CN109594176A - A kind of reflective cotton fiber fabric and preparation method thereof - Google Patents
A kind of reflective cotton fiber fabric and preparation method thereof Download PDFInfo
- Publication number
- CN109594176A CN109594176A CN201811591350.4A CN201811591350A CN109594176A CN 109594176 A CN109594176 A CN 109594176A CN 201811591350 A CN201811591350 A CN 201811591350A CN 109594176 A CN109594176 A CN 109594176A
- Authority
- CN
- China
- Prior art keywords
- reflective
- fiber
- fabric
- cotton fiber
- warping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of reflective cotton fiber fabric and preparation method thereof, belongs to face weave technical field.It is characterized by: fabric yarn is blended by reflective fiber and cotton fiber, fabric tissue is two lattice, and reflective fiber accounts for 5%wt ~ 15%wt in fabric, and cotton fiber accounts for 85%wt ~ 95%wt in fabric；The reflective fiber is the plastics wire material of poly- two rouge of ethylene.Weaving step: using reflective fiber in proportion in weft yarn after warping, sizing, reflective fiber individually does small axis with wheel in one's ear, and loom main shaft angle is 63 ° ~ 65 °, and adjusts weft-recepting sword head and reached at first dent of reed at 62 ° ~ 64 °.Fabric of the invention is blended appropriate reflective fiber in cotton fiber, and the fabric for having both reflective and comfortable effect is made.Compared with reflective fiber is added when warping again, because reflective fiber is different from the tension of cotton fiber in weaving process, tension can be preferably adjusted using wheel in one's ear.
Description
Technical field
A kind of reflective cotton fiber fabric and preparation method thereof, belongs to face weave technical field.
Background technique
With people's lives Quality advance, people's nocturnalism increases, safety and comfortable, product for increase people
Durability.Therefore inventor carries out this research and development, no longer office after understanding in face of various coating class Reflection fabrics in the market
It is limited to various coating class Reflection fabrics in the market.
It is that glass microballoon is applied on PET film that reflective fiber, which is also referred to as Reflect light line, is cut into silk thread by filament cutter.It can compile
It is made into the reflective braided fabric of various patterns, such as light-reflection fabric ribbon, reflective wrapped belt, reflective braid over braid.It can also be handed over simultaneously with fabric
It knits, forms Reflection fabric.It is not only that various products are decorated, in night or bad visibility environment, with the anti-of high refractive index
Light bead is densely coated on various types of resins substrate, generates strong reflecting effect, enables a wearer to have in the dark splendid
Visuality enhances warning, recognition effect.It is both a kind of safety article and a kind of good fashion decorations.Main ingredient:
PET/ reflectorized material/Environment-friendlyglue glue.
Reflective: reflected light function admirable, such as reflectorized material, the usual 500CPL white of reflective silver products and yellow fluorescence are anti-
Optical plastic is the typical plant film strength of 700CPL in the environment of night or low visibility, and intensity of light reflection provides super for client
Effectively super reliable personal safety.
Angle: reflectorized material is not only the similar product that reflecting effect is better than other brands, and has wide-angle, and work clothes is worked as
Become a biggish reflecting effect from incidence angle reflecting surface.
Durability: reflectorized material has good ageing-resistant, wear-resisting, abrasion resistance.Washable or dry-cleaning, it is not easily to fall off,
Continuous washing, it can still remain above 75% former reflecting effect.
Flexibility and range: reflectorized material, which is widely applied range, can be used for weaving safety and camisole, work clothes, outside
Set, rain gear, raincoat, gym suit, knapsack, gloves, shoes, the fields such as cap.
Existing reflective fiber is based on metallized thread, and after prolonged use, a universal problem is exactly to cause fabric strong
Degree is remarkably decreased, easy fracture.
