CN110204917A - A method of preparing multi-functional TPO composite lether - Google Patents
A method of preparing multi-functional TPO composite lether Download PDFInfo
- Publication number
- CN110204917A CN110204917A CN201910512361.7A CN201910512361A CN110204917A CN 110204917 A CN110204917 A CN 110204917A CN 201910512361 A CN201910512361 A CN 201910512361A CN 110204917 A CN110204917 A CN 110204917A
- Authority
- CN
- China
- Prior art keywords
- added
- tpo
- tpo composite
- solution
- preparing multi
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of methods for preparing multi-functional TPO composite lether, the method of the direct doping inorganic powder object of abandoning tradition, using the organic coating of inorganic powder particle, realize the surface organic of inorganic particulate, a strata amide has been wrapped up in inorganic powder particle surface, has solved the inhomogeneities of reunion and doping of the inorganic powder object during preparing TPO synthetic leather.TPO film sheet is made in single screw extrusion machine progress reactive extrursion, press polish, cooling, curling in the electrodeless powder object being modified and TPO composite material, maleic anhydride.
Description
Technical field
The present invention relates to a kind of methods for preparing multi-functional TPO composite lether, are applied to TPO and produce and process technical field.
Background technique
With the development of society, building trade development is getting faster, the demand of required TPO composite lether is increasing,
And nowadays the high-quality TPO of complex building finishing of market production etc. is by special working process, so that TPO has
There is better performance, meets the quality material that can nowadays cope with mal-condition.It is most of to be in the modification for carrying out TPO
Using the method that inorganic filler is added, and the addition of inorganic filler will lead to the reunion of inorganic powder in process, to production
Processing brings many troubles.Therefore the organic coating for carrying out inorganic particulate, may be implemented the surface organic of inorganic particulate, from
And improve itself and the interface compatibility of organic matter and the dispersibility in organic matter.Solves the group of inorganic particulate in processing reaction
Poly- problem is a kind of method by electrodeless dusty material in conjunction with TPO composite material well.
Summary of the invention
The present invention solves the technical problem of: in view of the deficiencies of the prior art, provide a kind of preparation of TPO composite lether
The method of method, the direct doping inorganic powder object of abandoning tradition realizes inorganic grain using the organic coating of inorganic powder particle
The surface organic of son, solves the inhomogeneities of reunion and the doping of inorganic powder object.
In order to solve the technical problem, one technical scheme adopted by the invention is that: a kind of nothing preparing TPO composite material is provided
The organic coating method of machine powder particle, realizes the surface organic of inorganic particulate, to improve its interface phase with organic matter
Capacitive and the dispersibility in organic matter.
The present invention also provides a kind of methods for preparing multi-functional TPO composite lether, include the following steps:
(1) 30-50% pure water is added in polymeric kettle, acidic materials are added, temperature is controlled at 0-5 DEG C;
(2) stirring of polymeric kettle high speed is added in a certain amount of aniline (being evaporated under reduced pressure twice), certain density mistake is added dropwise
Ammonium sulfate (APS), hydrochloric acid solution, inorganic material powders, dispersing agent, the PH for controlling solution is 2.5-4.5, continues to stir 1h;
(3) the above solution is added in the mixed solution for filling a certain amount of aniline, hydrochloric acid, the reaction was continued 2h;(4) successively
With dilute hydrochloric acid, dehydrated alcohol, deionized water washing is filtered, until when BaCl2 solution is added in filtrate without white precipitate,
OP-10 is added dropwise into the solution made quickly to stir, obtains the Polyaniline emulsion of load organic/inorganic substance powder;
(5) Polyaniline emulsion of inorganic powder is filtered resulting load, it is dry;
(6) single screw extrusion machine is added in the product after drying TPO composite material, maleic anhydride, step (5), through molten
Melt hybrid reaction extrusion, TPO film sheet is made in press polish, cooling, curling;
In above-mentioned steps,
Acidic materials are hydrochloric acid solution, concentration 1mol/L;
The molar ratio of aniline and ammonium persulfate is 1:2;
Electrodeless powder object have calcite, kaolin, wollastonite, talcum, mica, rutile, sericite, pyrophillite, mica,
Montmorillonite, shepardite, quartzy calcite, chalk, zeolite, illite, montmorillonite, diatomite, graphite, shepardite, the tremolite, thoroughly
The one or several kinds of lime stone, asbestos, quartz;
Dispersing agent is the one or several kinds of white oil, paraffin, low molecular weight polyethylene;
The particle size of inorganic powder object is 50-400 mesh.
