CN110653333A - 一种球墨铸铁井盖消失模铸造涂料及其制备方法 - Google Patents
一种球墨铸铁井盖消失模铸造涂料及其制备方法 Download PDFInfo
- Publication number
- CN110653333A CN110653333A CN201910939449.7A CN201910939449A CN110653333A CN 110653333 A CN110653333 A CN 110653333A CN 201910939449 A CN201910939449 A CN 201910939449A CN 110653333 A CN110653333 A CN 110653333A
- Authority
- CN
- China
- Prior art keywords
- parts
- lost foam
- foam casting
- casting coating
- cast iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种球墨铸铁井盖消失模铸造涂料。所述球墨铸铁井盖消失模铸造涂料由以下重量配比的原料制成：石英粉20~30份、铝矾土50~70份、滑石粉3~7份、海泡石7~12份、钠基膨润土2~6份、羧甲基纤维素1~2份、白乳胶1~5份、OP‑10活性剂1~4份、正丁醇0.5~1.5份、苯甲酸钠0.8~1.5份、聚乙烯醇2~6份，水适量。本发明提供一种球墨铸铁井盖消失模铸造涂料及其制备方法，该涂料能很好地涂挂在消失模样表面，形成均匀的内外无气孔的涂层，且涂层具有高强度、高透气性、高耐火度，经高温铁水浇注烧结后易从铸件上剥落。
Description
技术领域
本发明涉及金属铸造加工技术领域，具体的，涉及一种球墨铸铁井盖消失模铸造涂料及其制备方法。
背景技术
消失模铸造工艺具有高精度尺寸、洁净表面，环保的特点。消失模涂料为获得表面高质量的消失模铸件扮演着重要的角色，是消失模铸造工艺中必要环节。对于消失模铸铁件的生产，要求涂料的配方和性能满足实际需求，不然铸件会发生气孔、夹砂等缺点，致使铸造出的件质量差以及合格率低。因而，研发一种的新涂料，来满足铸铁件生产的需求。
发明内容
为了满足铸铁件生产的需求的技术问题，本发明提供一种球墨铸铁井盖消失模铸造涂料及其制备方法，该涂料能很好地涂挂在消失模样表面，形成均匀的内外无气孔的涂层，且涂层具有高强度、高透气性、高耐火度，经高温铁水浇注烧结后易从铸件上剥落。
本发明提供了一种球墨铸铁井盖消失模铸造涂料，由以下重量配比的原料制成：石英粉20~30份、铝矾土50~70份、滑石粉3~7份、海泡石7~12份、钠基膨润土2~6份、羧甲基纤维素1~2份、白乳胶1~5份、OP-10活性剂1~4份、正丁醇0.5~1.5份、苯甲酸钠0.8~1.5份、聚乙烯醇2~6份，水适量。
在本发明提供的球墨铸铁井盖消失模铸造涂料的一种较佳实施例中，所述球墨铸铁井盖消失模铸造涂料由以下重量配比的原料制成：石英粉22~26份、铝矾土55~65份、滑石粉4~6份、海泡石8~10份、钠基膨润土3~5份、羧甲基纤维素1.2~1.5份、白乳胶2~3份、OP-10活性剂1.5~2.5份、正丁醇0.7~1份、苯甲酸钠1~1.2份、聚乙烯醇3~4份，水适量。
在本发明提供的球墨铸铁井盖消失模铸造涂料的一种较佳实施例中，所述球墨铸铁井盖消失模铸造涂料由以下重量配比的原料制成：石英粉25份、铝矾土60份、滑石粉5份、海泡石9份、钠基膨润土4份、羧甲基纤维素1.3份、白乳胶2.5份、OP-10活性剂2份、正丁醇0.8份、苯甲酸钠1.1份、聚乙烯醇3.5份，水适量。
