CN109826018A - A kind of warming Reflection fabric of traffic police's uniform - Google Patents
A kind of warming Reflection fabric of traffic police's uniform Download PDFInfo
- Publication number
- CN109826018A CN109826018A CN201910135080.4A CN201910135080A CN109826018A CN 109826018 A CN109826018 A CN 109826018A CN 201910135080 A CN201910135080 A CN 201910135080A CN 109826018 A CN109826018 A CN 109826018A
- Authority
- CN
- China
- Prior art keywords
- fabric
- parts
- warming
- traffic police
- subdues
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of traffic police to subdue warming Reflection fabric, and the fabric is prepared by the following method: (1) being uniformly mixed reflective resin, aluminium silver powder, luminescent powder, butyl acetate;Then glass microballoon, dispersing agent and curing agent are sequentially added, continuously stirs 30~60min after mixing, reflecting coating is made;(2) by as mass percent be 55~65% bombax cotton, 20~30% nylon fibre and 15~25% blend polyester made of composite fiber material be immersed in impregnate 2~3d in far-infrared emission material and anti-biotic material finishing fluid after take out and roll, primary, washing of continuously soaping after drying is dried afterwards to get thermal fabric twice;(3) coating is carried out with the thermal fabric that reflecting coating prepared by step (1) prepares step (2), obtains warming Reflection fabric.Fabric prepared by the present invention has preferable warmth retention property and reflectivity, while also having centainly antibacterial, uvioresistant and far infrared transmission performance, and rear each performance is substantially unaffected fabric after washing several times.
Description
Technical field
The present invention relates to a kind of traffic police to subdue warming Reflection fabric, belongs to traffic police and subdues reflectorized material preparation technical field.
Background technique
Reflectorized material, also referred to as retroreflecting material or reflecting material, including reflective membrane, reflective ink, reflector marking
Paint, reflective fabric, reflective leather, reflective fabric and reflection safety sex pilus fabric etc..Its principle is introduced on corresponding material surface
A kind of glass microballoon or the micro- lattice structure of prism of high refractive index, are widely used in traffic mark, License Plate, clothing shoes
Cap, fire-fighting, railway, water transport, mining area etc..Reflective cloth is relatively conventional one of reflectorized material, is mainly used for various reflecting clothes
The production of object, such as the production for traffic police's uniform.
With the continuous improvement of social progress and living standard, the requirement for subduing fabric to traffic police is also higher and higher.Therefore
The traffic police that a kind of thermal property is good, reflecting effect is good is provided and subdues warming Reflection fabric, is suitble to use under cold environment,
While increasing traffic police's safety, the warming effect of uniform is also increased.
Summary of the invention
In view of the above existing problems in the prior art, the present invention provides a kind of traffic police to subdue warming Reflection fabric, prepared
Fabric have preferable warmth retention property and reflectivity, while also have certain biocidal property, uvioresistant and far infrared transmission
Can, and rear each performance is substantially unaffected fabric after washing several times.
To achieve the above object, the present invention adopts the following technical scheme:
A kind of warming Reflection fabric of traffic police's uniform, is prepared by the following method:
(1) reflective resin, aluminium silver powder, luminescent powder, butyl acetate are uniformly mixed;Then it sequentially adds glass microballoon, divide
Powder and curing agent, continuously stir 30~60min after mixing, and reflecting coating is made;
(2) composite fiber material is immersed in after impregnating 2~3d in far-infrared emission material and anti-biotic material finishing fluid and is taken
It rolls out, first 1~2min of preliminary drying in 110~120 DEG C of baking ovens, 3~5min is then dried at 130~140 DEG C, continuously soaps one
Secondary, washing is dried afterwards to get thermal fabric twice;The composite fiber material is fine by the kapok that mass percent is 55~65%
Dimension, 20~30% nylon fibre and 15~25% blend polyester form;
(3) coating is carried out with the thermal fabric that reflecting coating prepared by step (1) prepares step (2), must kept warm reflective
Fabric.
