CN110468478B - Light and thin warm-keeping rabbit hair and polyester fiber blended fabric - Google Patents
Light and thin warm-keeping rabbit hair and polyester fiber blended fabric Download PDFInfo
- Publication number
- CN110468478B CN110468478B CN201910582591.0A CN201910582591A CN110468478B CN 110468478 B CN110468478 B CN 110468478B CN 201910582591 A CN201910582591 A CN 201910582591A CN 110468478 B CN110468478 B CN 110468478B
- Authority
- CN
- China
- Prior art keywords
- fabric
- polyester fiber
- rabbit hair
- rabbit
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a light and thin warm-keeping rabbit hair and polyester fiber blended fabric, which consists of rabbit hair and polyester fiber, and the manufacturing method of the fabric comprises the following steps of mixing, electrostatic treatment, water washing and drying, spinning, immersion, plasma treatment, crease resistance and drying: mixing, namely mixing rabbit hair and polyester fiber in a certain proportion; b, electrostatic treatment: and putting the fully mixed rabbit hair and polyester fiber into water, putting an antistatic agent in an appropriate proportion into the water, heating the water to 60-80 ℃, and standing for 2-4 hours. According to the invention, the rabbit wool and the polyester fiber are mixed, so that the mixed fabric has the advantages of lightness and excellent heat preservation performance of the rabbit wool and excellent setting performance of the polyester, and meanwhile, the formed mixed fabric has higher performance, is light, thin, warm-keeping, waterproof and anti-wrinkle through electrostatic treatment, mixed emulsion treatment, plasma treatment and the like.
Description
Technical Field
The invention relates to the technical field of blended fabrics, in particular to a light, thin and warm blended fabric of rabbit hair and polyester fibers.
Background
The fabric is a flat soft piece block formed by connecting fine and flexible objects through crossing and winding knots. The woven fabric is formed from yarns that are in a crossing relationship. The knitted fabric is constituted by yarns having a winding relation. Nonwoven fabrics are constructed from yarns that are in a connected relationship. The third fabric is formed from yarns which are in a cross-over/bind-around relationship. The plurality of yarns are in a stable relationship to form the fabric. The crossing, the winding and the connection are three stable structural relations which can be formed by the yarn. The fabric keeps stable shape and specific mechanical property. Various fabrics can be clearly known by analyzing the yarn groups in the fabrics and the running direction, the running rule and the formed relationship thereof.
Along with the improvement of living standard of people, the functionality and the comfortableness of the textile are increasingly valued by consumers, and because of the lack of comfortableness of the traditional multilayer fabric or the thicker fabric, people select the multilayer fabric or the thicker fabric less and less, and the blended fabric is widely adopted.
The blended fabric is a textile product which is made by blending two or more different types of fibers as raw materials for forming the fabric into yarns, and is formed by mixing and spinning chemical fibers such as polyester-viscose, polyester-nitrile, polyester-cotton and the like with other natural fibers such as cotton wool, silk, hemp and the like. For example: polyester cotton cloth, polyester wool tweed and the like. The blended fabric has the advantages that through the organic combination of two or more different types of fibers, the advantages of the blended fabric are made up for the deficiencies of the fibers, the advantages of the blended fabric coexist, and different requirements of people on clothes are met. For example, the blended fabric of cotton and bamboo fiber has the advantages of heat preservation and comfort of cotton, sterilization, ventilation and coolness of bamboo fiber, no defect of easy wrinkle of cotton, no defect of bamboo fiber, hard hand feeling and the like.
Blended fabrics are also distinguished from blended and interwoven fabrics: the blended fabric is made of the raw materials of the fabric by combining single yarns of two fibers into a folded yarn, wherein the low-elasticity polyester filament yarns are blended with medium-length polyester filaments, and the polyester staple fibers and the low-elasticity polyester filament yarns are blended into the folded yarn. The interwoven fabric is made of raw materials forming two direction systems of the fabric, wherein the raw materials respectively adopt different fiber yarns, and the interwoven fabric comprises Guxiangsatin interwoven with silk and rayon, Nifu woven interwoven with nylon and rayon and the like.
The current hybrid fabrics have the following disadvantages:
1. the light weight and the heat retention can not be met at the same time, or the light weight and the heat retention can be met at the same time, and the functionality is single;
2. the traditional light, thin and breathable fabric is poor in waterproofness due to the air holes;
3. the blended fabric is mixed, the combination of the raw materials is not tight, wrinkles are easy to appear, and the wearing comfort is affected;
therefore, we propose a light and thin warm-keeping rabbit hair and polyester fiber blended fabric to solve the above problems.
