CN110253999A - A kind of paper plastic-aluminum epiphragma used for cosmetic and its production technology - Google Patents
A kind of paper plastic-aluminum epiphragma used for cosmetic and its production technology Download PDFInfo
- Publication number
- CN110253999A CN110253999A CN201910683403.3A CN201910683403A CN110253999A CN 110253999 A CN110253999 A CN 110253999A CN 201910683403 A CN201910683403 A CN 201910683403A CN 110253999 A CN110253999 A CN 110253999A
- Authority
- CN
- China
- Prior art keywords
- layer
- paper
- aluminium foil
- aluminum
- epiphragma
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of paper plastic-aluminum epiphragma used for cosmetic and its production technologies, including outer layer, aluminium foil layer and hot sealing layer, the outer layer and the hot sealing layer are respectively provided at the upper and lower two sides of the aluminium foil layer, the outer layer and the aluminium foil interlayer are equipped with outer adhesive layer, the aluminium foil layer and the heat-sealing interlayer are equipped with interior adhesive layer, the outer layer is synthesis paper layer, and the aluminium foil layer is O state aluminium foil;The outer adhesive layer and the interior adhesive layer are solvent borne polyurethane glue;The outer layer includes imitative paper layer and coating, and the imitative paper layer is set between the coating and the outer adhesive layer.By using PP synthetic paper as outer layer, paper plastic-aluminum epiphragma used for cosmetic relative to traditional paper as outer layer, resistance to oily stain can be more excellent, and has the preferable printing of traditional paper;Hot sealing layer is using easily taking off PE film, easily taking off EMA film or easily take off eva film etc. and easily take off film, and processing temperature is lower, and product heat seal strength is controllable.
Description
Technical field
The present invention relates to composite packaging technical field of membrane, especially a kind of paper plastic-aluminum epiphragma used for cosmetic and its production work
Skill.
Background technique
Existing epiphragma used for cosmetic is mostly plastic-aluminum membrane structure, and texture is poor, according to conventional paper plastic-aluminum structure, is made with paper
, because paper sheet thickness is too thick, cause the overall thickness of epiphragma partially thick though preferable texture can be obtained for outer layer printing layer, and conventional
Paper plastic-aluminum epiphragma is because outer paper is easy to adsorb cosmetics, if having cosmetic applying to will form in paper surface in process of production
Greasy dirt can directly reduce the consumption experience of consumer.
Authorization Notice No. provides one kind for the utility model patent of CN202781990U and easily opens cosmetic package envelope
Membrana oralis, it includes base, it is characterised in that surface layer is arranged in base, there is adhesive layer between surface layer and base, is arranged under base
Hot sealing layer has adhesive layer between base and hot sealing layer, above-mentioned surface layer uses polyester, and base uses aluminium foil, and hot sealing layer is using modification
Polyethylene, adhesive layer use polyurethane.Though the surface layer of the patent of invention is imitated using polyester, printing of its printing with respect to paper
Fruit is poor;Hot sealing layer use modified poly ethylene, it is more demanding to hot sealing process, manufacturer when being sealed required temperature compared with
Height easily causes the encapsulation deformation of epiphragma, influences product beauty.
In view of the above-mentioned problems, being intended to provide a kind of paper plastic-aluminum epiphragma used for cosmetic, the surface of epiphragma will not be infected with greasy dirt, and
It is beautifully printed, heat-sealing processing temperature is lower.
Summary of the invention
The first purpose of this invention is to provide a kind of paper plastic-aluminum epiphragma used for cosmetic, and second is designed to provide one
The production technology of kind paper plastic-aluminum epiphragma used for cosmetic.A kind of paper plastic-aluminum epiphragma used for cosmetic of the invention, is not only beautifully printed, and
The surface of paper plastic-aluminum epiphragma used for cosmetic will not be infected with greasy dirt, in paper plastic-aluminum epiphragma used for cosmetic in use, to heat-sealing processing temperature
The requirement of degree is lower.
