CN110452022A - A kind of durability degradation of formaldehyde Dali stone ceramic tile and preparation method thereof - Google Patents
A kind of durability degradation of formaldehyde Dali stone ceramic tile and preparation method thereof Download PDFInfo
- Publication number
- CN110452022A CN110452022A CN201910733110.1A CN201910733110A CN110452022A CN 110452022 A CN110452022 A CN 110452022A CN 201910733110 A CN201910733110 A CN 201910733110A CN 110452022 A CN110452022 A CN 110452022A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- formaldehyde
- preparation
- dali
- stone ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of preparation method of durability degradation of formaldehyde Dali stone ceramic tile, include the following steps: that (1) makes marble ceramic tile surface show concaveconvex structure;(2) it is uniformly coated with coating of wax water on marble ceramic tile surface concaveconvex structure, forms solidify coating;(3) waxing equipment is utilized, photocatalyst particle is squeezed into solidify coating, is embedded in photocatalyst particle in solidify coating, is locked on the stone ceramic tile of Dali with the hardening of solidify coating;(4) high-pressure injection equipment is used, the photocatalyst with visible light activity is equably injected on the stone ceramic tile of Dali;(5) solidification will be accelerated through step (4) treated solidify coating using the technique that is heating and curing.The present invention realizes photocatalyst particle with flush type and embedded combination ceramic tile, realizes the durability of degradation of formaldehyde function;Furthermore by the concave-convex physical structure of ceramic tile, photocatalyst particle is more not easy to be worn, and further increases its durability.
Description
Technical field
The present invention relates to degradation of formaldehyde ceramic tile preparation field, especially a kind of durability degradation of formaldehyde Dali stone ceramic tile and its
Preparation method.
Background technique
Currently the research about the degradation of formaldehyde technology of ceramic tile also has much, can substantially be divided into three classes, and one kind is that will have
There are the nano-titanium dioxide of photocatalytic effect or nanometer Zinc oxide powder to be added in glaze to fire together, on this method surface
It is to solve the problems, such as function durability, but can crystal transfer occur after firing due to high temperature and fail, and nano material
Mixing with glaze causes it largely to reunite, also its performance of further loss;It is exactly secondary firing there are also one kind, by the porcelain after firing
The presoma of the uniform titanium dioxide coating in brick surface, then calcining obtains expected crystal form, this method within specified temperatures
Can be obtained the degradation of formaldehyde tile product for having certain effect under ultraviolet light conditions, but this kind of ceramic tile cannot subsequent polishing waxing,
Antifouling and ceramic tile surface effect is all difficult to take into account, simultaneously because needing film and secondary firing, considerably increases production cost;Most
Latter class is directly to coat one layer of photocatalyst before ceramic tile is packaged, and this method operating procedure is simple, will not influence ceramic tile
All other performances, but since ceramic tile is largely wet look, photocatalyst particle can not be firmly bonded on ceramic tile, therefore be lost
The value of actual use.Therefore, these three types of technologies do not realize industrial application in ceramic industry, only reside within experiment
Room conceptual phase.
Summary of the invention
Based on this, a kind of durability degradation is provided it is an object of the invention to overcome above-mentioned the deficiencies in the prior art place
The preparation method of formaldehyde Dali stone ceramic tile.The present invention is directed to the photocatalyst with visible light activity is firmly bonded to marble porcelain
On brick, while not influencing Dali stone ceramic tile original performance, the function of Dali stone ceramic tile degradation of formaldehyde was not only imparted, but also can be real
The durability of this existing function.
To achieve the above object, a kind of the technical solution used in the present invention are as follows: durability degradation of formaldehyde Dali stone ceramic tile
Preparation method, include the following steps:
(1) marble ceramic tile surface is made to show concaveconvex structure;
(2) it is uniformly coated with coating of wax water on marble ceramic tile surface concaveconvex structure, forms solidify coating;
(3) waxing equipment is utilized, photocatalyst particle is squeezed into solidify coating, photocatalyst particle is made to be embedded in solidify coating
In, it is locked on the stone ceramic tile of Dali with the hardening of solidify coating;
(4) high-pressure injection equipment is used, the photocatalyst with visible light activity is equably injected on the stone ceramic tile of Dali;
(5) solidification will be accelerated through step (4) treated solidify coating using the technique that is heating and curing.
