CN110128764A - A kind of processing technology of pen resin pen tube - Google Patents
A kind of processing technology of pen resin pen tube Download PDFInfo
- Publication number
- CN110128764A CN110128764A CN201910481602.6A CN201910481602A CN110128764A CN 110128764 A CN110128764 A CN 110128764A CN 201910481602 A CN201910481602 A CN 201910481602A CN 110128764 A CN110128764 A CN 110128764A
- Authority
- CN
- China
- Prior art keywords
- pen
- pen tube
- tube
- injection molding
- carries out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing technologys of pen resin pen tube, raw material mixing, according to following weight percent, PVC 55%, PP 15%, glass fibre 6% and auxiliary agent 9%, it is mixed to get material A, according to following weight percent, PVC 15%, PP 45%, LDPE 15%, auxiliary agent 15%, graphene fiber 6% and pigment 4%, it is mixed to get material B, homogenizing control is wet, material A and material B are put into homogenizing tank be homogenized respectively, homogenising time is greater than 2 hours, primary injection molding, material A is put into injection molding machine and is molded, form pen tube inner tube, quadric injection mould, material B is put into and carries out quadric injection mould in injection molding machine, injection molding forms pen tube outer tube on the outside of pen tube inner tube, obtain semi-finished product.The present invention is conducive to promote the intensity of pen tube inner tube, promotes resistance to deformation and anti-pressure ability is conducive to rationally utilize resource so that pen pen tube is more durable, save production cost.
Description
Technical field
The present invention relates to pen production and processing technical field more particularly to a kind of processing technologys of pen resin pen tube.
Background technique
Pen is a kind of class writing implement for mainly regarding pen body with metal, and it is (more to contain ink by hollow pen tube
It is black or blue), it is write by gravity and capillarity, then via the nib of duck-beak type, weight is different when writing, and can say it is west
The writing implement of calligraphy.The ink of most of pen can refill.Most pen pen tube is made of metal material, resin pen
Pen tube is with respect to a conventional metals pen tube, and more merrily and lightheartedly, production cost is lower, but the processing work of existing pen resin pen tube
The mechanical strength of skill, the resin pen pen tube of production is general, and there are the wastings of resources for production process, so now proposing a kind of pen tree
The processing technology of rouge pen tube.
Summary of the invention
Technical problems based on background technology, the invention proposes a kind of processing technologys of pen resin pen tube.
A kind of processing technology of pen resin pen tube proposed by the present invention, comprising the following steps:
S1: raw material mixing, according to following weight percent, PVC 55%, PP 15%, glass fibre 6% and auxiliary agent 9%,
It is mixed to get material A, according to following weight percent, PVC 15%, PP 45%, LDPE 15%, auxiliary agent 15%, graphene are fine
Dimension 6% and pigment 4%, are mixed to get material B；
S2: homogenizing control is wet, and material A and material B are put into homogenizing tank be homogenized respectively, and it is small that homogenising time is greater than 2
When；
S3: material A is put into injection molding machine and is molded, forms pen tube inner tube by primary injection molding；
S4: material B is put into and carries out quadric injection mould in injection molding machine by quadric injection mould, is molded and is formed on the outside of pen tube inner tube
Pen tube outer tube, obtains semi-finished product；
S5: surface treatment, surface of semi-finished carries out cleaning treatment, and carries out on-line treatment to surface of semi-finished；
S6: then surface treated surface of semi-finished is carried out electroplating processes, obtains finished product pen tube by electroplating processes；
S7: product sampling observation carries out visual examination to finished product pen tube；
S8: it is packaged storage, the finished product pen tube of passed examination is subjected to packing storage, and record batch.
Preferably, in the S7, the underproof product of visual examination is isolated, and to its with a batch of product into
The sampling observation of row emphasis, is isolated batch, underproof finished product pen tube is collected, and carry out crushing recycling by pulverizer, is obtained
Plastics powder.
Preferably, the plastics powder is mixed into material A according to the ratio of 1:100 carries out recycling use.
