CN109554934A - Anti- preparation method, coating process and trademark belt for cutting trademark belt coating sizing material - Google Patents
Anti- preparation method, coating process and trademark belt for cutting trademark belt coating sizing material Download PDFInfo
- Publication number
- CN109554934A CN109554934A CN201811484645.1A CN201811484645A CN109554934A CN 109554934 A CN109554934 A CN 109554934A CN 201811484645 A CN201811484645 A CN 201811484645A CN 109554934 A CN109554934 A CN 109554934A
- Authority
- CN
- China
- Prior art keywords
- coating
- trademark belt
- sizing material
- preparation
- nylon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of anti-preparation method, coating process and trademark belts for cutting trademark belt coating sizing material, belong to trademark belt and preparation method thereof technical field.During preparing trademark belt coating sizing material, using nylon material as carrier, and alcohol-soluble synthetic oil is added as auxiliary agent in it, and the mass ratio of the nylon material and the alcohol-soluble synthetic oil is 7:(0.7 ~ 1.3).Coating sizing material is for the coating on trademark belt, so that trademark belt has good cutting performance, cuts test non-stick knife and printing test clear writing.
Description
Technical field
The invention belongs to trademark belt and preparation method thereof technical fields, and in particular to a kind of anti-cutting trademark belt coating sizing material
Preparation method, coating process and the trademark belt.
Background technique
With the development of society, people increasingly focus on the brand message of commodity, trademark belt is as textile product information
Printable fabric, there are its distinctive market values.
Coating trademark belt is to carry out adhesive tape made of high molecular polymer and the dip-coating of filler composition wet process to fabric blank
Class trademark belt comprising the pulp layer that intermediate base cloth layer and upper and lower surface high molecular polymer and filler composition are constituted, because of table
Face is flat and smooth, it is soft it is fine and smooth, richness is good, printing adaptability is strong, occupies in whole brand very big
The market share.
Such as application No. is 201310561192.9 Chinese invention patents to disclose a kind of wet-process coating fire-retardant nylon trade mark
Band and preparation method thereof includes the sizing material that halogen-free flame retardants, nylon resin and antistatic agent are formed in flame-retardant layer, using painting
The mode covered carries out coating.
Coating trademark belt manufacture craft is determined that the coating cloth of whole picture, which is most had in the end, cuts into several small dimension ribbons, is applied
Layer trademark belt is other than for cutting printing, greatly for cutting out a printing, in the slitting process, due to the suction of compound layer
Moist effect, it is easy to appear sticking phenomenon in cutting process, influence production efficiency, thus develop it is a can anti-cutting coating
Trademark belt solves to glue knife when its coating fabrics is cut, and causes to cut that trademark belt specification is irregular or even scrap of the product is asked
Topic.
Summary of the invention
In view of the above-mentioned problems, the present invention provide a kind of anti-preparation method for cutting trademark belt coating sizing material, coating process and
The trademark belt, so that trademark belt has good cutting performance, cuts test and does not glue for the preparation of trademark belt ATTACH LABEL coating
Knife and printing test clear writing.
Technical proposal that the invention solves the above-mentioned problems is as follows:
The anti-preparation method for cutting trademark belt coating sizing material, comprising having the following steps:
1. calcium chloride dissolves: methanol and calcium chloride being added in a kettle, stirring is warming up to 60 ~ 70 DEG C, the alcohol is then added
Dissolubility synthetic oil simultaneously continues to stir, until the calcium chloride is completely dissolved；
2. nylon dissolves: nylon material is added into the step liquid phase that 1. middle calcium chloride is completely dissolved, is stirred continuously until nylon
Material is completely dissolved；
3. adding fluorescent whitening agent: by step 2. described in the liquid phase that is completely dissolved of nylon material be warming up to 65 ~ 75 DEG C, be added glimmering
Optical brightener stirs 5 ~ 15 minutes；
4. adding filler: it is 2. added to step and adds pearl filler in the liquid phase of fluorescent whitening agent, stirred 1.5 ~ 2.5 hours,
It takes the dish out of the pot after the completion of stirring, the viscosity of material is about in 400 ~ 500CPS at this time；
5. cooling is stand-by: by step 4. in the liquid phase that takes the dish out of the pot be cooled to 30 ~ 40 DEG C, viscosity rises to 2000 ~ 3000CPS at this time,
It can come into operation.
