CN109736085A - A kind of wrinkle resistant cotton and its processing technology - Google Patents
A kind of wrinkle resistant cotton and its processing technology Download PDFInfo
- Publication number
- CN109736085A CN109736085A CN201811617980.4A CN201811617980A CN109736085A CN 109736085 A CN109736085 A CN 109736085A CN 201811617980 A CN201811617980 A CN 201811617980A CN 109736085 A CN109736085 A CN 109736085A
- Authority
- CN
- China
- Prior art keywords
- cotton
- ontology
- wrinkle resistant
- processing technology
- carbon fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wrinkle resistant cotton and its processing technology, including cotton ontology and protection bound edge, the cotton ontology is by being formed by weaving through husky and weft yarn.In the present invention, the wrinkle resistant cotton and its processing technology are blended by rubbing carbon fiber cotton thread and staple line, since carbon fiber cotton thread has more strongly tensile recovery capability, when cotton receives external force fold, after external force removal, carbon fiber cotton thread can be restored automatically, to have the function that wrinkle resistant and improve intensity, since the cotton thread content of this product is much larger than the content of carbon fiber, so it is warming still to retain cotton, soft characteristic, the wrinkle resistant cotton and its processing technology carry out cotton ontology by finishing fluid to pad processing, contain resin in finishing fluid, catalyst, polyethylene emulsion and bleeding agent through high temperature dry it is molten after crosslinked with fiber molecule or self cross-linking reaction, form net macromolecular, so that cotton reaches wrinkle resistant performance.
Description
Technical field
The present invention relates to cotton fabric technical field more particularly to a kind of wrinkle resistant cotton and its processing technologys.
Background technique
Cotton is the cloth being made into cotton yarn.It is the general name of all kinds of cotton textiles, it is mostly used for fashionable dress, easy dress, interior
The shortcomings that clothing and shirt, its advantages are easily to keep warm, and soft fit, hygroscopic, gas permeability are favourable, cotton is then easy contract, easily
Wrinkle, influence the beauty of cotton, when in use must ironing often, thus substantially increase the use cost of cotton articles, together
When long-term ironing will affect its service life used, so being badly in need of a kind of wrinkle resistant cotton fabric in the market.
Summary of the invention
The purpose of the present invention is to solve disadvantage existing in the prior art, and a kind of wrinkle resistant cotton that proposes and its add
Work technique.
To achieve the goals above, present invention employs following technical solutions: a kind of wrinkle resistant cotton and its processing technology, packet
Cotton ontology and protection bound edge are included, the cotton ontology is the outer side edges of the cotton ontology by being formed by weaving through husky and weft yarn
Protection bound edge is sewed with by suture single needle at frame position.
Further, the protection bound edge is made of cladding cloth and sponge strip, wherein cladding cloth two sides lead to respectively
The two sides that suture single needle is sewn to cotton ontology frame are crossed, and sponge strip is embedded in the inside of cladding cloth.
Further, the protection bound edge is made of cladding cloth and sponge strip, wherein cladding cloth two sides lead to respectively
The two sides that suture single needle is sewn to cotton ontology frame are crossed, and sponge strip is embedded in the inside of cladding cloth.
Further, described through husky identical with weft material, and rubbed through husky and weft yarn by carbon fiber cotton thread and staple line
It twists, wherein the ratio of carbon fiber cotton thread and staple line is 1 to 3.
Further, the carbon fiber cotton thread is rubbed by PAN base carbon fibre silk and staple, wherein PAN base carbon fiber
The mass percent for tieing up silk is 20%-40%, and the mass percent of staple is 60%-80%.
Further, the sponge strip is cylindrical strip structure, and the diameter of sponge strip is 0.1mm-0.2mm, described
The washing shrinkage for coating cloth is identical as the washing shrinkage of cotton ontology.
Further, the cotton ontology with a thickness of 0.1mm-0.3mm, and through husky through being 110/cm to density,
And the latitudinal density of weft yarn is 110/cm.
Further, the suture is polyester-cotton blend sewing thread, and the needle gage of suture is 0.3-0.5mm, and the shrink of suture
Rate is identical with the washing shrinkage of cotton ontology.
