CN110453354A - New fabric of a kind of three-dimensional big jacquard weave of band-like shorn velvet and preparation method thereof - Google Patents
New fabric of a kind of three-dimensional big jacquard weave of band-like shorn velvet and preparation method thereof Download PDFInfo
- Publication number
- CN110453354A CN110453354A CN201910785769.1A CN201910785769A CN110453354A CN 110453354 A CN110453354 A CN 110453354A CN 201910785769 A CN201910785769 A CN 201910785769A CN 110453354 A CN110453354 A CN 110453354A
- Authority
- CN
- China
- Prior art keywords
- cotton
- band
- fabric
- dyeing
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production methods of the new fabric of three-dimensional big jacquard weave of band-like shorn velvet, with cotton yarn for S twist yarn, super cotton-simulated terylene long filament is Z twist yarn, and bar-shape fabric is made with the longitude and latitude weaving method that rockets, and obtains the new fabric of the three-dimensional big jacquard weave of band-like shorn velvet by dyeing and setting treatment.On yarn material, the selection of consideration uses Compact-spun Yarn, is compared to conventional ring spinning yarn, no matter from intensity, filoplume, bar evenness etc., compact spinning has apparent quality heterosis.Face weave, using single-sided structure, the one-sided composition of similar flannelette.Flannelette reverse side has longer looped pile, prominent jacquard effect.On the basis of basic stitch, the collection of looped pile is punctuated reduction, forms significantly long looped pile, is conducive to subsequent three-dimensional plucking and cropping.In the flower pattern of jacquard fabric, using the figure of bar-shape, three-dimensional shorn velvet effect is showed by different band-like figures, embodies colourful novel jacquard style.
Description
Technical field
The present invention relates to knitting fabric fields, more particularly to a kind of three-dimensional big new fabric of jacquard weave of band-like shorn velvet and its preparation
Method.
Background technique
With China knitting fabric industry continuous development and the continuous improvement of society and living standards, people on clothes not
It only pursues again single warming and comfortable, has higher pursuit for the appearance of clothes.Product is knitted with its excellent performance,
In riotous profusion pattern, soft comfortable and the favor by more and more consumers.
Current knitting product will closer to adapt to consumer demand, develop to personalized direction.Market is to mentioning
The demand of flower fabric is being gradually increased, and occupies certain share, especially big jacquard weave, the even more outstanding person in jacquard fabric group.
Completely new jacquard fabric is researched and developed by enterprise independent innovation according to market popularity trend, is enterprise innovation energy
The concentrated reflection of power.For the three-dimensional key technical problem of the new fabric of jacquard weave greatly in exploitation of band-like shorn velvet of research, pass through core
The tackling key problem of heart technology, new research and development, achievement industrialization, realize that the product indirect export is earned foreign exchange, improve added value of product, promote enterprise
The extensive use of technology upgrading and core technology in new technology, new process development, further innovation research and development are suitble to international city
The band-like shorn velvet solid jacquard fabrics of field demand are very necessary.
Summary of the invention
The present invention is to solve the above problem in the prior art, propose a kind of three-dimensional big new fabric of jacquard weave of band-like shorn velvet and its
Preparation method.
It is an aspect of the invention to provide a kind of preparation methods of the new fabric of three-dimensional big jacquard weave of band-like shorn velvet, including step
It is rapid:
(1) weaving process: with cotton yarn for S twist yarn, super cotton-simulated terylene long filament is Z twist yarn, is rocketed weaving square legal system with longitude and latitude
Growth ribbon fabric；
(2) presetting technology: fabric made from step (1) is subjected to pre-setting, forming machine temperature setting is 185-195
DEG C, grammes per square metre is 245-255g/SQM after sizing, and door width is 165-175cm, and speed is 22~26m/min, setting time 1.8-
2.2min；
(3) dyeing: dyeing course includes pre-treatment, dye cotton and aftertreatment technology process:
1) pre-treating technology process: being first added pre-treatment auxiliary agent under room temperature, be warming up to 96 DEG C with the rate of 4 DEG C/min, protect
75 DEG C of drainings are cooled to the rate of 3 DEG C/min after warm 40min, are then washed 2 times, glacial acetic acid is washed 1 time, and catalase washes 1
It is secondary；
2) contaminate cotton process flow: 38 DEG C of addition cotton dyeing auxiliary agents and dyestuff are warming up to 60 DEG C with the rate of 2 DEG C/min, add
45min is kept the temperature after entering soda ash, is drained；
3) aftertreatment technology process: being cleaned after the completion of cotton dyeing with clear water, glacial acetic acid, detergent, and finally plus consistent lubricant is smart；
(4) dry: vibration is dried after the completion of dyeing；
(5) three-dimensional plucking: by the elongation sinker loop plucking of the loop construction of fabric, bristle, carding, cropping；
(6) it is formed: adding softening agent the final shaping, speed 18-22m/min.
