CN110295440A - The preparation method of soft clean yarn fabric for home textile - Google Patents
The preparation method of soft clean yarn fabric for home textile Download PDFInfo
- Publication number
- CN110295440A CN110295440A CN201810247912.7A CN201810247912A CN110295440A CN 110295440 A CN110295440 A CN 110295440A CN 201810247912 A CN201810247912 A CN 201810247912A CN 110295440 A CN110295440 A CN 110295440A
- Authority
- CN
- China
- Prior art keywords
- fiber
- soft clean
- fabric
- yarn
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is a kind of preparation method of soft clean yarn fabric for home textile.It includes the following steps: 1) to carry out mercerising anti-shrinking to wool；To flax fiber, 48h carries out fiber softening processing before spinning；2) it is mixed again with flax fiber item after being mixed wool with cotton fiber packet by cotton spinning machine, obtains composite fibre；Wherein, by mass percentage wool 10% ~ 15%, cotton fiber 60% ~ 70%, flax fiber 20% ~ 25%；3) successively to composite fibre carry out opening picking, cotton carding, it is mixed simultaneously, rove, spun yarn, obtain soft clean yarn；4) soft clean yarn is carried out longitude and latitude to interweave with forming fabric: soft clean yarn is by automatic winder winder, and fixed length and fault are removed while winder, reduces thickness section；Then warping, sizing and axis, leasing, gait denting and weaving are successively carried out；5): dyeing and finishing: carrying out processing of singing to fabric with weak fire, then successively desizing, bleaching, dye, soap, preshrunk, thermal finalization.
Description
Technical field
The present invention relates to the preparation methods of a kind of textile fabric, especially disclose a kind of soft clean yarn fabric for home textile
Preparation method.
Background technique
Soft clean spinning is that one kind carries out humid heat treatment to fiber in common ring spinning spinning frame, improves fiber spinnability
And the technology of yarn qualities.Flax fiber has the function of temperature adjustment, antiallergy, antistatic, antibacterial etc., referred to as " plant fiber emperor
Afterwards ", it but due to its bigger, wiriness of rigidity, is not easy to be twisted together, resultant yarn filoplume is more, and being in spin on fails to be transported extensively
With.Wool fiber is soft, warmth retention property is splendid, but the curling of fiber height, high resiliency, and fiber easily rebounds and is detached from and adds during resultant yarn
Rob the control of take-up force, the easily exposed formation Yarn filoplume of few fibers head end.
Although soft clean spinning technique reaches its maturity, the home textile product of soft clean yarn is without many currently on the market.
Summary of the invention
It is an object of the invention to overcome defect existing in the prior art, provide that a kind of Yarn filoplume prepared is few, light
Cleanliness is good, yarn evenness is uniform and intensity is good, the system of the good soft clean yarn fabric for home textile of the pilling resistance of fabric
Preparation Method.
The present invention is implemented as follows: a kind of preparation method of the soft clean yarn fabric for home textile, it is characterised in that: packet
Include following steps:
Step 1: mercerising anti-shrinking is carried out to wool；To flax fiber, 48h carries out fiber softening processing before spinning；
Step 2: being mixed again with flax fiber item after being mixed wool with cotton fiber packet by cotton spinning machine, obtain composite fibre；Wherein, it presses
Mass percentage wool 10% ~ 15%, cotton fiber 60% ~ 70%, flax fiber 20% ~ 25%；
Step 3: successively to step 2 gained composite fibre carry out opening picking, cotton carding, it is mixed simultaneously, rove, spun yarn, obtain soft clean spinning
Line；The wet place of heat wherein is carried out to the hot humidizer that composite fibre sprinkling dosage is (mass percentage) 2.7% during rove
Reason, the temperature of hot humidizer are 25 ~ 28 DEG C；
Step 4: the resulting soft clean yarn of step 3 is carried out longitude and latitude and interweaves with forming fabric: soft clean yarn passes through automatic winding
Machine winder, fixed length and fault are removed while winder, reduce thickness section；Then warping, sizing and axis are successively carried out, leasing, is worn
Comprehensive denting and weaving；Wherein the rate of sizing of sizing is 10% ~ 18%；
Step 5: dyeing and finishing: processing of singing being carried out to step 4 gained fabric with weak fire, then carries out desizing treatment；Then successively into
Row bleaching, dyeing, dyestuff when dyeing is bifunctionalreactive dyes, passes through two bath process；Then it is soaped with ammonium hydroxide,
Finally carry out preshrunk, thermal finalization.
Preferably, the processing of fiber softening described in step 1 is to flax fiber sprinkling finishing auxiliaries, the dosage of finishing auxiliaries
(mass percentage) is 1%-3%.
In step 4, in winder, the tension of soft clean yarn is controlled in 1500 ~ 1800N；
In step 4, the slurry of the sizing is starch or modified starch size.
