CN109701604B - 核壳结构多功能催化剂体系及用途 - Google Patents
核壳结构多功能催化剂体系及用途 Download PDFInfo
- Publication number
- CN109701604B CN109701604B CN201711016837.5A CN201711016837A CN109701604B CN 109701604 B CN109701604 B CN 109701604B CN 201711016837 A CN201711016837 A CN 201711016837A CN 109701604 B CN109701604 B CN 109701604B
- Authority
- CN
- China
- Prior art keywords
- core
- zncr
- shell
- molecular sieve
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及合成气转化生产芳烃联产轻烃的工艺以及所使用的核壳结构多功能催化剂。该催化剂体系具有合成气转化、芳烃/轻烃合成的催化活性。其中合成气转化活性由金属氧化物提供,芳烃/轻烃合成活性由分子筛提供。核壳结构催化剂的核层为金属氧化物,其活性组分优选自Cr、Zr、Mn、Ce、La、Ti、In、Ga、Zn中的一种或至少一种;壳层选自MFI或MEL结构分子筛中的一种或多种,其硅铝比范围12~∞。本发明提供了一条非费托路线、一步法实现合成气直接转化制芳烃联产轻烃的新路线,可用于合成气制烯烃芳烃的工业应用。
Description
技术领域
本发明涉及一种合成气转化生产芳烃联产轻烃的工艺及催化剂,具体涉及采用核壳结构多功能催化剂体系,由合成气转化生产芳烃联产轻烃的工艺。
背景技术
烃类是一类重要的基础化学品,作为能源组成以及合成材料单体,在国民经济和人民生活中具有不可或缺的作用。长期以来,烃类产品主要来源于石油炼制。随着石油资源的日益短缺,发掘烃类生产新路径成为缓解石化能源危机、实现化学工业可持续发展、促进我国经济发展与能源战略安全的必由之路。我国的能源结构具有富煤、贫油、少气的特点,煤炭资源在未来相当长一段时间内将占领我国能源领域的主导地位。因此,充分利用煤炭资源,寻求新的烃类合成方法,是我国在当前形势下的重要战略。合成气是煤炭资源转化利用的主要中间体之一,相关研究已有近百年历史。费托合成是合成气转化的重要途径,其研究可追溯至上世纪20年代。在含Fe、Co、Ni、Ru等第VIII族过渡金属的催化剂作用下,合成气可转化为C2+烃类产物,产物分布受Anderson-Schulz-Flory动力学限制,中间馏分的选择性难以实现较大的突破。
近年来,研究者们将费托合成催化剂与酸性分子筛结合,应用于费托合成体系,利用分子筛的裂化活性、择形效应,实现了特定产物选择性的提高。S.Kang等,CatalysisLetter,2008,125,264-270;S.Kang等,Fuel Processing Technology,2010,91,399-403将Fe或Fe-Cu-K负载于硅铝比Si/Al=25的ZSM-5分子筛上,与体相Fe或Fe-Cu-K催化剂相比,ZSM-5负载催化剂较强的酸性有利于提高产物中C2-C4选择性,此外产物烯烃/烷烃比也有所提高。此外,J.Kang等,Angewandte Chemie International Edition,2011,50,5200-5203采用介孔ZSM-5分子筛负载的Ru催化剂,提高了C5-C11选择性。X.Peng,Angewandte ChemieInternational Edition,2015,54,4553-4556提供了介孔Y分子筛负载Co催化剂的设计思路,利用介孔Y分子筛较弱的酸性和较大的孔道结构(相比于ZSM-5),该负载型催化剂显著提高了C10-C20的选择性。除了负载型催化剂,将费托合成催化剂与酸性分子筛催化剂以不同形式混合而成的复合催化剂体系也有较多报道。J.Bao,Angewandte Chemie,2008,120,359-362将Co/Al2O3包裹于Hβ分子筛内,制成具有核壳结构的复合催化剂;Q.Lin,Journalof Catalysis,2016,344,378-388以HZSM-5包覆Co/Pd/SiO2,提高了产物中C5-C11选择性。王德生等,催化学报,2002,23,333-335探讨了Fe/MnO与ZnZSM-5(Si/Al=25)机械混合多功能催化剂在合成气直接转化制芳烃体系的应用,得到了50%左右的芳烃选择性。
以上为基于费托合成的合成气定向转化技术现状,其特点为转化率高、而产物分布较宽、芳烃选择性较低。为突破费托合成路线的ASF动力学限制,基于甲醇等低碳醇及其醚等中间体转化成为实现合成气定向转化制化学品的重要思路之一。E.Javier等,Industrial&Engineering Chemistry Research,1998,37,1211-1219将Cr2O3-ZnO与硅铝比Si/Al=154的HZSM-5分子筛进行机械混合,实现了合成气经甲醇直接制汽油。Q.Zhang等,Fuel Processing Technology,2004,85,1139-1150比较了Cu-Zn、Zn-Cr、Pd/SiO2等甲醇合成催化剂与ZSM-5、USY、Hβ等甲醇转化催化剂复合体系在合成气转化体系的催化性能,其中Cu-Zn与USY按质量比1:1机械混合所得的复合催化剂体系具有较优的LPG选择性。根据K.Cheng等,Angewandte Chemie International Edition,2016,55,1-5;F.Jiao等,Science,2016,351,1065-1068的报道,ZnO-ZrO2、ZnO-Cr2O3与SAPO-34机械混合所得的复合催化剂,可以定向转化合成气制C2-C4低碳烯烃。张清德等,现代化工,2009,29,112-114将Cu/Zn/Al2O3、γ-Al2O3复合催化剂/HZSM-5(Si/Al=38)装填于等压串联流动体系的一/二反应段,分别控制一段、二段反应温度为270℃和360℃,实现了合成气高效转化制芳烃。相似的两段法工艺技术在张晶等,洁净煤技术,2013,19,60-67;Q.Zhang等,Journal ofIndustrial and Engineering Chemistry,2013,19,975-980中也有报道。此外,CN201610550701、CN201610348096以改性硅铝分子筛为载体制备负载型催化剂;专利CN200980149207采用含Ga硅酸盐沸石分子筛;专利CN200810079957采用HNKF-5、磷酸铝分子筛、Ga-Zn-Ba复合氧化物;专利CN201310149855采用高硅铝比的ZSM-5分子筛与甲醇合成催化剂联用;专利CN201610965244、CN201610609584采用含Zr复合氧化物与ZSM5复合催化剂,均实现了合成气直接转化制烃类化合物(含芳烃)。