Further, step (1) selects the cotton yarn of 40~60S, and the super cotton-simulated terylene long filament of 80~100D, finished product is through close 500
~600/10cm, 120~180/10cm of filling density.
Further, step (1) cotton yarn and super cotton-simulated terylene long filament use Compact-spun Yarn.Further, step
(1) each Ingredients Weight ratio are as follows: cotton yarn 30%-50%, super cotton-simulated terylene long filament 50%-70%.
It is further preferred that step (1) the fabric reverse side weaves bar-shape looped pile.
Further, the drying temperature of step (4) is 130-150 DEG C.
Further, the setting temperature of step (6) is 110-130 DEG C.
Further, in step (3) dyeing, dyeing type is day slope overflow dyeing machine, and main pump revolving speed 55 proposes cotton piece buff
Speed 60, nozzle location 90,60S/ circle, gap 4
Further, the formula of pre-treatment auxiliary agent is as follows in step (3) dyeing: hydrogen peroxide stabilizer 0.5g/L, closing
Fibre refining agent 1g/L, scouring agent 1g/L, soda ash 8g/L, hydrogen peroxide 10g/L, glacial acetic acid 1.2g/L, catalase 0.3g/L；
The formula of after treatment aid: glacial acetic acid 1.5g/L, detergent 4g/L, glacial acetic acid 0.3g/L, consistent lubricant essence 8g/L.
It is new that another aspect of the present invention is to provide the three-dimensional big jacquard weave of a kind of band-like shorn velvet prepared by any of the above-described method
Fabric.
The beneficial effects of the present invention are:
(1) on yarn material, the selection of consideration uses Compact-spun Yarn, no matter is compared to conventional ring spinning yarn
From intensity, filoplume, bar evenness etc., compact spinning has apparent quality heterosis；
(2) face weave, using single-sided structure, the one-sided composition of similar flannelette.Flannelette reverse side has longer looped pile, prominent
Jacquard effect.On the basis of basic stitch, the collection of looped pile is punctuated reduction, significantly long looped pile is formed, is conducive to subsequent
Three-dimensional plucking and cropping；
(3) in the flower pattern of jacquard fabric, using the figure of bar-shape, three-dimensional shorn velvet effect passes through different strip-charts
Shape shows, and embodies colourful novel jacquard style.
Specific embodiment
Current knitting product will closer to adapt to consumer demand, develop to personalized direction.Market is to mentioning
The demand of flower fabric is being gradually increased, and occupies certain share, especially big jacquard weave, the even more outstanding person in jacquard fabric group.
Specifically, the present invention provides a kind of preparation method of the new fabric of three-dimensional big jacquard weave of band-like shorn velvet, comprising steps of
(1) weaving process: with cotton yarn for S twist yarn, super cotton-simulated terylene long filament is Z twist yarn, is rocketed weaving square legal system with longitude and latitude
Growth ribbon fabric；Raw material using the yarn of two kinds of different orientations, mutually make between the two by a S twist yarn and a Z twist yarn
Weighing apparatus, bring cloth cover skew of weft due to yarn orientation of cancelling out each other.It is required that the twist of two stock yarn lines is identical or approximate, it so could most
Good achievees the effect that counteracting yarn twist internal stress, solves the problems, such as cloth cover skew of weft from source；
(2) presetting technology: fabric made from step (1) is subjected to pre-setting, forming machine temperature setting is 185-195
DEG C, grammes per square metre is 245-255g/SQM after sizing, and door width is 165-175cm, and speed is 22~26m/min, setting time 1.8-
2.2min；
(3) dyeing: dyeing course includes pre-treatment, dye cotton and aftertreatment technology process:
1) pre-treating technology process: being first added pre-treatment auxiliary agent under room temperature, be warming up to 96 DEG C with the rate of 4 DEG C/min, protect
75 DEG C of drainings are cooled to the rate of 3 DEG C/min after warm 40min, are then washed 2 times, glacial acetic acid is washed 1 time, and catalase washes 1
It is secondary；
2) contaminate cotton process flow: 38 DEG C of addition cotton dyeing auxiliary agents and dyestuff are warming up to 60 DEG C with the rate of 2 DEG C/min, add
45min is kept the temperature after entering soda ash, is drained；
3) aftertreatment technology process: being cleaned after the completion of cotton dyeing with clear water, glacial acetic acid, detergent, and finally plus consistent lubricant is smart；
(4) dry: vibration is dried after the completion of dyeing；
(5) three-dimensional plucking: by the elongation sinker loop plucking of the loop construction of fabric, bristle, carding, cropping；
(6) it is formed: adding softening agent the final shaping, speed 18-22m/min.