It is special to achieve the purpose that foregoing invention, first aspect of the present invention provide a kind of paper plastic-aluminum epiphragma used for cosmetic
Sign is: including outer layer, aluminium foil layer and hot sealing layer, the outer layer and the hot sealing layer are respectively provided at the upper and lower of the aluminium foil layer
Two sides, the outer layer and the aluminium foil interlayer are equipped with outer adhesive layer, and the aluminium foil layer and the heat-sealing interlayer are equipped with interior bonding
Layer, the outer layer are synthesis paper layer, and the synthesis paper layer includes imitative paper layer and coating, and the imitative paper layer is set to the coating and institute
It states between outer adhesive layer;The aluminium foil layer is O state aluminium foil;The outer adhesive layer and the interior adhesive layer are solvent borne polyurethane glue
Water.
Preferably, the outer layer with a thickness of 30-80 μm, wherein the imitative paper layer with a thickness of 29.5-78 μm, it is described
Coating with a thickness of 0.5-2 μm.
Preferably, the imitative paper layer is PP synthetic paper.
Preferably, the coating is by any in water soluble acrylic acid, waterborne polyester, solvent-type acrylic or solvent type polyester
Kind is made.
Preferably, 7-50 μm of the aluminium foil layer.
Preferably, the aluminium foil layer selects 8011 aluminium foils, any one of 8021 aluminium foils or 8079 aluminium foils.
Preferably, 30-50 μm of the hot sealing layer.
Preferably, the hot sealing layer is easily to take off PE film, easily take off EMA film or easily take off any one of eva film.
Preferably, printing layer is additionally provided in the upper surface of the coating.
The second aspect of the present invention provides a kind of production technology of paper plastic-aluminum epiphragma used for cosmetic, which is characterized in that specific
Steps are as follows:
(A) solvent borne polyurethane glue is coated in the side of aluminium foil layer on combination machine based on dry operation, dry out solvent obtains outer
Adhesive layer, by the imitative paper layer face aluminium foil layer of outer layer, by obtaining clad aluminum layers of foil after compound roll press;
(B) after the another side of aluminium foil layer coats solvent borne polyurethane glue, dry out solvent obtains interior adhesive layer, will
The aluminium foil surface face hot sealing layer of the resulting clad aluminum layers of foil of step (A), by obtaining semi-finished product after compound roll press;
(C) after curing semi-finished product obtained in step (B) 48 hours at 50 DEG C between heat preservation, then die cut is to obtain afterwards
Paper plastic-aluminum epiphragma finished product used for cosmetic.
A kind of paper plastic-aluminum epiphragma used for cosmetic of the invention is compared with the prior art and is had the advantage that
(1) using PP synthetic paper as outer layer, thinner thickness is controllable, has good texture, exquisite appearance is high-end, relatively
In used for cosmetic paper plastic-aluminum epiphragma of the traditional paper as outer layer, resistance to oily stain can be more excellent, and has the preferable of traditional paper
Printing;
(2) hot sealing layer easily takes off film using easily taking off PE film, easily take off EMA film or easily take off eva film etc., processing temperature compared with
It is low, and product heat seal strength is controllable.
Detailed description of the invention
Fig. 1 is a kind of structural schematic diagram of paper plastic-aluminum epiphragma used for cosmetic of the invention;
Appended drawing reference: 1, outer layer;11, paper layer is imitated;12, coating;2, outer adhesive layer;3, aluminium foil layer;4, interior adhesive layer;5, hot
Sealing.
Specific embodiment
By following specific embodiments, the present invention will be further described.Following embodiment is only used for helping this field skill
Art personnel understand the present invention, are not limitations of the present invention.
