CN110003653A - A kind of composition, preparation method and application - Google Patents
A kind of composition, preparation method and application Download PDFInfo
- Publication number
- CN110003653A CN110003653A CN201910201981.9A CN201910201981A CN110003653A CN 110003653 A CN110003653 A CN 110003653A CN 201910201981 A CN201910201981 A CN 201910201981A CN 110003653 A CN110003653 A CN 110003653A
- Authority
- CN
- China
- Prior art keywords
- composition
- preparation
- flowable
- agent
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to technical field of polymer materials more particularly to a kind of compositions, preparation method and application.The present invention provides a kind of compositions, comprising: rubber composition, elastomer, foaming agent, flowable, surfactant, antibacterial agent and curing agent；The elastomer is polyurethane elastomer.The present invention also provides a kind of preparation method of above-mentioned composition, a kind of application of the product obtained the present invention also provides above-mentioned composition or above-mentioned preparation method in preparation antibacterial, anti-aging and wear-resisting sole.In the present invention, antibacterial agent and foaming agent make sole have good damping, antibacterial and ventilative effect, and curing agent can effectively enhance the wear-resisting property of sole, and flowable and surfactant can effectively facilitate the fusion of each component.A kind of composition provided by the invention, preparation method and application, solve in the prior art, basketball shoes sole cannot be considered in terms of the technological deficiency of excellent air permeability, anti-microbial property, damping effect and wear-resisting property.
Description
Technical field
The invention belongs to technical field of polymer materials more particularly to a kind of compositions, preparation method and application.
Background technique
With being widely current for this movement of basketball, more and more young men or even a middle-aged person joined basketball fortune
Dynamic main forces, correspondingly, this market of basketball shoes also just grow stronger day by day.Basketball is a strenuous exercise, in order to deal with fierceness
Movement, for a pair of basketball shoes, it is desirable to which good durability, supportive, stability and good subtract comfort
Shake effect.Constantly starting, emergency stop, take-off and movement is rapidly moved left and right etc. in basketball movement, so that consumer selects basket
One of the characteristic of shoes must be placed on absolute first place when sneakers, and determine the critical function component of basketball shoes characteristic is exactly basketball shoes
Sole.
It can acutely perspire when due to playing basketball, the permeability and anti-microbial property of basketball shoes will be particularly important, no
Foot's bacteria breed will then be will lead to, cause foot uncomfortable；Meanwhile the sole as basketball shoes, it is necessary to have good damping
Performance and wear-resisting property are the characteristics of consumer pay close attention to very much.Basketball shoes sole in the prior art, there is cannot be considered in terms of
The defect of above-mentioned performance.
Therefore, a kind of composition, preparation method and application are developed, for solving in the prior art, basketball shoes sole without
Method takes into account the technological deficiency of excellent air permeability, anti-microbial property, damping effect and wear-resisting property, becomes those skilled in the art
Urgent problem to be solved,
Summary of the invention
In view of this, the present invention provides a kind of composition, preparation method and application, for solving in the prior art, basket
Sneakers sole cannot be considered in terms of the technological deficiency of excellent air permeability, anti-microbial property, damping effect and wear-resisting property.
The present invention provides a kind of composition, the raw material of the composition include: rubber composition, elastomer, foaming agent,
Flowable, surfactant, antibacterial agent and curing agent；
The elastomer is polyurethane elastomer.
Preferably, the rubber composition includes: isoprene rubber, nitrile rubber, polysulfide rubber and neoprene.
Preferably, in terms of mass parts, the raw material of the composition includes: 100~120 parts of rubber composition, elastomer 10
~15 parts, 5~10 parts of foaming agent, 2~5 parts of flowable, 5~15 parts of surfactant, 0.5~2 part of antibacterial agent and curing agent 3
~5 parts.
Preferably, the antibacterial agent is nano silver.
Preferably, the curing agent is selected from: 2- secondary butyl phenenyl-N- methyl carbamate, cumyl peroxide with
And any one or more in -2,5 bis(t-butylperoxy) hexane of 2,5- dimethyl.
Preferably, the flowable is selected from: polypropylene plastics flowable, polyester flowable and high impact polystyrene modeling
Expect any one or more in flowable.
Preferably, the foaming agent are as follows: calcium carbonate and/or carbon black.
Preferably, the surfactant is selected from: any one in sodium stearyl sulfate, odium stearate and Tween 80
Kind is a variety of.
The present invention also provides a kind of preparation method including one composition of any of the above, the preparation methods
Are as follows: isoprene rubber, polysulfide rubber, neoprene, elastomer, foaming agent, flowable, surfactant, resists nitrile rubber
After microbial inoculum and curing agent mixing, successively it is granulated, forms after being kneaded three times, obtain product.
