CN109158365A - A kind of glass cover-plate takes off ink and takes off electroplating method - Google Patents
A kind of glass cover-plate takes off ink and takes off electroplating method Download PDFInfo
- Publication number
- CN109158365A CN109158365A CN201810699400.4A CN201810699400A CN109158365A CN 109158365 A CN109158365 A CN 109158365A CN 201810699400 A CN201810699400 A CN 201810699400A CN 109158365 A CN109158365 A CN 109158365A
- Authority
- CN
- China
- Prior art keywords
- takes
- plate
- glass cover
- ink
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Ink is taken off the present invention provides a kind of glass cover-plate and takes off electroplating method, comprising the following steps: the first step just takes off ink, and HRS-M200 is taken off black liquid stoste and is heated to 70-80 DEG C, and glass cover-plate is put into above-mentioned take off in black liquid and is cleaned；Second step, rinsing, rinses above-mentioned glass cover-plate using deionized water；Third step takes off plating, will clean in decoating liquid that above-mentioned glass cover-plate is put under normal temperature state；4th step, rinsing, rinses above-mentioned glass cover-plate using deionized water；5th step, takes off ink again, and above-mentioned glass cover-plate is put into taking off in black liquid for the first step and is cleaned；6th step, rinsing, rinses above-mentioned glass cover-plate using deionized water.Plating mode is taken off using the ink that takes off of the application, temperature is low, and the time is short, and cleaning effect is good, greatly improves work efficiency.And in the prior art, the defective products of the type can only scrap processing, and have the defective products of the type after this technique that can take off by taking off ink and be reprocessed into finished product after plating is reprocessed, and save the cost is increased economic efficiency.
Description
Technical field
The invention belongs to glass cover-plate production technical fields, take off ink in particular to a kind of glass cover-plate and take off electroplating method.
Background technique
Glass product understands some defective products and such as scratches class in manufacturing process and after finished product is made, for save the cost,
It needs to reprocess it.It when reprocessing, needs that first the ink being printed on glass fades away, then passes through plain grinding for glass surface
The bad removing of scuffing.Prior art can be very good the glass product that ink prints to take off black removal, but many products at present
LOGO made by the way of vacuum coating, LOGO will not be removed during taking off ink, take off take off after ink only for a long time
LOGO (LOGO has reaction by taking off the immersion of black liquid long-time high temperature) can not be removed after LOGO by the way of taking off plating again,
And corrode around LOGO with the place of glass contact, form LOGO shape pit.Therefore, the defective products of this type product can only be reported
Useless processing, increases manufacturing cost.
Therefore, above-mentioned technological deficiency exists in the prior art, is those skilled in the art's technical problem urgently to be resolved.
Summary of the invention
Ink is taken off the main purpose of the present invention is to provide a kind of glass cover-plate and takes off electroplating method, it is intended to which solution is deposited in the prior art
The technical issues of.
In order to achieve the above purpose, ink is taken off the present invention provides a kind of glass cover-plate take off electroplating method, comprising the following steps:
The first step just takes off ink, and HRS-M200 is taken off black liquid stoste and is heated to 70-80 DEG C, and glass cover-plate is put into above-mentioned take off
It is cleaned in black liquid；
Second step, rinsing, rinses above-mentioned glass cover-plate using deionized water；
Third step takes off plating, will clean in decoating liquid that above-mentioned glass cover-plate is put under normal temperature state；
4th step, rinsing, rinses above-mentioned glass cover-plate using deionized water；
5th step, takes off ink again, and above-mentioned glass cover-plate is put into taking off in black liquid for the first step and is cleaned；
6th step, rinsing, rinses above-mentioned glass cover-plate using deionized water.
Further, the black scavenging period that takes off in the first step is 1min.
Further, the decoating liquid applied in the third step by the potassium ferricyanide, sodium hydroxide and water according to parts by weight
1:2:20 is formulated.
Further, it is 1-2min that the plating time is taken off in the third step.
Further, the black scavenging period that takes off in the 5th step is 3-5min.
Further, in the second step, the 4th step and the 6th step, 1min is rinsed under deionized water room temperature.
It applies the technical scheme of the present invention, takes off plating mode using the ink that takes off of the application, temperature is low, and the time is short, cleaning effect
It is good, it greatly improves work efficiency.And in the prior art, the defective products of the type can only scrap processing, and be somebody's turn to do after having this technique
The defective products of type, which can take off by taking off ink, is reprocessed into finished product after plating is reprocessed, save the cost is increased economic efficiency.
