CN110359157A - 一种具有抗皱保健的面料的制备方法 - Google Patents
一种具有抗皱保健的面料的制备方法 Download PDFInfo
- Publication number
- CN110359157A CN110359157A CN201910497789.9A CN201910497789A CN110359157A CN 110359157 A CN110359157 A CN 110359157A CN 201910497789 A CN201910497789 A CN 201910497789A CN 110359157 A CN110359157 A CN 110359157A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- fabric
- crease
- health care
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本案公开了一种具有抗皱保健的面料的制备方法,包括下述步骤:使坯布浸轧抗皱保健处理液,得到抗皱保健面料;坯布由下述重量份的原料混纺织造而成:棉纤维60~70重量份;香蕉纤维25~30重量份;莫代尔纤维3~6重量份。本发明的面料,使坯布浸轧抗皱保健处理液,得到抗皱保健面料;抗皱保健处理液中有机硅改性聚氨酯树脂作为坯布的固着性物质,在高温作用下,分子链段被锚牢在的坯布表面,提高表面抗皱性能;丁二醇单硬脂酸酯提高面料的具有滋润皮肤和抗静电作用;四氟丙烯提高有机硅改性聚氨酯树脂与纤维的联结性能;二氧化钛提高面料的抗皱保健性能;通过加入海藻酸钠提高抗皱保健处理液在坯布中的渗透性。
Description
技术领域
本发明涉及一种面料,特别是涉及一种具有抗皱保健的面料的制备方法。
背景技术
随着人们生活水平的不断提高以及科学技术的不断发展,满足人们不同需要的纺织品面料层出不穷,人们对服装性能的要求也不断提高,面料的表面抗皱性能、手感柔和度以及穿着舒适度越来越受到人们的关注。但是,部分面料加工而成的衣服清洗晾干后会出现褶皱,影响下次穿着的美观性,近年出现的抗皱面料舒适感差,且抗皱性能也有待进一步提高。
发明内容
针对上述不足之处,本发明的目的在于提供一种具备抗皱保健面料及其制备方法。
本发明的技术方案概述如下:
一种具有抗皱保健的面料的制备方法,其中,包括下述步骤:使坯布浸轧抗皱保健处理液,得到所述抗皱保健面料;所述坯布由下述重量份的原料混纺织造而成:
棉纤维 60~70重量份;
香蕉纤维 25~30重量份;
莫代尔纤维 3~6重量份。
优选的是,所述的具有抗皱保健的面料的制备方法,其中,还包括4~7重量份的大豆蛋白复合纤维。
优选的是,所述的具有抗皱保健的面料的制备方法,其中,还包括5~8重量份的聚氨酯弹性纤维。
优选的是,所述的具有抗皱保健的面料的制备方法,其中,还包括6~12重量份的菠萝纤维。
优选的是,所述的具有抗皱保健的面料的制备方法,其中,所述抗皱保健处理液由下述重量份的组分组成:
有机硅改性聚氨酯树脂 5~7重量份;
丁二醇单硬脂酸酯 6~10重量份;
四氟丙烯 1~3重量份;
二氧化钛 2~4重量份;
海藻酸钠 0.5~1重量份;
芦荟提取物 1~3重量份
环糊精 0.5~1重量份;
乙醇 6~10重量份。
优选的是,所述的具有抗皱保健的面料的制备方法,其中,还包括1~3重量份的甲基乙烯基硅油。
