CN104151761B - The resin dedicated composition of minute surface and its preparation method - Google Patents
The resin dedicated composition of minute surface and its preparation method Download PDFInfo
- Publication number
- CN104151761B CN104151761B CN201410401224.3A CN201410401224A CN104151761B CN 104151761 B CN104151761 B CN 104151761B CN 201410401224 A CN201410401224 A CN 201410401224A CN 104151761 B CN104151761 B CN 104151761B
- Authority
- CN
- China
- Prior art keywords
- minute surface
- resin
- parts
- dedicated composition
- escalol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The resin dedicated composition of minute surface and its preparation method, the resin dedicated composition of minute surface comprises the following raw material according to mass fraction meter: acryl resin 65-68 part, silicon carbide fiber 15-18 part, dimethyl silicone oil 3-5 part, trimethyl citrate 1-5 part, ESCALOL 567 0.3-0.8 part. Tradition acryl resin is carried out modification by the present invention, and rationally composite with other material auxiliary agents, gained resin combination has excellent wear resistance, uses for a long time as minute surface and still can keep clear no marking.
Description
Technical field
The invention belongs to polymeric material field, it is specifically related to a kind of resin dedicated composition of minute surface and its preparation method.
Background technology
Acrylic, chemical name is polymethylmethacrylate, and its transparency is as glass, therefore is commonly called as synthetic glass. Traditional glass has frangible danger, and glass cullet also can injure user, and synthetic glass just well overcomes above-mentioned deficiency, and also has the advantage of easy dyeing, easily processing, therefore more and more people selects the minute surface of acrylic material. But existing acrylic minute surface exists the poor deficiency of wear resistance, long-time use can cause minute surface smudgy.
In sum, how to overcome the deficiencies in the prior art and become existing field problem demanding prompt solution.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art and propose a kind of resin dedicated composition of minute surface and its preparation method, invention resin composition has excellent resistance to wear resistance, and long-time use still can keep minute surface no marking.
The technical scheme of the present invention is as follows:
The resin dedicated composition of minute surface, comprises the following raw material according to mass fraction meter: acryl resin 65-68 part, silicon carbide fiber 15-18 part, dimethyl silicone oil 3-5 part, trimethyl citrate 1-5 part, ESCALOL 567 0.3-0.8 part.
The resin dedicated composition of described minute surface, comprises the following raw material according to mass fraction meter: acryl resin 67 parts, silicon carbide fiber 16 parts, dimethyl silicone oil 4 parts, trimethyl citrate 3 parts, ESCALOL 567 0.5 part.
The preparation method of the resin dedicated composition of described minute surface, comprise the following steps: take each raw material according to quality proportioning, acryl resin, silicon carbide fiber, dimethyl silicone oil, trimethyl citrate, ESCALOL 567 are uniformly mixed, extrude by forcing machine, extruder temperature controls at 160-165 DEG C, obtains the resin dedicated composition of minute surface.
Useful effect: tradition acryl resin is carried out modification by the present invention, and rationally composite with other material auxiliary agents, gained resin combination has excellent wear resistance, uses for a long time as minute surface and still can keep clear no marking.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment 1
The resin dedicated composition of minute surface, comprises the following raw material according to mass fraction meter: acryl resin 65 parts, silicon carbide fiber 15 parts, dimethyl silicone oil 3 parts, trimethyl citrate 1 part, ESCALOL 567 0.3 part.
The preparation method of the present embodiment, comprise the following steps: take each raw material according to quality proportioning, acryl resin, silicon carbide fiber, dimethyl silicone oil, trimethyl citrate, ESCALOL 567 are uniformly mixed, extrude by forcing machine, extruder temperature controls at 160 DEG C, obtains the resin dedicated composition of minute surface.
This embodiment gained finished product is carried out Performance Detection, and detected result is in table 1.
Embodiment 2
The resin dedicated composition of minute surface, comprises the following raw material according to mass fraction meter: acryl resin 68 parts, silicon carbide fiber 18 parts, dimethyl silicone oil 5 parts, trimethyl citrate 5 parts, ESCALOL 567 0.8 part.
The preparation method of the present embodiment, comprise the following steps: take each raw material according to quality proportioning, acryl resin, silicon carbide fiber, dimethyl silicone oil, trimethyl citrate, ESCALOL 567 are uniformly mixed, extrude by forcing machine, extruder temperature controls at 165 DEG C, obtains the resin dedicated composition of minute surface.
This embodiment gained finished product is carried out Performance Detection, and detected result is in table 1.
Embodiment 3
The resin dedicated composition of minute surface, comprises the following raw material according to mass fraction meter: acryl resin 67 parts, silicon carbide fiber 16 parts, dimethyl silicone oil 4 parts, trimethyl citrate 3 parts, ESCALOL 567 0.5 part.
The preparation method of the present embodiment, comprise the following steps: take each raw material according to quality proportioning, acryl resin, silicon carbide fiber, dimethyl silicone oil, trimethyl citrate, ESCALOL 567 are uniformly mixed, extrude by forcing machine, extruder temperature controls at 165 DEG C, obtains the resin dedicated composition of minute surface.
Embodiment 1-3 gained finished product is carried out performance test, and after normally using 10000 times, wear rate the results are shown in following table 1:
Table 1 performance test data
| Performance | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Wear rate | 1% | 1% | 1% |
As seen from the above table, gained finished product of the present invention has good wear resisting property.
Above-described embodiment is only the explanation to product of the present invention; not the present invention is made any restriction in form; within the technical scheme scope not departing from the present invention, any equivalent utilizing the technology contents of above-mentioned announcement to make simple transformation, all belongs to protection scope of the present invention.
Claims (2)
1. the resin dedicated composition of minute surface, it is characterized in that, comprise the following raw material according to mass fraction meter: acryl resin 65-68 part, silicon carbide fiber 15-18 part, dimethyl silicone oil 3-5 part, trimethyl citrate 1-5 part, ESCALOL 567 0.3-0.8 part;
The resin dedicated composition of described minute surface is made up of following preparation method, step is as follows: take each raw material according to quality proportioning, acryl resin, silicon carbide fiber, dimethyl silicone oil, trimethyl citrate, ESCALOL 567 are uniformly mixed, extrude by forcing machine, extruder temperature controls at 160-165 DEG C, obtains the resin dedicated composition of minute surface.
2. the resin dedicated composition of minute surface according to claim 1, it is characterized in that, comprise the following raw material according to mass fraction meter: acryl resin 67 parts, silicon carbide fiber 16 parts, dimethyl silicone oil 4 parts, trimethyl citrate 3 parts, ESCALOL 567 0.5 part.