在本发明提供的球墨铸铁井盖消失模铸造涂料的一种较佳实施例中，所述石英粉及所述铝矾土的粒度均为270~350目。
本发明还提供了一种球墨铸铁井盖消失模铸造涂料的制备方法，包括以下步骤：
步骤一、按重量份计，分别取石英粉20~30份、铝矾土50~70份、滑石粉3~7份、海泡石7~12份及钠基膨润土2~6份，混匀，得混合物；
步骤二、按重量份计，分别取正丁醇0.5~1.5份、苯甲酸钠0.8~1.5份、聚乙烯醇2~6份及适量水，将所述聚乙烯醇与水按重量比1：20的比例混合后加热使所述聚乙烯醇完全溶解，再加入所述正丁醇及所苯甲酸钠，混匀后得复合剂；
步骤三、按重量份计，分别取羧甲基纤维素1~2份、白乳胶1~5份、OP-10活性剂1~4份及适量水，将所述混合物与水按重量比1: 8~10的比例混合，浸泡12~15h小时后搅拌30~50min，然后加入所述羧甲基纤维素、所述白乳胶、所述OP-10活性剂及所述复合剂，继续搅拌1~2h后静置20~24h，即得球墨铸铁井盖消失模铸造涂料。
在本发明提供的球墨铸铁井盖消失模铸造涂料的制备方法的一种较佳实施例中，所述石英粉及所述铝矾土的粒度均为270~350目。
相较于现有技术，本发明提供的球墨铸铁井盖消失模铸造涂料及其制备方法具有以下有益效果：本发明提供的消失模样涂料能很好地涂挂在消失模样表面，形成均匀的内外无气孔的涂层，且涂层具有高强度、高透气性，高耐火度，经高温铁水浇注烧结后易从铸件上剥落。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
实施例1
一种球墨铸铁井盖消失模铸造涂料，由以下重量配比的原料制成：石英粉22份、铝矾土55份、滑石粉4份、海泡石8份、钠基膨润土3份、羧甲基纤维素1.2份、白乳胶2份、OP-10活性剂1.5份、正丁醇0.7份、苯甲酸钠1份、聚乙烯醇3份，水适量。
所述石英粉及所述铝矾土的粒度均为270目。
制备方法包括以下步骤：
S1、按重量份配比分别取石英粉、铝矾土、滑石粉、海泡石及钠基膨润土，混匀，得混合物；
S2、按重量份配比分别取正丁醇、苯甲酸钠、聚乙烯醇及适量水，将所述聚乙烯醇与水按重量比1：20的比例混合后加热使所述聚乙烯醇完全溶解，再加入所述正丁醇及所苯甲酸钠，混匀后得复合剂；
S3、按重量份配比分别取羧甲基纤维素、白乳胶、OP-10活性剂份及适量水，将所述混合物与水按重量比1: 8的比例混合，浸泡12h小时后搅拌30min，然后加入所述羧甲基纤维素、所述白乳胶、所述OP-10活性剂及所述复合剂，继续搅拌1h后静置20h，即得球墨铸铁井盖消失模铸造涂料。
实施例2
一种球墨铸铁井盖消失模铸造涂料，由以下重量配比的原料制成：石英粉25份、铝矾土60份、滑石粉5份、海泡石9份、钠基膨润土4份、羧甲基纤维素1.3份、白乳胶2.5份、OP-10活性剂2份、正丁醇0.8份、苯甲酸钠1.1份、聚乙烯醇3.5份，水适量。
所述石英粉及所述铝矾土的粒度均为300目。
制备方法包括以下步骤：
S1、按重量份配比分别取石英粉、铝矾土、滑石粉、海泡石及钠基膨润土，混匀，得混合物；
S2、按重量份配比分别取正丁醇、苯甲酸钠、聚乙烯醇及适量水，将所述聚乙烯醇与水按重量比1：20的比例混合后加热使所述聚乙烯醇完全溶解，再加入所述正丁醇及所苯甲酸钠，混匀后得复合剂；
S3、按重量份配比分别取羧甲基纤维素、白乳胶、OP-10活性剂份及适量水，将所述混合物与水按重量比1:9的比例混合，浸泡13h小时后搅拌40min，然后加入所述羧甲基纤维素、所述白乳胶、所述OP-10活性剂及所述复合剂，继续搅拌1.5h后静置22h，即得球墨铸铁井盖消失模铸造涂料。