As shown in Figure 1, first aspect of the present invention provides a kind of paper plastic-aluminum epiphragma used for cosmetic, including outer layer 1, aluminium foil layer
3 and hot sealing layer 5, the outer layer 1 and the hot sealing layer 5 are respectively provided at the upper and lower two sides of the aluminium foil layer 3,1 He of outer layer
It is equipped with outer adhesive layer 2 between the aluminium foil layer 3, interior adhesive layer 4, the outer layer 1 are equipped between the aluminium foil layer 3 and the hot sealing layer 5
To synthesize paper layer, the aluminium foil layer is O state aluminium foil, and the outer adhesive layer 2, the interior adhesive layer 4 are solvent borne polyurethane glue.
The outer layer 1 includes imitative paper layer 11 and coating 12, the outer layer with a thickness of 30-80 μm, wherein the imitative paper layer
With a thickness of 29.5-78 μm, the coating with a thickness of 0.5-2 μm.The imitative paper layer 11 is set to the coating 12 and described outer
Between adhesive layer 2, the preferred PP synthetic paper of the imitative paper layer 11, the PP synthetic paper is PP base foamed plastic, density 0.8g/
cm3.For the ease of printing in paper aluminium-plastic cap film surface used for cosmetic, the coating 12 is by water soluble acrylic acid, waterborne polyester, solvent
Any one of type acrylic acid or solvent type polyester are made.Coating employed in the embodiment of the present invention is by water soluble acrylic acid system
At, but therefore do not limit the disclosure.
The hot sealing layer 5 is commercially available conventional selection, such as can be easily to take off PE film, easily take off EMA film or easily take off
Any one of eva film.
7-50 μm of the aluminium foil layer, the aluminium foil layer select 8011 aluminium foils, any one of 8021 aluminium foils or 8079 aluminium foils.
30-50 μm of the hot sealing layer, the hot sealing layer are easily to take off PE film, easily take off EMA film or easily take off in eva film
It is any.
Printing layer is additionally provided in the upper surface of the coating.
The second aspect of the present invention provides a kind of production technology of paper plastic-aluminum epiphragma used for cosmetic, which is characterized in that specific
Steps are as follows:
(A) solvent borne polyurethane glue is coated in the side of aluminium foil layer on combination machine based on dry operation, dry out solvent obtains outer
Adhesive layer, by the imitative paper layer face aluminium foil layer of outer layer, by obtaining clad aluminum layers of foil after compound roll press;
(B) after the another side of aluminium foil layer coats solvent borne polyurethane glue, dry out solvent obtains interior adhesive layer, will
The aluminium foil surface face hot sealing layer of the resulting clad aluminum layers of foil of step (A), by obtaining semi-finished product after compound roll press;
(C) after curing semi-finished product obtained in step (B) 48 hours at 50 DEG C between heat preservation, then die cut is to obtain afterwards
Paper plastic-aluminum epiphragma finished product used for cosmetic.
Below in conjunction with the drawings and specific embodiments, the present invention will be further described.Following embodiment is only used for helping this
Field technical staff understands the present invention, is not limitation of the present invention.
Embodiment 1:
A kind of paper plastic-aluminum epiphragma used for cosmetic of the present embodiment, outer layer 1 selects 30 μm of the white PP synthetic paper in Asia, wherein imitative paper
Layer 11 with a thickness of 29.5 μm of PP synthetic paper (manufacturer is Nanya Plastic Cement Industry Co., Ltd), the thickness of coating 12
For 0.5 μm of sub- white coating, select water soluble acrylic acid as coating material;
Aluminium foil layer 3 select with a thickness of 7 μm 8011 aluminium foils (aluminium foil model be 8011 O state aluminium foil, manufacturer is Xiamen
Tall building is along aluminium foil Co., Ltd).
The hot sealing layer 5 selects that (manufacturer is that tonneau Optoelectronics Technology in Jiangyin is limited with a thickness of 30 μm of PE film of easily taking off
Company);
Outer adhesive layer 2, interior adhesive layer 4 select solvent borne polyurethane glue, and (trade mark LH-3721, manufacturer are Jiangsu power
Close adhesive Co., Ltd).