As a preferred embodiment of the above technical solution, step 1. described in the mass ratio of methanol and nylon material be (45 ~ 55): 7,
The calcium chloride is (14 ~ 24) with the mass ratio with nylon material: 7.
As a preferred embodiment of the above technical solution, step 1. described in alcohol-soluble synthetic oil be polyol ester, polyethers, phosphoric acid
One of ester, dibasic acid esters.
As a preferred embodiment of the above technical solution, step 3. described in the mass ratio of fluorescent whitening agent and the nylon material be
(0.003 ~ 0.009): 1.
As a preferred embodiment of the above technical solution, step 4. described in calcium carbonate and the nylon material mass ratio be (12 ~
18): 7.
As a preferred embodiment of the above technical solution, the mass ratio of the nylon material and the alcohol-soluble synthetic oil is 7:(0.7
~ 1.3).
Trademark belt, using coating sizing material described in any bar in above-mentioned technical proposal as coating.Coating process is adopted
Coating sizing material, includes the following steps: described in any bar in above-mentioned technical proposal
1. stereotyped fabric forms coating by slurry tank hanging；
2. keeping coating surface uniform and smooth using scraper；
3. the fabric of coating enters coagulating bath conjunctiva；
4. washing with water remained on surface chemical substance；
5. into oven-baked.
As a preferred embodiment of the above technical solution, the setting of coating speed is in 20 ~ 26m/min, fabric tension control 25N ~
35N, blade thickness 1.5mm, oven temperature be 150 DEG C ~ 170 DEG C, coating output thickness 0.1mm ~ 0.12mm, grammes per square metre 55g ~
65g。
The performance and quality stability of coating are mainly influenced by following aspects:
The adjustment of tension: will adjust different tensions according to different cloth when coating, tension unevenly will result in coating not
Uniformly, some places thickness some places are thin, and feel also can be uneven, and the hard some places of some places are soft, and then lead to quotient
Marker tape product quality is not sufficiently stable.
The adjustment of scraper: will adjust the parameter of scraper according to different coating needs when coating, first is that the thickness of knife, according to
The coating that difference requires will select the knife of different-thickness, select mistake knife that cannot also guarantee the quality of coating, best painting is not achieved
Layer effect.
The cleaning of fabric surface: the cleaning of cloth cover when reality is exactly coating, if because wired in coat side in coating
Head or tiny sand, these tiny things will be stuck in the painting edge of a knife, and will result in coat side has strip generation, cause secondary
Product.So generally to be cleared up cloth cover applying before knife.General solution is to load onto hairbrush before painting knife, will
The end of a thread and tiny sand brush tune on cloth cover, while a little water are sprinkled on the ground, air humidity is kept, makes the dust of ground will not
It flies up and, and reduce the absorption of electrostatic.If being seized in the edge of a knife and generating strip, that operative employee will be with most fast speed handle
It is wiped off.
The temperature of baking oven controls: the coating that difference requires, solidification temperature is also different.So to control coating
Temperature.Temperature is too high, will cause Boardy Feeling, is easy blistering.Temperature is too low, will cause tacky, and fastness is poor, is easy to fall off.
The control of coating speed: as temperature above, the temperature and speed of coating want strict control, it will be straight
Connect the quality for influencing coating.Because the solidification of coating adhesive is depended on and two conditions, temperature and time.Although temperature is controlled
, if the time is not controlled, still will affect coating quality.Because two conditions are indispensable.So controlling
Also speed is controlled while temperature processed.Speed is too fast, and the cured time is inadequate, that still cannot be fully cured, and can also make
At tacky and fall off.Speed is too slow, too long in the time of drying chamber, and will cause and feel hard, embrittlement.Moreover, production efficiency is low,
Waste of energy.
