CN1091403A - 用炼铜渣制作彩色墙、地装饰砖的方法 - Google Patents
用炼铜渣制作彩色墙、地装饰砖的方法 Download PDFInfo
- Publication number
- CN1091403A CN1091403A CN93101692A CN93101692A CN1091403A CN 1091403 A CN1091403 A CN 1091403A CN 93101692 A CN93101692 A CN 93101692A CN 93101692 A CN93101692 A CN 93101692A CN 1091403 A CN1091403 A CN 1091403A
- Authority
- CN
- China
- Prior art keywords
- slag
- ground
- wall
- decorative block
- lining
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用炼铜渣制作彩色墙、地装饰
砖的方法。将炼铜渣球磨成100目以下的渣粉,筛
取一部分细渣粉化学处理成各种色彩,作为面料,其
余作底料。用工业磷酸、磷酸二氢铝或其混合液作粘
结剂,高压模制成型,经过热处理、抛光、以及低温玻
璃膜、不饱和紧酯涂料等第二次装饰加工,制作成高
级彩色墙、地装饰砖。用本发明制作的墙、地砖,强度
高、耐磨性好、装饰效果卓越。废物利用、价廉物美、
经济效益显著。
Description
本发明涉及一种用冶金渣制作建材,特别是用炼铜渣制作彩色墙、地装饰砖的方法。
用冶金渣或选矿尾砂生产建材的方法早有问世,但用炼铜渣制作彩色墙、地砖的技术,至今不多见。建筑业崛起后,室内外墙、地装饰形成热潮,传统的瓷砖装饰已不能满足广泛的需要,开发价廉物美的新颖墙、地砖是建材业的迫切任务。
本发明的任务是要提供一种能够用炼铜制作高级墙、地装饰砖的方法。本发明采用化学方法与物理技术结合,呈现出高强度和炼铜渣中多种金属氧化物的色彩特性。它具有成本低、节能、装饰效果卓越、变废为宝、治理环境,经济和社会效益显著等优点。
本发明用工业磷酸或磷酸二氢铝,或二者的混合液作化学粘结剂,可以是工业品原液,也可用水的稀释液,最好使用原液。物理技术采用高压模制成形,表面抛光及热处理。模压强度用50~500公斤/cm2,最好是100~200公斤/cm2,也可在真空及大气压下自由模制成形。热处理温度80℃~200℃,较好是100℃,加热时间1~2小时。
本发明所用炼铜渣是一种含铁、硅、铝、铜、钙、镁等多种金属化物的富铁冶金渣。使用时需要将其球磨成100目以下的渣粉。渣粉在200℃以上的温度下焙烤1小时以上,可使其氧化成红棕色,并延长成形凝固时间。焙烤温度越高、时间越长,渣粉的红棕色越深,成形凝固速度越慢。未作焙烤氧化的渣粉需用化学缓凝剂,减慢其成形凝固速度,以取得足够的模制作业时间。
用焙烤过的渣粉作原料,成品表面抛光后会显出红棕色的美丽光泽。用未焙烤过的渣粉作原料,抛光后显示银白色金属光泽。将一部分100目以下的细渣粉用化学方法处理成黑、红、黄、绿、兰、白等色彩后,作为面料,未处理的渣粉作底料,可模制成具有各种彩色表面的墙、地砖。
成品的装饰面可根据需要,采用不同的底模制成平面,浮雕、隐纹、漏花等类型。也可用低温玻璃膜及不饱和紧酯涂料进行第二次装饰加工,使产品具有更高的亮度和硬度,更好的耐磨性和装饰性。
本发明的彩色墙、地砖制作,以如下的方法完成:
1.在用上述制备好的彩色面料渣粉中,拌入为其重量28~40%,较好是34~38%的上述化学粘结剂,快速搅拌成粘滞状物质后,倒入底模内,高频震动底模,使成形物质与模底紧密吻合,并逸出成形物质中的气体,增加成品强度和表面光泽。
2.在未作任何处理的渣粉中,拌入为其重量18~28%,较好是22~25%的上述化学粘结剂,充分拌匀后作为底料,待底模内面料初凝开始后,均匀地平铺于面料上。
3.盖好上模,根据产品强度需要施加予定的压力成形。脱模后将成形物连同底模放在上述的热处理条件下,使成形物达到最大强度。
4.去掉底模,装饰面经抛光机抛光,即为成品。对成品表面用低温玻璃膜或不饱和紧酯涂料作第二次装饰加工,可获得高级墙、地砖产品。
实施例一:
将2000克炼铜渣球磨成100目以下的渣粉,放在400℃的炉内焙烤1小时后,筛取150目以下的细渣粉500克作面料。取190克工业磷酸二氢铝原液,与500克面料充分混合成粘滞状物质,倒入30cm×30cm×1cm的平面底模内摊平,高频震动底模。
再取330克工业磷酸二氢铝原液,与剩下的1500克渣粉充分拌匀作为底料。待底模中面料开始初凝,将底料均匀摊平在面料上,盖好上模,施加150公斤/cm2的压力成形后,将成形物连同模具放在100℃环境中加热1小时,脱模后抛光,即得一具红棕色美丽金属光泽的平面墙、地砖。其硬度、强度、装饰性均优于天然大理石。
实施例二:
将2000克炼铜渣粉磨成100目以下的渣粉,筛取150目以下的渣粉500克,用化学方法将其处理成兰色作为面料,剩下的1500克渣粉不作任何处理作为底料。在520克工业磷酸中加入16克化学缓凝剂(例如:磷酸钠),充分搅拌混匀,取194克拌入面料,342克拌入底料,使用浮雕底模,其它操作步骤与实施例1相同。脱模抛光后便获得具有漂亮兰色浮雕装饰图案的墙、地砖。
取90克无色不饱和紧酯涂料,加入4克安息香醚充分拌匀后,将其涂于用布擦净的装饰面上,然后放在紫外光下照射数分钟,可得一晶莹剔透、光泽鲜艳、兰宝石样的高级坪、地砖。其耐磨性、耐温变、装饰性更加卓越。
本发明开辟了生产装饰建材的新资源,既治理了冶金渣对环境的污染,又创造了大量社会财富,还增加了装饰建材的品种。
Claims (9)
1、一种由炼铜渣粉、化学粘结剂以及加压模制而成的彩色墙、地装饰砖,其特征是化学粘结剂为工业磷酸、磷酸二氢铝,或磷酸与磷酸二氢铝的混合液,或各自的水稀释液及混合稀释液;
2、按权利要求1所述的炼铜渣汾,其特征是在200℃以上的温度下,焙烤1~2小时,使其氧化成红棕色;
3、按权利要求1所述的炼铜渣粉,其特征是筛取一部分细渣粉,用化学方法将其处理成各种色彩,作为模制彩色墙、地砖的面料;
4、按权利要求1所述的化学粘结剂,其特征是在粘结剂中添加适量的化学缓凝剂;
5、按权利要求1所述的加压模制,其特征是加压强度为0~500公斤/CM2;
6、按权利要求1所述的加压模制,其特征是倒入面料时,底模进行高频震动,面料开始初凝时,倒入底料加压;
7、按权利要求1所述的彩色墙、地装饰砖其特征是脱模后连同底模放在80℃~200℃的温度下进行1~2小时的热处理;
8、按权利要求7所述的底模,其特征是底模可以作成平面、浮雕图案、隐纹、漏花等型式;
9、按权利要求1所述的彩色墙、地装饰砖,其特征是装饰面可以用低温玻璃膜,不饱和紧酯涂料等技术进行第二次装饰加工。