A kind of production technology of wrinkle resistant cotton, includes the following steps；
S1: 2-4 strands of PAN base carbon fibre silks and 6-8 strands of staples are carried out twisted filament and obtain carbon fiber cotton thread by production warp thread and weft yarn,
Then 10 strands of staples are subjected to twisted filaments and obtain staple line, then by 1 strand of carbon fiber cotton thread and 2 strands of staple lines carry out twisted filaments obtain through
Yarn and weft yarn；
S2: warp thread and weft yarn are weaved by weaving loom, form cotton ontology 1 by cotton manufacture；
S3: production finishing agent, weigh 40-60 parts of resin, 10-13 parts of catalyst, 20-30 parts of polyethylene emulsion, 1-5 parts of silicone oil,
1-3 parts of bleeding agent, 1-3 parts of citric acid and 20-35 parts of water are put into the charging basket of squeeze device, are mixed and finishing fluid is made；
S4: cotton pads, and cotton ontology 1 is placed in the charging basket of squeeze device and pad processing, the temperature of squeeze device charging basket
Degree is maintained at 20-25 degrees Celsius, and padding the time is 1h-1.5h；
S5: drying and processing, the cotton ontology after the completion of padding take out, and the inside for being then placed within cotton drying unit is dried
Dry-cure, drying temperature are 100 DEG C -120 DEG C, drying time 10-15min；
S6: the cotton ontology after drying is placed in washing machine and is cleaned, is dehydrated after the completion of cleaning, so by cleaning leveling
It is being dried afterwards, ironing leveling is being carried out by ironing equipment after drying；
S7: sewing bound edge by sewing cladding cloth on the cotton outer body frame of leveling, and is coating being internally embedded for cloth
Sponge strip, thus finished product cotton.
Beneficial effect
The present invention provides a kind of wrinkle resistant cotton and its processing technologys.Have it is following the utility model has the advantages that
(1): the wrinkle resistant cotton and its processing technology are blended by rubbing carbon fiber cotton thread and staple line, due to carbon fiber cotton thread
With more strongly tensile recovery capability, when cotton receives external force fold, after external force removal, carbon fiber cotton thread can carry out extensive automatically
It is multiple, thus have the function that wrinkle resistant and improve intensity, since the cotton thread content of this product is much larger than the content of carbon fiber, so according to
Cotton can so be retained to keep warm, soft characteristic.
(2)；The wrinkle resistant cotton and its processing technology carry out cotton ontology by finishing fluid to pad processing, contain in finishing fluid
Have resin, catalyst, polyethylene emulsion and bleeding agent through high temperature dry it is molten after crosslinked with fiber molecule or self cross-linking reaction,
Net macromolecular is formed, so that cotton reaches wrinkle resistant performance.It, can and by being equipped with protection bound edge in this outer body of face
To prevent from that fold occurs at its bezel locations by protecting bound edge to be supported protection to the bezel locations of cotton ontology.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of a kind of wrinkle resistant cotton proposed by the present invention and its processing technology；
Fig. 2 is the process flow diagram of a kind of wrinkle resistant cotton proposed by the present invention and its processing technology.
Marginal data
1, cotton ontology；11, through sand；12, weft yarn；2, bound edge is protected；21, cloth is coated；22 sponge strips；3, suture.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.
In the description of the present invention, it is to be understood that, term " aperture ", "upper", "lower", " thickness ", "top", " in ",
Indicating positions or the positional relationship such as " length ", "inner", " surrounding ", are merely for convenience of description of the present invention and simplification of the description, without
It is that the component of indication or suggestion meaning or element must have a particular orientation, is constructed and operated in a specific orientation, therefore not
It can be interpreted as limitation of the present invention.
Referring to Fig.1-2, a kind of wrinkle resistant cotton and its processing technology, including cotton ontology 1 and protection bound edge 2, cotton ontology 1
It is that protection packet is sewed with by 3 single needle of suture at the outside bezel locations of cotton ontology 1 by being formed by weaving through sand 11 and weft yarn 12
Side 2.
