CN110475930A - Paper and honeycomb prepared therefrom - Google Patents
Paper and honeycomb prepared therefrom Download PDFInfo
- Publication number
- CN110475930A CN110475930A CN201880019248.9A CN201880019248A CN110475930A CN 110475930 A CN110475930 A CN 110475930A CN 201880019248 A CN201880019248 A CN 201880019248A CN 110475930 A CN110475930 A CN 110475930A
- Authority
- CN
- China
- Prior art keywords
- paper
- weight
- honeycomb
- fibres
- fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of paper, are especially used to prepare honeycomb.The paper bag contains thermoplastic fibre and mineral fibres, wherein the thermoplastic fibre includes that fibril and/or aramid fiber short fibre are spun in aramid fiber spray.In addition, the present invention relates to by the standby honeycomb made of paper.
Description
The present invention relates to a kind of paper, are especially used to prepare honeycomb.
Honeycomb is in particular in light structures, such as in the structure of aircraft.Conventional honeycomb is by spy
It is fixed made of paper standby, one or both sides can be provided with coating.
Conventional honeycomb core, also referred to as honeycomb, such as by DuPont with trade mark Nomex sale.This paper is by fibril
Meta-aramid fibers change and during the preparation of paper as adhesive are constituted.Since this kind of paper and honeycomb core are relatively more high
It is expensive, therefore there is the demand to the paper that is suitable for preparing honeycomb and can cost-effectively prepare.
Therefore, it is suitable for preparing honeycomb and can cost-effectively make the object of the present invention is to provide one kind
Standby paper.
In order to realize the purpose, a kind of paper comprising thermoplastic fibre and mineral fibres is provided.
Paper according to the present invention, which has the advantage that, can cost-effectively obtain for component necessary to preparing, so that
It may be used as the substitution for conventional high price paper.Single component, i.e. thermoplastic fibre and mineral fibres are fire retardant or non-ignitable, so that this
The paper of invention meets fireproof requirement.
Fibril and/or aramid fiber short fibre are spun in paper bag aramid fiber containing thermoplastic fibre spray of the invention.Aramid fiber spray spins fibril with name
Twaron D8016 is claimed to be obtained commercially.Aramid fiber short fibre is obtained commercially with title Twaron 1080.
According to the present invention, paper bag asbestos fibre containing mineral, such as the MS 675Rockforce type of Lapinus.It is used as
Cost advantages and fire-retardant fibre fractionation.
Within the scope of the invention, it is preferred that mineral fibres includes basalt fibre.Do not enter lung especially herein
Basalt fibre.For example, the chopped strand with 4mm long.
It includes having by polyvinyl alcohol (PVA) preparation that preferred embodiment of the present invention, which is designed as paper according to the present invention,
Machine binder fibre.Preferably there is 4mm length, especially with polyvinyl alcohol-staple fiber of title VPB 105-2.
The preferred variants of paper of the invention have consisting of: fibril, 6-10 weight % are spun in the aramid fiber spray of 30-50 weight %
Aramid fiber short fibre, the mineral asbestos fibre of 15-30 weight %, the basalt fibre of 20-40 weight %, 1-10 weight % by
The organic fiber of polyvinyl alcohol preparation, wherein the summation of all the components is 100 weight %.
The paper prepared by this method can be prepared cost-effectively, it is characterised in that good mechanical performance simultaneously meets fire prevention
Regulation.
The particularly preferred variant of paper of the invention has consisting of: fibril, 9 weight % are spun in the aramid fiber spray of 36 weight %
Aramid fiber short fibre, the mineral asbestos fibre of 20 weight %, the basalt fibre of 30 weight % and 5 weight % by polyvinyl alcohol
The organic fiber of preparation.
Paper prepared in accordance with the present invention can have 30g/m2To 100g/m2Weight per unit area.The unit area weight
Amount preferably 70 to 80g/m2, particularly preferred 75g/m2。
In addition, the present invention relates to a kind of standby honeycombs made of paper by the type.The honeycomb can have
Hexagonal honeycomb, also referred to as " honeycomb ".Alternatively, the honeycomb can have sinusoidal honeycomb.Sinusoidal honeycomb is by ripple
The curved paper slip preparation of shape (sinusoidal), is accommodated between parallel paper slip.The hexagonal honeycomb and sinusoidal honeycomb are excellent
Choosing is provided with upper and lower coating.The coating can be prepared by being different from the material of paper, such as coating can be by glass
Fibre-reinforced plastics preparation, comprising epoxy resin as host material.
