CN104591790A - High-temperature iron-red glaze and preparation method thereof - Google Patents
High-temperature iron-red glaze and preparation method thereof Download PDFInfo
- Publication number
- CN104591790A CN104591790A CN201410820371.4A CN201410820371A CN104591790A CN 104591790 A CN104591790 A CN 104591790A CN 201410820371 A CN201410820371 A CN 201410820371A CN 104591790 A CN104591790 A CN 104591790A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- scorification
- component
- follows
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-temperature iron-red glaze and a preparation method thereof. The high-temperature iron-red glaze is a single-layer reaction crystalline glaze and comprises the following components in parts by mass: 35-45 parts of feldspars, 20-23 parts of quartz, 10-12 parts of calcite, 3-5 parts of kaolin, 5-8 parts of zinc oxide, 8-10 parts of titanium dioxide, 8-12 parts of dolomite, 6-8 parts of wollastonite, 10-15 parts of self-burnt clinker and 15-20 parts of chromophore, wherein the self-burnt clinker comprises the following components in parts by mass: 30-40 parts of feldspars, 15-25 parts of quartz, 10-15 parts of calcite and 20-25 parts of zinc oxide. The high-temperature iron-red glaze disclosed by the invention not only can be stably fired at a temperature of 1230-1250 DEG C, but also presents the style of ancient ceramics and has the amorous feelings of modern ceramics.
Description
Technical field
The present invention relates to a kind of high temperature iron-red glaze and preparation method thereof.
Background technology
At present, in ceramic industry, the moulding of porcelain base is that the allotment of the base glaze of quality products makes porcelain more dazzling brilliant, the porcelain base of same moulding, often because glaze paint is different, and make the vision of human consumer produce different impacts, this iron-red glaze, both there is the style of ancient pottery and porcelain, there are again the landscape of advanced ceramics, give people beautiful with modern combination, easy to operate for a kind of ancient times to people is a kind of, handicraft than complexity makes product and more has competitive prospect, product when this is also current porcelain industry a kind of.
Summary of the invention
Technical problem to be solved by this invention overcomes the deficiencies in the prior art, provides a kind of high temperature iron-red glaze, and it can not only make it stablely at the temperature of 1230 ~ 1250 DEG C burn till, and presents the style of ancient pottery and porcelain, has again the landscape of advanced ceramics.
In order to solve the problems of the technologies described above, technical scheme of the present invention is: a kind of high temperature iron-red glaze, and this glaze is that single-layer back answers crystalline glaze, its component and each constituent mass part as follows: feldspar: 35 parts ~ 45 parts; Quartz: 20 parts ~ 23 parts; Calcite: 10 parts ~ 12 parts; Kaolin: 3 parts ~ 5 parts; Zinc oxide: 5 parts ~ 8 parts; Titanium dioxide: 8 parts ~ 10 parts; Rhombspar 8 parts ~ 12 parts; Wollastonite: 6 parts ~ 8 parts; From scorification block 10 parts ~ 15 parts; 15 parts ~ 20 parts, color base; The described component from scorification block and each component mass parts as follows: feldspar: 30 parts ~ 40 parts; Quartz: 15 parts ~ 25 parts; Calcite: 10 parts ~ 15 parts; 20 parts ~ 25 parts, zinc oxide.
The present invention also provides a kind of making method of high temperature iron-red glaze, and the step of the method is as follows:
A) according to each component and each component mass parts for iron oxide red glaze; Wherein, excessively as follows from the preparation of scorification block: press from scorification Kuai Liao ︰ Qiu ︰ water=1 ︰ 1.7 ︰ 0.4, wet ball grinding 10 ~ 12 hours, after 160 mesh sieves crossed by the glaze after ball milling, put into crucible to burn till at 800 DEG C of temperature, burned frit is put into pulverizer and pulverizes;
B) by iron oxide red glaze ︰ ball ︰ water=1 ︰ 1.5 ︰ 0.5, wet ball grinding 11 ~ 13 hours, after 160 mesh sieves crossed by the glaze after ball milling, then the glaze slip of furnishing 50 ~ 70 degree Beaume, by the glazing of off-the-shelf biscuiting embryo, under the oxidizing atmosphere of 1230 ~ 1250 DEG C, fire finished product.