优选的是,所述的具有抗皱保健的面料的制备方法,其中,还包括1~3重量份的水杨酸己酯。
优选的是,所述的具有抗皱保健的面料的制备方法,其中,还包括1~3重量份的γ―(2,3-环氧丙氧) 丙基三甲氧基硅烷。
优选的是,所述的具有抗皱保健的面料的制备方法,其中,所述浸轧的具体操作如下:将所述抗皱保健处理液通过浸轧的方法施加到所述坯布上,得到浸轧有抗皱保健处理液的坯布,再进行焙烘,得到所述抗皱保健效果的面料。
优选的是,所述的具有抗皱保健的面料的制备方法,其中,所述坯布与所述抗皱保健处理液的质量比为100:4-6;所述浸轧的方式为一浸一轧。
本发明的有益效果是:本发明的面料,使坯布浸轧抗皱保健处理液,得到抗皱保健面料;抗皱保健处理液中有机硅改性聚氨酯树脂作为坯布的固着性物质,在高温作用下,分子链段被锚牢在的坯布表面,提高表面抗皱性能;丁二醇单硬脂酸酯提高面料的具有滋润皮肤和抗静电作用;四氟丙烯提高有机硅改性聚氨酯树脂与纤维的联结性能;二氧化钛提高面料的抗皱保健性能;通过加入海藻酸钠提高抗皱保健处理液在坯布中的渗透性;环糊精进一步改善面料的保健效果;芦荟提取物改善面料的美肤抗菌保健效果;通过加入甲基乙烯基硅油提高坯布的柔软性能,提高面料的穿着舒适性能;水杨酸己酯进一步提高坯布的浸轧性能;通过加入γ―(2,3-环氧丙氧) 丙基三甲氧基硅烷改善二氧化钛与有机硅改性聚氨酯树脂的相容性能。
具体实施方式
下面结合实施例对本发明做进一步的详细说明,以令本领域技术人员参照说明书文字能够据以实施。
本发明提供一种具有抗皱保健的面料的制备方法,包括下述步骤:使坯布浸轧抗皱保健处理液,得到抗皱保健面料;坯布由下述重量份的原料混纺织造而成:
棉纤维 60~70重量份;
香蕉纤维 25~30重量份;
莫代尔纤维 3~6重量份。
棉纤维是多孔性物质,且其纤维素大分子上存在许多亲水性基团(-OH),所以其吸湿性较好,一般大气条件下,棉纤维的回潮率可达8.5%左右;由于棉纤维的主要组成物质是纤维素,所以它较耐碱而不耐酸;烧碱可使棉纤维剧烈膨化,直径变大,长度缩短,以致引起棉制品的强烈收缩。此时,若施加张力,限制其收缩,棉制品表面会变得平整光亮且大大改善染色性能,此加工称为丝光;若不加张力任其收缩,称为碱缩。针织物经碱缩后会变得紧密而富有弹性,而且保形性好。酸能使棉纤维强度变差,尤其是强酸浓酸应忌用,它可溶于70%以上浓硫酸中,浓盐酸、浓硝酸对其强度也有严重影响; 香蕉纤维是利用香蕉茎杆为原料,主要是由纤维素、半纤维素和木质素组成,化学脱胶后的纤维可用于棉纺。采用生物酶和化学氧化联合处理工艺处理,经过干燥、精练、解纤而制成的纤维,其具有质量轻、光泽好、吸水性高、抗菌性强、易降解且环保等功能;莫代尔纤维改善面料的柔软度,悬垂感,光泽和吸湿性。
作为本案又一实施例,其中,还包括4~7重量份的大豆蛋白复合纤维。该纤维单丝纤度细、比重轻、强伸度较高、耐酸耐碱性较好,具有羊绒般的柔软手感、蚕丝般的优雅光泽、棉纤维的吸湿和导湿性及穿着舒适性,可提高面料的抗皱性能。
作为本案又一实施例,其中,还包括5~8重量份的聚氨酯弹性纤维。通过加入聚氨酯弹性纤维改善面料的弹性,提高抗皱性能。
作为本案又一实施例,其中,还包括6~12重量份的菠萝纤维。通过加入菠萝纤维改善面料的吸汗透气,挺括不起皱,穿着舒适性能。
作为本案又一实施例,其中,抗皱保健处理液由下述重量份的组分组成:
有机硅改性聚氨酯树脂 5~7重量份;
丁二醇单硬脂酸酯 6~10重量份;
四氟丙烯 1~3重量份;