实施例3
一种球墨铸铁井盖消失模铸造涂料，由以下重量配比的原料制成：石英粉26份、铝矾土65份、滑石粉6份、海泡石10份、钠基膨润土5份、羧甲基纤维素1.5份、白乳胶3份、OP-10活性剂2.5份、正丁醇1份、苯甲酸钠1.2份、聚乙烯醇4份，水适量。
所述石英粉及所述铝矾土的粒度均为350目。
制备方法包括以下步骤：
S1、按重量份配比分别取石英粉、铝矾土、滑石粉、海泡石及钠基膨润土，混匀，得混合物；
S2、按重量份配比分别取正丁醇、苯甲酸钠、聚乙烯醇及适量水，将所述聚乙烯醇与水按重量比1：20的比例混合后加热使所述聚乙烯醇完全溶解，再加入所述正丁醇及所苯甲酸钠，混匀后得复合剂；
S3、按重量份配比分别取羧甲基纤维素、白乳胶、OP-10活性剂份及适量水，将所述混合物与水按重量比1: 10的比例混合，浸泡15h小时后搅拌50min，然后加入所述羧甲基纤维素、所述白乳胶、所述OP-10活性剂及所述复合剂，继续搅拌2h后静置24h，即得球墨铸铁井盖消失模铸造涂料。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (6)
1.一种球墨铸铁井盖消失模铸造涂料，其特征在于，由以下重量配比的原料制成：石英粉20~30份、铝矾土50~70份、滑石粉3~7份、海泡石7~12份、钠基膨润土2~6份、羧甲基纤维素1~2份、白乳胶1~5份、OP-10活性剂1~4份、正丁醇0.5~1.5份、苯甲酸钠0.8~1.5份、聚乙烯醇2~6份，水适量。
2.根据权利要求1所述的球墨铸铁井盖消失模铸造涂料，其特征在于，所述球墨铸铁井盖消失模铸造涂料由以下重量配比的原料制成：石英粉22~26份、铝矾土55~65份、滑石粉4~6份、海泡石8~10份、钠基膨润土3~5份、羧甲基纤维素1.2~1.5份、白乳胶2~3份、OP-10活性剂1.5~2.5份、正丁醇0.7~1份、苯甲酸钠1~1.2份、聚乙烯醇3~4份，水适量。
3.根据权利要求2所述的球墨铸铁井盖消失模铸造涂料，其特征在于，所述球墨铸铁井盖消失模铸造涂料由以下重量配比的原料制成：石英粉25份、铝矾土60份、滑石粉5份、海泡石9份、钠基膨润土4份、羧甲基纤维素1.3份、白乳胶2.5份、OP-10活性剂2份、正丁醇0.8份、苯甲酸钠1.1份、聚乙烯醇3.5份，水适量。
4.根据权利要求1~3任一所述的球墨铸铁井盖消失模铸造涂料，其特征在于，所述石英粉及所述铝矾土的粒度均为270~350目。
5.一种球墨铸铁井盖消失模铸造涂料的制备方法，其特征在于，包括以下步骤：
步骤一、按重量份计，分别取石英粉20~30份、铝矾土50~70份、滑石粉3~7份、海泡石7~12份及钠基膨润土2~6份，混匀，得混合物；
步骤二、按重量份计，分别取正丁醇0.5~1.5份、苯甲酸钠0.8~1.5份、聚乙烯醇2~6份及适量水，将所述聚乙烯醇与水按重量比1：20的比例混合后加热使所述聚乙烯醇完全溶解，再加入所述正丁醇及所苯甲酸钠，混匀后得复合剂；
步骤三、按重量份计，分别取羧甲基纤维素1~2份、白乳胶1~5份、OP-10活性剂1~4份及适量水，将所述混合物与水按重量比1:8~10的比例混合，浸泡12~15h小时后搅拌30~50min，然后加入所述羧甲基纤维素、所述白乳胶、所述OP-10活性剂及所述复合剂，继续搅拌1~2h后静置20~24h，即得球墨铸铁井盖消失模铸造涂料。
6.根据权利要求5所述的球墨铸铁井盖消失模铸造涂料，其特征在于，所述石英粉及所述铝矾土的粒度均为270~350目。