CN110293616A - 一种桉木指接地板的制备工艺 - Google Patents
一种桉木指接地板的制备工艺 Download PDFInfo
- Publication number
- CN110293616A CN110293616A CN201910526006.5A CN201910526006A CN110293616A CN 110293616 A CN110293616 A CN 110293616A CN 201910526006 A CN201910526006 A CN 201910526006A CN 110293616 A CN110293616 A CN 110293616A
- Authority
- CN
- China
- Prior art keywords
- eucalyptus
- finger
- flitch
- preparation process
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于木材加工技术领域,涉及桉木指接地板的制备工艺包括:对原木桉木进行去皮、锯切等加工成木方;采用红外及热风联合干燥,再使用干燥窑对木方进行干燥,干燥时间3~30d;将木方按照结构设计在所需部位涂布胶黏剂,进行结构加工成指接板,所述胶黏剂为常用的聚氨酯冷压胶,地板加工。本发明将桉木原木加工、尺寸稳定干燥、指接胶合,较好地改变了作为速生材原本具有的不坚韧、质轻、易断的缺陷,经指接胶合后的桉木木方,能够满足惯用实木地板生产所需要的原木性能,所制得的桉木指接地板与普通实木地板理化性能无大的差异。本发明对桉木处理的工序简单,成本不高,可较好的缓解当前实木资源日趋紧张的现状,提高了速生材桉木的经济性能。
Description
技术领域
本发明属于木材加工技术领域,涉及实木地板的制备,尤其涉及一种桉木指接地板的制备工艺。
背景技术
目前,木质地板作为国内地面铺装材料市场的最重要的建材产品之一,在铺装材料市场的占有额达到40%以上。木质地板的优点是木质感强、纹理效果优美。但随着社会经济的发展和市场需求迅速增加,木材资源的供求矛盾越发明显和突出。
我国桉木资源较为丰富,业已成功开发了高性能桉木重组材、桉木单板层积材、竹桉复合材料、厚芯桉树实木复合板材和无醛桉木胶合板制造技术等,桉树的综合利用率可以提高至90%以上。桉木单板俗称桉木面板、桉木芯板,是由旋切机采侧面滚动旋切桉树而成的木质薄片状材料,其厚度通常为0.4-10mm之间。而除用作胶合板之外,作为速生材,如何将桉木通过结构和工艺处理,使之适用于地板生产,是本发明主要解决的问题。
发明内容
针对上述现有技术中存在的不足,本发明的目的是通过对桉木进行干燥处理以稳定尺寸,通过特殊的胶黏剂及结构处理成指接板,再进行地板加工。
一种桉木指接地板的制备工艺,包括桉木原木加工、尺寸稳定干燥、指接胶合、地板加工,包括如下步骤:
A、对原木桉木进行去皮、锯切等加工成木方,木方尺寸为400~2000mm×600~300mm×10~80mm;
B、采用红外及热风联合干燥,干燥温度180~240℃,干燥时间20~60min,再使用干燥窑对木方进行干燥,干燥时间3~30d;
C、指接胶合,将木方按照结构设计在所需部位涂布胶黏剂,进行结构加工成指接板,所述胶黏剂为常用的聚氨酯冷压胶,涂布量50~400g/㎡;
D、地板加工
(1)贴面,在指接板表面涂布胶粘剂,涂布量80~300g/㎡,再在表面压贴木皮,然后冷热压处理,
(2)开料成型,使用双端铣进行榫槽或锁扣成型加工,
(3)油漆加工,对素板进行油漆涂饰6~14道,涂布量70~200g/㎡。
本发明较优公开例中,步骤B所述采用红外及热风联合干燥,干燥温度210℃,干燥时间40min。
本发明较优公开例中,步骤B所述使用干燥窑对木方进行干燥,干燥时间16d。
本发明较优公开例中,步骤C所述胶黏剂的主要成分包括,组分A:三苯基丙烷氰酸酯;组分B:氨酯多元醇、聚乙二醇、促进剂、碳酸钙、催化剂、稳定剂;将组分A和组分B按照质量比1:0.8~1.2混合,搅拌均匀后即可。
本发明较优公开例中,步骤D所述在指接板表面涂布胶粘剂,涂布量190g/㎡。
有益效果