Cotton fiber has preferable hygroscopicity, and under normal conditions, fiber can absorb moisture in peripherad atmosphere,
Moisture content is 8 ~ 10%, so it contacts the skin of people, makes one to feel softness without stiff.If cotton humidity increases, surrounding temperature
Degree is higher, and the amount of moisture contained in fiber can all be evaporated and be dispersed, and so that fabric is kept water equilibrated state, makes people feel comfortable.Due to
Cotton fiber is the non-conductor of heat and electricity, and the coefficient of heat conduction is extremely low, and because cotton fiber itself has a porosity, the high advantage of elasticity,
Large quantity of air can be accumulated between fiber, air is the non-conductor of heat and electricity again, so, pure cotton fiber textile has good
Warmth retention property, wearing pure cotton fabric clothes makes one to feel warm.The resistance to thermal energy of cotton goods is good, at 110 DEG C Celsius or less, only meeting
Cause on fabric moisture to evaporate, fiber will not be damaged, so pure cotton fabric is at normal temperature, dress is used, and washing printing and dyeing etc. are to knitting
Product are all without influence, thus to improving pure cotton fabric wearability washable and durable.Cotton fiber is natural fiber, and main component is
Cellulose, there are also a small amount of waxy substances and nitrogenous object and pectic substance.Pure cotton fabric is checked through various aspects and practice, fabric and flesh
Skin contact is without any stimulation, no negative interaction, wears long useful and harmless to human body, and sanitation performance is good.
Lack a kind of mature technology that reflective fiber and cotton fiber can be made into fabric now, leads to not the two
Advantage is still remembered to combine.
Summary of the invention
The technical problem to be solved by the present invention is overcoming the deficiencies of the prior art and provide one kind has both reflective and comfortable effect
Reflective cotton fiber fabric of fruit and preparation method thereof.
The technical solution adopted by the present invention to solve the technical problems is: the reflective cotton fiber fabric, it is characterised in that: face
Material yarn is blended by reflective fiber and cotton fiber, and fabric tissue is two lattice, in fabric reflective fiber account for 5%wt ~
15% wt, cotton fiber accounts for the wt of 85% wt ~ 95% in fabric；The reflective fiber is the plastics silk material of poly- two rouge of ethylene
Material.
Fabric of the invention is blended appropriate reflective fiber in cotton fiber, and the fabric for having both reflective and comfortable effect is made.
Preferably, the cotton fiber is long-staple cotton.Elasticity and strength character are more suitable for being blended with reflective fiber.
Preferably, reflective fiber accounts for the wt of 5%wt ~ 10% in the fabric, and cotton fiber accounts for 90% wt ~ 95% in fabric
wt。
Preferably, reflective fiber accounts for the wt of 10%wt ~ 15% in the fabric, and cotton fiber accounts for 85% wt ~ 90% in fabric
wt。
A kind of preparation method of above-mentioned reflective cotton fiber fabric, which is characterized in that including following weaving step:
1) warping: cotton fiber takes batch warping；
2) sizing: cotton fiber midge, mud jacking after waxing, into dry leasing area after complete beam of a loom；
3) it weaves: using reflective fiber in weft yarn in proportion, reflective fiber individually does small axis with wheel in one's ear, is directly mounted at loom
On；Weaved using rapier loom, sword head is into the shed open time: loom main shaft angle is 63 ° ~ 65 °, and sword head is sent to be arranged in reed side iron
At item, adjustment weft-recepting sword head is reached at 62 ° ~ 64 ° at first dent of reed.
Because reflective fiber moulding is strong, surface is smooth, together with cotton fiber when warping, because of speed height, reflective fiber unwinding speed
Degree is fast, so that reflective fiber distorts on beam of a loom, so that reflecting effect reduces, and it is special individually to be made of wheel in one's ear to change this problem
Small axis, is directly mounted on loom, smooth in guarantee reflective fiber manufacturing process, non-warping.The present invention is knitted using rapier loom
It makes, adjustment weaving parameters are solved when reflective fiber does weft yarn, because reflective fiber is sheet silk, so that jet air point
It dissipates, the problems such as yarn is not easily controlled, and wefting insertion effect is poor, and jet loom for drawing weft yarn is difficult.With addition reflective fiber phase when warping again
Than can preferably adjust tension using wheel in one's ear because reflective fiber is different from the tension of cotton fiber in weaving process.