Preferably, in the step (1), the concaveconvex structure is micro- concaveconvex structure.
It is highly preferred that the roughness Ra of the concaveconvex structure is 0.05-2 μm.
The associativity and wearability of wax water cure layer and ceramic tile can be improved in above-mentioned roughness.On the one hand wax both can be improved
On the other hand the associativity and wearability of water cure layer and ceramic tile can guarantee that ceramic tile is antifouling up to standard and ceramic tile surface decoration is imitated again
Fruit is unaffected.
Preferably, in the step (1), concaveconvex structure is realized by silk-screen printing, anti-skidding processing.
Preferably, in the step (2), the wax water is slow solidification wax water.Not every wax water is attained by this hair
Obvious results fruit;First, it would be desirable to be able to solidify, second, wax water cure speed is moderate, will not be too fast, nor not solidifying, heating can accelerate
Solidification, third, coating transparency is high after solidification, does not influence ceramic tile surface and feels thoroughly, and the 4th, ceramic tile soil resistance can be promoted, is not influenced
Ceramic tile surface hardness.Slow solidification wax water needs 1-3 days ability completion of cures can be 1 if there is heat treatment under normal circumstances
Or so minute is cured, i.e. heating accelerates its solidification.
Preferably, in the step (2), the wax water includes the ingredient of following parts by weight: 80-85 parts of organic siliconresin,
1-3 parts of curing agent, 5-10 parts of solvent, 5-10 parts of auxiliary agent.The wax water of above-mentioned formula has following excellent performance: 1, solidifying rear defence
Dirt can reach 5 grades;2, ceramic tile surface effect is not influenced after solidifying;3, wearability is good, and conventional waxes water and this wax water are with dry wipe
After scouring, the ceramic tile surface glossiness of conventional waxes water preparation reduces by 30 degree or so, and ceramic tile glossiness prepared by the present invention reduces
2-5 degree.
It is highly preferred that the solvent is D40 solvent naphtha or dehydrated alcohol.
Preferably, in the step (4), the technological parameter of the high-pressure injection equipment are as follows: ceramic tile surface temperature: 45-60
℃;Jet velocity: 50-70g/min;Spray pressure: 0.4-0.5Mpa;Number of nozzle: 1-3;Nozzle diameter: 0.5-1.0mm.
The selection of above-mentioned technique comprehensively considers under comprehensive degradation of formaldehyde efficiency, performance durability and production cost three
Technological parameter optimizes;Ceramic tile surface temperature is in order to which the photocatalyst moisture of injection quickly volatilizees, and photocatalyst particle is preferably tied
Wax water layer is closed, guarantees durability.Jet velocity, injection pressure are the photocatalyst dosages in order to guarantee under degradation of formaldehyde efficiency term
It is minimum;And for promoting the firm connection of photocatalyst particle and ceramic tile surface, guarantee durability.Number of nozzle be in order to
What guarantee ceramic tile surface can all spray arrives, it is ensured that degradation of formaldehyde efficiency.Nozzle diameter is the photocatalyst atomization foot for injection
It is enough thin, photocatalyst dosage can be not only reduced, but also can guarantee degradation of formaldehyde efficiency.
Preferably, in the step (5), the temperature being heating and curing is 200-400 DEG C, the time being heating and curing
For 1-5min.Inventor passes through a large amount of exploration discoveries, and the selection of above-mentioned solidification temperature and time can enable wax water cure layer complete
All solidstate guarantees durability, reaches offline requirement.
Meanwhile the present invention also provides a kind of durability degradation of formaldehyde Dali stone ceramic tiles that the preparation method is prepared.
