CN107858778A - A kind of preparation method of moisture absorbing and sweat releasing yarn - Google Patents

A kind of preparation method of moisture absorbing and sweat releasing yarn Download PDF

Info

Publication number
CN107858778A
CN107858778A CN201711210734.2A CN201711210734A CN107858778A CN 107858778 A CN107858778 A CN 107858778A CN 201711210734 A CN201711210734 A CN 201711210734A CN 107858778 A CN107858778 A CN 107858778A
Authority
CN
China
Prior art keywords
yarn
temperature
moisture absorbing
sweat releasing
drying
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711210734.2A
Other languages
Chinese (zh)
Inventor
克劳斯·施蒂格
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhangjiagang Yangzi Spinning Co Ltd
Original Assignee
Zhangjiagang Yangzi Spinning Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhangjiagang Yangzi Spinning Co Ltd filed Critical Zhangjiagang Yangzi Spinning Co Ltd
Priority to CN201711210734.2A priority Critical patent/CN107858778A/en
Publication of CN107858778A publication Critical patent/CN107858778A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of moisture absorbing and sweat releasing yarn, combed using wool fiber and modified polyester fibre through combing machine, yarn is made in spinning frame drawing-off etc., the yarn is that hair washs composite blended yarn line；The invention also discloses a kind of preparation method of moisture absorbing and sweat releasing yarn, comprise the following steps：S1：Terylene surface is modified, S2：Surface Treatment with Plasma, S3：Flat drift, S4：Sizing, S5：Dyeing, S6：Tentering, S7：Preshrunk, S8：Resultant yarn pre-processes, S9：Drawing-off, S10：Sizing.The present invention passes through Surface Treatment with Plasma wool and the method modified polyester fibre of chemistry, solves the problems, such as yarn moisture absorbing and sweat releasing, ensure that yarn has the natural characteristic for also having wool fiber outside moisture absorbing and sweat releasing performance concurrently, meet the multi-functional demand of yarn, so that the use range of the present invention is more extensive.