Beneficial benefit of the invention is: by the method to TPO material composite inorganic compound filler, improving tradition
The performance of TPO composite material improves the performance of TPO by adding different inorganic powder objects, reaches required practicability
Can, while reducing the cost of TPO raw materials for production.With the difference of traditional polymer-doped electrodeless powder, the present invention is using inorganic
The organic coating of powder particle, realizes the surface organic of inorganic particulate, thus improve its interface compatibility with organic matter and
Dispersibility in organic matter.So, the performance of upper product being improved largely is being produced, is meeting reality
A demand to various environment in.
Specific embodiment
Example one:
(1) 30% pure water is added in polymeric kettle, acidic materials are added, temperature is controlled at 0-5 DEG C;
(2) stirring of polymeric kettle high speed is added in a certain amount of aniline (being evaporated under reduced pressure twice), certain density mistake is added dropwise
Ammonium sulfate (APS), hydrochloric acid solution, talcum, dispersing agent, the PH for controlling solution is 2.5, continues to stir 1h;
(3) the above solution is added in the mixed solution for filling a certain amount of aniline, hydrochloric acid, the reaction was continued 2h;
(4) dilute hydrochloric acid, dehydrated alcohol are successively used, deionized water washing filters, until BaCl is added in filtrate2When solution
Until without white precipitate, OP-10 is added dropwise into the solution made and quickly stirs, obtains the polyaniline cream of load organic/inorganic substance powder
Liquid;
(5) Polyaniline emulsion of inorganic powder is filtered resulting load, it is dry;
(6) single screw extrusion machine is added in the product after drying TPO composite material, maleic anhydride, step (5), through molten
Melt hybrid reaction extrusion, TPO film sheet is made in press polish, cooling, curling;
Example test data
Example two:
(1) 40% pure water is added in polymeric kettle, acidic materials are added, temperature is controlled at 0-5 DEG C;
(2) stirring of polymeric kettle high speed is added in a certain amount of aniline (being evaporated under reduced pressure twice), certain density mistake is added dropwise
Ammonium sulfate (APS), hydrochloric acid solution, calcite, dispersing agent, the PH for controlling solution is 3.5, continues to stir 1h;
(3) the above solution is added in the mixed solution for filling a certain amount of aniline, hydrochloric acid, the reaction was continued 2h;
(4) dilute hydrochloric acid, dehydrated alcohol are successively used, deionized water washing filters, until BaCl is added in filtrate2When solution
Until without white precipitate, OP-10 is added dropwise into the solution made and quickly stirs, obtains the polyaniline cream of load organic/inorganic substance powder
Liquid;
(5) Polyaniline emulsion of inorganic powder is filtered resulting load, it is dry;
(6) single screw extrusion machine is added in the product after drying TPO composite material, maleic anhydride, step (5), through molten
Melt hybrid reaction extrusion, TPO film sheet is made in press polish, cooling, curling;
Example test data
Example three:
(1) 50% pure water is added in polymeric kettle, acidic materials are added, temperature is controlled at 0-5 DEG C;
(2) stirring of polymeric kettle high speed is added in a certain amount of aniline (being evaporated under reduced pressure twice), certain density mistake is added dropwise
Ammonium sulfate (APS), hydrochloric acid solution, montmorillonite, dispersing agent, the PH for controlling solution is 4.5, continues to stir 1h;
(3) the above solution is added in the mixed solution for filling a certain amount of aniline, hydrochloric acid, the reaction was continued 2h;
