CN109704718A - A kind of multi-functional purple clay of health and preparation method thereof - Google Patents
A kind of multi-functional purple clay of health and preparation method thereof Download PDFInfo
- Publication number
- CN109704718A CN109704718A CN201910085368.5A CN201910085368A CN109704718A CN 109704718 A CN109704718 A CN 109704718A CN 201910085368 A CN201910085368 A CN 201910085368A CN 109704718 A CN109704718 A CN 109704718A
- Authority
- CN
- China
- Prior art keywords
- mud
- purple
- mixing
- sand
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses multi-functional purple clays of a kind of health and preparation method thereof, it is by purple sand mud and sand particle two parts is adjusted to form, and purple sand mud is made of the following components according to weight percent: this naze mud 35~40%, Dongshan first mud 15~20% and red soil 40~50%；Sand particle is adjusted to be made of the following components according to weight percent: carclazyte 5~10%, native bone 10~15%, negative ion powder 50~60%, medical stone powder 25~35%.The present invention is compared with prior art, by being specifically formulated and technique, so that purple clay, which has, inhibits bacterial growth, radiation protection, alkalization water quality, desalination nicotine and the multinomial additional function for decomposing ethyl alcohol, so that red stoneware ware made of purple clay has health-preserving function during use, this has greatly catered to the use demand of modern people, has fabulous market application prospect.
Description
Technical field
The present invention relates to a kind of purple clays, and in particular to a kind of multi-functional purple clay of health and preparation method thereof.
Background technique
Dark-red enameled pottery, purple ceramic cup etc. have become many families and make tea the boccaro of the tea set used and some other purposes
Vessel are also increasingly got the favour of people, but existing red stoneware ware is only made functionally still relatively simple
Tool is used to be a kind of, with the continuous improvement of people's quality of life, people need a kind of multi-functional red stoneware ware
Meet otherwise demand.
Therefore a kind of new technical solution is needed to realize above-mentioned purpose.
Summary of the invention
Goal of the invention: in order to overcome the deficiencies in the prior art, one kind is provided and has inhibition bacterial growth, anti-spoke
It penetrates, the water quality that alkalizes, desalinate nicotine and the multi-functional purple clay of health of decomposition ethyl alcohol function and preparation method thereof.
Technical solution: to achieve the above object, the present invention provides a kind of multi-functional purple clay of health, by purple sand mud and
Sand particle two parts composition is adjusted, the purple sand mud is made of the following components according to weight percent:
This naze mud 35~40%, Dongshan first mud 15~20% and red soil 40~50%；
The tune sand particle is made of the following components according to weight percent:
Carclazyte 5~10%, native bone 10~15%, negative ion powder 50~60%, medical stone powder 25~35%.
The weight for adjusting sand particle is the 20~30% of purple sand mud.
A kind of preparation method of the multi-functional purple clay of health, includes the following steps:
1) preparation of sand particle is adjusted, specific as follows:
1.1) ingredient: each raw material of sand particle will be adjusted to measure according to weight percent；
1.2) ball milling is carried out to the mixing of step 1.1；
1.3) mixing after step 1.2 ball milling is carried out inhaling iron sieving；
1.4) drying calcining: the mixing obtained after step 1.3 sub-sieve is dried, and is packed into casket after mixing is dry
Alms bowl is put into electric furnace and is calcined；
1.5) particle preparation: carrying out the calcining material that step 1.4 obtains to smash it through mesh screen, the particle conduct after taking sub-sieve
Adjust sand particle；
2) weight metering ingredient: is carried out to this naze mud, Dongshan first mud and red soil respectively by recipe requirements；
3) ball milling is carried out to the mixing that step 2 obtains；
4) mixing after ball milling is carried out inhaling iron sieving；
5) stock tank stirs: the mixing that step 4 is obtained, which is put into stock tank, to be stirred, and makes step 1 in whipping process
It is mixed in standby tune sand particle investment stock tank；
6) it filters pressing: adjusts the slurry of sand particle to carry out filters pressing incorporation, pug is made to form mud cake；
7) thick to practice: mud cake being put into vacuum pugging poplar and is slightly practiced；
8) aging: it is aging that the purple clay after thick practice being deposited in the progress of mud library；
9) vacuum pugging: the pug of aging mistake is subjected to vacuum pugging, is then packed；
10) packaged purple sand pug is burnt into, obtains final purple clay finished product.