In step 5, during desizing treatment, by the way that the softening agent that dosage is (mass percentage) 0.5% ~ 1% is added
Relaxation processes are carried out to fabric.
The beneficial effects of the present invention are: the present invention can be spun, number is relatively high, any surface finish, and filoplume is less, strongly compares
High yarn, yarn qualities are relatively good, and the wearability of fabric, pilling resistance are relatively good.Resulting fabric has after intertexture
Certain antibiotic property, warmth retention property, electrostatic is small, comfort is good, is used for home textile product, meets people at present to home textile product high-quality
Requirement.In addition, flax, cotton are all natural plant fibre, wool is animal origin, the synthetic fibers such as opposite chemical fibre, comparison operators
Close the requirement of sustainable development.
Specific embodiment
Preparation method of the present invention for the soft clean yarn fabric of home textile, includes the following steps:
Step 1: mercerising anti-shrinking is carried out to wool；To flax fiber, 48h carries out fiber softening processing before spinning；The fiber
Sofening treatment is that finishing auxiliaries are sprayed to flax fiber, and the dosage of finishing auxiliaries is 1%-3%.
Step 2: being mixed again with flax fiber item after being mixed wool with cotton fiber packet by cotton spinning machine, obtain composite fibre；Its
In, by mass percentage wool 10% ~ 15%, cotton fiber 60% ~ 70%, flax fiber 20% ~ 25%；It is preferred that wool 10%, cotton are fine
Tie up 70%, flax fiber 20%.
Step 3: successively to step 2 gained composite fibre carry out opening picking, cotton carding, it is mixed simultaneously, rove, spun yarn, obtain soft clean
Yarn；Heat wherein is carried out to the hot humidizer that composite fibre sprinkling dosage is (mass percentage) 2.7% during rove
Wet process, the temperature of hot humidizer are 25 ~ 28 DEG C, preferably 25 DEG C；
In step 3, the process of the opening picking, cotton carding are as follows:
Mix with flax fiber item again after packet is mixed using cotton and hair.
The opening and cleaning step of cotton wool use " it is thin feed, grab less, it is diligent grab, more pines, tip-tap, with comb for beat, jogging speed, big channel "
Principle, disc bale plucker hired roughneck declines 3mm every time, and small turning insert stretches out rib 3mm, accomplishes that diligent grab is grabbed less, keeps fiber abundant
Shredding changes porcupine hired roughneck into kirschner beater, and damage of the reduction of income to wool fiber increases the removal of impurities to cotton fiber.Two kinds of fibers
Cotton rolling quantity is 350g/m, the long 30m of cotton roll, roller revolving speed 10r/min, 500 r/min of kirschner beater speed.When cotton carding, by
It is crimped in wool fiber, be easy to cause cylinder around flower, 800 r/min of licker-in revolving speed, 310 r/min of cylinder revolving speed, doffing speed
18 r/min.Cover board linear velocity 169mm/min carries out combing.
Flax fiber 48h before spinning needs to spray a certain amount of finishing auxiliaries and carries out fiber softening, opening or cleaning follow " it is thin feed,
Grab less, diligent grab, is more pines, tip-tap, caducous " principle, lap roller revolving speed 12r/min, 540 r/min of kirschner beater speed.It is right
Carding device does some adjustment, cylinder, doffer needle cloth be " principle of readjustment, restructuring, consolidation and improvement, low close, small operating angle " convenient for flax fiber combing, turn
It moves, 700 r/min of licker-in revolving speed, 300 r/min of cylinder revolving speed, 15 r/min of doffing speed.
The mixed process simultaneously are as follows: using three and close, be sufficiently mixed.Roller gauge 7*8*15mm is mentioned using along drawing-off
Crotch straightening out effect before high microsteping, it is ensured that be uniformly mixed, relative humidity 65%-70%.
The process of the rove are as follows: using pressurization, the big twist again, reduce the misdraft generated when unwinding.Regular roving feeding
For 5.55g/10m, roving twist factor is set to 70,.Roving yarn quality control requires: Unevenness CV %≤4, weight unevenness≤1%.
The process of the spun yarn are as follows: use " big gauge, high twist factor, low velocity, small tension receiving coil " principle, reduce yarn hair
Plumage improves yarn quality.Ingot speed 15000r/min, twist factor 330, front roller speed 196 r/min, roller gauge 18*30mm.
The heat and wet treatment makes composite fibre under the wet synergy of heat, and bending modulus and rigidity moment are greatly lowered,
Softening speed and degree greatly improve, and realize that thicker composite fibre carries out flexible twisting in lower modulus, more Low rigidity performance
Resultant yarn causes composite fibre head end to be easier to shift and wind under twisting twisting resistance effect, is finally twisted into yarn body or patch volt exists
Sliver surface effectively eliminates resultant yarn filoplume, significantly improves the finish on resultant yarn surface.Simultaneously reduce yarn residual torque and
Residual stress not only effectively solves " kink " phenomenon of resultant yarn, also improves the pliability of resultant yarn.