The present invention also provides a kind of productions obtained including composition or above-mentioned preparation method described in any of the above one
Application of the product in preparation antibacterial, anti-aging and wear-resisting sole.
In conclusion the raw material of the composition includes: rubber composition, elasticity the present invention provides a kind of composition
Body, foaming agent, flowable, surfactant, antibacterial agent and curing agent；The elastomer is polyurethane elastomer.The present invention
A kind of preparation method of above-mentioned composition is additionally provided, the present invention also provides a kind of above-mentioned compositions or above-mentioned preparation method to obtain
To product in preparation antibacterial, the application in anti-aging and wear-resisting sole.In technical solution provided by the invention, the formula of sole
In include: antibacterial agent and foaming agent so that sole has good damping, antibacterial and ventilative effect, meanwhile, curing agent
The wear-resisting property of sole can effectively be enhanced, flowable and surfactant can effectively facilitate the fusion of each component, so that composition
Quality is stable, homogeneous when preparation；Further, it can be obtained through detection, compared with commercially available similar basketball shoes sole, the present invention is mentioned
Product made from the technical solution of confession, properties are significantly better than commercial product.A kind of composition provided by the invention, system
Preparation Method and application solve in the prior art, and basketball shoes sole cannot be considered in terms of excellent air permeability, anti-microbial property, damping effect
The technological deficiency of fruit and wear-resisting property.
Specific embodiment
The present invention provides a kind of composition, preparation method and application, for solving in the prior art, basketball shoes sole without
Method takes into account the technological deficiency of excellent air permeability, anti-microbial property, damping effect and wear-resisting property.
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
In order to which the present invention is described in more detail, below with reference to embodiment to a kind of composition provided by the invention, preparation method
And application, it is specifically described.
Embodiment 1
The present embodiment is the specific embodiment for preparing sole product 1.
105Kg rubber composition, 15Kg elastomer, 7Kg foaming agent, 5Kg flowable, 12Kg surfactant, 2Kg antibacterial
Agent and 5Kg curing agent after mixing, into mixing step.In the present embodiment, elastomer is polyurethane elastomer, antibacterial agent
For nano silver, curing agent is 2- secondary butyl phenenyl-N- methyl carbamate, and flowable is polypropylene plastics flowable, foaming
Agent is calcium carbonate, and surfactant is sodium stearyl sulfate；Rubber composition is by 20Kg isoprene rubber, 30Kg butyronitrile rubber
Glue, 40Kg polysulfide rubber and 15Kg neoprene mixing composition.
In the present embodiment, after being kneaded three times using conventional mixing method, pressing mold molding can obtain product 1.
Embodiment 2
The present embodiment is the specific embodiment for preparing sole product 2.
100Kg rubber composition, 10Kg elastomer, 5Kg foaming agent, 2Kg flowable, 5Kg surfactant, 0.5Kg are anti-
Microbial inoculum and 3Kg curing agent after mixing, into mixing step.In the present embodiment, elastomer is polyurethane elastomer, antibacterial
Agent is nano silver, and curing agent is cumyl peroxide, and flowable is polyester flowable, and foaming agent is carbon black, surfactant
For odium stearate；Rubber composition is by 25Kg isoprene rubber, 25Kg nitrile rubber, 25Kg polysulfide rubber and 25Kg neoprene
Rubber mix composition.
In the present embodiment, after being kneaded three times using conventional mixing method, pressing mold molding can obtain product 2.
Embodiment 3
The present embodiment is the specific embodiment for preparing sole product 3.
120Kg rubber composition, 14Kg elastomer, 10Kg foaming agent, 3Kg flowable, 15Kg surfactant, 1.5Kg
Antibacterial agent and 4Kg curing agent after mixing, into mixing step.In the present embodiment, elastomer is polyurethane elastomer, is resisted
Microbial inoculum is nano silver, and curing agent 2,5- dimethyl -2,5 bis(t-butylperoxy) hexane, flowable is high-impact polyphenyl second
Alkene plastics flowable, foaming agent are carbon black, and surfactant is Tween 80；Rubber composition by 30Kg isoprene rubber,
20Kg nitrile rubber, 20Kg polysulfide rubber and 50Kg neoprene mixing composition.
In the present embodiment, after being kneaded three times using conventional mixing method, pressing mold molding can obtain product 1.
Wear-resisting property, anti-microbial property, permeability and the damping property of product 1~3 made from Examples 1 to 3 are measured respectively
Can, and select commercial like product as control.It can be obtained through detection, technical solution provided in an embodiment of the present invention is obtained to be produced
Product, above-mentioned properties are superior to commercial like product, also, product made from technical solution provided in an embodiment of the present invention,
Also there is good anti-skidding, water-fastness and waterproof performance.