As the further improvement of invention, the weight proportion of each material in step (1) are as follows: 250~375 parts of reflective resin,
15~22.5 parts of aluminium silver powder, 15~20 parts of luminescent powder, 40~60 parts of butyl acetate;200~300 parts of glass microballoon, dispersing agent 20
~30 parts, 30~45 parts of curing agent.
As the further improvement of invention, far-infrared emission material and anti-biotic material finishing fluid in step (2) according to
Lower section method preparation: a, 87.5~106 parts of modified nanometer zirconium dioxide particles are added to 200~300 parts of pH be 7.5~
In 8.5 deionized water, transparent nano zirconium dioxide dispersion liquid is obtained after 10~20min of ultrasound;B, by 62.5~78.5 parts of antibacterials
Material, 10~13.5 parts of dispersing agents, 15~20 parts of adhesives are added in nano zirconium dioxide dispersion liquid, are uniformly mixed, continuously
It stirs 10~20min and target finishing fluid is made.
As the further improvement of invention, the preparation process of the modified nano zirconium dioxide is as follows: by nanometer two
Zirconia particles are mixed with 2.5~3.5 parts of zirconium class coupling agents, then 30~60min of ball milling in the ball mill, finally will be after ball milling
Sample 12~18h is dried in vacuo in 60 DEG C of baking ovens to get modified nano-silica particulate zirconia.
As the further improvement of invention, soaping condition in step (2) are as follows: fabric soaped to 20 at 50~60 DEG C~
30min, bath raio 1:60, soap lye concentration are 1.5~2g/L.
As the further improvement of invention, the anti-biotic material in step (2) includes that weight ratio is 0.8~1:0.8~1
Nano titanium dioxide particles and nano zine oxide particle.
As the further improvement of invention, the coating layer thickness is 150~250 μm.
As the further improvement of invention, the reflective resin is one of acrylic resin or polyester resin;It is described
Curing agent is amino resin curing agents.
The present invention has the advantage that compared with prior art
1, for the present invention using composite fiber material made of bombax cotton, nylon fibre and blend polyester as base fabric, polyamide fibre is fine
Peacekeeping polyester fiber is more commonly used raw material in thermal fabric, and bombax cotton hollow rate is high, and thermal-conduction resistance is high, therefore with this
Composite fiber material is that base fabric has preferable thermal property while ensuring snugness of fit;Bombax cotton is planted as natural
Unique functional fiber in fibres also has preferable biocidal property.
2, the present invention is during the preparation process by composite fiber material whole containing far-infrared emission material and anti-biotic material
Impregnated in reason liquid, and by roll, dry, soaping and etc. increase the adsorptivity of fabric, improve the viscous of functional material and fabric
Fastness is closed, and then improves the washing fastness of fabric;Far-infrared emission material can absorb what human body itself distributed outward at normal temperature
Heat, improves warming effect conscientiously, and anti-biotic material can further enhance the antibiotic property of fabric;And anti-biotic material is by nano-silica
Change particulate zirconia and nano zine oxide particle composition, while improving fabric antibacterial effect, can also enhance the uvioresistant of fabric
Performance;The present invention is first modified nanometer zirconium dioxide particle before preparing far-infrared emission material, it can be improved and is being situated between
Dispersion stabilization in matter, to enhance the performance of far-infrared emission material.
3, reflective resin and aluminium silver powder, glass microballoon etc. with reflection action are passed through curing agent to thermal surface by the present invention
Material carries out coating, and the reflective resin transparency after solidification is good, brightness is high, heat-resist, makes the Reflection fabric reflective of preparation
More preferably;The present invention also adds luminescent powder in reflecting coating, can be improved the reflective of fabric night use, to enhance traffic police
Personal safety.
4, traffic police prepared by the present invention subdues warming Reflection fabric, has preferable warmth retention property and reflecting properties, simultaneously also
With certain antibacterial, uvioresistant and far infrared transmission performance, and fabric after washing several times after each performance be substantially unaffected,
Therefore there is preferable market application prospect.
Specific embodiment
Below with reference to embodiment, the present invention will be described in detail, it is to be understood that protection scope of the present invention is not had
The limitation of body embodiment.