The production technology of paper plastic-aluminum epiphragma used for cosmetic is as follows:
(A) solvent borne polyurethane glue is coated in the side of aluminium foil layer 3 on combination machine based on dry operation, dry out solvent obtains outer
Adhesive layer 2, by the 11 face aluminium foil layer 3 of imitative paper layer of outer layer 1, by obtaining clad aluminum layers of foil after compound roll press;
(B) after the another side of aluminium foil layer 3 coats solvent borne polyurethane glue, dry out solvent obtains interior adhesive layer 4,
By the aluminium foil surface face hot sealing layer 5 of the resulting clad aluminum layers of foil of step (A), by obtaining semi-finished product after compound roll press;
(C) after curing semi-finished product obtained in step (B) 48 hours at 50 DEG C between heat preservation, then die cut is to obtain afterwards
Paper plastic-aluminum epiphragma finished product used for cosmetic.
According to the actual needs of client, 12 surface of coating of the paper plastic-aluminum epiphragma finished product used for cosmetic made from step (C)
It is printed, the paper plastic-aluminum epiphragma used for cosmetic containing printing layer can be obtained.
Embodiment 2:
A kind of paper plastic-aluminum epiphragma used for cosmetic of the present embodiment, the white PP synthetic paper in Asia that outer layer 1 is selected with a thickness of 55 μm,
In imitate paper layer 11 with a thickness of 54 μm of PP synthetic paper (manufacturer is Nanya Plastic Cement Industry Co., Ltd), coating 12
With a thickness of 1 μm of sub- white coating, select water soluble acrylic acid as coating material;
Aluminium foil layer 3 select with a thickness of 30 μm 8021 aluminium foils (trade mark be 8021 O state aluminium foil, manufacturer be middle aluminium aluminium
Foil Co., Ltd);
The hot sealing layer 5 selects that (manufacturer is that tonneau Optoelectronics Technology in Jiangyin is limited with a thickness of 40 μm of EMA film of easily taking off
Company);
Outer adhesive layer 2, interior adhesive layer 4 select solvent borne polyurethane glue, and (trade mark LH-3721, manufacturer are Jiangsu
Li He adhesive Co., Ltd).
The production technology of the paper plastic-aluminum epiphragma used for cosmetic of the present embodiment is the same as embodiment 1.
Embodiment 3:
A kind of paper plastic-aluminum epiphragma used for cosmetic of the present embodiment, the white synthetic paper in Asia that outer layer 1 is selected with a thickness of 80 μm, wherein
Imitative paper layer 11 with a thickness of 78 μm of PP synthetic paper (manufacturer is Nanya Plastic Cement Industry Co., Ltd), the thickness of coating 12
The sub- white coating that degree is 2 μm selects water soluble acrylic acid as coating material;
Aluminium foil layer 3 select with a thickness of 50 μm 8079 aluminium foils (trade mark be 8021 O state aluminium foil, manufacturer be Henan ten thousand
Base Aluminum limited liability company);
The hot sealing layer 5 selects that (manufacturer is that tonneau Optoelectronics Technology in Jiangyin is limited with a thickness of 50 μm of eva film of easily taking off
Company);
Outer adhesive layer 2, interior adhesive layer 4 select solvent borne polyurethane glue, and (trade mark LH-3721, manufacturer are Jiangsu
Li He adhesive Co., Ltd).
The production technology of the paper plastic-aluminum epiphragma used for cosmetic of the present embodiment is the same as embodiment 1.
Comparative example 1:
A kind of paper plastic-aluminum epiphragma used for cosmetic of this comparative example, outer layer 1 selects 80g composite base paper, and (manufacturer is red crowned crane
Limited liability company);
Aluminium foil layer 3 select with a thickness of 40 μm 8021 aluminium foils (trade mark be 8021 O state aluminium foil, manufacturer be middle aluminium aluminium
Foil Co., Ltd);
The curtain coating co-extrusion PE film that the hot sealing layer 5 is selected with a thickness of 30 μm;
Outer adhesive layer 2, interior adhesive layer 4 select solvent borne polyurethane glue, and (trade mark LH-3721, producer are the conjunction of Jiangsu power
Adhesive Co., Ltd).
