CN109111200A - A kind of double-colored purple ceramic cup manufacture craft - Google Patents
A kind of double-colored purple ceramic cup manufacture craft Download PDFInfo
- Publication number
- CN109111200A CN109111200A CN201710479528.5A CN201710479528A CN109111200A CN 109111200 A CN109111200 A CN 109111200A CN 201710479528 A CN201710479528 A CN 201710479528A CN 109111200 A CN109111200 A CN 109111200A
- Authority
- CN
- China
- Prior art keywords
- cup
- green body
- double
- temperature
- manufacture craft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of double-colored purple ceramic cup manufacture craft, the technique includes the following steps: that cup body green body makes, the production of attachment green body, the installation of cup body green body, cup colouring, and cup firing, the step of wherein cup is burnt into is before cup firing, first cup is put into the drying chamber of indoor 50 DEG C of temperature and is dried 3-4 hours, then cup green body is sent into kiln and is warming up between 100 DEG C -120 DEG C, after constant temperature 1~1.5 hour, it is stepped up temperature again, maximum temperature controls between 1170 DEG C -1200 DEG C, then gradually cool down, after stopping 1 hour again when dropping to 100 DEG C, cup could be taken out when dropping to 45 DEG C~55 DEG C.The present invention carves characters by hand, and beautiful, effect is good, without chemical raw material, more environmentally friendly, safety is no added, and not delamination, mouth line is clear, quarter draws background color and highlights effect, bisque thin and thick is uniform, whole clean, flower mud, different colours pug combination shrinkage rates do not control, extexine does not crack, and double-colored mud slurry green compact green body, which is combined, draws highlight products aesthetic effect by carving.
Description
Technical field
The present invention relates to field of porcelain fabrication, more specifically a kind of double-colored purple ceramic cup manufacture craft.
Background technique
Cup is that we are commonly used to contain the container of liquid day, and the cylinder figure modelling of width is usually all greater than using height,
In order to which hand is taken and retains the temperature of liquid.Some cups can also have handle, handle, or with additional anti-scald, heat preservation
Etc. functional structures.The general small volume of cup, people can very easily pick up one hand, and bottom of a cup is more roomy, can stablize and be placed on
On desk.Cup is firm using glass, ceramics, plastics, metal etc., material production not soluble in water, and can contain other liquid
Body, such as beverage or drinks.But house refuse, air pollution, industrial pollution aggravation, the pollution for the water that people drink is also more next
More serious, tap water is not only remaining a variety of harmful organic matters after disinfection, but also exists a variety of carcinogenic
Halogenated compound.But current cup is intended merely to drink water, and does not have and decompose substance harmful in drinking water
Effect.
The characteristics of natural purple ceramic cup is made by boccaro, its certain feature is with boccaro is very nearly the same.Purple sand material is saturating
The advantages of gas is excellent, has and makes tea and be not easy to lose flavour, and tealeaves is unlikely to deteriorate, allows the more aromatic deliciousness of millet paste.Currently on the market only
There is the molding purple ceramic cup of single purple clay, color is relatively simple.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the existing defects, provides a kind of double-colored purple ceramic cup manufacture craft.
In order to solve the above-mentioned technical problems, the present invention provides the following technical solutions:
A kind of double-colored purple ceramic cup manufacture craft, the technique include the following steps:
(1) cup body green body makes: using slice uniformly being patted repeatedly to 3~5mm thickness, according to the specification of cup, measuring
After cut off unnecessary portion, patted and formed with plastics while rolling slice, then with bright for patting the cup body green body of getting up
It is polished repeatedly;
(2) attachment green body makes: the attachment ornament including cup handle and cup lid is independent according to the moulding of design respectively
Production;
(3) cup body green body is installed: the mud of the identical cup pug processed of the connection use of cup handle green body and cup body green body connect and
At, it is 0.5-1 hours to be dried after with bright needle reparation;
(4) cup is painted: in cup blank forming, the two different colors of purple on the inside and outside manual homogeneous powder of cup
Sand mud;
(5) cup is burnt into: before cup firing, first cup is put into the drying chamber of indoor 50 DEG C of temperature and dried 3-4 hours,
Then cup green body is sent into kiln and is warming up between 100 DEG C -120 DEG C, after constant temperature 1~1.5 hour, then be stepped up temperature
Degree, maximum temperature controls between 1170 DEG C -1200 DEG C, then gradually cools down, after stopping 1 hour again when dropping to 100 DEG C,
Cup could be taken out when dropping to 45 DEG C~55 DEG C.