本发明将桉木原木加工、尺寸稳定干燥、指接胶合,较好地改变了作为速生材原本具有的不坚韧、质轻、易断的缺陷,经指接胶合后的桉木木方,能够满足惯用实木地板生产所需要的原木性能,所制得的桉木指接地板与普通实木地板理化性能无大的差异。本发明对桉木处理的工序简单,成本不高,能够较好的缓解当前实木资源日趋紧张的现状,提高了速生材桉木的经济性能。
具体实施方式
下面结合实施例对本发明进行详细说明,以使本领域技术人员更好地理解本发明,但本发明并不局限于以下实施例。
实施例1
一种桉木指接地板的制备工艺,包括如下步骤:
1、桉木原木加工,通过对原木进行去皮、锯切等加工成木方,木方尺寸920mm×135mm×11 mm。
2、尺寸稳定:应用联合干燥法,使用干燥窑对木方进行干燥,干燥时间10d。
3、指接胶合
(1)胶黏剂的合成,主要成分:组分A:三苯基丙烷氰酸酯;组分B:氨酯多元醇、聚乙二醇、促进剂、碳酸钙、催化剂、稳定剂。将组分A和组分B按照质量比1:0.9混合,搅拌均匀后,便可使用。(2)胶黏剂涂布量:120g/㎡。
(3)指接结构:将木方按照结构设计在所需部位涂布胶黏剂,进而进行结构加工成指接板。
4、地板加工
(1)贴面:在指接板表面涂布胶黏剂,涂布量110g/㎡,再在表面压贴木皮,木皮尺寸910×125×1.2mm,进而进行冷热压处理。
(2)开料成型:使用双端铣进行榫槽或锁扣成型加工,素板尺寸910×125×12mm。
(3)油漆加工:对素板进行油漆涂饰,油漆加工7道,涂布量90g/㎡。
实施例2
一种桉木指接地板的制备工艺,包括如下步骤:
1、桉木原木加工,通过对原木进行去皮、锯切等加工成木方,木方尺寸1220mm×175mm×14 mm。
2、尺寸稳定:应用联合干燥法,使用干燥窑对木方进行干燥,干燥时间15d。
3、指接胶合
(1)胶黏剂的合成,主要成分:组分A:三苯基丙烷氰酸酯;组分B:氨酯多元醇、聚乙二醇、促进剂、碳酸钙、催化剂、稳定剂。将组分A和组分B按照质量比1:1.05混合,搅拌均匀后,便可使用。(2)胶黏剂涂布量:130g/㎡。
(3)指接结构:将木方按照结构设计在所需部位涂布胶黏剂,进而进行结构加工成指接板。
4、地板加工
(1)贴面:在指接板表面涂布胶黏剂,涂布量130g/㎡,再在表面压贴木皮,木皮尺寸1210×165×1.2mm,进而进行冷热压处理。
(2)开料成型:使用双端铣进行榫槽或锁扣成型加工,素板尺寸1210×165×15mm。
(3)油漆加工:对素板进行油漆涂饰,油漆加工7道,涂布量110g/㎡。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (5)
1.一种桉木指接地板的制备工艺,包括桉木原木加工、尺寸稳定干燥、指接胶合、地板加工,其特征在于,包括如下步骤:
A. 对原木桉木进行去皮、锯切等加工成木方,木方尺寸为400~2000mm×600~300mm×10~80mm;
B. 采用红外及热风联合干燥,干燥温度180~240℃,干燥时间20~60min,再使用干燥窑对木方进行干燥,干燥时间3~30d;
C. 指接胶合,将木方按照结构设计在所需部位涂布胶黏剂,进行结构加工成指接板,所述胶黏剂为常用的聚氨酯冷压胶,涂布量50~400g/㎡;
D. 地板加工
(1)贴面,在指接板表面涂布胶粘剂,涂布量80~300g/㎡,再在表面压贴木皮,然后冷热压处理,
(2)开料成型,使用双端铣进行榫槽或锁扣成型加工,
(3)油漆加工,对素板进行油漆涂饰6~14道,涂布量70~200g/㎡。
2.根据权利要求1所述桉木指接地板的制备工艺,其特征在于:步骤B所述采用红外及热风联合干燥,干燥温度210℃,干燥时间40min。
3.根据权利要求1所述桉木指接地板的制备工艺,其特征在于:步骤B所述使用干燥窑对木方进行干燥,干燥时间16d。
4.根据权利要求1所述桉木指接地板的制备工艺,其特征在于:步骤C所述胶黏剂的主要成分包括,组分A:三苯基丙烷氰酸酯;组分B:氨酯多元醇、聚乙二醇、促进剂、碳酸钙、催化剂、稳定剂;将组分A和组分B按照质量比1:0.8~1.2混合,搅拌均匀后即可。
5.根据权利要求1所述桉木指接地板的制备工艺,其特征在于:步骤D所述在指接板表面涂布胶粘剂,涂布量190g/㎡。