Further, the mode of ball milling is wet ball-milling in the step 1.2, and wherein the weight ratio of mixing, ball and water is 1
: 0.7: 0.8, Ball-milling Time is 8~10 hours.
Further, be respectively adopted in the step 1.3 and step 4 40~60 mesh vibrating screens and 60~80 mesh vibrating screens into
Row inhales iron sieving.
Further, temperature dry in the step 1.4 is 140~180 DEG C, and the temperature of calcining is 800-850 DEG C.
Further, the mode of ball milling is wet ball-milling in the step 3, and wherein the weight ratio of mixing, ball and water is 1:
1.5: 0.3, Ball-milling Time is 10~12 hours.
Further, the time aging in the step 8 is not less than 3 months.
Further, it is burnt into the step 10 using oxidizing flame, firing temperature is 1170~1190 DEG C, firing week
Phase 8~12 hours.
Using red stoneware ware made of purple clay of the invention, since purple clay of the present invention is specifically formulated and prepares work
Skill, red stoneware ware has additional functions, specific as follows:
Inhibit bacterial growth: anion can be neutralized effectively in water and air pollution while decomposing in red stoneware ware
Harmful substance, to purify water, clean air.
Radiation protection: red stoneware ware itself can constantly decompose anion, and anion can effectively be reacted and be offset various
Ray, so radiation protection can be played the role of.
Alkalization water quality: red stoneware ware itself can allow water reaction at alkalescent, to form acid-base balance in maintenance human body
The effect of, immunity of human body itself is improved, the effect of health care is reached.
Desalination nicotine: anion plays the role of desalinating nicotine, can effectively reduce smoke tar in respiratory tract and lung
Absorption, weaken injury of the nicotine to human body, this function is also core of the invention innovative point.
Decompose ethyl alcohol: the ethyl alcohol in anion energy decomposing alcohol ingredient desalinates the concentration of wine, makes the mouthfeel of wine softer,
It is soft.
The utility model has the advantages that compared with prior art, the present invention by specifically formula and technique, so that purple clay has suppression
Bacterial growth, radiation protection, alkalization water quality, desalination nicotine and the multinomial additional function for decomposing ethyl alcohol processed, so that purple clay is made
Red stoneware ware have health-preserving function during use, this has greatly catered to the use demand of modern people, has
Fabulous market application prospect.
Specific embodiment
Embodiment 1:
A kind of multi-functional purple clay of health, by purple sand mud and adjust sand particle two parts form, purple sand mud according to
Weight percent is made of the following components:
This naze mud 35%, Dongshan first mud 15% and red soil 50%；
Sand particle is adjusted to be made of the following components according to weight percent:
Carclazyte 5%, native bone 10%, negative ion powder 50%, medical stone powder 35%.
The weight for wherein adjusting sand particle is the 20% of purple sand mud.