为实现合成气直接转化制芳烃,目前文献报道中较优的工艺技术主要包括基于费拓合成和酸性分子筛择形作用的一步法工艺,以及基于甲醇合成和酸性分子筛择形作用的两段法工艺。前者面临的主要问题包括:产物分布动力学限制难以完全突破,积碳失活严重等。而后者需要分别控制两段反应的工艺条件,装置和工艺复杂程度较一步法工艺更高。而采用多功能催化剂,为实现合成气经非费托路线一步法合成烃类化合物(芳烃等)提供了可能。
发明内容
本发明所要解决的技术问题是现有技术中存在的催化剂装填不方便、工业应用投资高、CO转化率低、目标产物芳烃选择性低、芳烃产物中轻质芳烃比例较低、催化剂制备复杂等问题,提供了一种新的催化剂体系,该体系用于合成气转化生产芳烃并联产轻烃时,具有催化剂制备简单、装填方便、CO转化率高、目标产物芳烃选择性高、芳烃中轻质芳烃占比高、设备投资成本低等优点。
为解决上述技术问题,本发明的技术方案如下:一种核壳结构多功能催化剂体系,其特征在于,催化剂为包括金属氧化物和分子筛的具有核壳结构的整体式多功能催化剂。
上述技术方案中,优选的,金属氧化物的金属组分选自碱金属、碱土金属、稀土金属、IVB、VIII、IB、IIB、IIIA族元素中的至少一种。上述技术方案中,更优选的,金属氧化物的金属组分选自Cr、Zr、Mn、Ce、La、Mo、Ti、In、Ga、Zn中的一种或至少一种。
上述技术方案中,更优选的,金属氧化物的金属组分选自Cr、Zr、Mn、In、Ga、Zn中的一种或至少一种。
上述技术方案中,更优选的,金属氧化物的金属组分选自Zn、In、Cr和Mn。
上述技术方案中,更优选的,金属氧化物的金属组分选自Zn、Cr和Mn。
上述技术方案中,更优选的,金属氧化物的金属组分选自Zn、Cr和In。
上述技术方案中,更优选的,金属氧化物的金属组分选自Zn和Cr。
上述技术方案中,更优选的,金属氧化物的金属组分选自Zn和Mn。
上述技术方案中,更优选的,金属氧化物的金属组分选自Ga、Mn和Cr。
上述技术方案中,更优选的,金属氧化物的金属组分选自Zn、Cr和Ga。上述技术方案中,优选的,分子筛选自MFI或MEL结构分子筛中的一种或多种。
上述技术方案中,更优选的,分子筛选自ZSM-5、ZSM-11、Silicalite-1、Silicalite-2中的一种或至少一种。
上述技术方案中,优选的,分子筛硅铝比为12~∞。
上述技术方案中,更优选的,分子筛硅铝比为12~250。
上述技术方案中,更优选的,分子筛硅铝比为70~100。
上述技术方案中,优选的,核壳结构催化剂至少包含1层壳层分子筛,更优选为2层或3层或4层。
上述技术方案中,优选的,当核壳结构催化剂包含2层或2层以上壳层分子筛时,外壳层分子筛的硅铝比优选为不低于内壳层分子筛;优选的,外壳层分子筛选自Silicalite-1、Silicalite-2中的一种或至少一种。
上述技术方案中,优选的,核壳结构催化剂中核层金属氧化物/壳层分子筛质量比范围(8:1)~(1:8)。
上述技术方案中,更优选的,核壳结构催化剂中核层金属氧化物/壳层分子筛质量比范围(3:1)~(1:3)。
上述技术方案中,更优选的,核壳结构催化剂中核层金属氧化物/壳层分子筛质量比范围(3:2)~(2:3)。
为解决上述技术问题,本发明采用的技术方案之二为:一种合成气转化生产芳烃联产轻烃的方法,以合成气为原料,原料与上述的催化剂体系接触反应得到含芳烃和轻烃的物流。
上述技术方案中,优选的,所述原料合成气包含体积分数10~50%的H2,和/或H2/CO摩尔比范围为0.25~5.0。
上述技术方案中,更优选的,所述原料合成气H2/CO摩尔比范围为0.25~1.0。
上述技术方案中,更优选的,所述原料合成气H2/CO摩尔比范围为0.5~1.0。
上述技术方案中,优选的,反应条件为:反应温度300~500℃、和/或反应压力0.5~10.0MPa、和/或体积空速1000~20000h-1。
上述技术方案中,更优选的,反应条件为:反应温度300~400℃、和/或反应压力1.0~8.0MPa、和/或体积空速2000~8000h-1。
本发明涉及的工艺过程由核壳结构多功能催化剂实现,核壳结构多功能催化剂由具有合成气转化活性的金属氧化物和具有芳烃/轻烃合成活性的分子筛组成。在包含核层金属氧化物和至少一层壳层分子筛的核壳结构催化剂中,合成气连续转化,首先生成低碳中间体,经进一步转化生成芳烃、轻烃等产物。
本发明试图提供由合成气制备芳烃、联产轻烃的新工艺。产物包含BTX芳烃、C9+芳烃及C1-C5+轻烃。对于分子筛,其酸性主要受硅铝比的影响。一般低硅铝比的分子筛具有更高的酸量,有利于甲醇等中间体的转化以及轻烃的齐聚、环化,从而有利于提高目标产物芳烃的收率。但过强的酸性或过高的酸量可能加剧积碳反应。此外,由于分子筛的择形作用,其孔道结构也是影响产物分布的一个重要因素,因此分子筛的选型对于目标产物的收率同样至关重要。本发明中涉及的芳烃/轻烃合成组分为核壳催化剂的壳层分子筛,选用硅铝比在12~∞范围的MFI或MEL结构分子筛。
合成气转化生产芳烃联产轻烃是一个多步反应,为促进主反应、同时抑制副反应,体系的工艺条件需要设定在对各反应适宜的范围内。同时,提供两种活性中心(合成气转化、芳烃/轻烃合成)的催化剂需具有足够强的耦合能力。对于多段催化剂体系,虽然可以通过调节各段的工艺条件以实现多步反应的进行,但各段间工艺条件差距过大会导致能耗以及运行成本的提高。因此,也需要解决多步反应催化剂及工艺条件匹配的问题。本发明选用的合成气转化催化剂为与核壳结构分子筛耦合能力较强的金属氧化物,金属组分优选自Cr、Zr、Mn、Ce、La、Mo、Ti、In、Ga、Zn中的一种或至少一种。
所采用的工艺条件如下:原料合成气包含体积分数10~50%的H2,和/或H2/CO摩尔比在0.25~5.0范围内;除H2、CO外,体系中还包括N2、CO2、H2O、惰性气体等组分中的一种或多种;床层温度300~500℃,和/或体系压力0.5~10.0MPa,和/或空速1000~20000h-1。
反应器类型可选用固定床、流化床、移动床等。
原料气选用H2/CO摩尔比范围0.25~5.0的合成气。不同来源的合成气,可以采用水煤气变换处理/逆水煤气变换处理调节其H2/CO摩尔比。处理所需的H2O和CO2部分来源于反应产物分离回流,部分来源于管道供气。