Protecting bound edge 2 is made of cladding cloth 21 and sponge strip 22, wherein cladding 21 two sides of cloth pass through suture respectively
3 single needles are sewn to the two sides of 1 frame of cotton ontology, and sponge strip 22 is embedded in the inside of cladding cloth 21, through sand 11 and weft yarn
12 materials are identical, and are rubbed through sand 11 and weft yarn 12 by carbon fiber cotton thread and staple line, wherein carbon fiber cotton thread and cotton
The ratio of silk thread is 1 to 3, and carbon fiber cotton thread is rubbed by PAN base carbon fibre silk and staple, wherein PAN base carbon fibre silk
Mass percent be 20%-40%, the mass percent of staple is 60%-80%, and sponge strip 22 is cylindrical strip structure, and sea
The diameter of continuous item 22 is 0.1mm-0.2mm, and the washing shrinkage for coating cloth 21 is identical as the washing shrinkage of cotton ontology 1, cotton ontology 1
With a thickness of 0.1mm-0.3mm, and through sand 11 through to density be 110/cm, and the latitudinal density of weft yarn 12 be 110/
Cm, suture 3 are polyester-cotton blend sewing thread, and the needle gage of suture 3 is 0.3-0.5mm, and the washing shrinkage of suture 3 and cotton ontology 1
Washing shrinkage is identical.
A kind of production technology of wrinkle resistant cotton, includes the following steps；
S1: 2-4 strands of PAN base carbon fibre silks and 6-8 strands of staples are carried out twisted filament and obtain carbon fiber cotton by production warp thread 11 and weft yarn 12
Then 10 strands of staples are carried out twisted filament and obtain staple line by line, 1 strand of carbon fiber cotton thread and 2 strands of staple lines are then carried out twisted filament and obtained
To warp thread 11 and weft yarn 12；
S2: warp thread 11 and weft yarn 12 are weaved by weaving loom, form cotton ontology 1 by cotton manufacture；
S3: production finishing agent, weigh 40-60 parts of resin, 10-13 parts of catalyst, 20-30 parts of polyethylene emulsion, 1-5 parts of silicone oil,
1-3 parts of bleeding agent, 1-3 parts of citric acid and 20-35 parts of water are put into the charging basket of squeeze device, are mixed and finishing fluid is made；
S4: cotton pads, and cotton ontology 1 is placed in the charging basket of squeeze device and pad processing, the temperature of squeeze device charging basket
Degree is maintained at 20-25 degrees Celsius, and padding the time is 1h-1.5h；
S5: drying and processing, the cotton ontology 1 after the completion of padding take out, and the inside for being then placed within cotton drying unit carries out
Drying and processing, drying temperature are 100 DEG C -120 DEG C, drying time 10-15min；
S6: the cotton ontology 1 after drying is placed in washing machine and cleans, is dehydrated after the completion of cleaning by cleaning leveling,
Then it is being dried, ironing leveling is carried out by ironing equipment again after drying；
S7: sewing bound edge, by sewing cladding cloth 21 on the 1 outside frame of cotton ontology of leveling, and in cladding cloth 21
Portion is embedded in sponge strip 22, thus finished product cotton.
When through the sewing protection bound edge 2 of suture 3, in order to ensure the quality and anti-wrinkle effect of 1 bezel locations of cotton ontology,
It is required that the washing shrinkage of suture 3 is identical with the washing shrinkage of cotton ontology 1, to guarantee the cotton ontology 1 when bound edge 2 is protected in sewing
Will not deform fold at bezel locations, while after washing, pleat will not equally occur at the bezel locations of cotton ontology 1
Wrinkle.
Drying and processing method with two kinds, first is that before bake method, i.e., fabric open width pads resin, the whole processes such as flat curing
It is completed by printing and dyeing mill, this is traditional process route, and shortcoming is to bring certain difficulty to clothes processing, it is very difficult to be given
Clothes assign certain folding Tuck and apparel modeling, therefore the arrangement that it is only applicable to cloth is processed, second is that after bake method, after bake method can
Embryo cloth and clothes are directly impregnated finishing fluid, then baked.
In the description of this specification, the description of reference term " one embodiment ", " example ", " specific example " etc. means
Specific features described in conjunction with this embodiment or example, structure, material live feature and are contained at least one implementation of the invention
In example or example.In the present specification, schematic expression of the above terms may not refer to the same embodiment or example.