Preferably, in the S2, so that material A and the water content of material B are less than 1%.
Preferably, the auxiliary agent in the S1 is one of red oil, antioxidant and plasticizer or combination.
Having the beneficial effect that in the present invention
1. being conducive to the intensity for promoting pen tube inner tube by the glass fibre of addition, promoting resistance to deformation and anti-pressure ability, make
Pen pen tube it is more durable, in combination with quadric injection mould formed pen tube outer tube, ensured the aesthetics of pen pen tube
And feel, promote usage experience.
2. being inspected by random samples by setting product, is conducive to control product quality, while the crushing recycling step being arranged, is conducive to close
Reason utilizes resource, saves production cost.
Detailed description of the invention
Fig. 1 is a kind of flow diagram of the processing technology of pen resin pen tube proposed by the present invention；
Fig. 2 is that a kind of each embodiment product testing result of processing technology of pen resin pen tube proposed by the present invention is bent
Line chart.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.
Embodiment 1, referring to Fig.1, a kind of processing technology of pen resin pen tube, comprising the following steps:
S1: raw material mixing, according to following weight percent, PVC 59%, PP 15%, glass fibre 2% and auxiliary agent 9%,
It is mixed to get material A, according to following weight percent, PVC 15%, PP 45%, LDPE 15%, auxiliary agent 15%, graphene are fine
Dimension 6% and pigment 4%, are mixed to get material B；
S2: homogenizing control is wet, and material A and material B are put into homogenizing tank be homogenized respectively, and it is small that homogenising time is greater than 2
When；
S3: material A is put into injection molding machine and is molded, forms pen tube inner tube by primary injection molding；
S4: material B is put into and carries out quadric injection mould in injection molding machine by quadric injection mould, is molded and is formed on the outside of pen tube inner tube
Pen tube outer tube, obtains semi-finished product；
S5: surface treatment, surface of semi-finished carries out cleaning treatment, and carries out on-line treatment to surface of semi-finished；
S6: then surface treated surface of semi-finished is carried out electroplating processes, obtains finished product pen tube by electroplating processes；
S7: product sampling observation carries out visual examination to finished product pen tube；
S8: it is packaged storage, the finished product pen tube of passed examination is subjected to packing storage, and record batch.
In the present embodiment, in S7, the underproof product of visual examination is isolated, and to its with a batch of product into
The sampling observation of row emphasis, is isolated batch, underproof finished product pen tube is collected, and carry out crushing recycling by pulverizer, is obtained
Plastics powder, plastics powder are mixed into material A according to the ratio of 1:100 and carry out recycling use, in S2, so that material A and material B
Water content less than the auxiliary agent in 1%, S1 be one of red oil, antioxidant and plasticizer or combination.
Embodiment 2, referring to Fig.1, a kind of processing technology of pen resin pen tube, comprising the following steps:
S1: raw material mixing, according to following weight percent, PVC 57%, PP 15%, glass fibre 4% and auxiliary agent 9%,
It is mixed to get material A, according to following weight percent, PVC 15%, PP 45%, LDPE 15%, auxiliary agent 15%, graphene are fine
Dimension 6% and pigment 4%, are mixed to get material B；
S2: homogenizing control is wet, and material A and material B are put into homogenizing tank be homogenized respectively, and it is small that homogenising time is greater than 2
When；
S3: material A is put into injection molding machine and is molded, forms pen tube inner tube by primary injection molding；
S4: material B is put into and carries out quadric injection mould in injection molding machine by quadric injection mould, is molded and is formed on the outside of pen tube inner tube
Pen tube outer tube, obtains semi-finished product；
S5: surface treatment, surface of semi-finished carries out cleaning treatment, and carries out on-line treatment to surface of semi-finished；
S6: then surface treated surface of semi-finished is carried out electroplating processes, obtains finished product pen tube by electroplating processes；
S7: product sampling observation carries out visual examination to finished product pen tube；
S8: it is packaged storage, the finished product pen tube of passed examination is subjected to packing storage, and record batch.