As an optimal technical scheme, step (1) selects the cotton yarn of 40~60S, the super cotton-simulated terylene long filament of 80~100D,
Finished product is through close 500~600/10cm, 120~180/10cm of filling density.
As another optimal technical scheme, step (1) cotton yarn and super cotton-simulated terylene long filament use Compact-spun Yarn.
It is compared to conventional ring spinning yarn, no matter from intensity, filoplume, bar evenness etc., compact spinning there are apparent product
Gesture of fine quality.
As an optimal technical scheme, step (1) each Ingredients Weight ratio are as follows: cotton yarn 30%-50%, super imitative cotton
Polyester filament 50%-70%；Preferably, cotton yarn 35%-45%, super cotton-simulated terylene long filament 55%-65%；It is further preferred that
Cotton yarn 40%, super cotton-simulated terylene long filament 60%.
As an optimal technical scheme, step (1) the fabric reverse side weaves bar-shape looped pile.In basic stitch
On the basis of, the collection of looped pile is punctuated reduction, significantly long looped pile is formed, is conducive to subsequent three-dimensional plucking and cropping.It is three-dimensional
Shorn velvet effect is showed by different band-like figures, embodies colourful novel jacquard style.
As an optimal technical scheme, the drying temperature of step (4) is 130-150 DEG C.Preferably, drying temperature is
140℃；In addition, the setting temperature of step (6) is 110-130 DEG C；It is further preferred that setting temperature is 120 DEG C.
As an optimal technical scheme, in step (3) dyeing, dyeing type is day slope overflow dyeing machine, main pump
Revolving speed 55 mentions cloth wheel speed 60, nozzle location 90,60S/ circle, gap 4
As an optimal technical scheme, the formula of pre-treatment auxiliary agent is as follows in step (3) dyeing: stabilized hydrogen peroxide
Agent 0.5g/L, fine refining agent 1g/L, scouring agent 1g/L, soda ash 8g/L, hydrogen peroxide 10g/L, glacial acetic acid 1.2g/L, peroxidating are closed
Hydrogen enzyme 0.3g/L；The formula of after treatment aid: glacial acetic acid 1.5g/L, detergent 4g/L, glacial acetic acid 0.3g/L, consistent lubricant essence 8g/L.
The present invention also provides the new fabrics of a kind of three-dimensional big jacquard weave of band-like shorn velvet prepared by any of the above-described method.In jacquard weave face
In the flower pattern of material, using the figure of bar-shape, three-dimensional shorn velvet effect is showed by different band-like figures, is embodied abundant
Colorful novel jacquard style.
The Specifications of fabric are made in the present invention are as follows: (1) shrink of becoming a cadre: directly to -4.9% lateral -3.8%；(2) resistance to
Color fastness 4-5 grades of washing, 4-5 grades of fastness to perspiration, 4-5 grades of color fastness to water, 4-5 grades of dry friction color fastness, wet friction color jail
4 grades of degree；(3) anti pilling, 3-4 grades before washing；3-4 grades of anti-hook silk；(4) bursting strength: 70psi；(5) pH value: 6~7.
The preferred embodiments of the present invention will be described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that so as to make a clearer definition of the protection scope of the present invention.
Embodiment 1
A kind of preparation method of the new fabric of the three-dimensional big jacquard weave of band-like shorn velvet:
(1) weaving process: with cotton yarn for S twist yarn, super cotton-simulated terylene long filament is Z twist yarn, is rocketed weaving square legal system with longitude and latitude
Growth ribbon fabric；
(2) presetting technology: fabric made from step (1) is subjected to pre-setting, forming machine temperature setting is 185-195
DEG C, grammes per square metre is 245-255g/SQM after sizing, and door width is 165-175cm, speed 22m/min, setting time 1.8-2.2min；
(3) dyeing: dyeing course includes pre-treatment, dye cotton and aftertreatment technology process:
1) pre-treating technology process: being first added pre-treatment auxiliary agent under room temperature, be warming up to 96 DEG C with the rate of 4 DEG C/min, protect
75 DEG C of drainings are cooled to the rate of 3 DEG C/min after warm 40min, are then washed 2 times, glacial acetic acid is washed 1 time, and catalase washes 1
It is secondary；
2) contaminate cotton process flow: 38 DEG C of addition cotton dyeing auxiliary agents and dyestuff are warming up to 60 DEG C with the rate of 2 DEG C/min, add
45min is kept the temperature after entering soda ash, is drained；
3) aftertreatment technology process: being cleaned after the completion of cotton dyeing with clear water, glacial acetic acid, detergent, and finally plus consistent lubricant is smart；
(4) dry: vibration is dried after the completion of dyeing, and drying temperature is 130 DEG C；
(5) three-dimensional plucking: by the elongation sinker loop plucking of the loop construction of fabric, bristle, carding, cropping；
(6) it is formed: adding softening agent the final shaping, setting temperature is 110 DEG C, speed 18-22m/min.