本发明中,反应后物流中包括未转化的CO和H2,CO2、以及烃类产物,烃类产物又由芳烃和C1~C5+烃类组成,芳烃包括C6~C9+芳烃。各产物选择性定义为各产物在有机产物总碳数中的占比(mol%)。具体计算方法如下:
有机产物总碳数=Σ(有机产物i的物质的量×有机产物i分子中碳原子数)
有机产物j的选择性=有机产物j的物质的量×有机产物j分子中碳原子数/有机产物总碳数×100%
芳烃选择性=C6芳烃选择性+C7芳烃选择性+C8芳烃选择性+C9+芳烃选择性
C6-C8芳烃占比=(C6芳烃选择性+C7芳烃选择性+C8芳烃选择性)/芳烃选择性×100%
本发明中涉及的轻质芳烃是指C6-C8芳烃;芳烃中的C6-C8等轻质芳烃广泛应用于合成橡胶、合成树脂、合成纤维的生产,同时也是合成洗涤剂、增塑剂、***、染料和农药等产品的工业原料,而C9+重质芳烃的需求量相对较小,往往需要经轻质化过程转化为轻质芳烃。因此,提高总芳烃中C6-C8芳烃的占比,可以有效降低后续芳烃产物处理的难度,具有较高的经济效益。
采用本发明的技术方案,通过筛选优选催化剂,优化复合催化体系中催化剂间的组合形式,实现了多步反应的高效耦合,不仅降低了设备投资成本,更通过中间产物的定向二次转化,提高了芳烃的选择性,同时优化了芳烃产物分布,实现了轻质芳烃的高效生产。将催化剂体系用于合成气制芳烃的反应中,芳烃选择性可达70%以上,C6-C8芳烃在总芳中占比可达70%以上,取得了良好的技术效果。
具体实施方式
【实施例1】
按Zn/Cr摩尔比1:3,采用溶胶凝胶法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比1/1,配备含硅溶胶、偏铝酸钠、四丙基溴化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);将ZnCr3Ox/HZ5(12)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。
原料气H2/CO/N2,产物由气相色谱在线分析,其中以N2为内标实现产物的定量分析。产物采用三柱分离,其中一根为hayesep-Q填充柱,分离产物进入热导池检测器检测氢气、氮气、一氧化碳、二氧化碳、甲烷等永久气体。采用二维中心切割技术对脂肪烃、芳香烃进行切割,并由两套氢火焰检测器分别检测,一根为HP-PLOT Al2O3毛细管柱,产物进入氢火焰检测器检测甲烷、乙烷、乙烯、丙烷、丙烯、丁烷、丁烯等脂肪烃产物;另一根为DB-WAXetr毛细管柱,产物进入氢火焰检测器检测苯、甲苯、二甲苯等芳烃产物。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例2】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比1/1,配备含硅溶胶、偏铝酸钠、四丁基溴化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-11(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ11(12);将ZnCr3Ox/HZ11(12)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例3】
按Zn/Cr摩尔比1:3,采用高温烧结法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=30、核/壳质量比1/1,配备含硅溶胶、偏铝酸钠、四丙基溴化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=30)的核壳结构分子筛,记作ZnCr3Ox/HZ5(30);将ZnCr3Ox/HZ5(30)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例4】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=50、核/壳质量比1/1,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=50)的核壳结构分子筛,记作ZnCr3Ox/HZ5(50);将ZnCr3Ox/HZ5(50)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例5】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=50、核/壳质量比1/1,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=70)的核壳结构分子筛,记作ZnCr3Ox/HZ5(70);将ZnCr3Ox/HZ5(70)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例6】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=100、核/壳质量比1/1,配备含正硅酸乙酯、异丙醇铝、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=100)的核壳结构分子筛,记作ZnCr3Ox/HZ5(100);将ZnCr3Ox/HZ5(100)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例7】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比5/1,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)(5:1);将ZnCr3Ox/HZ5(12)(5:1)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例8】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比3/2,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)(3:2);将ZnCr3Ox/HZ5(12)(3:2)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例9】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