The production technology of the paper plastic-aluminum epiphragma used for cosmetic of this comparative example is as follows:
(A) solvent borne polyurethane glue is coated in the side of aluminium foil layer on combination machine based on dry operation, dry out solvent obtains outer
Adhesive layer 2, by the non-printed side face aluminium foil layer 3 of the composite base paper of outer layer 1, by obtaining clad aluminum foil after compound roll press
Layer;
(B) after the another side of aluminium foil layer 3 coats solvent borne polyurethane glue, dry out solvent obtains interior adhesive layer 4,
By the aluminium foil surface face hot sealing layer 5 of the resulting clad aluminum layers of foil of step (A), by obtaining semi-finished product after compound roll press;
(C) after curing semi-finished product obtained in step (B) 48 hours at 50 DEG C between heat preservation, then die cut is to obtain afterwards
Paper plastic-aluminum epiphragma finished product used for cosmetic.
Comparative example 2:
A kind of plastic-aluminum epiphragma used for cosmetic of this comparative example, outer layer 1 select that (PET film is with a thickness of 12 μm of PET film
Refer to the film made of poly terephthalic acid class plastics, producer is Hangzhou great Hua Su industry Co., Ltd).
Aluminium foil layer 3 select with a thickness of 40 μm 8021 aluminium foils (trade mark be 8021 O state aluminium foil, manufacturer be middle aluminium aluminium
Foil Co., Ltd);
The hot sealing layer 5, which is selected, easily takes off film with a thickness of 30 μm of conventional curtain coating co-extrusion PE;
Outer adhesive layer 2, interior adhesive layer 4 select solvent borne polyurethane glue, and (trade mark LH-3721, manufacturer are Jiangsu
Li He adhesive Co., Ltd).
The production technology of the plastic-aluminum epiphragma used for cosmetic of this comparative example is the same as comparative example 1.
The performance test of embodiment is as follows:
1) openable cover test method and evaluation: the hot sealing layer of cosmetics epiphragma and PP sheet material are sealed, heat-sealing pressure
Power is 0.2MPa, and the heat-sealing time is 1s, and heat-seal equipment is that the HST-H3 of Labthink Instruments Co., Ltd. seals testing machine.
150 DEG C of temperature < when heat seal strength is greater than 3N/15mm are considered as OK, are considered as NG greater than 150 DEG C.
2) it resistance to oily stain test method and evaluation: selects a paste cosmetic applying in epiphragma superficies, wipes after ten minutes
It goes cosmetics to observe outer layer state, there is cosmetics residual to be considered as OK, no cosmetics residual is considered as NG.
3) printing test method and evaluation: this test uses letterpress, in paper plastic-aluminum epiphragma finished product used for cosmetic
Superficies are printed, and printing ink selects the UV161 series ink for Hang Hua ink limited liability company, after being completed for printing
Ink adhesion test is carried out using GB/T7706-2008 " relief printing plate decoration printed matter ", is if oil-free Motuo falls test result
OK, if having the ink test result that falls off is NG.
4) method for testing tightness and evaluation: using GB/T1038-2000 " plastic film and the test of thin slice gas-premeable
Method pressure differential method ", as gas transit dose≤0.5cm3/ ㎡ for 24 hours 0.1MPa when, leakproofness OK;When gas transit dose >=
0.5cm3/ ㎡ for 24 hours 0.1MPa when, leakproofness NG.
Using following test method easily taking off to plastic-aluminum epiphragma used for cosmetic prepared by embodiment 1-3 and comparative example 1-2
Gai Xing, resistance to oily stain, printing, leakproofness are tested, and test result is listed in table 1:
Table 1
Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 | Comparative example 2 | |
Openable cover | OK | OK | OK | NG | NG |
Resistance to oily stain | OK | OK | OK | NG | OK |
Printing | OK | OK | OK | OK | NG |
Leakproofness | OK | OK | OK | OK | OK |
It can be seen from the experimental result of table 1 plastic-aluminum epiphragma used for cosmetic provided by the invention not only have it is good easily
Lid and leakproofness are taken off, relative to traditional paper as outer layer, resistance to oily stain can be more excellent, and has the preferable of traditional paper
Printing;For hot sealing layer using easily taking off PE film, easily taking off EMA film or easily take off eva film etc. and easily take off film, processing temperature is lower,
And product heat seal strength is controllable.