In the present embodiment, in S7, the underproof product of visual examination is isolated, and to its with a batch of product into
The sampling observation of row emphasis, is isolated batch, underproof finished product pen tube is collected, and carry out crushing recycling by pulverizer, is obtained
Plastics powder, plastics powder are mixed into material A according to the ratio of 1:100 and carry out recycling use, in S2, so that material A and material B
Water content less than the auxiliary agent in 1%, S1 be one of red oil, antioxidant and plasticizer or combination.
Embodiment 3, referring to Fig.1, a kind of processing technology of pen resin pen tube, comprising the following steps:
S1: raw material mixing, according to following weight percent, PVC 55%, PP 15%, glass fibre 6% and auxiliary agent 9%,
It is mixed to get material A, according to following weight percent, PVC 15%, PP 45%, LDPE 15%, auxiliary agent 15%, graphene are fine
Dimension 6% and pigment 4%, are mixed to get material B；
S2: homogenizing control is wet, and material A and material B are put into homogenizing tank be homogenized respectively, and it is small that homogenising time is greater than 2
When；
S3: material A is put into injection molding machine and is molded, forms pen tube inner tube by primary injection molding；
S4: material B is put into and carries out quadric injection mould in injection molding machine by quadric injection mould, is molded and is formed on the outside of pen tube inner tube
Pen tube outer tube, obtains semi-finished product；
S5: surface treatment, surface of semi-finished carries out cleaning treatment, and carries out on-line treatment to surface of semi-finished；
S6: then surface treated surface of semi-finished is carried out electroplating processes, obtains finished product pen tube by electroplating processes；
S7: product sampling observation carries out visual examination to finished product pen tube；
S8: it is packaged storage, the finished product pen tube of passed examination is subjected to packing storage, and record batch.
In the present embodiment, in S7, the underproof product of visual examination is isolated, and to its with a batch of product into
The sampling observation of row emphasis, is isolated batch, underproof finished product pen tube is collected, and carry out crushing recycling by pulverizer, is obtained
Plastics powder, plastics powder are mixed into material A according to the ratio of 1:100 and carry out recycling use, in S2, so that material A and material B
Water content less than the auxiliary agent in 1%, S1 be one of red oil, antioxidant and plasticizer or combination.
Embodiment 4, referring to Fig.1, a kind of processing technology of pen resin pen tube, comprising the following steps:
S1: raw material mixing, according to following weight percent, PVC 53%, PP 15%, glass fibre 8% and auxiliary agent 9%,
It is mixed to get material A, according to following weight percent, PVC 15%, PP 45%, LDPE 15%, auxiliary agent 15%, graphene are fine
Dimension 6% and pigment 4%, are mixed to get material B；
S2: homogenizing control is wet, and material A and material B are put into homogenizing tank be homogenized respectively, and it is small that homogenising time is greater than 2
When；
S3: material A is put into injection molding machine and is molded, forms pen tube inner tube by primary injection molding；
S4: material B is put into and carries out quadric injection mould in injection molding machine by quadric injection mould, is molded and is formed on the outside of pen tube inner tube
Pen tube outer tube, obtains semi-finished product；
S5: surface treatment, surface of semi-finished carries out cleaning treatment, and carries out on-line treatment to surface of semi-finished；
S6: then surface treated surface of semi-finished is carried out electroplating processes, obtains finished product pen tube by electroplating processes；
S7: product sampling observation carries out visual examination to finished product pen tube；
S8: it is packaged storage, the finished product pen tube of passed examination is subjected to packing storage, and record batch.
In the present embodiment, in S7, the underproof product of visual examination is isolated, and to its with a batch of product into
The sampling observation of row emphasis, is isolated batch, underproof finished product pen tube is collected, and carry out crushing recycling by pulverizer, is obtained
Plastics powder, plastics powder are mixed into material A according to the ratio of 1:100 and carry out recycling use, in S2, so that material A and material B
Water content less than the auxiliary agent in 1%, S1 be one of red oil, antioxidant and plasticizer or combination.