Compared with the existing technology, the invention has the benefit that
1, present invention process is simple, haves no need to change existing production equipment, only need to add one on existing production line
Cover high-pressure injection equipment and high temperature oven;
2, the present invention solidifies wax water for photocatalyst particle with flush type and embedded combination ceramic tile, when solidification wax water using slow
After hardening, photocatalyst particle is just firmly locked on ceramic tile;
3, the present invention realizes photocatalyst particle with flush type and embedded combination ceramic tile, even if the embedded photocatalyst in surface layer
Be worn consumption in use, and flush type photocatalyst particle can supplement again and again again, realizes degradation of formaldehyde function
Durability;Furthermore by the concave-convex physical structure of ceramic tile, photocatalyst particle is more not easy to be worn, and it is durable to further increase its
Property.
Detailed description of the invention
Fig. 1 is the preparation process route of durability degradation of formaldehyde of the present invention Dali stone ceramic tile;
Fig. 2 is the ceramic tile performance degradation curve of different process preparation.
Specific embodiment
To better illustrate the object, technical solutions and advantages of the present invention, below in conjunction with the drawings and specific embodiments pair
The present invention is described further.
Embodiment 1
A kind of embodiment of durability degradation of formaldehyde of the present invention Dali stone ceramic tile, the degradation of durability described in the present embodiment
Formaldehyde Dali stone ceramic tile is prepared by the following method gained, and specific preparation flow figure is as shown in Fig. 1:
(1) marble ceramic tile surface is made to show micro- concaveconvex structure, the roughness Ra of the concaveconvex structure is 0.05 μm.
This can be obtained with the original technique of production line, such as silk-screen printing, anti-skidding processing;
(2) using slow solidification wax water, one layer of solidify coating in uniform treatment on marble ceramic tile surface concaveconvex structure should
Solidify coating is very good with ceramic tile surface wetability, and coating has excellent anti-pollution after solidification, and furthermore the solidify coating exists
It can accelerate to solidify under heating condition.The table that also there is coating after solidifying simultaneously excellent permeability will not influence Dali stone ceramic tile
Face decorative effect;The wax water includes the ingredient of following parts by weight: 80 parts of organic siliconresin, 1 part of curing agent, solvent (D40 solvent
Oil) 5 parts, 5 parts of auxiliary agent.
(3) waxing equipment is utilized, photocatalyst particle is squeezed into solidify coating, so that photocatalyst function particle is embedded in solidification and applies
In layer, firmly it is locked on the stone ceramic tile of Dali with the hardening of solidify coating.
(4) photocatalyst with visible light activity is equably injected on the stone ceramic tile of Dali using high-pressure injection equipment,
High-pressure injection equipment can be by the strong impact of photocatalyst particle in solidify coating, to reach photocatalyst particle insertion solidify coating
In;The technological parameter of the high-pressure injection equipment are as follows: ceramic tile surface temperature: 45 DEG C;Jet velocity: 50g/min;Spray pressure:
0.4Mpa;Number of nozzle: 3;Nozzle diameter: 0.5.
(5) solidify coating is accelerated to solidify using technique is heating and curing, the temperature being heating and curing is 200 DEG C, is heating and curing
Time be 5min.Since photocatalyst particle is either embedded in solidify coating before or embedded combination is in solidify coating
On, for solidify coating all there are no hardening, being heating and curing in this workshop section is fully hardened by solidify coating at this time, with this by whole light
Catalyst particle is firmly locked in marble ceramic tile surface, and finally sorting is packaged and can dispatch from the factory.
Embodiment 2
A kind of embodiment of durability degradation of formaldehyde of the present invention Dali stone ceramic tile, the degradation of durability described in the present embodiment
Formaldehyde Dali stone ceramic tile is prepared by the following method gained, and specific preparation flow figure is as shown in Fig. 1:
(1) marble ceramic tile surface is made to show micro- concaveconvex structure, the roughness Ra of the concaveconvex structure is 2 μm.This
It is a to be obtained with the original technique of production line, such as silk-screen printing, anti-skidding processing;
(2) using slow solidification wax water, one layer of solidify coating in uniform treatment on marble ceramic tile surface concaveconvex structure should
Solidify coating is very good with ceramic tile surface wetability, and coating has excellent anti-pollution after solidification, and furthermore the solidify coating exists
It can accelerate to solidify under heating condition.The table that also there is coating after solidifying simultaneously excellent permeability will not influence Dali stone ceramic tile
Face decorative effect;The wax water includes the ingredient of following parts by weight: 85 parts of organic siliconresin, 3 parts of curing agent, solvent (anhydrous second
Alcohol) 10 parts, 10 parts of auxiliary agent.