In the present embodiment, the preparation process of purple clay includes the following steps:
1) preparation of sand particle is adjusted, specific as follows:
1.1) ingredient: 5 jin of carclazyte, native 10 jin of bone, 50 jin of negative ion powder and 35 jin of medical stone powder are weighed, and are blended in
Together；
1.2) wet ball-milling is carried out to the mixing of step 1.1, wherein the weight ratio of mixing, ball and water is 1: 0.7: 0.8,
Ball-milling Time is 8 hours；
1.3) mixing after step 1.2 ball milling is carried out inhaling iron sieving using 40 mesh vibrating screens；
1.4) drying calcining: the mixing obtained after step 1.3 sub-sieve is dried, and is packed into casket after mixing is dry
Alms bowl is put into electric furnace and is calcined, wherein dry temperature is 140 DEG C, the temperature of calcining is 800 DEG C
1.5) particle preparation: the calcining material that step 1.4 obtains is carried out to smash it through 40 mesh and 60 mesh mesh screens, after taking sub-sieve
Particle as adjust sand particle；
2) sorting: selected naze mud, Dongshan first mud and red soil reject impurity, keep pug pure；Weathering: will be selected
Mineral material be deposited in open area at one's discretion solarization, wind, drench with rain, weathering time daytime is long, keeps mud pure good；Weigh respectively through
175 jin of this naze mud, 75 jin of Dongshan first mud and 250 jin of red soil after crossing weathering, and mix；
3) wet ball-milling is carried out to the mixing that step 2 obtains, wherein the weight ratio of mixing, ball and water is 1: 1.5: 0.3,
Ball-milling Time is 10 hours；
4) mixing after ball milling is carried out inhaling iron sieving using 60 mesh vibrating screens；
5) stock tank stirs: the mixing that step 4 is obtained, which is put into stock tank, to be stirred, and makes step 1 in whipping process
It is mixed in standby tune sand particle investment stock tank；
6) it filters pressing: adjusts the slurry of sand particle to carry out filters pressing incorporation, pug is made to form mud cake；
7) thick to practice: mud cake being put into vacuum pugging poplar and is slightly practiced；
8) aging: it is 3.5 months that the purple clay after thick practice, which is deposited in mud library to carry out aging, the aging time,；
9) vacuum pugging: the pug of aging mistake is subjected to vacuum pugging, then segmentation is carried out with polybag and packs；
10) packaged purple sand pug is burnt into using oxidizing flame, firing temperature is 1170 DEG C, and firing period 8 is small
When, obtain final purple clay finished product.
Embodiment 2:
A kind of multi-functional purple clay of health, by purple sand mud and adjust sand particle two parts form, purple sand mud according to
Weight percent is made of the following components:
This naze mud 40%, Dongshan first mud 20% and red soil 40%；
Sand particle is adjusted to be made of the following components according to weight percent:
Carclazyte 10%, native bone 15%, negative ion powder 50%, medical stone powder 25%.
The weight for wherein adjusting sand particle is the 25% of purple sand mud.
In the present embodiment, the preparation process of purple clay includes the following steps:
1) preparation of sand particle is adjusted, specific as follows:
1.1) ingredient: 10 jin of carclazyte, native 15 jin of bone, 50 jin of negative ion powder and 25 jin of medical stone powder are weighed, and are blended in
Together；
1.2) wet ball-milling is carried out to the mixing of step 1.1, wherein the weight ratio of mixing, ball and water is 1: 0.7: 0.8,
Ball-milling Time is 10 hours；
1.3) mixing after step 1.2 ball milling is carried out inhaling iron sieving using 60 mesh vibrating screens；
1.4) drying calcining: the mixing obtained after step 1.3 sub-sieve is dried, and is packed into casket after mixing is dry
Alms bowl is put into electric furnace and is calcined, wherein dry temperature is 180 DEG C, the temperature of calcining is 850 DEG C
1.5) particle preparation: the calcining material that step 1.4 obtains is carried out to smash it through 40 mesh and 60 mesh mesh screens, after taking sub-sieve
Particle as adjust sand particle；
2) sorting: selected naze mud, Dongshan first mud and red soil reject impurity, keep pug pure；Weathering: will be selected
Mineral material be deposited in open area at one's discretion solarization, wind, drench with rain, weathering time daytime is long, keeps mud pure good；Weigh respectively through
160 jin of this naze mud, 80 jin of Dongshan first mud and 160 jin of red soil after crossing weathering, and mix；
3) wet ball-milling is carried out to the mixing that step 2 obtains, wherein the weight ratio of mixing, ball and water is 1: 1.5: 0.3,
Ball-milling Time is 12 hours；
4) mixing after ball milling is carried out inhaling iron sieving using 80 mesh vibrating screens；
5) stock tank stirs: the mixing that step 4 is obtained, which is put into stock tank, to be stirred, and makes step 1 in whipping process
It is mixed in standby tune sand particle investment stock tank；
6) it filters pressing: adjusts the slurry of sand particle to carry out filters pressing incorporation, pug is made to form mud cake；
7) thick to practice: mud cake being put into vacuum pugging poplar and is slightly practiced；
8) aging: it is 3.5 months that the purple clay after thick practice, which is deposited in mud library to carry out aging, the aging time,；
9) vacuum pugging: the pug of aging mistake is subjected to vacuum pugging, then segmentation is carried out with polybag and packs；
10) packaged purple sand pug is burnt into using oxidizing flame, firing temperature is 1190 DEG C, firing period 12
Hour, obtain final purple clay finished product.