Description

A kind of preparation method of moisture absorbing and sweat releasing yarn
Technical field
The present invention relates to yarn production field, specially a kind of preparation method of moisture absorbing and sweat releasing yarn.
Background technology
Traditional all woolen yarn process can not meet the functional requirement of consumer, but some chemical fibres such as terylene, The added value of existing product can just be increased well.Such as after fibre modification, utilize capillary caused by its surface minute groove Phenomenon makes sweat surface and the diverging of fabric are rapidly migrated to, through absorbing, spreading, the effect such as transmitting so as to reach wet-guide quick-drying Purpose and effect, but modified fiber only has the function of moisture absorbing and sweat releasing, soft without the warming of natural wool, hair quality It is soft, elasticity is good, thermal insulation is strong, comfortableness is good, the advantages that being not easy to crumple, be soft, the scope used is limited.
The content of the invention
It is an object of the invention to provide a kind of preparation method of moisture absorbing and sweat releasing yarn, to solve to carry in above-mentioned background technology The problem of going out.
To achieve the above object, the present invention provides following technical scheme：A kind of moisture absorbing and sweat releasing yarn, using wool fiber with Modified polyester fibre combs through combing machine, yarn is made in spinning frame drawing-off etc., and the yarn is that hair washs composite blended yarn line；
A kind of preparation method of water proof rubber coating, comprises the following steps：
S1：Terylene surface is modified, using an immersing and rolling mode, by polyester fiber be put into 1% antistatic additive, 1%~ 10% high temperature levelling agent, 20g healants pad working solution, pad rear liquid carrying rate 40%, 10rpm, then baked drying, bake and bank up with earth Temperature be 180 DEG C, the time is 1~3min；
S2：Surface Treatment with Plasma, the positive and negative of wool fiber pass through Surface Treatment with Plasma respectively；
S3：Flat drift, adds bleaching enzymes, 12~25g/l sodium chlorite and 30% in flat drift machine head tank and Lower tank Hydrogen peroxide, polyester fiber is soaked and expected, through 90~110 DEG C of decatizes 45~60 minutes, several hot water followed by 90~100 DEG C Ring case carries out hot water wash, drying, cropping；
S4：Sizing, 180~220 DEG C low-temperature shaped, and speed is 50~60m/min；
S5：Dyeing, using high-temperature and high pressure dyeing process, polyester fiber is placed in the closed container for filling dye liquor, and 120 ~300 DEG C, dyed under 2~3kgf/cm2 pressure conditions, the first pre- 70~80 DEG C of temperature of drying room control, the second pre- drying room 80 ~90 DEG C, drying machine drying, 190~200 DEG C of baking oven temperature, then wash through the immersing and rolling of fixation liquid one, cold water, hot water wash, soap, Cropping；
S6：Tentering, arrange stenter clear water tentering cropping, 50~60m/min of speed；
S7：Preshrunk, arrange preshrunk car and fall dry cloth, 50~60m/min of speed；
S8：Resultant yarn pre-processes, and controls 25 ± 3 DEG C of workshop temperature, humidity 60~70%, carries out opening picking and cotton carding processing, Cotton yarn quantitative 300~500g/m during opening picking, fixed length 30.6m, lap roller rotating speed are 11r/min, the carded sliver in carding process Quantitative 18.5g/5m；
S9：Drawing-off, using spinning frame rear-guard drawing-off yarn, drafting multiple is 1.25~1.4；
S10：Sizing, is shaped in yarn shaping machine, use 100~105 DEG C of steam carry out the time for 60~ 90min decatize.
Compared with prior art, the beneficial effects of the invention are as follows：Into polyester fiber add different performance antistatic additive, The chemical assistants such as high temperature levelling agent, healant are modified to terylene, terylene is had the performance of moisture absorbing and sweat releasing, at plasma Wool after reason can be good, hydrophilic with any fiber blend, yarn Machine Washable, energy roller drying after processing, pilling performance Property it is high the features such as, the present invention not only realizes the moisture absorption sweat discharging functions of yarn, is also provided with the characteristic of wool fiber, improves product Quality and meet people's multi-functional the needs of using, widened market.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation Example only part of the embodiment of the present invention, rather than whole embodiments.It is common based on the embodiment in the present invention, this area The every other embodiment that technical staff is obtained under the premise of creative work is not made, belong to the model that the present invention protects Enclose.
A kind of moisture absorbing and sweat releasing yarn, combed using wool fiber and modified polyester fibre through combing machine, spinning frame drawing-off etc. Yarn is made, the yarn is that hair washs composite blended yarn line；
Embodiment one
The present invention provides a kind of technical scheme：A kind of preparation method of moisture absorbing and sweat releasing yarn, comprises the following steps：
S1：Terylene surface is modified, using an immersing and rolling mode, by polyester fiber be put into 1% antistatic additive, 1% High temperature levelling agent, 20g healants pad working solution, pad rear liquid carrying rate 40%, 10rpm, then baked drying, the temperature baked and banked up with earth For 180 DEG C, time 2min；
S2：Surface Treatment with Plasma, the positive and negative of wool fiber pass through Surface Treatment with Plasma respectively；
S3：Flat drift, bleaching enzymes, 15g/l sodium chlorite and 30% pair are added in flat drift machine head tank and Lower tank Oxygen water, polyester fiber is soaked and expected, through 100 DEG C of decatizes 55 minutes, carried out hot water wash by 95 DEG C of several hot water circuit casees, dry Dry, cropping；
S4：Sizing, 200 DEG C low-temperature shaped, speed 55m/min；
S5：Dyeing, using high-temperature and high pressure dyeing process, polyester fiber is placed in the closed container for filling dye liquor, and 200 DEG C, dyed under 2kgf/cm2 pressure conditions, the first pre- 75 DEG C of temperature of drying room control, the second pre- 85 DEG C of drying room, dryer dries It is dry, 195 DEG C of baking oven temperature, then wash through the immersing and rolling of fixation liquid one, cold water, hot water wash, soap, cropping；
S6：Tentering, arrange stenter clear water tentering cropping, speed 55m/min；
S7：Preshrunk, arrange preshrunk car and fall dry cloth, speed 55m/min；
S8：Resultant yarn pre-processes, and controls 25 DEG C of workshop temperature, humidity 65%, opening picking and cotton carding processing is carried out, during opening picking Cotton yarn quantitative 400g/m, fixed length 30.6m, lap roller rotating speed are 11r/min, weight of card sliver 18.5g/5m in carding process；
S9：Drawing-off, using spinning frame rear-guard drawing-off yarn, drafting multiple 1.25；
S10：Sizing, is shaped in yarn shaping machine, uses 100 DEG C of steam to carry out vapour of the time for 60min Steam.
Embodiment two
The present invention provides a kind of technical scheme：A kind of preparation method of moisture absorbing and sweat releasing yarn, comprises the following steps：
S1：Terylene surface is modified, using an immersing and rolling mode, by polyester fiber be put into 1% antistatic additive, 510% High temperature levelling agent, 20g healants pad working solution, pad rear liquid carrying rate 40%, 10rpm, then baked drying, the temperature baked and banked up with earth Spend for 180 DEG C, time 3min；
S2：Surface Treatment with Plasma, the positive and negative of wool fiber pass through Surface Treatment with Plasma respectively；
S3：Flat drift, bleaching enzymes, 20g/l sodium chlorite and 30% pair are added in flat drift machine head tank and Lower tank Oxygen water, polyester fiber is soaked and expected, through 105 DEG C of decatizes 55 minutes, carried out hot water wash by 95 DEG C of several hot water circuit casees, dry Dry, cropping；
S4：Sizing, 200 DEG C low-temperature shaped, speed 55m/min；
S5：Dyeing, using high-temperature and high pressure dyeing process, polyester fiber is placed in the closed container for filling dye liquor, and 200 DEG C, dyed under 2.53kgf/cm2 pressure conditions, the first pre- 80 DEG C of temperature of drying room control, the second pre- 90 DEG C of drying room, dryer Drying, 195 DEG C of baking oven temperature, then wash through the immersing and rolling of fixation liquid one, cold water, hot water wash, soap, cropping；
S6：Tentering, arrange stenter clear water tentering cropping, speed 55m/min；
S7：Preshrunk, arrange preshrunk car and fall dry cloth, speed 55m/min；
S8：Resultant yarn pre-processes, and controls 25 DEG C of workshop temperature, humidity 65%, opening picking and cotton carding processing is carried out, during opening picking Cotton yarn quantitative 400g/m, fixed length 30.6m, lap roller rotating speed are 11r/min, weight of card sliver 18.5g/5m in carding process；
S9：Drawing-off, using spinning frame rear-guard drawing-off yarn, drafting multiple 1.3；
S10：Sizing, is shaped in yarn shaping machine, uses 105 DEG C of steam to carry out vapour of the time for 60min Steam.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding And modification, the scope of the present invention is defined by the appended.