Preferably, the warping speed 600m/min of warping described in step 1), 630 ~ 720 bobbins of warping head point, warping
12 ~ 14g of tension.Better warping effect can be reached.
Preferably, sizing described in step 2 uses dual-box slasher.
Preferably, stock tank viscosity 8% in cotton fiber midge described in step 2, the rate of sizing 14%, hundred meters with slurry 2.34kg.Energy
Enough reach better sizing effect.
Preferably, loom main shaft angle is 64 ° in step 2.Better wefting insertion can be reached under preferred loom main shaft angle
Effect.
Compared with prior art, beneficial effect possessed by a kind of reflective cotton fiber fabric of the invention and preparation method thereof
Be: fabric of the invention is blended appropriate reflective fiber in cotton fiber, and the fabric for having both reflective and comfortable effect is made.Because reflective
Fiber moulding is strong, and surface is smooth, and together with cotton fiber when warping, because of speed height, reflective fiber withdrawal speed is fast, so that on beam of a loom
Reflective fiber distortion, so that reflecting effect reduces, it is special individually to do small axis with wheel in one's ear to change this problem, it is directly mounted at
It is smooth in guarantee reflective fiber manufacturing process on loom, it is non-warping.The present invention is weaved using rapier loom, adjusts weaving parameters
It solves when reflective fiber does weft yarn, because reflective fiber is sheet silk, so that jet air disperses, yarn is not allowed easily-controllable
The problems such as system, wefting insertion effect is poor, and jet loom for drawing weft yarn is difficult.Compared with reflective fiber is added when warping again, in weaving process
Because reflective fiber is different from the tension of cotton fiber, tension can be preferably adjusted using wheel in one's ear.Reflective cotton fiber of the invention
Fabric can be used for weaving safety and camisole, work clothes, housing, rain gear, raincoat, gym suit, knapsack, gloves, shoes, cap etc.
Field.
Specific embodiment
The present invention will be further described combined with specific embodiments below, and wherein embodiment 1 is best implements.
Embodiment 1
Warp Tension Test is 23:1, weft yarn arrangement 14:2, selects the reed of 64.5#/2 ", and ground enters number 3 and enters, total quantity of warps 6348；
Fabric yarn is blended by reflective fiber and cotton fiber, and fabric tissue is two lattice, and reflective fiber accounts in fabric
8% wt, cotton fiber accounts for 82% wt in fabric；Reflective fiber chooses moulding, the good material of reflecting effect.Reflective fiber is polyphenyl
The plastics wire material of two rouge of dioctyl phthalate second；100% long-staple cotton of long wool cotton content is selected in the selection of cotton fiber；
Warping: cotton fiber takes batch warping, warping speed 600m/min；650 bobbins of warping head point, yarn gripper opening time
5s, tension rail opening time 4s, reed blow-time 30s, reed blowing-out time 2s, break end 6 ~ 8s of action time, and tension in Warping 12 ~
14g；
Sizing: dual-box slasher is used, yarn is by creel (creel unwinding tension control is in 5N/ axis) by drawing yarn rod
Cotton fiber is set to enter a stock tank, (cotton fiber is carried out without PVA starching, and mixing cirtern technique determines viscosity after base into midge in slurries
9S, stock tank viscosity 8%, solid content 12.1%, the rate of sizing 14%, for slurry product 900L, slurry dry weight 109.525kg, hundred meters with slurry
2.34kg), the air in yarn is extruded using mud jacking rod, squeezes out extra slurries, and fraction slurries are pressed into yarn interior,
Then secondary soaking paste mud jacking (wrapping up fiber sufficiently by slurries) hygroscopic water layer, after then waxing enters dry leasing area after cylinder
According to technique row reed completion beam of a loom (sizing speed 80m/min, elongation 1%, regain 9.5%, stock tank viscosity 8-9%, slurries temperature
90-93 DEG C of degree, stock tank coverage coefficient A33% B33%, A130 DEG C B130 DEG C of cylinder temperature, tension (10N): unwinding tension 88 is fed
Enter tension -0.2, -0.2, drying chamber 0.3 0, leasing 0.9 1, winding 210, the throwing of weft 0.25)；
Weaving: because reflective fiber moulding is strong, surface is smooth, together with cotton fiber when warping, because of speed height, reflective fiber unwinding speed
Degree is fast, so that reflective fiber distorts on beam of a loom, so that reflecting effect reduces, and it is special individually to be made of wheel in one's ear to change this problem
