CN109056304A - 一种抗菌消毒棉的制备方法 - Google Patents
一种抗菌消毒棉的制备方法 Download PDFInfo
- Publication number
- CN109056304A CN109056304A CN201810608195.6A CN201810608195A CN109056304A CN 109056304 A CN109056304 A CN 109056304A CN 201810608195 A CN201810608195 A CN 201810608195A CN 109056304 A CN109056304 A CN 109056304A
- Authority
- CN
- China
- Prior art keywords
- cotton
- parts
- antibiotic
- preparation
- sterilizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明属于医疗材料技术领域，具体涉及一种抗菌消毒棉的制备方法。所述抗菌消毒棉的制备方法包括：(1)改性棉花的制备；(2)消毒棉的制备(3)产品消毒性能检测；(4)产品包装处理；通过对棉花合理的改性，并加入一系列消毒功能的物质，本发明通过加入2,4‑二甲醛苯甲酸，利用其羧基和棉花上的羟基进行酯化反应，在增强抗菌效果的同时，也延长了抗菌时间，可投入日常使用。
Description
技术领域
本发明属于医疗材料技术领域，具体涉及一种抗菌消毒棉的制备方法。
背景技术
中国专利申请CN 106948062 A公开了本发明公开了一种消毒灭菌医用的面料，包括砂纸和线芯，所述砂纸按重量分数有如下组分组成：玻璃纤维：20-40份，活性炭纤维：15-30份，超细纤维：10-20份，棉纤维：10-20份，竹纤维：10-40份；天然竹原纤维具有吸湿、透气、抗菌抑菌、除臭、防紫外线等良好的性能，玻璃纤维强度高，无毒、不危害人体健康，这种消毒灭菌医用绷带的面料，强度高、重量轻、操作简单方便、透气性好等优点。
中国专利申请CN 105963072 A公开了本发明公开了一种医用竹纤维绷带，包括依次叠加设置的消毒纱布、竹纤维层及防水透气层；所述消毒纱布呈网状，包括50～60％的棉、10～20％的氨纶及20～40％的竹纤维，该消毒纱布两侧从内向外依次设置有吸水带及防水带；所述防水透气层包括覆盖在竹纤维层上端的PTFE膜及设置在PTFE膜上端的布料；该发明中消毒纱布较传统的纱布在其中添加了竹纤维，竹纤维具有良好的透气性、瞬间吸水性、较强的耐磨性和良好的染色性等特性，同时又具有天然抗菌、抑菌、除螨、防臭和抗紫外线功能；防水透气层采用PTFE膜及布料的组合，PTFE膜的织物基材为玻璃纤维，具有很好的透气防水性。
随着人们对生活质量的追求，及医疗水平的提高，抗菌消毒棉的需求及使用日益增长，因此抗菌消毒棉的制备显得尤为重要。
发明内容
为了达到背景技术中的目的，本发明提出的一种抗菌消毒棉的制备方法；通过对棉花合理的改性，并加入一系列消毒功能的物质，本发明通过加入2,4-二甲醛苯甲酸，利用其羧基和棉花上的羟基进行酯化反应，在增强抗菌效果的同时，也延长了抗菌时间，可投入日常使用。
本发明通过如下的技术方案实现的
一种抗菌消毒棉的制备方法，其特征在于,所述抗菌消毒棉的制备方法下：(1)改性棉花的制备