二氧化钛 2~4重量份;
海藻酸钠 0.5~1重量份;
芦荟提取物 1~3重量份
环糊精 0.5~1重量份;
乙醇 6~10重量份。
有机硅改性聚氨酯树脂作为坯布的固着性物质,在高温作用下,分子链段被锚牢在的坯布表面,提高表面抗皱性能;丁二醇单硬脂酸酯提高面料的具有滋润皮肤和抗静电作用;四氟丙烯提高有机硅改性聚氨酯树脂与纤维的联结性能;二氧化钛提高面料的抗皱保健性能;海藻酸钠具有良好的扩散性,通过加入海藻酸钠提高抗皱保健处理液在坯布中的渗透性;环糊精进一步改善面料的保健抗皱效果;芦荟提取物改善面料的美肤抗菌保健效果。
作为本案又一实施例,其中,还包括1~3重量份的甲基乙烯基硅油。通过加入甲基乙烯基硅油提高坯布的柔软性能,提高面料的穿着舒适性能和抗皱效果。
作为本案又一实施例,其中,还包括1~3重量份的水杨酸己酯。水杨酸己酯进一步提高坯布的浸轧性能。
作为本案又一实施例,其中,还包括1~3重量份的γ―(2,3-环氧丙氧) 丙基三甲氧基硅烷。通过加入γ―(2,3-环氧丙氧) 丙基三甲氧基硅烷改善二氧化钛与有机硅改性聚氨酯树脂的相容性能。
作为本案又一实施例,其中,浸轧的具体操作如下:将所述抗皱保健处理液通过浸轧的方法施加到所述坯布上,得到浸轧有抗皱保健处理液的坯布,再进行焙烘,得到所述抗皱保健效果的面料。
作为本案又一实施例,其中,坯布与所述抗皱保健处理液的质量比为100:4-6;所述浸轧的方式为一浸一轧。
下面列出具体的实施例和对比例:
实施例1:
一种具有抗皱保健的面料的制备方法,包括下述步骤:使坯布浸轧抗皱保健处理液,得到抗皱保健面料;坯布由下述重量份的原料混纺织造而成:
棉纤维 60重量份;
香蕉纤维 25重量份;
莫代尔纤维 3重量份。
大豆蛋白复合纤维 4重量份;
聚氨酯弹性纤维 5重量份;
菠萝纤维 6重量份;
抗皱保健处理液由下述重量份的组分组成:
有机硅改性聚氨酯树脂 5重量份;
丁二醇单硬脂酸酯 6重量份;
四氟丙烯 1重量份;
二氧化钛 2重量份;
海藻酸钠 0.5重量份;
芦荟提取物 1重量份
环糊精 0.5重量份;
乙醇 6重量份;
甲基乙烯基硅油 1重量份;
水杨酸己酯 1重量份;
γ―(2,3-环氧丙氧) 丙基三甲氧基硅烷 1重量份;
浸轧的具体操作如下:将所述抗皱保健处理液通过浸轧的方法施加到坯布上,得到浸轧有抗皱保健处理液的坯布,坯布与抗皱保健处理液的质量比为100:4;浸轧的方式为一浸一轧,再进行焙烘,得到抗皱保健效果的面料,烘干的温度为120℃,时间为2分钟;焙烘的温度为150℃,时间为5 分钟。
实施例2:
一种具有抗皱保健的面料的制备方法,包括下述步骤:使坯布浸轧抗皱保健处理液,得到所述抗皱保健面料;所述坯布由下述重量份的原料混纺织造而成:
棉纤维 62重量份;
香蕉纤维 28重量份;
莫代尔纤维 4重量份;
大豆蛋白复合纤维 5重量份;
聚氨酯弹性纤维 6重量份;
菠萝纤维 10重量份;
抗皱保健处理液由下述重量份的组分组成:
有机硅改性聚氨酯树脂 6重量份;
丁二醇单硬脂酸酯 9重量份;
四氟丙烯 2重量份;
二氧化钛 3重量份;
海藻酸钠 0.6重量份;
芦荟提取物 2重量份
环糊精 0.8重量份;
乙醇 9重量份;
甲基乙烯基硅油 2重量份;
水杨酸己酯 2重量份;
γ―(2,3-环氧丙氧) 丙基三甲氧基硅烷 2重量份;
浸轧的具体操作如下:将抗皱保健处理液通过浸轧的方法施加到坯布上,得到浸轧有抗皱保健处理液的坯布,坯布与抗皱保健处理液的质量比为100:5;浸轧的方式为一浸一轧,再进行焙烘,得到抗皱保健效果的面料,烘干的温度为120℃,时间为2分钟;焙烘的温度为150℃,时间为5 分钟。