Embodiment 1
A kind of traffic police subdues warming Reflection fabric, it is specific the preparation method is as follows:
(1) 375 parts of reflective resins, 22.5 parts of aluminium silver powder, 20 parts of luminescent powders, 60 parts of butyl acetates are uniformly mixed;Then
300 parts of glass microballoons, 30 parts of dispersing agents, 45 parts of amino resin curing agents are sequentially added, continuously stir 30 after mixing~
Reflecting coating is made in 60min;
It (2) will be 55~65% bombax cotton, 20~30% nylon fibre and 15~25% by mass percent
Composite fiber material made of blend polyester is immersed in far-infrared emission material and anti-biotic material finishing fluid and takes after 2~3d of dipping
It rolls out, first 1~2min of preliminary drying in 110~120 DEG C of baking ovens, 3~5min is then dried at 130~140 DEG C, continuously soaps one
Secondary, washing is dried afterwards to get thermal fabric twice;
(3) coating is carried out with the thermal fabric that reflecting coating prepared by step (1) prepares step (2), coating layer thickness is
150~250 μm, obtain warming Reflection fabric.
Above-mentioned far-infrared emission material and anti-biotic material finishing fluid are prepared in accordance with the following methods: a, modified by 106 parts
Nanometer zirconium dioxide particle is added in the deionized water that 200~300 parts of pH are 7.5~8.5, is obtained thoroughly after 10~20min of ultrasound
Bright nano zirconium dioxide dispersion liquid;B, 78.5 parts of anti-biotic materials, 13.5 parts of dispersing agents, 20 parts of adhesives are added to nano-silica
Change in zirconium dispersion liquid, be uniformly mixed, continuously stirs 10~20min and target finishing fluid is made.
Wherein, the preparation process of modified nano zirconium dioxide is as follows: by nanometer zirconium dioxide particle and 3.5 parts of zirconium classes
Coupling agent mixing, then the sample after ball milling, is finally dried in vacuo by 30~60min of ball milling in the ball mill in 60 DEG C of baking ovens
12~18h is to get modified nano-silica particulate zirconia.
Wherein, anti-biotic material includes the nano titanium dioxide particles and nano oxygen that weight ratio is 0.8~1:0.8~1
Change zinc particle.
Above-mentioned soaping condition are as follows: fabric is soaped 20~30min at 50~60 DEG C, bath raio 1:60, soap lye concentration is
1.5~2g/L.
Above-mentioned reflective resin is one of acrylic resin or polyester resin.
Embodiment 2
A kind of traffic police subdues warming Reflection fabric, it is specific the preparation method is as follows:
(1) 375 parts of reflective resins, 22.5 parts of aluminium silver powder, 20 parts of luminescent powders, 60 parts of butyl acetates are uniformly mixed;Then
300 parts of glass microballoons, 30 parts of dispersing agents, 45 parts of amino resin curing agents are sequentially added, continuously stir 30 after mixing~
Reflecting coating is made in 60min;
It (2) will be 55~65% bombax cotton, 20~30% nylon fibre and 15~25% by mass percent
Composite fiber material made of blend polyester is immersed in far-infrared emission material and anti-biotic material finishing fluid and takes after 2~3d of dipping
It rolls out, first 1~2min of preliminary drying in 110~120 DEG C of baking ovens, 3~5min is then dried at 130~140 DEG C, continuously soaps one
Secondary, washing is dried afterwards to get thermal fabric twice;
(3) coating is carried out with the thermal fabric that reflecting coating prepared by step (1) prepares step (2), coating layer thickness is
150~250 μm, obtain warming Reflection fabric.
Above-mentioned far-infrared emission material and anti-biotic material finishing fluid are prepared in accordance with the following methods: a, modified receiving 95 parts
Rice zirconium dioxide particle is added in the deionized water that 200~300 parts of pH are 7.5~8.5, is obtained after 10~20min of ultrasound transparent
Nano zirconium dioxide dispersion liquid;B, 70 parts of anti-biotic materials, 11.5 parts of dispersing agents, 16 parts of adhesives are added to nano zirconium dioxide
It in dispersion liquid, is uniformly mixed, continuously stirs 10~20min and target finishing fluid is made.