Small axis, is directly mounted on loom, smooth in guarantee reflective fiber manufacturing process, non-warping.When reflective fiber does weft yarn, because
It is sheet silk for reflective fiber, so that jet air disperses, yarn is not easily controlled, and wefting insertion effect is poor, and jet loom for drawing weft yarn is tired
Difficulty, spy are weaved using rapier loom, and sword head is into the shed open time: sword belt being placed in sword belt wheel, the fastening spiral shell of belt wheel and axis is unclamped
Silk, loom main shaft go to 64 °, and rotation belt wheel makes that sword head is sent to enter at the iron bar of reed side, fastening screw.Equally, weft-recepting sword head exists
At 63 °, reach at first dent of reed.Back-bearer height is 70mm, and warp stop frame height is 25mm.It is added when with warping again
Reflective fiber is compared, and because reflective fiber is different from the tension of cotton fiber in weaving process, can preferably be adjusted using wheel in one's ear
Save tension.
Embodiment 2
Warp Tension Test 167:1 selects the reed of 88#/2 ", and ground enters number 4 and enters, yarn more than total quantity of warps 19284+3 root；
Fabric yarn is blended by reflective fiber and cotton fiber, and fabric tissue is two lattice, and reflective fiber accounts in fabric
5%wt wt, cotton fiber accounts for 95% wt in fabric；Reflective fiber chooses moulding, the good material of reflecting effect.Reflective fiber is poly-
The plastics wire material of two rouge of ethylene；100% long-staple cotton of long wool cotton content is selected in the selection of cotton fiber；
Warping: cotton fiber takes batch warping, warping speed 600m/min；630 bobbins of warping head point, yarn gripper opening time
5s, tension rail opening time 4s, reed blow-time 30s, reed blowing-out time 2s, break end 6 ~ 8s of action time, and tension in Warping 12 ~
14g；
Sizing: dual-box slasher is used, yarn is by creel (creel unwinding tension control is in 5N/ axis) by drawing yarn
Rod makes cotton fiber enter a stock tank, and into midge in slurries, (cotton fiber is carried out without PVA starching, and mixing cirtern technique is glued after determining base
Spend 9S, stock tank viscosity 8%, solid content 12.1%, the rate of sizing 14%, for slurry product 900L, slurry dry weight 109.525kg, hundred meters with slurry
2.34kg), the air in yarn is extruded using mud jacking rod, squeezes out extra slurries, and fraction slurries are pressed into yarn interior,
Then secondary soaking paste mud jacking (wrapping up fiber sufficiently by slurries) hygroscopic water layer, after then waxing enters dry leasing area after cylinder
According to technique row reed completion beam of a loom (sizing speed 80m/min, elongation 1%, regain 9.5%, stock tank viscosity 8-9%, slurries temperature
90-93 DEG C of degree, stock tank coverage coefficient A33% B33%, A130 DEG C B130 DEG C of cylinder temperature, tension (10N): unwinding tension 88 is fed
Enter tension -0.2, -0.2, drying chamber 0.3 0, leasing 0.9 1, winding 210, the throwing of weft 0.25)；
Weaving: because reflective fiber moulding is strong, surface is smooth, together with cotton fiber when warping, because of speed height, reflective fiber unwinding speed
Degree is fast, so that reflective fiber distorts on beam of a loom, so that reflecting effect reduces, and it is special individually to be made of wheel in one's ear to change this problem
Small axis, is directly mounted on loom, smooth in guarantee reflective fiber manufacturing process, non-warping.When reflective fiber does weft yarn, because
It is sheet silk for reflective fiber, so that jet air disperses, yarn is not easily controlled, and wefting insertion effect is poor, and jet loom for drawing weft yarn is tired
Difficulty, spy are weaved using rapier loom, and sword head is into the shed open time: sword belt being placed in sword belt wheel, the fastening spiral shell of belt wheel and axis is unclamped
Silk, loom main shaft go to 63 °, and rotation belt wheel makes that sword head is sent to enter at the iron bar of reed side, fastening screw.Equally, weft-recepting sword head exists
At 62 °, reach at first dent of reed.Back-bearer height is 70mm, and warp stop frame height is 25mm.It is added when with warping again
Reflective fiber is compared, and because reflective fiber is different from the tension of cotton fiber in weaving process, can preferably be adjusted using wheel in one's ear
Save tension.
