CN109181078A - A kind of straw fiber board - Google Patents
A kind of straw fiber board Download PDFInfo
- Publication number
- CN109181078A CN109181078A CN201811119678.6A CN201811119678A CN109181078A CN 109181078 A CN109181078 A CN 109181078A CN 201811119678 A CN201811119678 A CN 201811119678A CN 109181078 A CN109181078 A CN 109181078A
- Authority
- CN
- China
- Prior art keywords
- parts
- straw
- powder
- calcium
- fiber board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of straw fiber boards, including following parts by weight of component: 50-60 parts of polyvinyl resin powder, 30-35 parts of polyvinyl chloride resin powder, 20-22 parts of straw powder, 5-10 parts of calcium powder, ACR are 7-11 parts, 4-6 parts of calcium-zinc composite stabilizing agent, 0.5-0.6 parts of polyethylene wax, 1-1.5 parts of stearic acid, 2-3 parts of paraffin, 5-7 parts of magnesia, 3-5 parts of magnesium chloride, 16-20 parts of Lauxite.The present invention is more preferably mutually merged by being modified to enable with resin and plastic using straw refuse as raw material, makes full use of stalk, and reach the intensity of existing bamboo and woods fiber plate;It realizes that the high efficiente callback for having straw powder utilizes, solves contamination hazard of the existing processing mode of agricultural crop straw to environment.
Description
Technical field
The present invention relates to integrated wall plate technical field more particularly to a kind of straw fiber boards.
Background technique
Fiberboard, which refers to be interweaved lignocellulose fiber, to be formed and utilizes wood-based plate made of its intrinsic glueability.It is fine
Dimension plate has many advantages, such as that uniform in material, intensity difference is not small, easy to crack in length and breadth, widely used.
Existing fiberboard is all made of bamboo fibre and wood-fibred is made, and the material utilized is that timber and bamboo wood produce
Raw, with social development, the supply of the great attention of Environmental, timber and bamboo wood is persistently reduced, so that fiberboard
Cost cannot reduce.
China is large agricultural country, there is a large amount of crop straw refuse every year, due to the recycling effect to stalk
Rate is low, causes a large amount of stalk that cannot be recycled, and is simply incinerated, and crop straw burning refers to agricultural crop straw fire
Burn a kind of behavior to destroy;Crop straw burning causes haze weather, and generates a large amount of poisonous and harmful substances, to people and other lifes
Object health, which is formed, to threaten;And crop straw burning, the combustibles for surrounding of easily igniting often are difficult to control once causing wheatland high fire
System, causes economic loss.Especially near mountain forest, consequence is even more hardly imaginable;Crop straw burning also destroys soil texture, causes
Farm land quality decline, crop straw burning also enter three points of ground, and the microorganism in earth's surface is scorched to death, and humus, organic matter are mineralized, field
Crop straw burning destroys the balance of this set biosystem, changes the physical behavior of soil, has aggravated soil hardening, destroys ground
Power, exacerbates arid, and the growth of crops is thus affected.Forbid burning crops for this purpose, the Chinese government all orders
Burning processing, promotion are recycled agricultural crop straw.
Summary of the invention
Present invention aim to address above-mentioned deficiencies, provide a kind of straw fiber board.
A kind of straw fiber board provided by the invention, it is characterised in that including following parts by weight of component: polyvinyl resin powder
50-60 parts, 30-35 parts of polyvinyl chloride resin powder, 20-22 parts of straw powder, 5-10 parts of calcium powder, ACR be 7-11 parts, Ca Zn composite it is steady
Determine 4-6 parts of agent, 0.5-0.6 parts of polyethylene wax, 1-1.5 parts of stearic acid, 2-3 parts of paraffin, 5-7 parts of magnesia, 3-5 parts of magnesium chloride,
16-20 parts of Lauxite.
Further, a kind of production method of straw fiber board, as follows:
Step 1, the stalk of recycling will be crushed by stalk crasher, the fragment size of crushing is 1-3mm;
Step 2, straw powder is cleaned 4-5 times with clear water;Then straw powder is put into 30%NaOH aqueous solution and is impregnated 20 minutes,
Soaking solution temperature is 90-95 °C;Then straw powder is filtered and is dried;
Step 3, dry straw powder and polyvinyl resin powder, polyvinyl chloride resin powder, straw powder, calcium powder, ACR, calcium zinc are answered
Close stabilizer, polyethylene wax, stearic acid, paraffin, magnesia, magnesium chloride, Lauxite are mixed according to the ratio, when mixing, uses
50-60 rpms stirs at low speed 10 minutes, and mixed slurry is made;
Step 4, mixed slurry is added in high temperature and pressure generator, imports extrusion equipment and carries out extrusion forming;The plate of formation
Cooling and shaping is carried out by the distilled water of low temperature;Sizing plate smooth standing 4-5 days;Straw fiber board is made.
A kind of straw fiber board provided by the invention, using straw refuse as raw material, and by modified so that with tree
Rouge plastics more preferably can be merged mutually, make full use of stalk, and reach the intensity of existing bamboo and woods fiber plate;Realization has straw powder
High efficiente callback utilizes, and solves contamination hazard of the existing processing mode of agricultural crop straw to environment.