Claims (2)

1. a kind of moisture absorbing and sweat releasing yarn, it is characterised in that combed using wool fiber and modified polyester fibre through combing machine, spun yarn Yarn is made in machine drawing-off etc., and the yarn is that hair washs composite blended yarn line.
2. a kind of preparation method of moisture absorbing and sweat releasing yarn as claimed in claim 1, it is characterised in that comprise the following steps：
S1：Terylene surface is modified, using an immersing and rolling mode, by polyester fiber be put into 1% antistatic additive, 1%~10% High temperature levelling agent, 20g healants pad working solution, pad rear liquid carrying rate 40%, 10rpm, then baked drying, the temperature baked and banked up with earth Spend for 180 DEG C, the time is 1~3min；
S2：Surface Treatment with Plasma, the positive and negative of wool fiber pass through Surface Treatment with Plasma respectively；
S3：Flat drift, bleaching enzymes, 12~25g/l sodium chlorite and 30% pair are added in flat drift machine head tank and Lower tank Oxygen water, polyester fiber is soaked and expected, through 90~110 DEG C of decatizes 45~60 minutes, several hot water circuit casees entered by 90~100 DEG C Row hot water wash, drying, cropping；
S4：Sizing, 180~220 DEG C low-temperature shaped, and speed is 50~60m/min；
S5：Dyeing, using high-temperature and high pressure dyeing process, polyester fiber is placed in the closed container for filling dye liquor, and 120~ 300 DEG C, dyed under 2~3kgf/cm2 pressure conditions, the first pre- 70~80 DEG C of temperature of drying room control, the second pre- drying room 80~ 90 DEG C, drying machine drying, 190~200 DEG C of baking oven temperature, then wash through the immersing and rolling of fixation liquid one, cold water, hot water wash, soap, fall Cloth；
S6：Tentering, arrange stenter clear water tentering cropping, 50~60m/min of speed；
S7：Preshrunk, arrange preshrunk car and fall dry cloth, 50~60m/min of speed；
S8：Resultant yarn pre-processes, and controls 25 ± 3 DEG C of workshop temperature, humidity 60~70%, carries out opening picking and cotton carding processing, opening or cleaning Cotton yarn quantitative 300~500g/m during cotton, fixed length 30.6m, lap roller rotating speed are 11r/min, weight of card sliver in carding process 18.5g/5m；
S9：Drawing-off, using spinning frame rear-guard drawing-off yarn, drafting multiple is 1.25~1.4；
S10：Sizing, is shaped in yarn shaping machine, uses 100~105 DEG C of steam to carry out the time as 60~90min's Decatize.
CN201711210734.2A 2017-11-28 2017-11-28 A kind of preparation method of moisture absorbing and sweat releasing yarn Pending CN107858778A (en)