Further, first green body is gradually dried before the step (5), winter is 36-40 hours, and summer, 24-32 was small
When, season in spring and autumn is 20-26 hours.
Further, it is described after the completion of the green body of cup body and rim of a cup further according to the size of rim of a cup, according to being not more than
The requirement of 0.5mm, then make cup lid green body.
Further, it carves to draw in cup body and needs to add acrylic paints.
A kind of double-colored purple ceramic cup manufacture craft of the present invention, carving characters by hand, beautiful, effect is good, more environmentally friendly without chemical raw material,
Safety is no added, and not delamination, mouth line is clear, quarter draws background color and highlights effect, and bisque thin and thick is uniform, and whole clean, flower mud, not different
The control of color pug combination shrinkage rates, extexine do not crack, and double-colored mud slurry green compact green body, which is combined, draws highlight products by carving
Aesthetic effect, the double-deck pug double medium filtration are ventilative, the collocation of different colours pug to traditional monochromatic purple ceramic cup slurry way more
It is apparent to carve drawing face for beauty.
Specific embodiment
It is right below in conjunction with specific embodiment in order to which the purpose of the present invention, technical solution and advantage is more clearly understood
The present invention is described in detail.
A kind of double-colored purple ceramic cup manufacture craft of the present invention, the technique include the following steps:
(1) cup body green body makes: using slice uniformly being patted repeatedly to 3~5mm thickness, according to the specification of cup, measuring
After cut off unnecessary portion, patted and formed with plastics while rolling slice, then with bright for patting the cup body green body of getting up
It is polished repeatedly;
(2) attachment green body makes: the attachment ornament including cup handle and cup lid is independent according to the moulding of design respectively
Production;
(3) cup body green body is installed: the mud of the identical cup pug processed of the connection use of cup handle green body and cup body green body connect and
At, it is 0.5-1 hours to be dried after with bright needle reparation;
(4) cup is painted: in cup blank forming, the two different colors of purple on the inside and outside manual homogeneous powder of cup
Sand mud;
(5) cup is burnt into: before cup firing, first cup is put into the drying chamber of indoor 50 DEG C of temperature and dried 3-4 hours,
Then cup green body is sent into kiln and is warming up between 100 DEG C -120 DEG C, after constant temperature 1~1.5 hour, then be stepped up temperature
Degree, maximum temperature controls between 1170 DEG C -1200 DEG C, then gradually cools down, after stopping 1 hour again when dropping to 100 DEG C,
Cup could be taken out when dropping to 45 DEG C~55 DEG C.
First green body is gradually dried before the step (5), winter is 36-40 hours, summer 24-32 hour, spring and autumn
Section is 20-26 hours;It is described the green body of cup body and rim of a cup completion after further according to rim of a cup size, according to be not more than 0.5mm
Requirement, then make cup lid green body;It carves to draw in cup body and needs to add acrylic paints.