Therefore, when practical operation, the temperature and coating speed of baking oven are set first, in accordance with above-mentioned technical proposal, and will
For the tension force of fabric between 25N ~ 35N, the thickness of scraper is set as 1.5mm, and stereotyped fabric first passes around slurry tank
Hanging is carried out, then the surface of coating is made to become uniform and smooth after scraper striking, enters back into coagulating bath conjunctiva, used after conjunctiva
Clear water washes away the remaining chemical substance of coating surface, subsequently into the baking oven that temperature has been previously set, after drying, and the thickness of coating
About 0.1 ~ 0.12mm, grammes per square metre is between 55 ~ 65g.
Wherein, coagulating bath be manufacture chemical fibre when, make spinning colloidal solution by spinning head thread solidification or simultaneously
It plays chemical change and forms the bath foam of fiber, also known as weaving bath；
The lubricity of the coating is good, so that knife not easy to stick when cutting, i.e., anti-cutting performance enhancement, meanwhile, printing writing maintains
Original clarity.
In conclusion the invention has the following advantages:
The application provides a kind of anti-preparation method, coating process and trademark belt for cutting trademark belt coating sizing material, using the painting
The trademark belt of layer sizing preparation cuts test non-stick knife, printing test clear writing, i.e. the addition of alcohol-soluble synthetic oil increases table
The lubricity of finishing coat plays the effect of anti-cutting, while the addition of alcohol-soluble synthetic oil does not influence product printing effect.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Embodiment in the present invention, ordinary skill
Personnel's all other embodiment obtained under the premise of not doing creative work, shall fall within the protection scope of the present invention.
The following describes the present invention in detail with reference to examples.
1 ~ embodiment of embodiment 5 is preparation method, coating process and the manufactured trademark belt of coating sizing material, wherein is prepared
The parameter of method is shown in Tables 1 and 2 respectively:
The formulation parameter of coating sizing material described in 11 ~ embodiment of embodiment 5 of table
| Embodiment number | Nylon mass fraction | Alcohol-soluble synthetic oil type | Alcohol-soluble synthetic oil | Methanol quality score | Calcium chloride mass fraction | Fluorescent whitening agent mass fraction | Calcium carbonate mass fraction |
| 1 | 7 | Polyol ester | 1 | 55 | 24 | 0.006 | 15 |
| 2 | 7 | Dibasic acid esters | 1.3 | 45 | 19 | 0.006 | 12 |
| 3 | 7 | Polyethers | 1 | 50 | 19 | 0.003 | 15 |
| 4 | 7 | Dibasic acid esters | 1 | 50 | 19 | 0.006 | 15 |
| 5 | 7 | Phosphate | 0.7 | 50 | 14 | 0.009 | 18 |
The preparing process parameter of coating sizing material described in 21 ~ embodiment of embodiment 5 of table
| Embodiment number | Step 1. warming temperature/DEG C | Step 3. warming temperature/DEG C | Step 3. mixing time/mins | Step 4. mixing time/h | Step 5. cooling temperature/DEG C |
| 1 | 70 | 75 | 15 | 2.5 | 30 |
| 2 | 60 | 65 | 5 | 2 | 30 |
| 3 | 65 | 70 | 5 | 1.5 | 40 |
| 4 | 65 | 70 | 10 | 2 | 35 |
| 5 | 65 | 70 | 10 | 2 | 40 |
Fabric used by 1 ~ embodiment of embodiment 5 is tatting plain cloth, and warp thread is pure polyamide fibre, thickness of yarn 30D, density
For 42 ~ 44/cm, weft yarn is that brocade washs composite filament, thickness of yarn 70D, polyamide fibre packet terylene, and polyamide fibre ingredient is 30% ~ 40%, density
For 21 ~ 23/cm.