(4) dilute hydrochloric acid, dehydrated alcohol are successively used, deionized water washing filters, until BaCl is added in filtrate2When solution
Until without white precipitate, OP-10 is added dropwise into the solution made and quickly stirs, obtains the polyaniline cream of load organic/inorganic substance powder
Liquid;
(5) Polyaniline emulsion of inorganic powder is filtered resulting load, it is dry;
(6) single screw extrusion machine is added in the product after drying TPO composite material, maleic anhydride, step (5), through molten
Melt hybrid reaction extrusion, TPO film sheet is made in press polish, cooling, curling;
Example test data
Claims (7)
1. a kind of method for preparing multi-functional TPO composite lether, which is characterized in that comprise the steps of:
(1) 30-50% pure water is added in polymeric kettle, acidic materials are added, temperature is controlled at 0-5 DEG C;
(2) stirring of polymeric kettle high speed is added in a certain amount of aniline (being evaporated under reduced pressure twice), certain density persulfuric acid is added dropwise
Ammonium (APS), hydrochloric acid solution, inorganic material powders, dispersing agent, the PH for controlling solution is 2.5-4.5, continues to stir 1h;
(3) the above solution is added in the mixed solution for filling a certain amount of aniline, hydrochloric acid, the reaction was continued 2h;
(4) dilute hydrochloric acid, dehydrated alcohol are successively used, deionized water washing filters, until BaCl2 solution Shi Wubai is added in filtrate
Until color precipitates, OP-10 is added dropwise into the solution made and quickly stirs, obtains the Polyaniline emulsion of load organic/inorganic substance powder;
(5) Polyaniline emulsion of inorganic powder is filtered resulting load, it is dry;
(6) single screw extrusion machine is added in the product after drying TPO composite material, maleic anhydride, step (5), mixed through melting
TPO film sheet is made in conjunction reactive extrursion, press polish, cooling, curling.
2. a kind of method for preparing multi-functional TPO composite lether according to claim 1, which is characterized in that above-mentioned steps
(1) in: acidic materials are hydrochloric acid solution, concentration 1mol/L.
3. a kind of method for preparing multi-functional TPO composite lether according to claim 1, which is characterized in that above-mentioned steps
(2) in: the molar ratio of aniline and ammonium persulfate is 1:2.
4. a kind of method for preparing multi-functional TPO composite lether according to claim 1, which is characterized in that above-mentioned steps
(2) in: electrodeless powder object has calcite, kaolin, wollastonite, talcum, mica, rutile, sericite, pyrophillite, mica, illiteracy
De- soil, shepardite, quartzy calcite, chalk, zeolite, illite, montmorillonite, diatomite, graphite, shepardite, the tremolite, thoroughly ash
The one or several kinds of stone, asbestos, quartz.
5. a kind of method for preparing multi-functional TPO composite lether according to claim 1, which is characterized in that above-mentioned steps
(2) in: dispersing agent is the one or several kinds of white oil, paraffin, low molecular weight polyethylene.
6. a kind of method for preparing multi-functional TPO composite lether according to claim 1, which is characterized in that above-mentioned steps
(2) in: the particle size of inorganic powder object is 50-400 mesh.
7. a kind of method for preparing multi-functional TPO composite lether according to claim 1, which is characterized in that above-mentioned steps
(6) in: TPO composite material mass percent are as follows: 40-60 parts of block copolymerization polypropylene, 10-20 parts of polyolefin elastomer, poly- second
20-30 parts of alkene, 0.03-1 parts of light stabilizer, 8-10 parts of pigment, light stabilizer 0.1-0.5,5-20 parts of anti-wear agent.