Embodiment 3:
A kind of multi-functional purple clay of health, by purple sand mud and adjust sand particle two parts form, purple sand mud according to
Weight percent is made of the following components:
This naze mud 38%, Dongshan first mud 18% and red soil 44%；
Sand particle is adjusted to be made of the following components according to weight percent:
Carclazyte 8%, native bone 12%, negative ion powder 55%, medical stone powder 25%.
The weight for wherein adjusting sand particle is the 30% of purple sand mud.
In the present embodiment, the preparation process of purple clay includes the following steps:
1) preparation of sand particle is adjusted, specific as follows:
1.1) ingredient: 8 jin of carclazyte, native 12 jin of bone, 55 jin of negative ion powder and 25 jin of medical stone powder are weighed, and are blended in
Together；
1.2) wet ball-milling is carried out to the mixing of step 1.1, wherein the weight ratio of mixing, ball and water is 1: 0.7: 0.8,
Ball-milling Time is 9 hours；
1.3) mixing after step 1.2 ball milling is carried out inhaling iron sieving using 60 mesh vibrating screens；
1.4) drying calcining: the mixing obtained after step 1.3 sub-sieve is dried, and is packed into casket after mixing is dry
Alms bowl is put into electric furnace and is calcined, wherein dry temperature is 160 DEG C, the temperature of calcining is 825 DEG C
1.5) particle preparation: the calcining material that step 1.4 obtains is carried out to smash it through 40 mesh and 60 mesh mesh screens, after taking sub-sieve
Particle as adjust sand particle；
2) sorting: selected naze mud, Dongshan first mud and red soil reject impurity, keep pug pure；Weathering: will be selected
Mineral material be deposited in open area at one's discretion solarization, wind, drench with rain, weathering time daytime is long, keeps mud pure good；Weigh respectively through
127 jin of this naze mud, 60 jin of Dongshan first mud and 147 jin of red soil after crossing weathering, and mix；
3) wet ball-milling is carried out to the mixing that step 2 obtains, wherein the weight ratio of mixing, ball and water is 1: 1.5: 0.3,
Ball-milling Time is 11 hours；
4) mixing after ball milling is carried out inhaling iron sieving using 80 mesh vibrating screens；
5) stock tank stirs: the mixing that step 4 is obtained, which is put into stock tank, to be stirred, and makes step 1 in whipping process
It is mixed in standby tune sand particle investment stock tank；
6) it filters pressing: adjusts the slurry of sand particle to carry out filters pressing incorporation, pug is made to form mud cake；
7) thick to practice: mud cake being put into vacuum pugging poplar and is slightly practiced；
8) aging: it is 3.5 months that the purple clay after thick practice, which is deposited in mud library to carry out aging, the aging time,；
9) vacuum pugging: the pug of aging mistake is subjected to vacuum pugging, then segmentation is carried out with polybag and packs；
10) packaged purple sand pug is burnt into using oxidizing flame, firing temperature is 1180 DEG C, firing period 10
Hour, obtain final purple clay finished product.
Embodiment 4:
A kind of multi-functional purple clay of health, by purple sand mud and adjust sand particle two parts form, purple sand mud according to
Weight percent is made of the following components:
This naze mud 35%, Dongshan first mud 20% and red soil 45%；
Sand particle is adjusted to be made of the following components according to weight percent:
Carclazyte 5%, native bone 10%, negative ion powder 60%, medical stone powder 25%.
The weight for wherein adjusting sand particle is the 25% of purple sand mud.