(3) waxing equipment is utilized, photocatalyst particle is squeezed into solidify coating, so that photocatalyst function particle is embedded in solidification and applies
In layer, firmly it is locked on the stone ceramic tile of Dali with the hardening of solidify coating.
(4) photocatalyst with visible light activity is equably injected on the stone ceramic tile of Dali using high-pressure injection equipment,
High-pressure injection equipment can be by the strong impact of photocatalyst particle in solidify coating, to reach photocatalyst particle insertion solidify coating
In;The technological parameter of the high-pressure injection equipment are as follows: ceramic tile surface temperature: 60 DEG C;Jet velocity: 70g/min;Spray pressure:
0.5Mpa;Number of nozzle: 1;Nozzle diameter: 1.0mm.
(5) solidify coating is accelerated to solidify using technique is heating and curing, the temperature being heating and curing is 400 DEG C, is heating and curing
Time be 1min.Since photocatalyst particle is either embedded in solidify coating before or embedded combination is in solidify coating
On, for solidify coating all there are no hardening, being heating and curing in this workshop section is fully hardened by solidify coating at this time, with this by whole light
Catalyst particle is firmly locked in marble ceramic tile surface, and finally sorting is packaged and can dispatch from the factory.
Embodiment 3
A kind of embodiment of durability degradation of formaldehyde of the present invention Dali stone ceramic tile, the degradation of durability described in the present embodiment
Formaldehyde Dali stone ceramic tile is prepared by the following method gained, and specific preparation flow figure is as shown in Fig. 1:
(1) marble ceramic tile surface is made to show micro- concaveconvex structure, the roughness Ra of the concaveconvex structure is 1 μm.This
It is a to be obtained with the original technique of production line, such as silk-screen printing, anti-skidding processing;
(2) using slow solidification wax water, one layer of solidify coating in uniform treatment on marble ceramic tile surface concaveconvex structure should
Solidify coating is very good with ceramic tile surface wetability, and coating has excellent anti-pollution after solidification, and furthermore the solidify coating exists
It can accelerate to solidify under heating condition.The table that also there is coating after solidifying simultaneously excellent permeability will not influence Dali stone ceramic tile
Face decorative effect;The wax water includes the ingredient of following parts by weight: 82 parts of organic siliconresin, 1 part of curing agent, solvent (D40 solvent
Oil or dehydrated alcohol) 6 parts, 7 parts of auxiliary agent.
(3) waxing equipment is utilized, photocatalyst particle is squeezed into solidify coating, so that photocatalyst function particle is embedded in solidification and applies
In layer, firmly it is locked on the stone ceramic tile of Dali with the hardening of solidify coating.
(4) photocatalyst with visible light activity is equably injected on the stone ceramic tile of Dali using high-pressure injection equipment,
High-pressure injection equipment can be by the strong impact of photocatalyst particle in solidify coating, to reach photocatalyst particle insertion solidify coating
In;The technological parameter of the high-pressure injection equipment are as follows: ceramic tile surface temperature: 46 DEG C;Jet velocity: 60g/min;Spray pressure:
0.45Mpa;Number of nozzle: 2;Nozzle diameter: 0.7mm.
(5) solidify coating is accelerated to solidify using technique is heating and curing, the temperature being heating and curing is 300 DEG C, is heating and curing
Time be 4min.Since photocatalyst particle is either embedded in solidify coating before or embedded combination is in solidify coating
On, for solidify coating all there are no hardening, being heating and curing in this workshop section is fully hardened by solidify coating at this time, with this by whole light
Catalyst particle is firmly locked in marble ceramic tile surface, and finally sorting is packaged and can dispatch from the factory.