将市场购买的棉花进行清理，除去杂质，然后将棉花浸泡在浓度为5-10％的漂洗液中进行漂洗1-5小时，除去漂洗液，用清水进行清洗2-3次后将棉花进行烘干得到干燥的棉花，然后将该棉花放置在紫外光照射发生器中进行紫外线杀菌10-20小时后取出棉花，称取质量份数为100-120份的棉花，加入反应釜中，然后加入300-400份的工业酒精、1-2份的2,4-二甲醛苯甲酸、0.1-0.2份的催化剂、1-2份的十二烷基磺酸钠溶剂进行回流反应2-4小时，其中反应釜温度控制在80-100℃，待反应完全后，将得到物质进行干燥除去酒精溶剂，得到干燥的棉花，此棉花就是改性棉；
(2)消毒棉的制备
将步骤(1)中制备的改性棉，称取质量份数为100-120加入反应釜中，然后加入10-20份双氧水、1-5份的抗菌剂进行浸泡10-20小时后，取出，进行干燥得到的物质就是抗菌消毒棉；
(3)产品消毒性能检测
将得到的产品进行检测，测试其细菌含量，抗菌性能检测以及安全性能是否符合国家标准的要求；
(4)产品包装处理
将步骤(2)得到的抗菌消毒棉，进行包装，密封保存，该产品就是抗菌消毒棉，其可以用来制备棉签或者直接使用。
进一步，所述的漂洗液为，将质量份数为10-20份的次氯酸钠、1-5份的亚硫酸氢钠、8-12份的次氯酸钾、100-300份的蒸馏水进行混合均匀后制备而得到的物质。
进一步，所述的催化剂为，将10-20份的对甲基苯磺酸、1-2份盐酸、4-6份的硫酸进行混合制备得到的物质。
进一步，所述的抗菌剂为，将1-2份的碘、1-3份的碘化钾、30-50份的乙醇溶液进行混合均匀后而制备得到的物质。
进一步，所述步骤(2)中反应的温度为，40-60℃，且在反应过程中远离火源。
进一步，所述的十二烷基磺酸钠溶剂为，在50-60℃的反应釜中将质量份数为10-20份十二烷基磺酸钠、10-20份的酒精、20-30份的蒸馏水进行混合均匀后制备得到的物质。
进一步，所述的双氧水为质量分数在20-30％的双氧水。
进一步，所述的抗菌消毒棉的制备过程是在干净无菌的室内进行生产制备的。
有益效益
1、本发明通过加入2,4-二甲醛苯甲酸，利用其羧基和棉花上的羟基进行酯化反应，有效的将1-2份的2,4-二甲醛苯甲酸接枝到了棉花的纤维素上，有效的提高了抗菌消毒棉的抗菌时间；
2、本发明通过加入抗菌剂，从而有效的加强了该消毒棉的抗菌效果；
3、本发明通过利用紫外线杀菌效果，有效的保证了，抗菌消毒棉的无菌性，以及通过加入双氧水有效的提高了其消毒效果。
具体实施方式
为了使本发明的目的、技术方案和有益效果更加清楚，下面将结合实验数据，对本发明的优选实施例进行详细的说明，以方便技术人员理解。
实施例1
一种抗菌消毒棉的制备方法包括以下步骤：
(1)改性棉花的制备
将市场购买的棉花进行清理，除去杂质，然后将棉花浸泡在浓度为5％的漂洗液中进行漂洗3小时，除去漂洗液，用清水进行清洗3次后将棉花进行烘干得到干燥的棉花，然后将该棉花放置在紫外光照射发生器中进行紫外线杀菌12小时后取出棉花，称取质量份数为120份的棉花，加入反应釜中，然后加入300份的工业酒精、1份的2,4-二甲醛苯甲酸、0.1份的催化剂、1份的十二烷基磺酸钠溶剂进行回流反应4小时，其中反应釜温度控制在80℃，待反应完全后，将得到物质进行干燥除去酒精溶剂，得到干燥的棉花，此棉花就是改性棉；
(2)消毒棉的制备