)(2:3);将ZnCr3Ox/HZ5(12)(2:3)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例10】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比1/5,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)(1:5);将ZnCr3Ox/HZ5(12)(1:5)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例11】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比1/1,配备含正硅酸乙酯、硝酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);以ZnCr3Ox/HZ5(12)为核,按外壳层Si/Al=100、核/壳质量比4/1,配备含正硅酸乙酯、硝酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12),所得混合体系经水热处理,最终得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为HZSM-5(Si/Al=100)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/HZ5(100);将ZnCr3Ox/HZ5(12)/HZ5(100)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例12】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比1/1,配备含硅酸钠、硫酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);以ZnCr3Ox/HZ5(12)为核,按外壳层Si/Al=100、核/壳质量比4/1,配备含正硅酸乙酯、异丙醇铝、四丁基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12),所得混合体系经水热处理,最终得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为HZSM-11(Si/Al=100)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/HZ11(100);将ZnCr3Ox/HZ5(12)/HZ11(100)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例13】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比1/1,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);以ZnCr3Ox/HZ5(12)为核,按核/壳质量比4/1,配备含硅酸钠、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12),所得混合体系经水热处理,得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/S1;将ZnCr3Ox/HZ5(12)/S1造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例14】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比1/1,配备含硅酸钠、硫酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);以ZnCr3Ox/HZ5(12)为核,按核/壳质量比4/1,配备含正硅酸乙酯、四丁基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12),所得混合体系经水热处理,最终得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-2(Si/Al=∞)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/S2;将ZnCr3Ox/HZ5(12)/S2造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例15】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);以ZnCr3Ox/HZ5(12)为核,按核/壳质量比5/1,配备含硅酸钠、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12),所得混合体系经水热处理,得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/S1(2:3:1);将ZnCr3Ox/HZ5(12)/S1(2:3:1)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例16】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);以ZnCr3Ox/HZ5(12)为核,按核/壳质量比5/2,配备含硅酸钠、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12),所得混合体系经水热处理,得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/S1(2:3:2);将ZnCr3Ox/HZ5(12)/S1(2:3:2)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例17】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按核/壳质量比2/1,配备含正硅酸乙酯、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnCr3Ox/S1;以ZnCr3Ox/S1为核,按核/壳质量比1/1,配备含硅酸钠、铝酸钠、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