Compared with prior art, herein described durability degradation of formaldehyde Dali stone ceramic tile and preparation method thereof has following
Advantage:
1, present invention process is simple, haves no need to change existing production equipment, only need to add one on existing production line
Cover high-pressure injection equipment and roller-way baking oven;
2, the present invention solidifies wax water for photocatalyst particle with flush type and embedded combination ceramic tile, when solidification wax water using slow
After hardening, photocatalyst particle is just firmly locked on ceramic tile;
3, the present invention realizes photocatalyst particle with flush type and embedded combination ceramic tile, even if the embedded photocatalyst in surface layer
Be worn consumption in use, and flush type photocatalyst particle can supplement again and again again, realizes degradation of formaldehyde function
Durability;Furthermore by the concave-convex physical structure of ceramic tile, photocatalyst particle is more not easy to be worn, and it is durable to further increase its
Property.
Attached drawing 2 is the degradation of formaldehyde Dali stone ceramic tile performance degradation of the different process preparation after being cleaned several times with dry towel
Curve, as can be known from Fig. 2, the degradation of formaldehyde ceramic tile of other coating processes preparation is substantially without durability, and dry towel is once cleaning
Without, and present invention degradation of formaldehyde performance after cleaning 10000 times also maintains 60% or so, and later period attenuation rate is basic
It is constant, excellent durability.
Finally, it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention rather than protects to the present invention
The limitation of range is protected, although the invention is described in detail with reference to the preferred embodiments, those skilled in the art should
Understand, it can be with modification or equivalent replacement of the technical solution of the present invention are made, without departing from the essence of technical solution of the present invention
And range.
Claims (9)
1. a kind of preparation method of durability degradation of formaldehyde Dali stone ceramic tile, which comprises the steps of:
(1) marble ceramic tile surface is made to show concaveconvex structure;
(2) it is uniformly coated with coating of wax water on marble ceramic tile surface concaveconvex structure, forms solidify coating;
(3) waxing equipment is utilized, photocatalyst particle is squeezed into solidify coating, is embedded in photocatalyst particle in solidify coating, with
The hardening of solidify coating and be locked on the stone ceramic tile of Dali;
(4) high-pressure injection equipment is used, the photocatalyst with visible light activity is equably injected on the stone ceramic tile of Dali;
(5) solidification will be accelerated through step (4) treated solidify coating using the technique that is heating and curing.
2. the preparation method of durability degradation of formaldehyde as described in claim 1 Dali stone ceramic tile, which is characterized in that the step
(1) in, the concaveconvex structure is micro- concaveconvex structure.
3. the preparation method of durability degradation of formaldehyde as claimed in claim 2 Dali stone ceramic tile, which is characterized in that the bumps
The roughness Ra of structure is 0.05-2 μm.
4. the preparation method of durability degradation of formaldehyde as described in claim 1 Dali stone ceramic tile, which is characterized in that the step
(1) in, concaveconvex structure is realized by silk-screen printing, anti-skidding processing.
5. the preparation method of durability degradation of formaldehyde as described in claim 1 Dali stone ceramic tile, which is characterized in that the step
(2) in, the wax water include following parts by weight ingredient: 80-85 parts of organic siliconresin, 1-3 parts of curing agent, 5-10 parts of solvent,
5-10 parts of auxiliary agent.
6. the preparation method of durability degradation of formaldehyde as claimed in claim 5 Dali stone ceramic tile, which is characterized in that the solvent
For D40 solvent naphtha or dehydrated alcohol.
7. the preparation method of durability degradation of formaldehyde as described in claim 1 Dali stone ceramic tile, which is characterized in that the step
(4) in, the technological parameter of the high-pressure injection equipment are as follows: ceramic tile surface temperature: 45-60 DEG C;Jet velocity: 50-70g/min;
Spray pressure: 0.4-0.5Mpa;Number of nozzle: 1-3;Nozzle diameter: 0.5-1.0mm.
8. the preparation method of durability degradation of formaldehyde as described in claim 1 Dali stone ceramic tile, which is characterized in that the step
(5) in, the temperature being heating and curing is 200-400 DEG C, and the time being heating and curing is 1-5min.
9. a kind of durability degradation of formaldehyde Dali stone ceramic tile being prepared by any one of claim 1~8 preparation method.