Specific embodiment
Below by embodiment to further instruction of the present invention, the embodiment of the present invention is with technical solution of the present invention
Premised under implemented, the detailed implementation method and specific operation process are given, but protection scope of the present invention is unlimited
In following embodiments:
Embodiment 1:
Step 1, the stalk of recycling will be crushed by stalk crasher, the fragment size of crushing is 1-3mm;
Step 2, straw powder is cleaned 4-5 times with clear water;Then straw powder is put into 30%NaOH aqueous solution and is impregnated 20 minutes,
Soaking solution temperature is 90-95 °C;Then straw powder is filtered and is dried;
Step 3, by 20 parts dry of straw powder and 50 parts of polyvinyl resin powder, 30 parts of polyvinyl chloride resin powder, 5 parts of calcium powder, ACR
For 7 parts, 6 parts of calcium-zinc composite stabilizing agent, 0.6 part of polyethylene wax, 1.5 parts of stearic acid, 3 parts of paraffin, 7 parts of magnesia, magnesium chloride 5
Part, 20 parts of Lauxite mixed, stirred at low speed 10 minutes using 50 rpms when mixing, mixed slurry be made;
Step 4, mixed slurry is added in high temperature and pressure generator, imports extrusion equipment and carries out extrusion forming;The plate of formation
Cooling and shaping is carried out by the distilled water of low temperature;Plate of being formed is smooth to stand 4 days;Straw fiber board is made.
To straw fiber board test result obtained are as follows: compression strength 41.3Mpa, surface abrasion resistance revolution are 8200 turns.
Embodiment 2:
Step 1, the stalk of recycling will be crushed by stalk crasher, the fragment size of crushing is 1-3mm;
Step 2, straw powder is cleaned 4-5 times with clear water;Then straw powder is put into 30%NaOH aqueous solution and is impregnated 20 minutes,
Soaking solution temperature is 90-95 °C;Then straw powder is filtered and is dried;
Step 3, by 60 parts of 22 parts of dry straw powder and polyvinyl resin powder, 35 parts of polyvinyl chloride resin powder, 10 parts of calcium powder,
ACR11 parts, 6 parts of calcium-zinc composite stabilizing agent, 0.6 part of polyethylene wax, 1.5 parts of stearic acid, 2 parts of paraffin, 5 parts of magnesia, magnesium chloride 3
Part, 16 parts of Lauxite mixed, stirred at low speed 10 minutes using 50 rpms when mixing, mixed slurry be made;
Step 4, mixed slurry is added in high temperature and pressure generator, imports extrusion equipment and carries out extrusion forming;The plate of formation
Cooling and shaping is carried out by the distilled water of low temperature;Plate of being formed is smooth to stand 4 days;Straw fiber board is made.
To straw fiber board test result obtained are as follows: compression strength 39.6Mpa, surface abrasion resistance revolution are 8500 turns.
Embodiment 3:
Step 1, the stalk of recycling will be crushed by stalk crasher, the fragment size of crushing is 1-3mm;
Step 2, straw powder is cleaned 4-5 times with clear water;Then straw powder is put into 30%NaOH aqueous solution and is impregnated 20 minutes,
Soaking solution temperature is 90-95 °C;Then straw powder is filtered and is dried;
Step 3, by 22 parts dry of straw powder and 50 parts of polyvinyl resin powder, 30 parts of polyvinyl chloride resin powder, 5 parts of calcium powder, ACR
For 7 parts, 4 parts of calcium-zinc composite stabilizing agent, 0.5 part of polyethylene wax, 1 part of stearic acid, 2 parts of paraffin, 7 parts of magnesia, 5 parts of magnesium chloride,
20 parts of Lauxite are mixed, and are stirred at low speed 10 minutes when mixing using 60 rpms, and mixed slurry is made;
Step 4, mixed slurry is added in high temperature and pressure generator, imports extrusion equipment and carries out extrusion forming;The plate of formation
Cooling and shaping is carried out by the distilled water of low temperature;Plate of being formed is smooth to stand 4 days;Straw fiber board is made.
To straw fiber board test result obtained are as follows: compression strength 40.8Mpa, surface abrasion resistance revolution are 7800 turns.
Claims (2)
1. a kind of straw fiber board, it is characterised in that including following parts by weight of component: 50-60 parts of polyvinyl resin powder, polychlorostyrene second
30-35 parts of olefine resin powder, 20-22 parts of straw powder, 5-10 parts of calcium powder, ACR are 7-11 parts, 4-6 parts of calcium-zinc composite stabilizing agent, poly- second
0.5-0.6 parts of alkene wax, 1-1.5 parts of stearic acid, 2-3 parts of paraffin, 5-7 parts of magnesia, 3-5 parts of magnesium chloride, Lauxite 16-20
Part.
2. a kind of production method of straw fiber board as described in claim 1, it is characterised in that as follows: step 1, will
The stalk of recycling is crushed by stalk crasher, the fragment size of crushing is 1-3mm;
Step 2, straw powder is cleaned 4-5 times with clear water;Then straw powder is put into 30%NaOH aqueous solution and is impregnated 20 minutes,
Soaking solution temperature is 90-95 °C;Then straw powder is filtered and is dried;
Step 3, dry straw powder and polyvinyl resin powder, polyvinyl chloride resin powder, straw powder, calcium powder, ACR, calcium zinc are answered
Close stabilizer, polyethylene wax, stearic acid, paraffin, magnesia, magnesium chloride, Lauxite are mixed according to the ratio, when mixing, uses
50-60 rpms stirs at low speed 10 minutes, and mixed slurry is made;
Step 4, mixed slurry is added in high temperature and pressure generator, imports extrusion equipment and carries out extrusion forming;The plate of formation
Cooling and shaping is carried out by the distilled water of low temperature;Sizing plate smooth standing 4-5 days;Straw fiber board is made.