From above-described embodiment, it can be concluded that, technical solution provided by the invention is had the advantage that
1, in formula provided by the invention, the selection of elastomer and foaming agent may make product to have good elasticity, from
And ensure its good damping effect；
2, in technical solution provided by the invention, the selection of antibacterial agent may make product to have good anti-microbial property, prevent
Only every uncomfortable situation such as foot's itch occurs, and optimizes user experience；
3, in technical solution provided by the invention, the selection of surfactant and flowable can effectively facilitate raw material each group
Point fusion, the difficulty during the subsequent mixed refining process of product and melting temperature is effectively reduced, simultaneously, it is ensured that each component uniformly melts
It closes, it is ensured that the stability of product quality；
4, in technical solution provided by the invention, the selection of curing agent generates synergistic effect with elastomer, foaming agent, into
One step enhances elastomer, mechanical property brought by foaming agent, meanwhile, can also further be promoted the wearability of product, skid resistance,
Wash durability and anti-yellowing property；
5, in technical solution provided by the invention, rubber composition is mixed with a variety of rubber, and obtained product has been taken into account respectively
The advantages of kind rubber, properties of product are excellent.
In conclusion the raw material of the composition includes: rubber composition, elasticity the present invention provides a kind of composition
Body, foaming agent, flowable, surfactant, antibacterial agent and curing agent；The elastomer is polyurethane elastomer.The present invention
A kind of preparation method of above-mentioned composition is additionally provided, the present invention also provides a kind of above-mentioned compositions or above-mentioned preparation method to obtain
To product in preparation antibacterial, the application in anti-aging and wear-resisting sole.In technical solution provided by the invention, the formula of sole
In include: antibacterial agent and foaming agent so that sole has good damping, antibacterial and ventilative effect, meanwhile, curing agent
The wear-resisting property of sole can effectively be enhanced, flowable and surfactant can effectively facilitate the fusion of each component, so that composition
Quality is stable, homogeneous when preparation；Further, it can be obtained through detection, compared with commercially available similar basketball shoes sole, the present invention is mentioned
Product made from the technical solution of confession, properties are significantly better than commercial product.A kind of composition provided by the invention, system
Preparation Method and application solve in the prior art, and basketball shoes sole cannot be considered in terms of excellent air permeability, anti-microbial property, damping effect
The technological deficiency of fruit and wear-resisting property.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, various improvements and modifications may be made without departing from the principle of the present invention, these improvements and modifications are also answered
It is considered as protection scope of the present invention.
Claims (10)
1. a kind of composition, which is characterized in that the raw material of the composition includes: rubber composition, elastomer, foaming agent, stream
Dynamic agent, surfactant, antibacterial agent and curing agent；
The elastomer is polyurethane elastomer.
2. composition according to claim 1, which is characterized in that the rubber composition includes: isoprene rubber, fourth
Nitrile rubber, polysulfide rubber and neoprene.
3. composition according to claim 1, which is characterized in that in terms of mass parts, the raw material of the composition includes: rubber
100~120 parts of glue mixture, 10~15 parts of elastomer, 5~10 parts of foaming agent, 2~5 parts of flowable, surfactant 5~15
Part, 0.5~2 part of antibacterial agent and 3~5 parts of curing agent.
4. composition according to claim 1, which is characterized in that the antibacterial agent is nano silver.
5. composition according to claim 1, which is characterized in that the curing agent is selected from: 2- secondary butyl phenenyl-N- methyl
In -2,5 bis(t-butylperoxy) hexane of carbamate, cumyl peroxide and 2,5- dimethyl any one or
It is a variety of.
6. composition according to claim 1, which is characterized in that the flowable is selected from: polypropylene plastics flowable gathers
Any one or more in ester flowable and Hips Plastics flowable.
7. composition according to claim 1, which is characterized in that the foaming agent are as follows: calcium carbonate and/or carbon black.
8. composition according to claim 1, which is characterized in that the surfactant is selected from: sodium stearyl sulfate,
Any one or more in odium stearate and Tween 80.
9. a kind of preparation method including composition described in claim 1 to 8 any one, which is characterized in that the preparation side
Method are as follows:
Isoprene rubber, nitrile rubber, polysulfide rubber, neoprene, elastomer, foaming agent, flowable, surfactant,
After antibacterial agent and curing agent mixing, successively it is granulated, forms after being kneaded three times, obtain product.
10. a kind of obtain including composition described in claim 1 to 8 any one or preparation method as claimed in claim 9
Product in preparation antibacterial, the application in anti-aging and wear-resisting sole.