Embodiment 3
Warp Tension Test 167:1 selects the reed of 88#/2 ", and ground enters number 4 and enters, yarn more than total quantity of warps 19284+3 root；
Fabric yarn is blended by reflective fiber and cotton fiber, and fabric tissue is two lattice, and reflective fiber accounts in fabric
15% wt, cotton fiber accounts for 85% wt in fabric；Reflective fiber chooses moulding, the good material of reflecting effect.Reflective fiber is poly-
The plastics wire material of two rouge of ethylene；100% long-staple cotton of long wool cotton content is selected in the selection of cotton fiber；
Warping: cotton fiber takes batch warping, warping speed 600m/min；720 bobbins of warping head point, yarn gripper opening time
5s, tension rail opening time 4s, reed blow-time 30s, reed blowing-out time 2s, break end 6 ~ 8s of action time, and tension in Warping 12 ~
14g；
Sizing: dual-box slasher is used, yarn is by creel (creel unwinding tension control is in 5N/ axis) by drawing yarn
Rod makes cotton fiber enter a stock tank, and into midge in slurries, (cotton fiber is carried out without PVA starching, and mixing cirtern technique is glued after determining base
Spend 9S, stock tank viscosity 8%, solid content 12.1%, the rate of sizing 14%, for slurry product 900L, slurry dry weight 109.525kg, hundred meters with slurry
2.34kg), the air in yarn is extruded using mud jacking rod, squeezes out extra slurries, and fraction slurries are pressed into yarn interior,
Then secondary soaking paste mud jacking (wrapping up fiber sufficiently by slurries) hygroscopic water layer, after then waxing enters dry leasing area after cylinder
According to technique row reed completion beam of a loom (sizing speed 80m/min, elongation 1%, regain 9.5%, stock tank viscosity 8-9%, slurries temperature
90-93 DEG C of degree, stock tank coverage coefficient A33% B33%, A130 DEG C B130 DEG C of cylinder temperature, tension (10N): unwinding tension 88 is fed
Enter tension -0.2, -0.2, drying chamber 0.3 0, leasing 0.9 1, winding 210, the throwing of weft 0.25)；
Weaving: because reflective fiber moulding is strong, surface is smooth, together with cotton fiber when warping, because of speed height, reflective fiber unwinding speed
Degree is fast, so that reflective fiber distorts on beam of a loom, so that reflecting effect reduces, and it is special individually to be made of wheel in one's ear to change this problem
Small axis, is directly mounted on loom, smooth in guarantee reflective fiber manufacturing process, non-warping.When reflective fiber does weft yarn, because
It is sheet silk for reflective fiber, so that jet air disperses, yarn is not easily controlled, and wefting insertion effect is poor, and jet loom for drawing weft yarn is tired
Difficulty, spy are weaved using rapier loom, and sword head is into the shed open time: sword belt being placed in sword belt wheel, the fastening spiral shell of belt wheel and axis is unclamped
Silk, loom main shaft go to 65 °, and rotation belt wheel makes that sword head is sent to enter at the iron bar of reed side, fastening screw.Equally, weft-recepting sword head exists
At 64 °, reach at first dent of reed.Back-bearer height is 70mm, and warp stop frame height is 25mm.It is added when with warping again
Reflective fiber is compared, and because reflective fiber is different from the tension of cotton fiber in weaving process, can preferably be adjusted using wheel in one's ear
Save tension.