/S1,所得混合体系经水热处理,得到核心为ZnCr3Ox、内壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)、外壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/S1/HZ5(12)(2:1:3);将ZnCr3Ox/S1/HZ5(12)(2:1:3)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例18】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比1/1,配备含正硅酸乙酯、硝酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);以ZnCr3Ox/HZ5(12)为核,按外壳层Si/Al=100、核/壳质量比4/0.1,配备含正硅酸乙酯、硝酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12),所得混合体系经水热处理,得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为HZSM-5(Si/Al=100)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/HZ5(100);以ZnCr3Ox/HZ5(12)/HZ5(100)为核,按核/壳质量比4.1/0.9,配备含正硅酸乙酯、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12)/HZ5(100),最终得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、中间壳层为HZSM-5(Si/Al=100)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/HZ5(100)/S1(2:2:0.1:0.9);将ZnCr3Ox/HZ5(12)/HZ5(100)/S1(2:2:0.1:0.9)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例19】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比1/1,配备含正硅酸乙酯、硝酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);以ZnCr3Ox/HZ5(12)为核,按外壳层Si/Al=100、核/壳质量比4/0.9,配备含正硅酸乙酯、硝酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12),所得混合体系经水热处理,得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为HZSM-5(Si/Al=100)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/HZ5(100);以ZnCr3Ox/HZ5(12)/HZ5(100)为核,按核/壳质量比4.9/0.1,配备含正硅酸乙酯、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12)/HZ5(100),最终得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、中间壳层为HZSM-5(Si/Al=100)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/HZ5(100)/S1(2:2:0.9:0.1);将ZnCr3Ox/HZ5(12)/HZ5(100)/S1(2:2:0.9:0.1)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例20】
按Zn/Zr摩尔比1:3,采用共沉淀法制备Zn-Zr氧化物,记作ZnZr3Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含硅酸钠、硫酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnZr3Ox,所得混合体系经水热处理,得到核心为ZnZr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnZr3Ox/HZ5(12);以ZnZr3Ox/HZ5(12)为核,按核/壳质量比5/1,配备含正硅酸乙酯、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnZr3Ox/HZ5(12),所得混合体系经水热处理,最终得到核心为ZnZr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnZr3Ox/HZ5(12)/S1;将ZnZr3Ox/HZ5(12)/S1造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例21】
按Zn/Mn摩尔比1:5,采用共沉淀法制备Zn-Mn氧化物,记作ZnMn5Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含硅酸钠、硫酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnMn5Ox核心,所得混合体系经水热处理,得到核心为ZnMn5Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnMn5Ox/HZ5(12);以ZnMn5Ox/HZ5(12)为核,按核/壳质量比5/1,配备含正硅酸乙酯、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnMn5Ox/HZ5(12),所得混合体系经水热处理,最终得到核心为ZnMn5Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnMn5Ox/HZ5(12)/S1;将ZnMn5Ox/HZ5(12)/S1造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例22】