In the present embodiment, the preparation process of purple clay includes the following steps:
1) preparation of sand particle is adjusted, specific as follows:
1.1) ingredient: 5 jin of carclazyte, native 10 jin of bone, 60 jin of negative ion powder and 25 jin of medical stone powder are weighed, and are blended in
Together；
1.2) wet ball-milling is carried out to the mixing of step 1.1, wherein the weight ratio of mixing, ball and water is 1: 0.7: 0.8,
Ball-milling Time is 9 hours；
1.3) mixing after step 1.2 ball milling is carried out inhaling iron sieving using 60 mesh vibrating screens；
1.4) drying calcining: the mixing obtained after step 1.3 sub-sieve is dried, and is packed into casket after mixing is dry
Alms bowl is put into electric furnace and is calcined, wherein dry temperature is 160 DEG C, the temperature of calcining is 825 DEG C
1.5) particle preparation: the calcining material that step 1.4 obtains is carried out to smash it through 40 mesh and 60 mesh mesh screens, after taking sub-sieve
Particle as adjust sand particle；
2) sorting: selected naze mud, Dongshan first mud and red soil reject impurity, keep pug pure；Weathering: will be selected
Mineral material be deposited in open area at one's discretion solarization, wind, drench with rain, weathering time daytime is long, keeps mud pure good；Weigh respectively through
140 jin of this naze mud, 80 jin of Dongshan first mud and 180 jin of red soil after crossing weathering, and mix；
3) wet ball-milling is carried out to the mixing that step 2 obtains, wherein the weight ratio of mixing, ball and water is 1: 1.5: 0.3,
Ball-milling Time is 11 hours；
4) mixing after ball milling is carried out inhaling iron sieving using 80 mesh vibrating screens；
5) stock tank stirs: the mixing that step 4 is obtained, which is put into stock tank, to be stirred, and makes step 1 in whipping process
It is mixed in standby tune sand particle investment stock tank；
6) it filters pressing: adjusts the slurry of sand particle to carry out filters pressing incorporation, pug is made to form mud cake；
7) thick to practice: mud cake being put into vacuum pugging poplar and is slightly practiced；
8) aging: it is 3.5 months that the purple clay after thick practice, which is deposited in mud library to carry out aging, the aging time,；
9) vacuum pugging: the pug of aging mistake is subjected to vacuum pugging, then segmentation is carried out with polybag and packs；
10) packaged purple sand pug is burnt into using oxidizing flame, firing temperature is 1180 DEG C, firing period 10
Hour, obtain final purple clay finished product.
Embodiment 5:
As raw material purple ceramic cup is made by technique, below in the purple clay finished product obtained in the present embodiment using embodiment 1
The purple ceramic cup and traditional purple ceramic cup that the present embodiment is obtained from inhibition bacterial growth, alkalization water quality and decompose ethyl alcohol three respectively
A aspect is tested for the property experiment, and specific test comparison data are as shown in the table:
1, inhibit bacterial growth:
According to upper table data it is found that the purple ceramic cup of the present embodiment and comparing for traditional purple ceramic cup, can effectively press down
The growth of bacterium in purple ceramic cup processed, and there is no this functions for traditional purple ceramic cup.
2, alkalize water quality:
According to upper table data it is found that the purple ceramic cup of the present embodiment and comparing for traditional purple ceramic cup, the boccaro of the present embodiment
Cup can effectively improve the pH value of boccaro water in the cup, and the pH value of traditional boccaro water in the cup is held essentially constant, so
Say that the purple ceramic cup of the present embodiment has the function of extraordinary alkalization water quality.
In this way using the purple ceramic cup of the present embodiment as the cup drunk tea or drunk water, due to sterilizing and alkalizing, water quality is
Beneficial to human body, for a long time, people can play good health effect during normally drinking tea or drinking water
Fruit.
3, ethyl alcohol is decomposed:
According to upper table data it is found that the purple ceramic cup of the present embodiment and comparing for traditional purple ceramic cup, the boccaro of the present embodiment
Cup can effectively reduce the alcoholic strength of wine in cup, and the alcoholic strength of wine is held essentially constant in traditional purple ceramic cup, sharp in this way
Use the purple ceramic cup of the present embodiment as tass in use, just in the practical intake of alcohol for virtually reducing the people that drinks,
Has certain health effect.