Embodiment 2
A kind of preparation method of the new fabric of the three-dimensional big jacquard weave of band-like shorn velvet:
(1) weaving process: with cotton yarn for S twist yarn, super cotton-simulated terylene long filament is Z twist yarn, is rocketed weaving square legal system with longitude and latitude
Growth ribbon fabric；
(2) presetting technology: fabric made from step (1) is subjected to pre-setting, forming machine temperature setting is 185-195
DEG C, grammes per square metre is 245-255g/SQM after sizing, and door width is 165-175cm, speed 24m/min, setting time 1.8-2.2min；
(3) dyeing: dyeing course includes pre-treatment, dye cotton and aftertreatment technology process:
1) pre-treating technology process: being first added pre-treatment auxiliary agent under room temperature, be warming up to 96 DEG C with the rate of 4 DEG C/min, protect
75 DEG C of drainings are cooled to the rate of 3 DEG C/min after warm 40min, are then washed 2 times, glacial acetic acid is washed 1 time, and catalase washes 1
It is secondary；
2) contaminate cotton process flow: 38 DEG C of addition cotton dyeing auxiliary agents and dyestuff are warming up to 60 DEG C with the rate of 2 DEG C/min, add
45min is kept the temperature after entering soda ash, is drained；
3) aftertreatment technology process: being cleaned after the completion of cotton dyeing with clear water, glacial acetic acid, detergent, and finally plus consistent lubricant is smart；
(4) dry: vibration is dried after the completion of dyeing, and drying temperature is 140 DEG C；
(5) three-dimensional plucking: by the elongation sinker loop plucking of the loop construction of fabric, bristle, carding, cropping；
(6) it is formed: adding softening agent the final shaping, setting temperature is 120 DEG C, speed 18-22m/min.
Embodiment 3
A kind of preparation method of the new fabric of the three-dimensional big jacquard weave of band-like shorn velvet:
(1) weaving process: with cotton yarn for S twist yarn, super cotton-simulated terylene long filament is Z twist yarn, is rocketed weaving square legal system with longitude and latitude
Growth ribbon fabric；
(2) presetting technology: fabric made from step (1) is subjected to pre-setting, forming machine temperature setting is 185-195
DEG C, grammes per square metre is 245-255g/SQM after sizing, and door width is 165-175cm, speed 26m/min, setting time 1.8-2.2min；
(3) dyeing: dyeing course includes pre-treatment, dye cotton and aftertreatment technology process:
1) pre-treating technology process: being first added pre-treatment auxiliary agent under room temperature, be warming up to 96 DEG C with the rate of 4 DEG C/min, protect
75 DEG C of drainings are cooled to the rate of 3 DEG C/min after warm 40min, are then washed 2 times, glacial acetic acid is washed 1 time, and catalase washes 1
It is secondary；
2) contaminate cotton process flow: 38 DEG C of addition cotton dyeing auxiliary agents and dyestuff are warming up to 60 DEG C with the rate of 2 DEG C/min, add
45min is kept the temperature after entering soda ash, is drained；
3) aftertreatment technology process: being cleaned after the completion of cotton dyeing with clear water, glacial acetic acid, detergent, and finally plus consistent lubricant is smart；
(4) dry: vibration is dried after the completion of dyeing, and drying temperature is 150 DEG C；
(5) three-dimensional plucking: by the elongation sinker loop plucking of the loop construction of fabric, bristle, carding, cropping；
(6) it is formed: adding softening agent the final shaping, setting temperature is 130 DEG C, speed 18-22m/min.
The preferred embodiment of the present invention has been described in detail above.It should be appreciated that the ordinary skill of this field is without wound
The property made labour, which according to the present invention can conceive, makes many modifications and variations.Therefore, all technician in the art
Pass through the available technology of logical analysis, reasoning, or a limited experiment on the basis of existing technology under this invention's idea
Scheme, all should be within the scope of the present invention.