按Zn/In/Cr摩尔比4:1:15,采用共沉淀法制备Zn-In-Cr氧化物,记作Zn0.8In0.2Cr3Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含硅酸钠、硫酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的Zn0.8In0.2Cr3Ox,所得混合体系经水热处理,得到核心为Zn0.8In0.2Cr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作Zn0.8In0.2Cr3Ox/HZ5(12);以Zn0.8In0.2Cr3Ox/HZ5(12)为核,按核/壳质量比5/1,配备含正硅酸乙酯、四丙基氢氧化铵的母液,并向母液中投入一定量的Zn0.8In0.2Cr3Ox/HZ5(12),所得混合体系经水热处理,最终得到核心为Zn0.8In0.2Cr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作Zn0.8In0.2Cr3Ox/HZ5(12)/S1;将Zn0.8In0.2Cr3Ox/HZ5(12)/S1造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例23】
按Zn/Cr/Mn摩尔比1:2:2,采用共沉淀法制备Zn-Cr-Mn氧化物,记作ZnCr2Mn2Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含硅酸钠、硫酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr2Mn2Ox,所得混合体系经水热处理,得到核心为ZnCr2Mn2Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr2Mn2Ox/HZ5(12);以ZnCr2Mn2Ox/HZ5(12)为核,按核/壳质量比5/1,配备含正硅酸乙酯、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr2Mn2Ox/HZ5(12),所得混合体系经水热处理,最终得到核心为ZnCr2Mn2Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnCr2Mn2Ox/HZ5(12)/S1;将ZnCr2Mn2Ox/HZ5(12)/S1造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例24】
按Zn/In/Cr/Mn摩尔比4:1:10:10,采用共沉淀法制备Zn-In-Cr-Mn氧化物,记作Zn0.8In0.2Cr2Mn2Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含硅酸钠、硫酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的Zn0.8In0.2Cr2Mn2Ox,所得混合体系经水热处理,得到核心为Zn0.8In0.2Cr2Mn2Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作Zn0.8In0.2Cr2Mn2Ox/HZ5(12);以Zn0.8In0.2Cr2Mn2Ox/HZ5(12)为核,按核/壳质量比5/1,配备含正硅酸乙酯、四丙基氢氧化铵的母液,并向母液中投入一定量的Zn0.8In0.2Cr2Mn2Ox/HZ5(12),所得混合体系经水热处理,最终得到核心为Zn0.8In0.2Cr2Mn2Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作Zn0.8In0.2Cr2Mn2Ox/HZ5(12)/S1;将Zn0.8In0.2Cr2Mn2Ox/HZ5(12)/S1造粒、破碎得到20~40目的催化剂颗粒。称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例25】
按Zn/Ga/Cr摩尔比0.9:0.1:3,采用共沉淀法制备Zn-Ga-Cr氧化物,记作Zn0.9Ga0.1Cr3Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含硅酸钠、硫酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的Zn0.9Ga0.1Cr3Ox,所得混合体系经水热处理,得到核心为Zn0.9Ga0.1Cr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作Zn0.9Ga0.1Cr3Ox/HZ5(12);以Zn0.9Ga0.1Cr3Ox/HZ5(12)为核,按核/壳质量比5/1,配备含正硅酸乙酯、四丙基氢氧化铵的母液,并向母液中投入一定量的Zn0.9Ga0.1Cr3Ox/HZ5(12)核心,所得混合体系经水热处理,最终得到核心为Zn0.9Ga0.1Cr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作Zn0.9Ga0.1Cr3Ox/HZ5(12)/S1;将Zn0.9Ga0.1Cr3Ox/HZ5(12)/S1造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例26】
按Ga/Cr/Mn摩尔比1:2:3,采用共沉淀法制备Ga-Cr-Mn氧化物,记作GaCr2Mn3Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含硅酸钠、硫酸铝、四丙基氢氧化铵的母液,并向母液中投入一定量的GaCr2Mn3Ox,所得混合体系经水热处理,得到核心为GaCr2Mn3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作GaCr2Mn3Ox/HZ5(12);以GaCr2Mn3Ox/HZ5(12)为核,按核/壳质量比5/1,配备含正硅酸乙酯、四丙基氢氧化铵的母液,并向母液中投入一定量的GaCr2Mn3Ox/HZ5(12)核心,所得混合体系经水热处理,最终得到核心为GaCr2Mn3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作GaCr2Mn3Ox/HZ5(12)/S1;将GaCr2Mn3Ox/HZ5(12)/S1造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【对比例1】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;采用水热法合成Si/Al比为12的HZSM-5分子筛,所得分子筛记作HZ5(12);将ZnCr3Ox、HZ5(12)粉末按质量比1:1进行机械混合,再造粒、破碎得到20~40目的催化剂颗粒。称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃温度下以H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【对比例2】
