CN110102587A - A kind of wire-drawing lubrication powder - Google Patents
A kind of wire-drawing lubrication powder Download PDFInfo
- Publication number
- CN110102587A CN110102587A CN201910404844.5A CN201910404844A CN110102587A CN 110102587 A CN110102587 A CN 110102587A CN 201910404844 A CN201910404844 A CN 201910404844A CN 110102587 A CN110102587 A CN 110102587A
- Authority
- CN
- China
- Prior art keywords
- agent
- wire
- drawing lubrication
- powder according
- lubrication
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of wire-drawing lubrication powder, is made of the following components by weight: lubrication filler 20-60, EP agent 4-20, auxiliary agent 8-20, modifying agent 2-15, graphene 6-20, water absorbing agent 8-25.The invention has the advantages and positive effects of: providing a kind of wire-drawing lubrication powder, there are good extensibility and lubricity, steel wire surface can not only be firmly adsorbed on, and extensional can be carried out with steel wire, lubricating film is in layer structure, molecular binding affinities are strong in every layer, and molecular binding affinities are weak between each layer.
Description
Technical field
The invention is related to lubriation material field, is specifically related to a kind of wire-drawing lubrication powder.
Background technique
Wire-drawing lubrication powder plays greasy property during wire cold-drawing machining deformation, reduces coefficient of friction, saves energy
Consumption, extends the service life of wire-drawing die.In drawing mild steel wire, high-carbon steel wire, specific alloy steel wire, stainless steel steel wire etc.
When a series of metal wire rods, steel wire can be made as the extension of steel wire deforms, a kind of lubricating film to be formed, to finished product during the drawing process
Silk plays the protective effects such as anti-corrosion, improves the surface quality of finished silk, and the coating on subsequent technique is facilitated to handle etc..
Summary of the invention
The problem to be solved by the invention is to provide a kind of wire-drawing lubrication powder, have good extensibility and lubricity, i.e.,
It can not only be firmly adsorbed on steel wire surface, and extensional can be carried out with steel wire, lubricating film is in layer structure, is divided in every layer
Sub- binding force is strong, and molecular binding affinities are weak between each layer.
In order to solve the above technical problems, the invention the technical solution adopted is that: a kind of wire-drawing lubrication powder, by weight
Meter is made of the following components: lubrication filler 20-60, EP agent 4-20, auxiliary agent 8-20, modifying agent 2-15, graphene 6-20,
Water absorbing agent 8-25.
Further, the EP agent is selected fatty acid, vulcanization butter, tripolyphosphate, kodalk or phosphoric acid
Sodium.
Further, the lubrication filler is in lime, talcum powder, land plaster, mineral powder, titanium dioxide and organobentonite
One or more of compounds；
Further, the auxiliary agent be to be mixed by soluble alkali metal salts, glycerol stearate monoesters or polyvinyl alcohol with water
It forms.
Further, the water absorbing agent is layered sodium disilicate.
Further, the modifying agent be alkali or alkaline earth metal hydroxide, mono-quaternaries, over-expense quaternary ammonium salt in one
Kind.
Further, it is made of the following components by weight: lubrication filler 25-50, EP agent 4-15, auxiliary agent 10-
18, modifying agent 4-10, graphene 10-15, water absorbing agent 10-15.
The invention has the advantages and positive effects of: a kind of wire-drawing lubrication powder is provided, have good extensibility and
Lubricity can not only be firmly adsorbed on steel wire surface, and can carry out extensional with steel wire, lubricating film is in stratiform knot
Structure, molecular binding affinities are strong in every layer, and molecular binding affinities are weak between each layer.
Specific embodiment
Detailed description of specific embodiments of the invention is provided below.
A kind of following wire-drawing lubrication powder as described in the examples, the EP agent be selected fatty acid, vulcanization butter,
Tripolyphosphate, kodalk or sodium phosphate.The lubrication filler be lime, talcum powder, land plaster, mineral powder, titanium dioxide with
And the compound of one or more of organobentonite.The auxiliary agent be by soluble alkali metal salts, glycerol stearate list
Ester or polyvinyl alcohol are mixed with water.The water absorbing agent is layered sodium disilicate.The modifying agent is alkali metal or alkaline earth gold
Belong to one of hydroxide, mono-quaternaries, over-expense quaternary ammonium salt.
Embodiment 1
A kind of wire-drawing lubrication powder, is made of the following components by weight: lubrication filler 30, EP agent 10, auxiliary agent
10, modifying agent 12, graphene 18, water absorbing agent 20.
Embodiment 2
A kind of wire-drawing lubrication powder, is made of the following components by weight: lubrication filler 50, EP agent 5, auxiliary agent
10, modifying agent 5, graphene 6, water absorbing agent 24.
Embodiment 3
A kind of wire-drawing lubrication powder, is made of the following components by weight: lubrication filler 60, EP agent 4, auxiliary agent 8,
Modifying agent 3, graphene 10, water absorbing agent 15.
The embodiment of the invention is described in detail above, but the content is only the preferable of the invention
Embodiment should not be considered as limiting the scope of the invention.It is all according to equivalent change made by the invention range with
Improve etc., it shall still fall within the scope of this patent.
Claims (7)
1. a kind of wire-drawing lubrication powder, it is characterised in that: be made of the following components by weight: lubrication filler 20-60, extreme pressure add
Add agent 4-20, auxiliary agent 8-20, modifying agent 2-15, graphene 6-20, water absorbing agent 8-25.
2. a kind of wire-drawing lubrication powder according to claim 1, it is characterised in that: the EP agent is to select fat
Acid, vulcanization butter, tripolyphosphate, kodalk or sodium phosphate.
3. a kind of wire-drawing lubrication powder according to claim 1, it is characterised in that: the lubrication filler be lime, talcum powder,
The compound of one or more of land plaster, mineral powder, titanium dioxide and organobentonite.
4. a kind of wire-drawing lubrication powder according to claim 1, it is characterised in that: the auxiliary agent be by soluble alkali metal
Salt, glycerol stearate monoesters or polyvinyl alcohol and water mix.
5. a kind of wire-drawing lubrication powder according to claim 1, it is characterised in that: the water absorbing agent is layered sodium disilicate.
6. a kind of wire-drawing lubrication powder according to claim 1, it is characterised in that: the modifying agent is alkali metal or alkaline earth gold
Belong to one of hydroxide, mono-quaternaries, over-expense quaternary ammonium salt.
7. a kind of wire-drawing lubrication powder according to claim 1, it is characterised in that: be made of the following components by weight:
Lubricate filler 25-50, EP agent 4-15, auxiliary agent 10-18, modifying agent 4-10, graphene 10-15, water absorbing agent 10-15.