实施例3:
一种具有抗皱保健的面料的制备方法,包括下述步骤:使坯布浸轧抗皱保健处理液,得到抗皱保健面料;坯布由下述重量份的原料混纺织造而成:
棉纤维 70重量份;
香蕉纤维 30重量份;
莫代尔纤维 6重量份;
大豆蛋白复合纤维 7重量份;
聚氨酯弹性纤维 8重量份;
菠萝纤维 12重量份;
抗皱保健处理液由下述重量份的组分组成:
有机硅改性聚氨酯树脂 7重量份;
丁二醇单硬脂酸酯 10重量份;
四氟丙烯 3重量份;
二氧化钛 4重量份;
海藻酸钠 1重量份;
芦荟提取物 3重量份
环糊精 1重量份;
乙醇 10重量份。
甲基乙烯基硅油 3重量份;
水杨酸己酯 3重量份;
γ―(2,3-环氧丙氧) 丙基三甲氧基硅烷 3重量份;
浸轧的具体操作如下:将抗皱保健处理液通过浸轧的方法施加到坯布上,得到浸轧有抗皱保健处理液的坯布,坯布与抗皱保健处理液的质量比为100:6;浸轧的方式为一浸一轧,再进行焙烘,得到抗皱保健效果的面料,烘干的温度为120℃,时间为2分钟;焙烘的温度为150℃,时间为5 分钟。
对比例1:
一种具有抗皱保健的面料的制备方法,包括下述步骤:使坯布浸轧抗皱保健处理液,得到抗皱保健面料;坯布由下述重量份的原料混纺织造而成:
棉纤维 60重量份;
莫代尔纤维 3重量份。
大豆蛋白复合纤维 4重量份;
聚氨酯弹性纤维 5重量份;
菠萝纤维 6重量份;
抗皱保健处理液由下述重量份的组分组成:
有机硅改性聚氨酯树脂 5重量份;
丁二醇单硬脂酸酯 6重量份;
四氟丙烯 1重量份;
二氧化钛 2重量份;
海藻酸钠 0.5重量份;
芦荟提取物 1重量份
环糊精 0.5重量份;
乙醇 6重量份;
甲基乙烯基硅油 1重量份;
水杨酸己酯 1重量份;
γ―(2,3-环氧丙氧) 丙基三甲氧基硅烷 1重量份;
浸轧的具体操作如下:将所述抗皱保健处理液通过浸轧的方法施加到坯布上,得到浸轧有抗皱保健处理液的坯布,坯布与抗皱保健处理液的质量比为100:4;浸轧的方式为一浸一轧,再进行焙烘,得到抗皱保健效果的面料,烘干的温度为120℃,时间为2分钟;焙烘的温度为150℃,时间为5 分钟。
对比例2:
一种具有抗皱保健的面料的制备方法,包括下述步骤:使坯布浸轧抗皱保健处理液,得到抗皱保健面料;坯布由下述重量份的原料混纺织造而成:
棉纤维 60重量份;
香蕉纤维 25重量份;
莫代尔纤维 3重量份。
大豆蛋白复合纤维 4重量份;
菠萝纤维 6重量份;
抗皱保健处理液由下述重量份的组分组成:
有机硅改性聚氨酯树脂 5重量份;
丁二醇单硬脂酸酯 6重量份;
四氟丙烯 1重量份;
二氧化钛 2重量份;
海藻酸钠 0.5重量份;
芦荟提取物 1重量份
环糊精 0.5重量份;
乙醇 6重量份;
甲基乙烯基硅油 1重量份;
水杨酸己酯 1重量份;
γ―(2,3-环氧丙氧) 丙基三甲氧基硅烷 1重量份;
浸轧的具体操作如下:将所述抗皱保健处理液通过浸轧的方法施加到坯布上,得到浸轧有抗皱保健处理液的坯布,坯布与抗皱保健处理液的质量比为100:4;浸轧的方式为一浸一轧,再进行焙烘,得到抗皱保健效果的面料,烘干的温度为120℃,时间为2分钟;焙烘的温度为150℃,时间为5 分钟。
对比例3:
一种具有抗皱保健的面料的制备方法,包括下述步骤:使坯布浸轧抗皱保健处理液,得到所述抗皱保健面料;所述坯布由下述重量份的原料混纺织造而成:
棉纤维 62重量份;
香蕉纤维 28重量份;
莫代尔纤维 4重量份;
大豆蛋白复合纤维 5重量份;
聚氨酯弹性纤维 6重量份;
抗皱保健处理液由下述重量份的组分组成:
有机硅改性聚氨酯树脂 6重量份;
丁二醇单硬脂酸酯 9重量份;
四氟丙烯 2重量份;
二氧化钛 3重量份;
海藻酸钠 0.6重量份;
芦荟提取物 2重量份
环糊精 0.8重量份;
乙醇 9重量份;
甲基乙烯基硅油 2重量份;
水杨酸己酯 2重量份;
γ―(2,3-环氧丙氧) 丙基三甲氧基硅烷 2重量份;
浸轧的具体操作如下:将抗皱保健处理液通过浸轧的方法施加到坯布上,得到浸轧有抗皱保健处理液的坯布,坯布与抗皱保健处理液的质量比为100:5;浸轧的方式为一浸一轧,再进行焙烘,得到抗皱保健效果的面料,烘干的温度为120℃,时间为2分钟;焙烘的温度为150℃,时间为5 分钟。
对比例4:
一种具有抗皱保健的面料的制备方法,包括下述步骤:使坯布浸轧抗皱保健处理液,得到所述抗皱保健面料;所述坯布由下述重量份的原料混纺织造而成:
棉纤维 62重量份;
香蕉纤维 28重量份;
莫代尔纤维 4重量份;
大豆蛋白复合纤维 5重量份;
聚氨酯弹性纤维 6重量份;
菠萝纤维 10重量份;
抗皱保健处理液由下述重量份的组分组成:
有机硅改性聚氨酯树脂 6重量份;
丁二醇单硬脂酸酯 9重量份;
二氧化钛 3重量份;
海藻酸钠 0.6重量份;
芦荟提取物 2重量份
环糊精 0.8重量份;
乙醇 9重量份;
甲基乙烯基硅油 2重量份;
水杨酸己酯 2重量份;
γ―(2,3-环氧丙氧) 丙基三甲氧基硅烷 2重量份;
浸轧的具体操作如下:将抗皱保健处理液通过浸轧的方法施加到坯布上,得到浸轧有抗皱保健处理液的坯布,坯布与抗皱保健处理液的质量比为100:5;浸轧的方式为一浸一轧,再进行焙烘,得到抗皱保健效果的面料,烘干的温度为120℃,时间为2分钟;焙烘的温度为150℃,时间为5 分钟。
对比例5:
一种具有抗皱保健的面料的制备方法,包括下述步骤:使坯布浸轧抗皱保健处理液,得到抗皱保健面料;坯布由下述重量份的原料混纺织造而成:
棉纤维 70重量份;
香蕉纤维 30重量份;
莫代尔纤维 6重量份;
大豆蛋白复合纤维 7重量份;
聚氨酯弹性纤维 8重量份;
菠萝纤维 12重量份;
抗皱保健处理液由下述重量份的组分组成:
有机硅改性聚氨酯树脂 7重量份;
丁二醇单硬脂酸酯 10重量份;
四氟丙烯 3重量份;
海藻酸钠 1重量份;
芦荟提取物 3重量份;
环糊精 1重量份;
乙醇 10重量份;
甲基乙烯基硅油 3重量份;
水杨酸己酯 3重量份;
γ―(2,3-环氧丙氧) 丙基三甲氧基硅烷 3重量份;
浸轧的具体操作如下:将抗皱保健处理液通过浸轧的方法施加到坯布上,得到浸轧有抗皱保健处理液的坯布,坯布与抗皱保健处理液的质量比为100:6;浸轧的方式为一浸一轧,再进行焙烘,得到抗皱保健效果的面料,烘干的温度为120℃,时间为2分钟;焙烘的温度为150℃,时间为5 分钟。
对比例6:
一种具有抗皱保健的面料的制备方法,包括下述步骤:使坯布浸轧抗皱保健处理液,得到抗皱保健面料;坯布由下述重量份的原料混纺织造而成:
棉纤维 70重量份;
香蕉纤维 30重量份;
莫代尔纤维 6重量份;
大豆蛋白复合纤维 7重量份;
聚氨酯弹性纤维 8重量份;
菠萝纤维 12重量份;
抗皱保健处理液由下述重量份的组分组成:
有机硅改性聚氨酯树脂 7重量份;
丁二醇单硬脂酸酯 10重量份;
四氟丙烯 3重量份;