Presently preferred embodiments of the present invention is illustrated above, but the present invention is not limited in the implementation
Example, those skilled in the art can also make various equivalent changes on the premise of not violating the inventive spirit of the present invention
Type or replacement, these equivalent modifications or replacement are all included in the scope defined by the claims of the present application.
Claims (10)
1. a kind of paper plastic-aluminum epiphragma used for cosmetic, it is characterised in that: including outer layer, aluminium foil layer and hot sealing layer, the outer layer and institute
The upper and lower two sides that hot sealing layer is respectively provided at the aluminium foil layer are stated, the outer layer and the aluminium foil interlayer are equipped with outer adhesive layer, institute
It states aluminium foil layer and the heat-sealing interlayer is equipped with interior adhesive layer, the outer layer is synthesis paper layer, and the synthesis paper layer includes imitative paper layer
And coating, the imitative paper layer are set between the coating and the outer adhesive layer;The aluminium foil layer is O state aluminium foil;It is described outer viscous
It ties layer and the interior adhesive layer is solvent borne polyurethane glue.
2. a kind of paper plastic-aluminum epiphragma used for cosmetic according to claim 1, which is characterized in that the outer layer with a thickness of
30-80 μm, wherein the imitative paper layer with a thickness of 29.5-78 μm, the coating with a thickness of 0.5-2 μm.
3. a kind of paper plastic-aluminum epiphragma used for cosmetic according to claim 2, which is characterized in that the imitative paper layer is PP synthesis
Paper.
4. a kind of paper plastic-aluminum epiphragma used for cosmetic according to claim 2, which is characterized in that the coating is by aqueous acrylamide
Any one of acid, waterborne polyester, solvent-type acrylic or solvent type polyester are made.
5. a kind of paper plastic-aluminum epiphragma used for cosmetic according to claim 1, which is characterized in that 7-50 μm of the aluminium foil layer.
6. a kind of paper plastic-aluminum epiphragma used for cosmetic according to claim 5, which is characterized in that the aluminium foil layer selects 8011
Aluminium foil, any one of 8021 aluminium foils or 8079 aluminium foils.
7. a kind of paper plastic-aluminum epiphragma used for cosmetic according to claim 1, which is characterized in that 30-50 μm of the hot sealing layer.
8. a kind of paper plastic-aluminum epiphragma used for cosmetic according to claim 7, which is characterized in that the hot sealing layer is easily to take off PE
Film easily takes off EMA film or easily takes off any one of eva film.
9. a kind of paper plastic-aluminum epiphragma used for cosmetic according to any one of claims 1 to 8, which is characterized in that in the painting
The upper surface of layer is additionally provided with printing layer.
10. a kind of production technology of paper plastic-aluminum epiphragma used for cosmetic as claimed in any one of claims 1 to 8, which is characterized in that
Specific step is as follows:
(A) solvent borne polyurethane glue is coated in the side of aluminium foil layer on combination machine based on dry operation, dry out solvent obtains outer bonding
Layer, by the imitative paper layer face aluminium foil layer of outer layer, by obtaining clad aluminum layers of foil after compound roll press;
(B) after the another side of aluminium foil layer coats solvent borne polyurethane glue, dry out solvent obtains interior adhesive layer, by step
(A) the aluminium foil surface face hot sealing layer of resulting clad aluminum layers of foil, by obtaining semi-finished product after compound roll press;
(C) after curing semi-finished product obtained in step (B) 48 hours at 50 DEG C between heat preservation, then die cut is to be made up afterwards
Product paper plastic-aluminum epiphragma finished product.