按Fe/Mn摩尔比2:3,采用共沉淀法制备Fe-Mn氧化物,记作Fe2Mn3Ox;采用水热法合成Si/Al比为12的HZSM-5分子筛,记作HZ5(12);将Fe2Mn3Ox、HZ5(12)分别造粒、破碎得到20~40目的颗粒。称取0.75g Fe2Mn3Ox、0.75g HZ5(12)颗粒并均匀混合。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃下H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【对比例3】
按Zn/Cr摩尔比2:1,采用共沉淀法制备Zn-Cr氧化物,记作Zn2CrOx;采用水热法合成Si/Al比为40的Hβ分子筛,记作Hβ(40);将Zn2CrOx、Hβ(40)分别造粒、破碎得到20~40目的颗粒。称取0.75g Zn2CrOx、0.75g Hβ(40)颗粒并均匀混合。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃下H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【对比例4】
按Zn/Zr摩尔比0.02:1,称取Zr(NO3)4·5H2O加入乙醇中并于50℃下搅拌2h,加入聚乙烯醇继续搅拌3h,再加入ZnCl2于50℃下继续搅拌2h。向所得溶液中加入10wt%NaOH溶液,调节体系pH值为9.5,在70℃下回流搅拌5h。所得样品经抽滤、洗涤、干燥、焙烧得到催化剂Zn0.02ZrOx;采用水热法合成Si/Al比为40的USY分子筛,记作USY(40);称取质量比2:3的Zn0.02ZrOx、USY(40)粉末,加入至乙醇溶剂中超声分散,混合物经抽滤、乙醇洗涤、真空干燥、研钵研磨后,移至管式炉中于流动空气气氛中550℃下焙烧12h,所得样品经造粒、破碎得到20~40目催化剂颗粒。称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃下H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【对比例5】
按Zn/Zr摩尔比0.02:1,称取Zr(NO3)4·5H2O加入乙醇中并于50℃下搅拌2h,加入聚乙烯醇继续搅拌3h,再加入ZnCl2于50℃下继续搅拌2h。向所得溶液中加入10wt%NaOH溶液,调节体系pH值为9.5,在70℃下回流搅拌5h。所得样品经抽滤、洗涤、干燥、焙烧得到催化剂Zn0.02ZrOx;采用水热法合成Si/Al比为12的USY分子筛,记作USY(12);将Zn0.02ZrOx、USY(12)粉末按质量比1:1进行机械混合,再造粒、破碎得到20~40目的催化剂颗粒。称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力2.0MPa,原料气H2/CO比例1.0,空速2000h-1的条件下进行催化剂评价。反应前催化剂于395℃下H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表1所示。
【实施例27】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);以ZnCr3Ox/HZ5(12)为核,按核/壳质量比5/1,配备含硅酸钠、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12),所得混合体系经水热处理,得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/S1(2:3:1);将ZnCr3Ox/HZ5(12)/S1(2:3:1)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度350℃、压力8.0MPa,原料气H2/CO比例1.0,空速8000h-1的条件下进行催化剂评价。反应前催化剂于395℃下H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表2所示。
【实施例28】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);以ZnCr3Ox/HZ5(12)为核,按核/壳质量比5/1,配备含硅酸钠、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12),所得混合体系经水热处理,得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/S1(2:3:1);将ZnCr3Ox/HZ5(12)/S1(2:3:1)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力8.0MPa,原料气H2/CO比例0.25,空速10000h-1的条件下进行催化剂评价。反应前催化剂于395℃下H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表2所示。
【实施例29】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);以ZnCr3Ox/HZ5(12)为核,按核/壳质量比5/1,配备含硅酸钠、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12),所得混合体系经水热处理,得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/S1(2:3:1);将ZnCr3Ox/HZ5(12)/S1(2:3:1)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度350℃、压力5.0MPa,原料气H2/CO比例4.0,空速18000h-1的条件下进行催化剂评价。反应前催化剂于395℃下H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表2所示。