Embodiment 6:
Boccaro cupule is made by technique as raw material in the purple clay finished product obtained in the present embodiment using embodiment 2, this
Boccaro cupule is mainly used for placing cigarette, and the present embodiment dismantles same cigarette package, and half is placed in the purple ceramic cup of the present embodiment
In device, in addition half is placed in traditional boccaro cupule, then the cigarette in two boccaro cupules of point in time measurement respectively
Nicotine content, specific correlation data are as shown in the table:
According to upper table data it is found that the boccaro cup of the present embodiment and comparing for traditional boccaro cup, the present embodiment
Boccaro cup can effectively reduce the nicotine content in cigarette, and traditional boccaro cup does not have this function, this
Cigarette can be placed in the present embodiment in advance when smoking and when smoker talks thing or chat together by one people of sample
Boccaro cup in, just reduce the practical soakage of nicotine in smoking process in this way, to a certain extent reduce smoke pair
In the desalination nicotine function of the harm of human body, the present embodiment be also core of the invention innovative function.
Claims (9)
1. a kind of multi-functional purple clay of health, it is characterised in that: by purple sand mud and sand particle two parts is adjusted to form, the purple
Sand mud raw material is made of the following components according to weight percent:
This naze mud 35~40%, Dongshan first mud 15~20% and red soil 40~50%；
The tune sand particle is made of the following components according to weight percent:
Carclazyte 5~10%, native bone 10~15%, negative ion powder 50~60%, medical stone powder 25~35%.
2. the multi-functional purple clay of a kind of health according to claim 1, it is characterised in that: it is described adjust sand particle weight be
The 20~30% of purple sand mud.
3. a kind of preparation method of the multi-functional purple clay of health according to claim 1 or 2, it is characterised in that: including such as
Lower step:
1) preparation of sand particle is adjusted, specific as follows:
1.1) ingredient: each raw material of sand particle will be adjusted to measure according to weight percent；
1.2) ball milling is carried out to the mixing of step 1.1；
1.3) mixing after step 1.2 ball milling is carried out inhaling iron sieving；
1.4) drying calcining: the mixing obtained after step 1.3 sub-sieve is dried, and is packed into saggar after mixing is dry,
It is put into electric furnace and is calcined；
1.5) particle preparation: carrying out the calcining material that step 1.4 obtains to smash it through mesh screen, and the particle after taking sub-sieve is as tune sand
Particle；
2) weight metering ingredient: is carried out to this naze mud, Dongshan first mud and red soil respectively by recipe requirements；
3) ball milling is carried out to the mixing that step 2 obtains；
4) mixing after ball milling is carried out inhaling iron sieving；
5) stock tank stirs: the mixing that step 4 is obtained, which is put into stock tank, to be stirred, and prepares step 1 in whipping process
It adjusts and is mixed in sand particle investment stock tank；
6) it filters pressing: adjusts the slurry of sand particle to carry out filters pressing incorporation, pug is made to form mud cake；
7) thick to practice: mud cake being put into vacuum pugging poplar and is slightly practiced；
8) aging: it is aging that the purple clay after thick practice being deposited in the progress of mud library；
9) vacuum pugging: the pug of aging mistake is subjected to vacuum pugging, is then packed；
10) packaged purple sand pug is burnt into, obtains final purple clay finished product.
4. a kind of preparation method of the multi-functional purple clay of health according to claim 3, it is characterised in that: the step
The mode of ball milling is wet ball-milling in 1.2, and wherein the weight ratio of mixing, ball and water is 1: 0.7: 0.8, and Ball-milling Time is 8~10
Hour.
5. a kind of preparation method of the multi-functional purple clay of health according to claim 3, it is characterised in that: the step
1.3 and step 4 in be respectively adopted 40~60 mesh vibrating screens and 60~80 mesh vibrating screens carry out inhaling iron sieving.
6. a kind of preparation method of the multi-functional purple clay of health according to claim 3, it is characterised in that: the step
Dry temperature is 140~180 DEG C in 1.4, and the temperature of calcining is 800-850 DEG C.
7. a kind of preparation method of the multi-functional purple clay of health according to claim 3, it is characterised in that: the step 3
The mode of middle ball milling is wet ball-milling, and wherein the weight ratio of mixing, ball and water is 1: 1.5: 0.3, and Ball-milling Time is 10~12 small
When.
8. a kind of preparation method of the multi-functional purple clay of health according to claim 3, it is characterised in that: the step 8
In aging time be not less than 3 months.
9. a kind of preparation method of the multi-functional purple clay of health according to claim 3, it is characterised in that: the step 10
Middle to be burnt into using oxidizing flame, firing temperature is 1170~1190 DEG C, firing period 8~12 hours.