Embodiment 1
A kind of double-colored purple ceramic cup manufacture craft, the technique include the following steps:
(1) cup body green body makes: it is thick to 3mm using slice is uniformly patted repeatedly, according to the specification of cup, cut after measuring
It except unnecessary portion, is patted and is formed with plastics while rolling slice, then carried out with the bright cup body green body to get up for beating
It polishes repeatedly;
(2) attachment green body makes: the attachment ornament including cup handle and cup lid is independent according to the moulding of design respectively
Production;Cup lid and cup body are to avoid losing round or wide bore defect using first complete cup body and rim of a cup, then according to rim of a cup
Size then make cup lid according to the requirement for being not more than 0.5mm;
(3) cup body green body is installed: the mud of the identical cup pug processed of the connection use of cup handle green body and cup body green body connect and
At with bright needle reparation after 0.5 hour to be dried;
(4) cup is painted: in cup blank forming, the two different colors of purple on the inside and outside manual homogeneous powder of cup
Sand mud;It carves to draw in cup body and needs to add acrylic paints;
(5) cup is burnt into: first gradually being dried green body, winter is 36-40 hours, and summer 24-32 hour, season in spring and autumn is
20-26 hours.It can ensure that cup has certain plasticity in firing in this way, yield rate is higher.Cup lid is arbitrarily exchanged after firing
Orientation can match with rim of a cup, and lid quasi- seam is tight, and gap between the two (or displacement tolerance) is within 0.5mm.Again
Cup is put into the drying chamber of indoor 50 DEG C of temperature and dried 3 hours, makes cup into when kiln firing, moisture control is in 8%-
Between 10%.Finally cup green body is sent into kiln and is sintered, specific procedure is that cup green body is sent into kiln to heat up
To between 100 DEG C -110 DEG C, after constant temperature 1.5 hours, then it is stepped up temperature, at 1170 DEG C, then gradually maximum temperature controls
Cooling, after stopping 1 hour again when dropping to 100 DEG C, cup could be taken out when temperature drops to 50 DEG C.
Embodiment 2
A kind of double-colored purple ceramic cup manufacture craft, the technique include the following steps:
(1) cup body green body makes: it is thick to 4mm using slice is uniformly patted repeatedly, according to the specification of cup, cut after measuring
It except unnecessary portion, is patted and is formed with plastics while rolling slice, then carried out with the bright cup body green body to get up for beating
It polishes repeatedly;
(2) attachment green body makes: the attachment ornament including cup handle and cup lid is independent according to the moulding of design respectively
Production;Cup lid and cup body are to avoid losing round or wide bore defect using first complete cup body and rim of a cup, then according to rim of a cup
Size then make cup lid according to the requirement for being not more than 0.5mm;
(3) cup body green body is installed: the mud of the identical cup pug processed of the connection use of cup handle green body and cup body green body connect and
At with bright needle reparation after 45 minutes to be dried;
(4) cup is painted: in cup blank forming, the two different colors of purple on the inside and outside manual homogeneous powder of cup
Sand mud;It carves to draw in cup body and needs to add acrylic paints;
(5) cup is burnt into: first gradually being dried green body, winter is 36-40 hours, and summer 24-32 hour, season in spring and autumn is
20-26 hours.It can ensure that cup has certain plasticity in firing in this way, yield rate is higher.Cup lid is arbitrarily exchanged after firing
Orientation can match with rim of a cup, and lid quasi- seam is tight, and gap between the two (or displacement tolerance) is within 0.5mm.Again
Cup is put into the drying chamber of indoor 50 DEG C of temperature and dried 4 hours, makes cup into when kiln firing, moisture control is in 8%-
Between 10%.Finally cup green body is sent into kiln and is sintered, specific procedure is that cup green body is sent into kiln to heat up
To between 110 DEG C -120 DEG C, after constant temperature 1 hour, then it is stepped up temperature, maximum temperature is controlled at 1180 DEG C, is then gradually dropped
Temperature could take out cup when temperature drops to 50 DEG C after stopping 1 hour again when dropping to 100 DEG C.