Below in conjunction with specific embodiment, the present invention will be further described.
Specific embodiment
Specific embodiment
The present embodiment to mobile phone glass cover-plate (specific size 14.5cm*7.0cm, both ends and the side ink area Jun You, and
There is LOGO coating in upper end) curing ink and coating LOGO carry out taking off ink and take off plating, the specific steps are as follows:
The first step just takes off ink, and it is former that HRS-M200 is taken off black liquid (Suzhou Hao Ruisi tech materials Co., Ltd, which produces, takes off black liquid)
Liquid is put into heating container, and this is taken off black liquid and is heated to 70-80 DEG C, by glass cover-plate be put into it is above-mentioned take off in black liquid, keep the temperature
Clean 1min.In this step, just the ink of coating surface can be removed, and will not be with cladding portion overreaction.When
Between be less than 1min will cause ink removal it is not clean, overlong time will lead to glass corrosion and take off black liquid reacts with LOGO.
Second step, rinsing, rinses above-mentioned glass cover-plate using the deionized water of room temperature, rinsing time 1min,
Glass cover plate surfaces can be taken off black liquid removal, and can cooled down for glass cover-plate, reach room temperature.
Third step takes off plating, and in this step, decoating liquid is by the potassium ferricyanide, sodium hydroxide and water 1:2:20 according to parts by weight
It is formulated, will be cleaned in decoating liquid that the glass cover-plate after above-mentioned rinsing is put under normal temperature state, time 1-2min, energy
It is enough to remove coating completely.
4th step, rinsing, rinses above-mentioned glass cover-plate using deionized water, rinsing time 1min, can incite somebody to action
Glass cover plate surfaces take off plating solution removal.
5th step, takes off ink again, and above-mentioned glass cover-plate is put into taking off in black liquid for the first step and is cleaned, and in this step
In to take off the black time be 3-5min, therefore, the step for passing through, can completely remove the product that only remain part ink by take off ink
Ink.Ink is identical to take off black liquid using taking off with the first step, and temperature is identical, takes off about 3-5min of black time, and ink can be thoroughly
Removal.
6th step, rinsing, rinses above-mentioned glass cover-plate using deionized water, rinsing time 1min, similarly
It can achieve the effect that rinsed surfaces take off black liquid and cooling.After this step, by visual observation detect glass cover plate surfaces without
Ink residual, glass cover-plate is dried, rework process can be entered.
It applies the technical scheme of the present invention, takes off plating mode using the ink that takes off of the application, temperature is low, and the time is short, cleaning effect
It is good, it greatly improves work efficiency.And in the prior art, the defective products of the type can only scrap processing, and be somebody's turn to do after having this technique
The defective products of type, which can take off by taking off ink, is reprocessed into finished product after plating is reprocessed, save the cost is increased economic efficiency.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, made any to repair
Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (6)
1. a kind of glass cover-plate takes off ink and takes off electroplating method, it is characterised in that: the following steps are included:
The first step just takes off ink, and HRS-M200 is taken off black liquid stoste and is heated to 70-80 DEG C, and glass cover-plate is put into and above-mentioned takes off black liquid
Middle cleaning；
Second step, rinsing, rinses above-mentioned glass cover-plate using deionized water；
Third step takes off plating, will clean in decoating liquid that above-mentioned glass cover-plate is put under normal temperature state；
4th step, rinsing, rinses above-mentioned glass cover-plate using deionized water；
5th step, takes off ink again, and above-mentioned glass cover-plate is put into taking off in black liquid for the first step and is cleaned；
6th step, rinsing, rinses above-mentioned glass cover-plate using deionized water.
2. glass cover-plate as described in claim 1 takes off ink and takes off electroplating method, it is characterised in that: take off black cleaning in the first step
Time is 1min.
3. glass cover-plate as described in claim 1 takes off ink and takes off electroplating method, it is characterised in that: the strip applied in the third step
By the potassium ferricyanide, sodium hydroxide and water, 1:2:20 is formulated liquid according to parts by weight.
4. glass cover-plate as claimed in claim 3 takes off ink and takes off electroplating method, it is characterised in that: taken off in the third step plating time be
1-2min。
5. glass cover-plate as described in claim 1 takes off ink and takes off electroplating method, it is characterised in that: take off black cleaning in the 5th step
Time is 3-5min.
6. glass cover-plate as described in claim 1 takes off ink and takes off electroplating method, it is characterised in that: the second step, the 4th step and
In six steps, 1min is rinsed under deionized water room temperature.