Step 4: the resulting soft clean yarn of step 3 is carried out longitude and latitude and interweaves with forming fabric: soft clean yarn passes through automatic
Bobbin-winding machine winder, fixed length and fault are removed while winder, reduce thickness section；Then warping, sizing and axis are successively carried out, is divided
It twists, gait denting and weaving；Wherein the rate of sizing of sizing is 10% ~ 18%, preferably 18%；The slurry of the sizing is starch or change
Property starch size.In winder, the tension of soft clean yarn is controlled in 1500 ~ 1800N, preferably 1800N.
Step 5: dyeing and finishing: processing of singing being carried out to step 4 gained fabric with weak fire, then carries out desizing treatment；Then according to
Secondary to be bleached, dyed, bleaching is to more preferably paint in advance；Dyestuff when dyeing is bifunctionalreactive dyes, passes through two
The dyeing of bath method: after fabric crosses water, first dye wool fiber under mildly acidic conditions, fabric is after water, then in alkaline condition
Under make flax fiber and cotton fiber dyeing.Then it is soaped with ammonium hydroxide, to obtain higher wet fastness, finally progress preshrunk,
Thermal finalization.Preferably, during desizing treatment, by the way that the softening agent pair that dosage is (mass percentage) 0.5% ~ 1% is added
Fabric carries out relaxation processes, carries out relaxation processes to fabric by softening agent, promotes the feel of fabric.Wherein, desizing, dyeing can
It is carried out in the same cylinder, saving the time improves efficiency.The softening agent be commercially available softening agent, HY-008, XL-GL, PES,
It chooses any one kind of them in YN803 or LTJ03.
Fabric produced by the present invention has a characteristic that 1) weaving finished product washing size changing rate: through to ± 5%, broadwise
±5%；(2) weaving finished product color fastness: washable (discoloration, staining) >=3 grades；Perspiration resistance (discoloration, staining) >=3 grades；Resistance to dry friction >=
3 grades, resistance to wet friction >=2-3 grades；(3) weaving finished product content of formaldehyde :≤75mg/kg.
Claims (5)
1. a kind of preparation method of the soft clean yarn fabric for home textile, characterized by the following steps:
Step 1: mercerising anti-shrinking is carried out to wool；To flax fiber, 48h carries out fiber softening processing before spinning；
Step 2: being mixed again with flax fiber item after being mixed wool with cotton fiber packet by cotton spinning machine, obtain composite fibre；Wherein, it presses
Mass percentage wool 10% ~ 15%, cotton fiber 60% ~ 70%, flax fiber 20% ~ 25%；
Step 3: successively to step 2 gained composite fibre carry out opening picking, cotton carding, it is mixed simultaneously, rove, spun yarn, obtain soft clean spinning
Line；The hot humidizer for being wherein 2.7% to composite fibre sprinkling dosage during rove carries out heat and wet treatment, hot humidizer
Temperature is 25 ~ 28 DEG C；
Step 4: the resulting soft clean yarn of step 3 is carried out longitude and latitude and interweaves with forming fabric: soft clean yarn passes through automatic winding
Machine winder, fixed length and fault are removed while winder, reduce thickness section；Then warping, sizing and axis are successively carried out, leasing, is worn
Comprehensive denting and weaving；Wherein the rate of sizing of sizing is 10% ~ 18%；
Step 5: dyeing and finishing: processing of singing being carried out to step 4 gained fabric with weak fire, then carries out desizing treatment；Then successively into
Row bleaching, dyeing, dyestuff when dyeing is bifunctionalreactive dyes, passes through two bath process；Then it is soaped with ammonium hydroxide,
Finally carry out preshrunk, thermal finalization.
2. the preparation method of the soft clean yarn fabric for home textile according to claim 1, it is characterised in that: step 1
Described in fiber softening processing to spray finishing auxiliaries to flax fiber, the dosages of finishing auxiliaries is 1%-3%.
3. the preparation method of the soft clean yarn fabric for home textile according to claim 1, it is characterised in that: step 4
In, in winder, the tension of soft clean yarn is controlled in 1500 ~ 1800N.
4. the preparation method of the soft clean yarn fabric for home textile according to claim 1, it is characterised in that: step 4
In, the slurry of the sizing is starch or modified starch size.
5. the preparation method of the soft clean yarn fabric for home textile according to claim 1, it is characterised in that: step 5
In, during desizing treatment, relaxation processes are carried out to fabric by the way that the softening agent that dosage is 0.5% ~ 1% is added.