Embodiment 3
A kind of double-colored purple ceramic cup manufacture craft, the technique include the following steps:
(1) cup body green body makes: it is thick to 5mm using slice is uniformly patted repeatedly, according to the specification of cup, cut after measuring
It except unnecessary portion, is patted and is formed with plastics while rolling slice, then carried out with the bright cup body green body to get up for beating
It polishes repeatedly;
(2) attachment green body makes: the attachment ornament including cup handle and cup lid is independent according to the moulding of design respectively
Production;Cup lid and cup body are to avoid losing round or wide bore defect using first complete cup body and rim of a cup, then according to rim of a cup
Size then make cup lid according to the requirement for being not more than 0.5mm;
(3) cup body green body is installed: the mud of the identical cup pug processed of the connection use of cup handle green body and cup body green body connect and
At with bright needle reparation after 1 hour to be dried;
(4) cup is painted: in cup blank forming, the two different colors of purple on the inside and outside manual homogeneous powder of cup
Sand mud;It carves to draw in cup body and needs to add acrylic paints;
(5) cup is burnt into: first gradually being dried green body, winter is 36-40 hours, and summer 24-32 hour, season in spring and autumn is
20-26 hours.It can ensure that cup has certain plasticity in firing in this way, yield rate is higher.Cup lid is arbitrarily exchanged after firing
Orientation can match with rim of a cup, and lid quasi- seam is tight, and gap between the two (or displacement tolerance) is within 0.5mm.Again
Cup is put into the drying chamber of indoor 50 DEG C of temperature and dried 4 hours, makes cup into when kiln firing, moisture control is in 8%-
Between 10%.Finally cup green body is sent into kiln and is sintered, specific procedure is that cup green body is sent into kiln to heat up
To between 115 DEG C -120 DEG C, after constant temperature 1 hour, then it is stepped up temperature, maximum temperature is controlled at 1200 DEG C, is then gradually dropped
Temperature could take out cup when temperature drops to 50 DEG C after stopping 1 hour again when dropping to 100 DEG C.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although referring to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features.It is all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (4)
1. a kind of double-colored purple ceramic cup manufacture craft, it is characterised in that: the technique includes the following steps:
(1) cup body green body makes: using slice uniformly being patted repeatedly to 3~5mm thickness, according to the specification of cup, cutting after measuring
It except unnecessary portion, is patted and is formed with plastics while rolling slice, then carried out with the bright cup body green body to get up for beating
It polishes repeatedly;
(2) attachment green body makes: the attachment ornament including cup handle and cup lid is fabricated separately according to the moulding of design respectively;
(3) cup body green body is installed: the mud of cup handle green body cup pug processed identical as the connection use of cup body green body is formed by connecting, to
With bright needle reparation after 0.5-1 hours dry;
(4) cup is painted: in cup blank forming, the two different colors of boccaro on the inside and outside manual homogeneous powder of cup
Mud;
(5) cup is burnt into: before cup firing, first cup being put into and dries 3-4 hours in the drying chamber of indoor 50 DEG C of temperature, then
Cup green body is sent into kiln and is warming up between 100 DEG C -120 DEG C, after constant temperature 1~1.5 hour, then is stepped up temperature, most
High-temperature controls between 1170 DEG C -1200 DEG C, then gradually cools down, after stopping 1 hour again when dropping to 100 DEG C, is dropping to
Cup could be taken out at 45 DEG C~55 DEG C.
2. a kind of double-colored purple ceramic cup manufacture craft according to claim 1, it is characterised in that: before the step (5) first
Green body is gradually dried, winter is 36-40 hours, and summer 24-32 hour, season in spring and autumn is 20-26 hours.
3. a kind of double-colored purple ceramic cup manufacture craft according to claim 1, it is characterised in that: described in cup body and rim of a cup
Further according to the size of rim of a cup after green body completion, according to the requirement no more than 0.5mm, then cup lid green body is made.
4. a kind of double-colored purple ceramic cup manufacture craft according to claim 1, it is characterised in that: quarter draws needs and adds in cup body
Add acrylic paints.