电解电容器用电解液进行指标测试，所得结果如下表所示：
| 溶质及其占比 | 主溶剂及其占比 | 辅助溶剂及其占比 | 添加剂占比 | 闪火电压（V） | |
| 实施例1 | 2-己基己二酸铵（10%） | 乙二醇（50%） | 乙二醇单丁醚（30%） | 10% | 476 |
| 实施例2 | 2-己基己二酸与其铵盐的组合物（25%） | 丙三醇（56.5%） | 二甘醇单丁醚（15%） | 3.5% | 493 |
以上所述是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明所述原理的前提下，还可以作出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (8)
1.一种450-500V铝电解电容器用电解液，其特征在于，包括溶质、主溶剂、辅助溶剂及其他添加剂，其中，所述溶质为2-己基己二酸铵或2-己基己二酸与其铵盐的组合；
所述溶质、主溶剂、辅助溶剂及其他添加剂的质量百分比为：
溶质 1-30%；
主溶剂 40-60%；
辅助溶剂 10-30%；
添加剂 0.3-10%。
2.根据权利要求1所述的450-500V铝电解电容器用电解液，其特征在于，所述主溶剂为醇类溶剂。
3.根据权利要求1或2所述的450-500V铝电解电容器用电解液，其特征在于，所述主溶剂为乙二醇、二甘醇、丙三醇中的一种或多种；
所述辅助溶剂为乙二醇、乙二醇单丁醚、二甘醇、丙二醇、丙三醇、正丁醇、正辛醇、二甘醇单丁醚、二甘醇二丁醚、二甘醇单甲醚、二甘醇二甲醚、二甘醇二***、γ-丁内酯、聚乙二醇和醋酸丁酯中的一种或多种。
4.根据权利要求1所述的450-500V铝电解电容器用电解液，其特征在于，所述添加剂包括消氢添加剂、防水合添加剂和闪火电压提升剂；其中，
所述消氢添加剂选自间苯二酚、对硝基苯甲酸、对硝基苯甲醇、间硝基乙酰苯、对硝基苯酚、邻硝基苯甲醚和对苯醌中的一种或多种；
所述防水合添加剂选自磷酸、磷酸铵盐、亚磷酸及其铵盐、次亚磷酸及其铵盐和硅酸化合物或其铝盐的一种或多种；
所述闪火电压提升剂选自聚乙二醇400-20000、聚丙二醇、聚丙烯醇、聚合脂肪酸、聚合脂肪酸铵和纳米无机氧化物的一种或多种。
5.根据权利要求1所述的450-500V铝电解电容器用电解液，其特征在于，所述电解液中各成分的质量百分比为：
2-己基己二酸铵 10%；
乙二醇 50%；
乙二醇单丁醚 30%；
对硝基苯甲酸 3%；
亚磷酸铵盐 2%；
聚丙二醇 5%。
6.根据权利要求1所述的450-500V铝电解电容器用电解液，其特征在于，所述电解液中各成分的质量百分比为：
2-己基己二酸与其铵盐的组合 25%；
丙三醇 56.5%；
二甘醇单丁醚 15%；
对硝基苯酚 1%；
次亚磷酸铵盐 0.5%；
聚乙二醇1000 2%。
7.一种铝电解电容器用电解液的制备方法，其特征在于，包括如下步骤：
（1）提供1-30份溶质、40-60份主溶剂、10-30份辅助溶剂和0.3-10份添加剂，其中，所述溶质为2-己基己二酸铵或2-己基己二酸与其铵盐的组合，所述主溶剂为醇类溶剂；
（2）混合主溶剂和辅助溶质，加热至50-80℃，加入溶质，搅拌至混合均匀，得到混合液A；
（3）将混合液A继续加热至95-120℃，保温60-90min，保温过程中，加入添加剂，缓慢搅拌至混合均匀，然后自然冷却至室温，即可得到铝电解电容器用电解液。
8.一种铝电解电容器，其特征在于，包括铝电解电容器用电解液，所述铝电解电容器用电解液由权利要求7所述的制备方法制备得到。