Disclosure of Invention
In order to achieve the purpose, the invention adopts the following technical scheme:
a light and thin warm-keeping rabbit hair and polyester fiber blended fabric is composed of rabbit hair and polyester fiber, and the manufacturing method of the fabric comprises the following steps of mixing, electrostatic treatment, washing and drying, spinning, immersion, plasma treatment, crease resistance and drying:
mixing, namely mixing rabbit hair and polyester fiber in a certain proportion;
b, electrostatic treatment: putting the fully mixed rabbit hair and polyester fiber into water, putting an antistatic agent in an appropriate proportion into the water, heating the water to 60-80 ℃, and standing for 2-4 hours;
c, washing and drying: fishing out the rabbit hair and the polyester fiber after the electrostatic treatment, washing the rabbit hair and the polyester fiber in a reciprocating manner by adopting clear water, repeating for 3-7min, and putting the rabbit hair and the polyester fiber into a dryer for 3-5min for full drying;
d, spinning: obtaining rabbit hair polyester blended fabric through a roving process, a spinning process and a winding process;
e, immersion liquid: stirring and mixing the blended fabric and the mixed emulsion for 10-30min, taking out the fabric, washing the fabric for 2-3 times by adopting clear water, and drying the fabric;
f, plasma treatment: steaming the fabric in steam at 90-110 deg.C for 5-10min, and placing the fabric in a plasma treatment instrument for 3-7 min;
g, crease resistance: taking out the fabric after plasma treatment, putting the fabric into a treatment box with an anti-wrinkle agent, pressurizing the fabric to 20-35Pa through an external supercharger, and uniformly stirring the anti-wrinkle agent for 10-15min through an external stirrer;
h, drying: taking out the fabric subjected to crease-resistant treatment, washing with clear water at 50-80 ℃, washing for 3-6min, and drying the fabric by a dryer.
Preferably, the mixing mode of the rabbit hair and the polyester fiber is as follows: the rabbit hair and the polyester fiber are scattered and put into a bale plucker, and high-pressure airflow is introduced.
Preferably, the high-pressure gas flow is 2-7 MPa.
Preferably, the mixed emulsion is formed by mixing butyl acrylate, a surfactant, an emulsifier, potassium persulfate and deionized water.
Preferably, the butyl acrylate, the surfactant, the emulsifier, the potassium persulfate and the deionized water in the mixed emulsion are 10-20 parts, 2-5 parts, 3-7 parts, 10-15 parts and 60-80 parts.
Compared with the prior art, the invention has the beneficial effects that: according to the invention, the rabbit wool and the polyester fiber are mixed, so that the mixed fabric has the advantages of lightness and excellent heat preservation performance of the rabbit wool and excellent setting performance of the polyester, and meanwhile, the formed mixed fabric has higher performance, is light, thin, warm-keeping, waterproof and anti-wrinkle through electrostatic treatment, mixed emulsion treatment, plasma treatment and the like.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments.
A light and thin warm-keeping rabbit hair and polyester fiber blended fabric is composed of rabbit hair and polyester fiber, and a manufacturing method of the fabric comprises the following steps of mixing, electrostatic treatment, washing and drying, spinning, immersion, plasma treatment, crease resistance and drying:
mixing, namely mixing rabbit hair and polyester fiber in a certain proportion;
the mixing mode of the rabbit wool and the polyester fiber is as follows: the rabbit hair and the polyester fiber are scattered and put into a plucker, high-pressure airflow is introduced, the high-pressure airflow is 2-7MPa, the rabbit hair and the polyester fiber are blown away by introducing the high-pressure airflow, and the rabbit hair and the polyester fiber are mixed at two sides by the scattering action of the plucker on the rabbit hair and the polyester fiber;
b, electrostatic treatment: putting the fully mixed rabbit hair and polyester fiber into water, putting an antistatic agent in an appropriate proportion into the water, heating the water to 60-80 ℃, and standing for 2-4 hours;
c, washing and drying: fishing out the rabbit hair and the polyester fiber after the electrostatic treatment, washing the rabbit hair and the polyester fiber in a reciprocating manner by adopting clear water, repeating for 3-7min, and putting the rabbit hair and the polyester fiber into a dryer for 3-5min for full drying; the rabbit wool and the polyester fiber are subjected to electrostatic treatment, so that the surface layer static electricity and the inner layer static electricity of the rabbit wool and the polyester fiber are removed, the two can be fully combined after subsequent spinning and weaving, the static electricity is prevented from repelling each other, and meanwhile, the generation of the static electricity in the subsequent steps is reduced after the electrostatic treatment;
d, spinning: obtaining rabbit hair polyester blended fabric through a roving process, a spinning process and a winding process;
e, immersion liquid: stirring and mixing the blended fabric and the mixed emulsion for 10-30min, taking out the fabric, washing the fabric for 2-3 times by adopting clear water, and drying the fabric;
the mixed emulsion is formed by mixing butyl acrylate, a surfactant, an emulsifier, potassium persulfate and deionized water, wherein the butyl acrylate, the surfactant, the emulsifier, the potassium persulfate and the deionized water in the mixed emulsion are 10-20 parts, 2-5 parts, 3-7 parts, 10-15 parts and 60-80 parts, and the mixed emulsion formed by mixing the butyl acrylate, the surfactant, the emulsifier, the potassium persulfate and the deionized water has good waterproofness.