Fabric pre-treating technology are as follows: the fabric weaved is processed into the big volume of 3000 ~ 5000m by clot, fixed by washing
The processing of type machine, washing forming machine are divided into two parts, and first part is two water baths, and 30% liquid alkaline is added in first water bath,
Alkali concentration is set to reach 5 ~ 10g/L, second water bath is added clear water and cleans cloth cover residuals；Second part is that 6 baking ovens are used
Make setting process, fabric enters baking oven after front twice water bath is water washed and is formed.150 DEG C ~ 180 DEG C of setting temperature, vehicle
60 ~ 80m/min of speed.
Coating process are as follows: stereotyped fabric is formed into coating by slurry tank hanging, speed is arranged in 20 ~ 26m/min,
Fabric tension is controlled in 25N ~ 35N, keeps coating surface uniform and smooth using the scraper with a thickness of 1.5mm, by knitting for coating
Object enters coagulating bath conjunctiva, washes with water remained on surface chemical substance, and the oven-baked for being 150 DEG C ~ 170 DEG C into temperature is dry
?.
The band coating output of trade mark obtained by 1 ~ embodiment of embodiment 5 with a thickness of 0.1mm ~ 0.12mm, grammes per square metre 55g ~
Between 65g, test non-stick knife and printing test clear writing are cut.
Claims (9)
1. the anti-preparation method for cutting trademark belt coating sizing material, which is characterized in that comprising having the following steps:
1. calcium chloride dissolves: methanol and calcium chloride being added in a kettle, stirring is warming up to 60 ~ 70 DEG C, alcohol-soluble is then added
Synthetic oil simultaneously continues to stir, until the calcium chloride is completely dissolved；
2. nylon dissolves: to step 1. described in nylon material is added in the liquid phase that is completely dissolved of calcium chloride, be stirred continuously until
Nylon material is completely dissolved；
3. adding fluorescent whitening agent: by step 2. described in the liquid phase that is completely dissolved of nylon material be warming up to 65 ~ 75 DEG C, be added glimmering
Optical brightener stirs 5 ~ 15 minutes；
4. adding filler: it is 2. added to step and adds pearl filler in the liquid phase of fluorescent whitening agent, stirred 1.5 ~ 2.5 hours,
It takes the dish out of the pot after the completion of stirring；
5. cooling is stand-by: by step 4. in the liquid phase that takes the dish out of the pot be cooled to 30 ~ 40 DEG C, can come into operation.
2. it is according to claim 1 it is anti-cut trademark belt coating sizing material preparation method, it is characterised in that: step 1. in institute
The mass ratio for stating methanol and nylon material is (45 ~ 55): 7, the calcium chloride is (14 ~ 24) with the mass ratio with nylon material:
7。
3. it is according to claim 1 it is anti-cut trademark belt coating sizing material preparation method, it is characterised in that: step 1. in institute
Stating alcohol-soluble synthetic oil is one of polyol ester, polyethers, phosphate, dibasic acid esters.
4. it is according to claim 1 it is anti-cut trademark belt coating sizing material preparation method, it is characterised in that: step 3. in institute
The mass ratio for stating fluorescent whitening agent and the nylon material is (0.003 ~ 0.009): 1.
5. it is according to claim 1 it is anti-cut trademark belt coating sizing material preparation method, it is characterised in that: step 4. in institute
The mass ratio for stating calcium carbonate and the nylon material is (12 ~ 18): 7.
6. the anti-preparation method for cutting trademark belt coating sizing material according to claim 1, it is characterised in that: the nylon material
The mass ratio of material and the alcohol-soluble synthetic oil is 7:(0.7 ~ 1.3).
7. trademark belt, it is characterised in that: using coating sizing material described in any bar in claim 1 ~ 6 as coating.
8. coating process, using coating sizing material described in any bar in claim 1 ~ 6, which comprises the steps of:
1. stereotyped fabric forms coating by slurry tank hanging；
2. keeping coating surface uniform and smooth using scraper；
3. the fabric of coating enters coagulating bath conjunctiva；
4. washing with water remained on surface chemical substance；
5. into oven-baked.
9. coating process according to claim 8, it is characterised in that: the setting of coating speed is in 20 ~ 26m/min, fabric
Power control is 150 DEG C ~ 170 DEG C in 25N ~ 35N, blade thickness 1.5mm, oven temperature.