After have employed technique scheme, make high temperature iron-red glaze more stable by making of adopting new technology, present the style of ancient pottery and porcelain, there are again the landscape of advanced ceramics, give people beautiful with modern combination for a kind of ancient times to people is a kind of, easy to operate, handicraft than complexity makes product and more has competitive prospect, and wide at 1230 ~ 1250 DEG C of firing ranges, glaze paint is attractive in appearance, do things creatively, be well received by consumers.
Embodiment
In order to make content of the present invention more easily be clearly understood, below according to specific embodiment, the present invention is further detailed explanation.
Embodiment one
A kind of high temperature iron-red glaze, this glaze is that single-layer back answers crystalline glaze, its component and each constituent mass part as follows: feldspar: 40 parts; Quartz: 21 parts; Calcite: 12 parts; Kaolin: 5 parts; Zinc oxide: 8 parts; Titanium dioxide: 9 parts; Rhombspar 12 parts; Wollastonite: 6 parts; From scorification block 15 parts; 15 parts, color base; The described component from scorification block and each component mass parts as follows: feldspar: 40 parts; Quartz: 15 parts; Calcite: 15 parts; 25 parts, zinc oxide.
The making method of this high temperature iron-red glaze, the step of the method is as follows:
A) according to each component and each component mass parts for iron oxide red glaze; Wherein, excessively as follows from the preparation of scorification block: press from scorification Kuai Liao ︰ Qiu ︰ water=1 ︰ 1.7 ︰ 0.4, wet ball grinding 10 hours, after 160 mesh sieves crossed by the glaze after ball milling, puts into crucible and burn till at 800 DEG C of temperature, burned frit is put into pulverizer and pulverizes;
B) by iron oxide red glaze ︰ ball ︰ water=1 ︰ 1.5 ︰ 0.5, wet ball grinding 13 hours, after 160 mesh sieves crossed by the glaze after ball milling, then the glaze slip of furnishing 50 ~ 70 degree Beaume, by the glazing of off-the-shelf biscuiting embryo, under the oxidizing atmosphere of 1230 ~ 1250 DEG C, fire finished product.
Embodiment two
A kind of high temperature iron-red glaze, this glaze is that single-layer back answers crystalline glaze.Its component mass ratio of described iron-red glaze is as follows: feldspar: 40 parts; Quartz: 23 parts; Calcite: 12 parts; Kaolin: 5 parts; Zinc oxide: 8 parts; Titanium dioxide: 9 parts; Rhombspar 12 parts; Wollastonite: 8 parts; From scorification block 10 parts; 15 parts, color base; The described component from scorification block and each component mass parts as follows: feldspar: 40 parts; Quartz: 15 parts; Calcite: 15 parts; 25 parts, zinc oxide.
The making method of this high temperature iron-red glaze, the step of the method is as follows:
A) according to each component and each component mass parts for iron oxide red glaze; Wherein, excessively as follows from the preparation of scorification block: press from scorification Kuai Liao ︰ Qiu ︰ water=1 ︰ 1.7 ︰ 0.4, wet ball grinding 12 hours, after 160 mesh sieves crossed by the glaze after ball milling, puts into crucible and burn till at 800 DEG C of temperature, burned frit is put into pulverizer and pulverizes;
B) by iron oxide red glaze ︰ ball ︰ water=1 ︰ 1.5 ︰ 0.5, wet ball grinding 11 hours, after 160 mesh sieves crossed by the glaze after ball milling, then the glaze slip of furnishing 50 ~ 70 degree Beaume, by the glazing of off-the-shelf biscuiting embryo, under the oxidizing atmosphere of 1230 ~ 1250 DEG C, fire finished product.