Moreover, particular features, structures, materials, or characteristics described can be in any one or more of the embodiments or examples to close
Suitable mode combines.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (8)
1. a kind of wrinkle resistant cotton and its processing technology, including cotton ontology (1) and protection bound edge (2), which is characterized in that the cotton
Cloth ontology (1) is to pass through seam at the outside bezel locations of the cotton ontology (1) by being formed by weaving through husky (11) and weft yarn (12)
Line (3) single needle is sewed with protection bound edge (2).
2. a kind of wrinkle resistant cotton according to claim 1 and its processing technology, which is characterized in that the protection bound edge (2)
It is to be made of cladding cloth (21) and sponge strip (22), wherein cladding cloth (21) two sides pass through the suture of suture (3) single needle respectively
In the two sides of cotton ontology (1) frame, and sponge strip (22) is embedded in the inside of cladding cloth (21).
3. a kind of wrinkle resistant cotton according to claim 2 and its processing technology, which is characterized in that described through husky (11) and latitude
Yarn (12) material is identical, and is rubbed through husky (11) and weft yarn (12) by carbon fiber cotton thread and staple line, wherein carbon fiber
The ratio of cotton thread and staple line is 1 to 3.
4. a kind of wrinkle resistant cotton according to claim 3 and its processing technology, which is characterized in that the carbon fiber cotton thread is
It is rubbed by PAN base carbon fibre silk and staple, wherein the mass percent of PAN base carbon fibre silk is 20%-40%, staple
Mass percent is 60%-80%.
5. a kind of wrinkle resistant cotton according to claim 2 and its processing technology, which is characterized in that the sponge strip (22) is
Cylindrical strip structure, and the diameter of sponge strip (22) is 0.1mm-0.2mm, the washing shrinkage and cotton of cladding cloth (21)
The washing shrinkage of ontology (1) is identical.
6. a kind of wrinkle resistant cotton according to claim 1 and its processing technology, which is characterized in that the cotton ontology (1)
With a thickness of 0.1mm-0.3mm, and through husky (11) through being 110/cm to density, and the latitudinal density of weft yarn (12) is
110/cm.
7. a kind of wrinkle resistant cotton according to claim 1 and its processing technology, which is characterized in that the suture (3) is to wash
Cotton sewing thread, and the needle gage of suture (3) is 0.3-0.5mm, and the washing shrinkage of the washing shrinkage of suture (3) and cotton ontology (1)
It is identical.
8. a kind of production technology of wrinkle resistant cotton according to claim 1, includes the following steps；
S1: 2-4 strands of PAN base carbon fibre silks and 6-8 strands of staples are carried out twisted filament and obtain carbon fiber by production warp thread (11) and weft yarn (12)
Then 10 strands of staples are carried out twisted filament and obtain staple line, then twist 1 strand of carbon fiber cotton thread and 2 strands of staple lines by vinylon and cotton blend line
Silk obtains warp thread (11) and weft yarn (12)；
S2: warp thread (11) and weft yarn (12) are weaved by weaving loom, are formed cotton ontology (1) by cotton manufacture；
S3: production finishing agent, weigh 40-60 parts of resin, 10-13 parts of catalyst, 20-30 parts of polyethylene emulsion, 1-5 parts of silicone oil,
1-3 parts of bleeding agent, 1-3 parts of citric acid and 20-35 parts of water are put into the charging basket of squeeze device, are mixed and finishing fluid is made；
S4: cotton pads, and cotton ontology (1) is placed in the charging basket of squeeze device and pad processing, squeeze device charging basket
Temperature is maintained at 20-25 degrees Celsius, and padding the time is 1h-1.5h；
S5: drying and processing, cotton ontology (1) after the completion of padding take out, be then placed within the inside of cotton drying unit into
Row drying and processing, drying temperature are 100 DEG C -120 DEG C, drying time 10-15min；
S6: the cotton ontology (1) after drying is placed in washing machine and is cleaned, is dehydrated after the completion of cleaning by cleaning leveling,
Then it is being dried, ironing leveling is being carried out by ironing equipment after drying；
S7: sewing bound edge, by sewing cladding cloth (21) on frame on the outside of the cotton ontology (1) of leveling, and in cladding cloth
(21) be internally embedded sponge strip (22), thus finished product cotton.