One variant designs of honeycomb are to be bonded to each other by standby component made of paper by ultrasonic bonding.Due to this
The advantageous mechanical property of the paper of invention, can the thermoforming under relatively low temperature, such as on groove device.
Paper of the invention and advantageous burning behavior is characterized in that by the standby honeycomb made of paper, in addition, being used for
The raw material of the paper can be obtained cost-effectively.
Claims (according to the 19th article of modification of treaty)
1. a kind of paper, is especially used to prepare honeycomb, wherein the paper bag contains thermoplastic fibre and mineral fibres, wherein institute
Stating thermoplastic fibre includes that fibril and/or aramid fiber short fibre are spun in aramid fiber spray, which is characterized in that and it includes mineral asbestos fibres, and
The mineral fibres includes basalt fibre.
2. paper according to claim 1, which is characterized in that it includes the organic fibers prepared by polyvinyl alcohol.
3. paper according to claim 2, which is characterized in that it is with consisting of:
Fibril is spun in the spray of -30 to 50 weight % aramid fibers,
- 6 to 10 weight % aramid fiber short fibres,
- 15 to 30 weight % mineral asbestos fibres,
- 20 to 40 weight % basalt fibres,
The organic fiber that -1 to 10 weight % is prepared by polyvinyl alcohol,
Wherein the sum of all shares are 100 weight %.
4. paper according to claim 3, which is characterized in that it is with consisting of:
Fibril is spun in the spray of -36 weight % aramid fibers,
- 9 weight % aramid fiber short fibres,
- 20 weight % mineral asbestos fibres,
- 30 weight % basalt fibres,
The organic fiber that -5 weight % are prepared by polyvinyl alcohol.
5. according to the described in any item paper of preceding claims, which is characterized in that weight per unit area is 30 to 100g/m2, preferably
70 to 80g/m2, particularly preferred 75g/m2。
6. honeycomb, which is characterized in that it is by described in any one of claim 1 to 5 made of paper standby.
7. honeycomb according to claim 6, which is characterized in that its with hexagonal honeycomb or sinusoidal honeycomb, wherein
The honeycomb preferably has coating.
8. honeycomb according to claim 6 or 7, which is characterized in that formed cellular paper by ultrasonic bonding that
This is combined.
Claims (9)
1. a kind of paper, is especially used to prepare honeycomb, wherein the paper bag contains thermoplastic fibre and mineral fibres, wherein institute
Stating thermoplastic fibre includes that fibril and/or aramid fiber short fibre are spun in aramid fiber spray, which is characterized in that it includes mineral asbestos fibres.
2. according to the described in any item paper of preceding claims, which is characterized in that the mineral fibres includes basalt fibre.
3. paper according to claim 1 or 2, which is characterized in that it includes the organic fibers prepared by polyvinyl alcohol.
4. according to the described in any item paper of preceding claims, which is characterized in that it is with consisting of:
Fibril is spun in the spray of -30 to 50 weight % aramid fibers,
- 6 to 10 weight % aramid fiber short fibres,
- 15 to 30 weight % mineral asbestos fibres,
- 20 to 40 weight % basalt fibres,
The organic fiber that -1 to 10 weight % is prepared by polyvinyl alcohol,
Wherein the sum of all shares are 100 weight %.
5. paper according to claim 4, which is characterized in that it is with consisting of:
Fibril is spun in the spray of -36 weight % aramid fibers,
- 9 weight % aramid fiber short fibres,
- 20 weight % mineral asbestos fibres,
- 30 weight % basalt fibres,
The organic fiber that -5 weight % are prepared by polyvinyl alcohol.
6. according to the described in any item paper of preceding claims, which is characterized in that weight per unit area is 30 to 100g/m2, preferably
70 to 80g/m2, particularly preferred 75g/m2。
7. honeycomb, which is characterized in that it is by as claimed in any one of claims 1 to 6 made of paper standby.
8. honeycomb according to claim 7, which is characterized in that its with hexagonal honeycomb or sinusoidal honeycomb, wherein
The honeycomb preferably has coating.
9. honeycomb according to claim 7 or 8, which is characterized in that formed cellular paper by ultrasonic bonding that
This is combined.