Comparative example 1
Preparation process is with embodiment 1, the difference is that reflective fiber accounts for 1% wt, cotton fiber accounts for 99% wt in fabric.Obtained face
Material does not have enough reflecting effects.
Comparative example 2
Preparation process is with embodiment 1, the difference is that reflective fiber accounts for 20% wt, cotton fiber accounts for 20% wt in fabric.It is obtained
Fabric elasticity is poor, and it is poor to take adaptive.
Comparative example 3
Preparation process is with embodiment 1, the difference is that reflective fiber is set up directly on weft yarn cylinder；Rapier loom main shaft goes to 70 °,
Weft-recepting sword head reaches at first dent of reed at 69 °.Reflective fiber distorts on beam of a loom, and wefting insertion effect is poor, can not carry out
Normal weaving.
The above described is only a preferred embodiment of the present invention, being not that the invention has other forms of limitations, appoint
What those skilled in the art changed or be modified as possibly also with the technology contents of the disclosure above equivalent variations etc.
Imitate embodiment.But without departing from the technical solutions of the present invention, according to the technical essence of the invention to above embodiments institute
Any simple modification, equivalent variations and the remodeling made, still fall within the protection scope of technical solution of the present invention.
Claims (9)
1. a kind of reflective cotton fiber fabric, it is characterised in that: fabric yarn is blended by reflective fiber and cotton fiber, and fabric is knitted
Object tissue is two lattice, and reflective fiber accounts for the wt of 5%wt ~ 15% in fabric, and cotton fiber accounts for the wt of 85% wt ~ 95% in fabric；It is described
Reflective fiber is the plastics wire material of poly- two rouge of ethylene.
2. a kind of reflective cotton fiber fabric according to claim 1, it is characterised in that: the cotton fiber is long-staple cotton.
3. a kind of reflective cotton fiber fabric according to claim 1, it is characterised in that: reflective fiber accounts in the fabric
The wt of 5%wt ~ 10%, cotton fiber accounts for the wt of 90% wt ~ 95% in fabric.
4. a kind of reflective cotton fiber fabric according to claim 1, it is characterised in that: reflective fiber accounts in the fabric
The wt of 10%wt ~ 15%, cotton fiber accounts for the wt of 85% wt ~ 90% in fabric.
5. a kind of preparation method of the described in any item reflective cotton fiber fabrics of claim 1 ~ 4, which is characterized in that including following
Weaving step:
1) warping: cotton fiber takes batch warping；
2) sizing: cotton fiber midge, mud jacking after waxing, into dry leasing area after complete beam of a loom；
3) it weaves: using reflective fiber in weft yarn in proportion, reflective fiber individually does small axis with wheel in one's ear, is directly mounted at loom
On；Weaved using rapier loom, sword head is into the shed open time: loom main shaft angle is 63 ° ~ 65 °, and sword head is sent to be arranged in reed side iron
At item, adjustment weft-recepting sword head is reached at 62 ° ~ 64 ° at first dent of reed.
6. a kind of preparation method of reflective cotton fiber fabric according to claim 5, it is characterised in that: described in step 1)
The warping speed 600m/min of warping, 630 ~ 720 bobbins of warping head point, 12 ~ 14g of tension in Warping.
7. a kind of preparation method of reflective cotton fiber fabric according to claim 5, it is characterised in that: described in step 2
Sizing uses dual-box slasher.
8. a kind of preparation method of reflective cotton fiber fabric according to claim 5, it is characterised in that: described in step 2
Stock tank viscosity 8% in cotton fiber midge, the rate of sizing 14%, hundred meters with slurry 2.34kg.
9. a kind of preparation method of reflective cotton fiber fabric according to claim 5, it is characterised in that: loom in step 3)
Main shaft angle is 64 °.