Wherein, the preparation process of modified nano zirconium dioxide is as follows: nanometer zirconium dioxide particle and 3 parts of zirconium classes is even
Join agent mixing, then 30~60min of ball milling in the ball mill, is finally dried in vacuo 12 in 60 DEG C of baking ovens for the sample after ball milling
~18h is to get modified nano-silica particulate zirconia.
Wherein, anti-biotic material includes the nano titanium dioxide particles and nano oxygen that weight ratio is 0.8~1:0.8~1
Change zinc particle.
Above-mentioned soaping condition are as follows: fabric is soaped 20~30min at 50~60 DEG C, bath raio 1:60, soap lye concentration is
1.5~2g/L.
Above-mentioned reflective resin is one of acrylic resin or polyester resin.
Embodiment 3
A kind of traffic police subdues warming Reflection fabric, it is specific the preparation method is as follows:
(1) 300 parts of reflective resins, 18 parts of aluminium silver powder, 18 parts of luminescent powders, 50 parts of butyl acetates are uniformly mixed;Then according to
250 parts of glass microballoons of secondary addition, 25 parts of dispersing agents, 38 parts of amino resin curing agents, continuously stir 30 after mixing~
Reflecting coating is made in 60min;.
It (2) will be 55~65% bombax cotton, 20~30% nylon fibre and 15~25% by mass percent
Composite fiber material made of blend polyester is immersed in far-infrared emission material and anti-biotic material finishing fluid and takes after 2~3d of dipping
It rolls out, first 1~2min of preliminary drying in 110~120 DEG C of baking ovens, 3~5min is then dried at 130~140 DEG C, continuously soaps one
Secondary, washing is dried afterwards to get thermal fabric twice;
(3) coating is carried out with the thermal fabric that reflecting coating prepared by step (1) prepares step (2), coating layer thickness is
150~250 μm, obtain warming Reflection fabric.
Above-mentioned far-infrared emission material and anti-biotic material finishing fluid are prepared in accordance with the following methods: a, modified by 106 parts
Nanometer zirconium dioxide particle is added in the deionized water that 200~300 parts of pH are 7.5~8.5, is obtained thoroughly after 10~20min of ultrasound
Bright nano zirconium dioxide dispersion liquid;B, 78.5 parts of anti-biotic materials, 13.5 parts of dispersing agents, 20 parts of adhesives are added to nano-silica
Change in zirconium dispersion liquid, be uniformly mixed, continuously stirs 10~20min and target finishing fluid is made.
Wherein, the preparation process of modified nano zirconium dioxide is as follows: by nanometer zirconium dioxide particle and 3.5 parts of zirconium classes
Coupling agent mixing, then the sample after ball milling, is finally dried in vacuo by 30~60min of ball milling in the ball mill in 60 DEG C of baking ovens
12~18h is to get modified nano-silica particulate zirconia.
Wherein, anti-biotic material includes the nano titanium dioxide particles and nano oxygen that weight ratio is 0.8~1:0.8~1
Change zinc particle.
Above-mentioned soaping condition are as follows: fabric is soaped 20~30min at 50~60 DEG C, bath raio 1:60, soap lye concentration is
1.5~2g/L.
Above-mentioned reflective resin is one of acrylic resin or polyester resin.
Traffic police prepared by Example 1 to 3 subdues warming Reflection fabric sample 5cm × 5cm piece sample, respectively according to GB/
The standard of T3979-2008, GB/T11048-2008, GB/T20944.3-2008, AATCC183, GB/T30127-2013, to sample
Piece reflectivity, warmth retention property, fungistatic effect, anti-ultraviolet property and far infrared performance are tested, and with not collated and coating
Composite fiber material print compare group, while according to identical standard and method to each embodiment continuous washing 15 times after
Sample is tested, as a result as shown in Table 1 and Table 2 respectively.