Embodiment three
A kind of high temperature iron-red glaze, this glaze is that single-layer back answers crystalline glaze.Its component mass ratio of described iron-red glaze is as follows: feldspar: 40 parts; Quartz: 21 parts; Calcite: 12 parts; Kaolin 4 parts; Zinc oxide: 6 parts; Titanium dioxide: 9 parts; Rhombspar 10 parts; Wollastonite: 8 parts; From scorification block 15 parts; 20 parts, color base; The described component from scorification block and each component mass parts as follows: feldspar: 40 parts; Quartz: 15 parts; Calcite: 15 parts; 25 parts, zinc oxide.
The making method of this high temperature iron-red glaze, the step of the method is as follows:
A) according to each component and each component mass parts for iron oxide red glaze; Wherein, excessively as follows from the preparation of scorification block: press from scorification Kuai Liao ︰ Qiu ︰ water=1 ︰ 1.7 ︰ 0.4, wet ball grinding 10 hours, after 160 mesh sieves crossed by the glaze after ball milling, puts into crucible and burn till at 800 DEG C of temperature, burned frit is put into pulverizer and pulverizes;
B) by iron oxide red glaze ︰ ball ︰ water=1 ︰ 1.5 ︰ 0.5, wet ball grinding 13 hours, after 160 mesh sieves crossed by the glaze after ball milling, then the glaze slip of furnishing 50 ~ 70 degree Beaume, by the glazing of off-the-shelf biscuiting embryo, under the oxidizing atmosphere of 1230 ~ 1250 DEG C, fire finished product.
High temperature iron-red glaze prepared by above-mentioned three embodiments has the effect of high temperature iron-red glaze, and the effect of three kinds of experiments is relatively stable, this iron-red glaze, both there is the style of ancient pottery and porcelain, there are again the landscape of advanced ceramics, give people beautiful with modern combination, easy to operate for a kind of ancient times to people is a kind of, the handicraft than complexity makes product and more has competitive prospect.
In the present invention, mix according to each corresponding component and mass parts from scorification block material, iron oxide red glaze is also be mixed into ball mill according to each component and mass parts.
Above-described specific embodiment; technical problem, technical scheme and beneficial effect that the present invention solves are further described; be understood that; the foregoing is only specific embodiments of the invention; be not limited to the present invention; within the spirit and principles in the present invention all, any amendment made, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (2)
1. a high temperature iron-red glaze, this glaze is that single-layer back answers crystalline glaze, it is characterized in that: its component and each constituent mass part as follows: feldspar: 35 parts ~ 45 parts; Quartz: 20 parts ~ 23 parts; Calcite: 10 parts ~ 12 parts; Kaolin: 3 parts ~ 5 parts; Zinc oxide: 5 parts ~ 8 parts; Titanium dioxide: 8 parts ~ 10 parts; Rhombspar 8 parts ~ 12 parts; Wollastonite: 6 parts ~ 8 parts; From scorification block 10 parts ~ 15 parts; 15 parts ~ 20 parts, color base; The described component from scorification block and each component mass parts as follows: feldspar: 30 parts ~ 40 parts; Quartz: 15 parts ~ 25 parts; Calcite: 10 parts ~ 15 parts; 20 parts ~ 25 parts, zinc oxide.
2. a making method for high temperature iron-red glaze as claimed in claim 1, is characterized in that the step of the method is as follows:
A) according to each component and each component mass parts for iron oxide red glaze; Wherein, excessively as follows from the preparation of scorification block: press from scorification Kuai Liao ︰ Qiu ︰ water=1 ︰ 1.7 ︰ 0.4, wet ball grinding 10 ~ 12 hours, after 160 mesh sieves crossed by the glaze after ball milling, put into crucible to burn till at 800 DEG C of temperature, burned frit is put into pulverizer and pulverizes;
B) by iron oxide red glaze ︰ ball ︰ water=1 ︰ 1.5 ︰ 0.5, wet ball grinding 11 ~ 13 hours, after 160 mesh sieves crossed by the glaze after ball milling, then the glaze slip of furnishing 50 ~ 70 degree Beaume, by the glazing of off-the-shelf biscuiting embryo, under the oxidizing atmosphere of 1230 ~ 1250 DEG C, fire finished product.