Claims (10)
1. a kind of preparation method of the new fabric of three-dimensional big jacquard weave of band-like shorn velvet, which is characterized in that comprising steps of
(1) weaving process: with cotton yarn for S twist yarn, super cotton-simulated terylene long filament is Z twist yarn, and length is made with the longitude and latitude weaving method that rockets
Ribbon fabric；
(2) presetting technology: fabric made from step (1) is subjected to pre-setting, forming machine temperature setting is 185-195 DEG C, fixed
Grammes per square metre is 245-255g/SQM after type, and door width is 165-175cm, and speed is 22~26m/min, setting time 1.8-2.2min；
(3) dyeing: dyeing course includes pre-treatment, dye cotton and aftertreatment technology process:
1) pre-treating technology process: being first added pre-treatment auxiliary agent under room temperature, is warming up to 96 DEG C with the rate of 4 DEG C/min, heat preservation
75 DEG C of drainings are cooled to the rate of 3 DEG C/min after 40min, are then washed 2 times, glacial acetic acid is washed 1 time, and catalase is washed 1 time；
2) cotton process flow: 38 DEG C of addition cotton dyeing auxiliary agents and dyestuff is contaminated, 60 DEG C is warming up to the rate of 2 DEG C/min, is added pure
45min is kept the temperature after alkali, is drained；
3) aftertreatment technology process: being cleaned after the completion of cotton dyeing with clear water, glacial acetic acid, detergent, and finally plus consistent lubricant is smart；
(4) dry: vibration is dried after the completion of dyeing；
(5) three-dimensional plucking: by the elongation sinker loop plucking of the loop construction of fabric, bristle, carding, cropping；
(6) it is formed: adding softening agent the final shaping, speed 18-22m/min.
2. a kind of preparation method of the new fabric of three-dimensional big jacquard weave of band-like shorn velvet according to claim 1, which is characterized in that step
Suddenly (1) selects the cotton yarn of 40~60S, and the super cotton-simulated terylene long filament of 80~100D, finished product is through close 500~600/10cm, filling density 120
~180/10cm.
3. a kind of preparation method of the new fabric of three-dimensional big jacquard weave of band-like shorn velvet according to claim 1, which is characterized in that step
Suddenly (1) described cotton yarn and super cotton-simulated terylene long filament use Compact-spun Yarn.
4. a kind of preparation method of the new fabric of three-dimensional big jacquard weave of band-like shorn velvet according to claim 1, which is characterized in that step
Suddenly (1) each Ingredients Weight ratio are as follows: cotton yarn 30%-50%, super cotton-simulated terylene long filament 50%-70%.
5. a kind of preparation method of the new fabric of three-dimensional big jacquard weave of band-like shorn velvet according to claim 1, which is characterized in that step
Suddenly (1) described fabric reverse side weaves bar-shape looped pile.
6. a kind of preparation method of the new fabric of three-dimensional big jacquard weave of band-like shorn velvet according to claim 1, which is characterized in that step
Suddenly the drying temperature of (4) is 130-150 DEG C.
7. a kind of preparation method of the new fabric of three-dimensional big jacquard weave of band-like shorn velvet according to claim 1, which is characterized in that step
Suddenly the setting temperature of (6) is 110-130 DEG C.
8. a kind of preparation method of the new fabric of three-dimensional big jacquard weave of band-like shorn velvet according to claim 1, which is characterized in that step
Suddenly in (3) dyeing, dyeing type be day slope overflow dyeing machine, main pump revolving speed 55, mention cloth wheel speed 60, nozzle location 90,
60S/ circle, gap 4.
9. a kind of preparation method of the new fabric of three-dimensional big jacquard weave of band-like shorn velvet according to claim 1, which is characterized in that step
Suddenly the formula of pre-treatment auxiliary agent is as follows in (3) dyeing: hydrogen peroxide stabilizer 0.5g/L, closing fibre refining agent 1g/L, is concise
Agent 1g/L, soda ash 8g/L, hydrogen peroxide 10g/L, glacial acetic acid 1.2g/L, catalase 0.3g/L；The formula of after treatment aid: ice
Acetic acid 1.5g/L, detergent 4g/L, glacial acetic acid 0.3g/L, consistent lubricant essence 8g/L.
10. a kind of such as a kind of three-dimensional new fabric of jacquard weave greatly of band-like shorn velvet of any one of claim 1-9 the method preparation.