1 print performance of table
Print performance after 1 continuous washing of table 15 times
Referring to the evaluation criterion of each standard, the traffic police of the preparation of embodiment 1 to 3 can be seen that according to the result of Tables 1 and 2
Subduing warming Reflection fabric has preferable reflectivity, warmth retention property, fungistatic effect and far infrared performance, and after continuous washing 15 times
The performance of each embodiment print is substantially unaffected, illustrate traffic police prepared by the present invention subdue warming Reflection fabric water-wash resistance compared with
Good, subduing field in traffic police has certain application prospect.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit and essential characteristics of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.In addition, it should be understood that although this specification is described in terms of embodiments, but it is not each
Embodiment only contains an independent technical solution, this narrating mode of specification only for clarity, this field skill
Art personnel should consider the specification as a whole, and the technical solutions in the various embodiments may also be suitably combined, form ability
The other embodiments that field technique personnel are understood that.
Claims (8)
1. a kind of traffic police subdues warming Reflection fabric, which is characterized in that the fabric is prepared by the following method:
(1) reflective resin, aluminium silver powder, luminescent powder, butyl acetate are uniformly mixed;Then glass microballoon, dispersing agent are sequentially added
And curing agent, 30~60min is continuously stirred after mixing, and reflecting coating is made;
(2) composite fiber material is immersed in far-infrared emission material and anti-biotic material finishing fluid to take out after impregnating 2~3d and is ground
Pressure, first 1~2min of preliminary drying in 110~120 DEG C of baking ovens, then dries 3~5min at 130~140 DEG C, continuously soap once,
Washing is dried afterwards to get thermal fabric twice;The composite fiber material by mass percent be 55~65% bombax cotton,
20~30% nylon fibre and 15~25% blend polyester form;
(3) coating is carried out with the thermal fabric that reflecting coating prepared by step (1) prepares step (2), obtains warming Reflection fabric.
2. a kind of traffic police according to claim 1 subdues warming Reflection fabric, which is characterized in that each material in step (1)
Weight proportion are as follows: 250~375 parts of reflective resin, 15~22.5 parts of aluminium silver powder, 15~20 parts of luminescent powder, butyl acetate 40~
60 parts;200~300 parts of glass microballoon, 20~30 parts of dispersing agent, 30~45 parts of curing agent.
3. a kind of traffic police according to claim 1 subdues warming Reflection fabric, which is characterized in that remote red in step (2)
Outer emissive material and anti-biotic material finishing fluid are prepared in accordance with the following methods: a, by 87.5~106 parts of modified nanometer titanium dioxides
Particulate zirconia is added in the deionized water that 200~300 parts of pH are 7.5~8.5, and transparent nano dioxy is obtained after 10~20min of ultrasound
Change zirconium dispersion liquid;B, 62.5~78.5 parts of anti-biotic materials, 10~13.5 parts of dispersing agents, 15~20 parts of adhesives are added to nanometer
It in zirconium dioxide dispersion liquid, is uniformly mixed, continuously stirs 10~20min and target finishing fluid is made.
4. a kind of traffic police according to claim 3 subdues warming Reflection fabric, which is characterized in that the modified nanometer
The preparation process of zirconium dioxide is as follows: nanometer zirconium dioxide particle being mixed with 2.5~3.5 parts of zirconium class coupling agents, then in ball
Sample after ball milling is finally dried in vacuo 12~18h in 60 DEG C of baking ovens and received to get modification by 30~60min of ball milling in grinding machine
Rice zirconium dioxide particle.
5. a kind of traffic police according to claim 1 subdues warming Reflection fabric, which is characterized in that item of soaping in step (2)
Part are as follows: fabric is soaped 20~30min at 50~60 DEG C, bath raio 1:60, soap lye concentration is 1.5~2g/L.
6. a kind of traffic police according to claim 1 subdues warming Reflection fabric, which is characterized in that the antibacterial in step (2)
Material includes the nano titanium dioxide particles and nano zine oxide particle that weight ratio is 0.8~1:0.8~1.
7. a kind of traffic police according to claim 1 subdues warming Reflection fabric, which is characterized in that the coating layer thickness is
150~250 μm.
8. a kind of traffic police according to claim 1 subdues warming Reflection fabric, which is characterized in that the reflective resin is third
One of olefin(e) acid resin or polyester resin;The curing agent is amino resin curing agents.