f, plasma treatment: steaming the fabric in steam at 90-110 deg.C for 5-10min, and placing the fabric in a plasma treatment instrument for 3-7 min;
g, crease resistance: taking out the fabric after plasma treatment, putting the fabric into a treatment box with an anti-wrinkle agent, pressurizing the fabric to 20-35Pa through an external supercharger, and uniformly stirring the anti-wrinkle agent for 10-15min through an external stirrer; the fabric is subjected to plasma treatment by a plasma instrument, a large number of active particles such as ions, excited molecules, free radicals and the like in the plasma act on the surface of the solid sample, so that not only are original pollutants and impurities on the surface removed, but also an etching effect is generated, the surface of the sample is roughened, a plurality of micro pits are formed, and the specific surface of the sample is increased. The wettability of the solid surface is improved, the particle energy in the plasma is 0-20 eV, most bonds in the polymer are 0-10 eV, after the plasma acts on the solid surface, the original chemical bonds on the solid surface can be broken, free radicals in the plasma and the bonds form a net-shaped cross-linking structure, the surface activity is greatly activated, if reactive gas is introduced into the discharge gas, complex chemical reaction can be generated on the surface of the activated material, new functional groups such as alkyl, amino, carboxyl and the like are introduced, the functional groups are active groups, the surface activity of the material can be obviously improved, the active material is mixed with the anti-wrinkling agent, the mixing degree and efficiency of the anti-wrinkling agent are improved, the formed fabric has anti-wrinkling property, the smoothness of the fabric is guaranteed, and the fabric is comfortable to wear.
h, drying: and taking out the fabric subjected to the crease-resistant treatment, washing the fabric by using clear water at the temperature of 50-80 ℃, drying the fabric by using a dryer after washing for 3-6min, washing and cleaning to remove residual liquid on the surface of the fabric, and drying to obtain the formed fabric.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.
Claims (5)
1. The light and thin warm-keeping rabbit hair and polyester fiber blended fabric is characterized in that the fabric is composed of rabbit hair and polyester fiber, and the manufacturing method of the fabric comprises the following steps of mixing, electrostatic treatment, water washing and drying, spinning, immersion, plasma treatment, crease resistance and drying:
mixing, namely mixing rabbit hair and polyester fiber in a certain proportion;
b, electrostatic treatment: putting the fully mixed rabbit hair and polyester fiber into water, putting an antistatic agent in an appropriate proportion into the water, heating the water to 60-80 ℃, and standing for 2-4 hours;
c, washing and drying: fishing out the rabbit hair and the polyester fiber after the electrostatic treatment, washing the rabbit hair and the polyester fiber in a reciprocating manner by adopting clear water, repeating for 3-7min, and putting the rabbit hair and the polyester fiber into a dryer for 3-5min for full drying;
d, spinning: obtaining rabbit hair polyester blended fabric through a roving process, a spinning process and a winding process;
e, immersion liquid: stirring and mixing the blended fabric and the mixed emulsion for 10-30min, taking out the fabric, washing the fabric for 2-3 times by adopting clear water, and drying the fabric;
f, plasma treatment: steaming the fabric in steam at 90-110 deg.C for 5-10min, and placing the fabric in a plasma treatment instrument for 3-7 min;
g, crease resistance: taking out the fabric after plasma treatment, putting the fabric into a treatment box with an anti-wrinkle agent, pressurizing the fabric to 20-35Pa through an external supercharger, and uniformly stirring the anti-wrinkle agent for 10-15min through an external stirrer;
h, drying: taking out the fabric subjected to crease-resistant treatment, washing with clear water at 50-80 ℃, washing for 3-6min, and drying the fabric by a dryer.
2. The light, thin and warm rabbit hair and polyester fiber blended fabric according to claim 1, characterized in that the rabbit hair and the polyester fiber are mixed in a manner that: the rabbit hair and the polyester fiber are scattered and put into a bale plucker, and high-pressure airflow is introduced.
3. The blended fabric of rabbit wool and polyester fibers with light weight, thinness and warmth as claimed in claim 2, wherein the high pressure air flow is 2-7 MPa.
4. The blended fabric of rabbit wool and polyester fibers with characteristics of lightness, thinness and warmth as claimed in claim 1, wherein the mixed emulsion is formed by mixing butyl acrylate, a surfactant, an emulsifier, potassium persulfate and deionized water.
5. The blended fabric of rabbit wool and polyester fiber with light weight, thinness and warm keeping performance according to claim 4, wherein the butyl acrylate, the surfactant, the emulsifier, the potassium persulfate and the deionized water in the mixed emulsion are 10-20 parts, 2-5 parts, 3-7 parts, 10-15 parts and 60-80 parts.