【实施例30】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);以ZnCr3Ox/HZ5(12)为核,按核/壳质量比5/1,配备含硅酸钠、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12),所得混合体系经水热处理,得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/S1(2:3:1);将ZnCr3Ox/HZ5(12)/S1(2:3:1)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力5.0MPa,原料气H2/CO比例1.0,空速18000h-1的条件下进行催化剂评价。反应前催化剂于395℃下H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表2所示。
【实施例31】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);以ZnCr3Ox/HZ5(12)为核,按核/壳质量比5/1,配备含硅酸钠、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12),所得混合体系经水热处理,得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/S1(2:3:1);将ZnCr3Ox/HZ5(12)/S1(2:3:1)造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度450℃、压力5.0MPa,原料气H2/CO比例1.0,空速18000h-1的条件下进行催化剂评价。反应前催化剂于395℃下H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表2所示。
【实施例32】
按Zn/Cr摩尔比1:3,采用共沉淀法制备Zn-Cr氧化物,记作ZnCr3Ox;按壳层Si/Al=12、核/壳质量比2/3,配备含正硅酸乙酯、拟薄水铝石、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox,所得混合体系经水热处理,得到核心为ZnCr3Ox、壳层为HZSM-5(Si/Al=12)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12);以ZnCr3Ox/HZ5(12)为核,按核/壳质量比5/1,配备含硅酸钠、四丙基氢氧化铵的母液,并向母液中投入一定量的ZnCr3Ox/HZ5(12),所得混合体系经水热处理,得到核心为ZnCr3Ox、内壳层为HZSM-5(Si/Al=12)、外壳层为Silicalite-1(全硅ZSM-5,Si/Al=∞)的核壳结构分子筛,记作ZnCr3Ox/HZ5(12)/S1(2:3:1);将ZnCr3Ox/HZ5(12)/S1(2:3:1)、P2O5粉末按质量比1:0.02进行机械混合,再造粒、破碎得到20~40目的催化剂颗粒,称取1.5g催化剂颗粒装填于反应器中。在反应温度395℃、压力4.0MPa,原料气H2/CO比例0.5,空速5000h-1的条件下进行催化剂评价。反应前催化剂于395℃下H2预处理2h。CO转化率、芳烃选择性及芳烃产物分布结果如表2所示。
【实施例1~26】
表1
【实施例27~32】
取实施例15制备得到的催化剂用于合成气制芳烃联产轻烃的反应,反应条件和评价结果见表2。
表2
Claims (16)
1.一种核壳结构多功能催化剂体系,其特征在于,催化剂为具有核壳结构的整体式多功能催化剂,核层为金属氧化物,壳层为分子筛;
所述壳层分子筛的硅铝比为12-∞;
所述壳层分子筛选自MFI或MEL结构分子筛中的一种或多种;
所述核壳结构催化剂至少包含2层壳层分子筛。
2.根据权利要求1所述的核壳结构多功能催化剂体系,其特征在于金属氧化物的金属组分选自碱金属、碱土金属、稀土金属、IVB、VIII、IB、IIB、IIIA族元素中的一种或至少一种。
3.根据权利要求2所述的核壳结构多功能催化剂体系,其特征在于金属氧化物的金属组分选自Cr、Zr、Mn、Ce、La、Mo、Ti、In、Ga、Zn中的一种或至少一种。
4.根据权利要求2或3所述的核壳结构多功能催化剂体系,其特征在于金属氧化物的金属组分选自Cr、Zr、Mn、In、Ga、Zn中的一种或至少一种。
5.根据权利要求2或3所述的核壳结构多功能催化剂体系,其特征在于金属氧化物的金属组分选自Zn、Ce、La、Mo、Ti中的一种或至少一种。
6.根据权利要求2所述的核壳结构多功能催化剂体系,其特征在于金属氧化物为单金属氧化物或双金属氧化物或多金属氧化物。
7.根据权利要求1所述的核壳结构多功能催化剂体系,其特征在于壳层分子筛选自ZSM-5、ZSM-11、Silicalite-1、Silicalite-2中的一种或至少一种。
8.根据权利要求1所述的核壳结构多功能催化剂体系,其特征在于壳层分子筛的硅铝比为12-250。
9.根据权利要求1所述的核壳结构多功能催化剂体系,其特征在于核壳结构催化剂至少包含3层壳层分子筛。
10.根据权利要求1所述的核壳结构多功能催化剂体系,其特征在于核层金属氧化物/壳层分子筛质量比范围(8:1)-(1:8)。
11.根据权利要求1所述的核壳结构多功能催化剂体系,其特征在于核层金属氧化物/壳层分子筛质量比范围(3:1)-(1:3)。
12.一种合成气转化生产芳烃联产轻烃的方法,以合成气为原料,原料与权利要求1-11中任一项所述的核壳结构多功能催化剂接触反应得到含芳烃和轻烃的物流。
13.根据权利要求12所述合成气转化生产芳烃联产轻烃的方法,其特征在于所述原料合成气包含体积分数10~50%的H2。
14.根据权利要求12所述合成气转化生产芳烃联产轻烃的方法,其特征在于H2/CO摩尔比范围为0.25-5.0。
15.根据权利要求12所述合成气转化生产芳烃联产轻烃的方法,其特征在于H2/CO摩尔比范围为0.25-1.0。
16.根据权利要求12所述合成气转化生产芳烃联产轻烃的方法,其特征在于反应条件为:反应温度300-500℃;和/或反应压力0.5-10.0MPa;和/或体积空速1000-20000h-1。