Embodiment 5, referring to Fig.1, a kind of processing technology of pen resin pen tube, comprising the following steps:
S1: raw material mixing, according to following weight percent, PVC 51%, PP 15%, glass fibre 10% and auxiliary agent
9%, it is mixed to get material A, according to following weight percent, PVC 15%, PP 45%, LDPE 15%, auxiliary agent 15%, graphite
Alkene fiber 6% and pigment 4%, are mixed to get material B；
S2: homogenizing control is wet, and material A and material B are put into homogenizing tank be homogenized respectively, and it is small that homogenising time is greater than 2
When；
S3: material A is put into injection molding machine and is molded, forms pen tube inner tube by primary injection molding；
S4: material B is put into and carries out quadric injection mould in injection molding machine by quadric injection mould, is molded and is formed on the outside of pen tube inner tube
Pen tube outer tube, obtains semi-finished product；
S5: surface treatment, surface of semi-finished carries out cleaning treatment, and carries out on-line treatment to surface of semi-finished；
S6: then surface treated surface of semi-finished is carried out electroplating processes, obtains finished product pen tube by electroplating processes；
S7: product sampling observation carries out visual examination to finished product pen tube；
S8: it is packaged storage, the finished product pen tube of passed examination is subjected to packing storage, and record batch.
In the present embodiment, in S7, the underproof product of visual examination is isolated, and to its with a batch of product into
The sampling observation of row emphasis, is isolated batch, underproof finished product pen tube is collected, and carry out crushing recycling by pulverizer, is obtained
Plastics powder, plastics powder are mixed into material A according to the ratio of 1:100 and carry out recycling use, in S2, so that material A and material B
Water content less than the auxiliary agent in 1%, S1 be one of red oil, antioxidant and plasticizer or combination.
Carrying out puncture to the finished product pen tube in embodiment 1-5 can test, and test results are shown in figure 2.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (5)
1. a kind of processing technology of pen resin pen tube, which comprises the following steps:
S1: raw material mixing, according to following weight percent, PVC55%, PP15%, glass fibre 6% and auxiliary agent 9% are mixed
To material A, according to following weight percent, PVC15%, PP45%, LDPE15%, auxiliary agent 15%, graphene fiber 6% and face
Material 4%, is mixed to get material B；
S2: homogenizing control is wet, and material A and material B are put into homogenizing tank be homogenized respectively, and homogenising time is greater than 2 hours；
S3: material A is put into injection molding machine and is molded, forms pen tube inner tube by primary injection molding；
S4: material B is put into and carries out quadric injection mould in injection molding machine by quadric injection mould, and injection molding forms pen tube on the outside of pen tube inner tube
Outer tube obtains semi-finished product；
S5: surface treatment, surface of semi-finished carries out cleaning treatment, and carries out on-line treatment to surface of semi-finished；
S6: then surface treated surface of semi-finished is carried out electroplating processes, obtains finished product pen tube by electroplating processes；
S7: product sampling observation carries out visual examination to finished product pen tube；
S8: it is packaged storage, the finished product pen tube of passed examination is subjected to packing storage, and record batch.
2. a kind of processing technology of pen resin pen tube according to claim 1, which is characterized in that in the S7, externally
It sees and checks that underproof product is isolated, and emphasis sampling observation is carried out with a batch of product to it, batch is isolated, it will be unqualified
Finished product pen tube be collected, and crushing recycling is carried out by pulverizer, obtains plastics powder.
3. a kind of processing technology of pen resin pen tube according to claim 2, which is characterized in that the plastics powder is pressed
It is mixed into material A according to the ratio of 1:100 and carries out recycling use.
4. a kind of processing technology of pen resin pen tube according to claim 1, which is characterized in that in the S2, so that
Material A and the water content of material B are less than 1%.
5. a kind of processing technology of pen resin pen tube according to claim 1, which is characterized in that the auxiliary agent in the S1
For one of red oil, antioxidant and plasticizer or combination.