二氧化钛 4重量份;
海藻酸钠 1重量份;
芦荟提取物 3重量份;
乙醇 10重量份;
甲基乙烯基硅油 3重量份;
水杨酸己酯 3重量份;
γ―(2,3-环氧丙氧) 丙基三甲氧基硅烷 3重量份;
浸轧的具体操作如下:将抗皱保健处理液通过浸轧的方法施加到坯布上,得到浸轧有抗皱保健处理液的坯布,坯布与抗皱保健处理液的质量比为100:6;浸轧的方式为一浸一轧,再进行焙烘,得到抗皱保健效果的面料,烘干的温度为120℃,时间为2分钟;焙烘的温度为150℃,时间为5 分钟。
实施例1~3和对比例1~6的面料抗菌性能评价:参考GB/T 15979-2002方法测试。
下面列出实施例和对比例的性能测试结果:
实施例1 | 实施例2 | 实施例3 | 对比例1 | 对比例2 | 对比例3 | 对比例4 | 对比例5 | 对比例6 | |
强力保留率/% | 82 | 85 | 86 | 88 | 97 | 93 | 62 | 98 | 90 |
褶皱回复角/° | 247 | 251 | 242 | 221 | 206 | 216 | 208 | 191 | 237 |
由表1中的测试数据可知,实施例1~3与对比例1~6相比,抗皱性能较好,因此可以更好的应用于对纺织品要求抗皱领域。
尽管本发明的实施方案已公开如上,但其并不仅仅限于说明书和实施方式中所列运用,它完全可以被适用于各种适合本发明的领域,对于熟悉本领域的人员而言,可容易地实现另外的修改,因此在不背离权利要求及等同范围所限定的一般概念下,本发明并不限于特定的细节。
Claims (10)
1.一种具有抗皱保健的面料的制备方法,其特征在于,包括下述步骤:使坯布浸轧抗皱保健处理液,得到所述抗皱保健面料;所述坯布由下述重量份的原料混纺织造而成:
棉纤维 60~70重量份;
香蕉纤维 25~30重量份;
莫代尔纤维 3~6重量份。
2.根据权利要求1所述的具有抗皱保健的面料的制备方法,其特征在于,还包括4~7重量份的大豆蛋白复合纤维。
3.根据权利要求1所述的具有抗皱保健的面料的制备方法,其特征在于,还包括5~8重量份的聚氨酯弹性纤维。
4.根据权利要求1所述的具有抗皱保健的面料的制备方法,其特征在于,还包括6~12重量份的菠萝纤维。
5.根据权利要求1所述的具有抗皱保健的面料的制备方法,其特征在于,所述抗皱保健处理液由下述重量份的组分组成:
有机硅改性聚氨酯树脂 5~7重量份;
丁二醇单硬脂酸酯 6~10重量份;
四氟丙烯 1~3重量份;
二氧化钛 2~4重量份;
海藻酸钠 0.5~1重量份;
芦荟提取物 1~3重量份
环糊精 0.5~1重量份;
乙醇 6~10重量份。
6.根据权利要求5所述的具有抗皱保健的面料的制备方法,其特征在于,还包括1~3重量份的甲基乙烯基硅油。
7.根据权利要求5所述的具有抗皱保健的面料的制备方法,其特征在于,还包括1~3重量份的水杨酸己酯。
8.根据权利要求5所述的具有抗皱保健的面料的制备方法,其特征在于,还包括1~3重量份的γ―(2,3-环氧丙氧) 丙基三甲氧基硅烷。
9.根据权利要求1所述的具有抗皱保健的面料的制备方法,其特征在于,所述浸轧的具体操作如下:将所述抗皱保健处理液通过浸轧的方法施加到所述坯布上,得到浸轧有抗皱保健处理液的坯布,再进行焙烘,得到所述抗皱保健效果的面料。
10.根据权利要求9所述的具有抗皱保健的面料的制备方法,其特征在于,所述坯布与所述抗皱保健处理液的质量比为100:4-6;所述浸轧的方式为一浸一轧。