将步骤(1)中制备的改性棉，称取质量份数为120加入反应釜中，然后加入20份双氧水、5份的抗菌剂进行浸泡20小时后，取出，进行干燥得到的物质就是抗菌消毒棉；
(3)产品消毒性能检测
将得到的产品进行检测，测试其细菌含量，抗菌性能检测以及安全性能是否符合国家标准的要求；
(4)产品包装处理
将步骤(2)得到的抗菌消毒棉，进行包装，密封保存，该产品就是抗菌消毒棉，其可以用来制备棉签或者直接使用。
作为优选，所述的漂洗液为，将质量份数为20份的次氯酸钠、3份的亚硫酸氢钠、10份的次氯酸钾、200份的蒸馏水进行混合均匀后制备而得到的物质。
作为优选，所述的催化剂为，将15份的对甲基苯磺酸、1份盐酸、4份的硫酸进行混合制备得到的物质。
作为优选，所述的抗菌剂为，将1份的碘、3份的碘化钾、35份的乙醇溶液进行混合均匀后而制备得到的物质。
作为优选，所述步骤(2)中反应的温度为，50℃，且在反应过程中远离火源。
作为优选，所述的十二烷基磺酸钠溶剂为，在50℃的反应釜中将质量份数为10份十二烷基磺酸钠、12份的酒精、30份的蒸馏水进行混合均匀后制备得到的物质。
实施例2
一种抗菌消毒棉的制备方法包括以下步骤：
(1)改性棉花的制备
将市场购买的棉花进行清理，除去杂质，然后将棉花浸泡在浓度为8％的漂洗液中进行漂洗5小时，除去漂洗液，用清水进行清洗3次后将棉花进行烘干得到干燥的棉花，然后将该棉花放置在紫外光照射发生器中进行紫外线杀菌20小时后取出棉花，称取质量份数为120份的棉花，加入反应釜中，然后加入400份的工业酒精、1份的2,4-二甲醛苯甲酸、0.2份的催化剂、2份的十二烷基磺酸钠溶剂进行回流反应4小时，其中反应釜温度控制在100℃，待反应完全后，将得到物质进行干燥除去酒精溶剂，得到干燥的棉花，此棉花就是改性棉；
(2)消毒棉的制备
将步骤(1)中制备的改性棉，称取质量份数为110加入反应釜中，然后加入12份双氧水、4份的抗菌剂进行浸泡20小时后，取出，进行干燥得到的物质就是抗菌消毒棉；
(3)产品消毒性能检测
将得到的产品进行检测，测试其细菌含量，抗菌性能检测以及安全性能是否符合国家标准的要求；
(4)产品包装处理
将步骤(2)得到的抗菌消毒棉，进行包装，密封保存，该产品就是抗菌消毒棉，其可以用来制备棉签或者直接使用。
作为优选，所述的漂洗液为，将质量份数为15份的次氯酸钠、3份的亚硫酸氢钠、10份的次氯酸钾、200份的蒸馏水进行混合均匀后制备而得到的物质。
作为优选，所述的催化剂为，将15份的对甲基苯磺酸、2份盐酸、4份的硫酸进行混合制备得到的物质。
作为优选，所述的抗菌剂为，将1份的碘、1份的碘化钾、30份的乙醇溶液进行混合均匀后而制备得到的物质。
作为优选，所述步骤(2)中反应的温度为，60℃，且在反应过程中远离火源。
作为优选，所述的十二烷基磺酸钠溶剂为，在55℃的反应釜中将质量份数为15份十二烷基磺酸钠、15份的酒精、25份的蒸馏水进行混合均匀后制备得到的物质。
实施例3
一种抗菌消毒棉的制备方法包括以下步骤：
(1)改性棉花的制备
将市场购买的棉花进行清理，除去杂质，然后将棉花浸泡在浓度为10％的漂洗液中进行漂洗3小时，除去漂洗液，用清水进行清洗2-3次后将棉花进行烘干得到干燥的棉花，然后将该棉花放置在紫外光照射发生器中进行紫外线杀菌20小时后取出棉花，称取质量份数为120份的棉花，加入反应釜中，然后加入350份的工业酒精、1份的2,4-二甲醛苯甲酸、0.1份的催化剂、2份的十二烷基磺酸钠溶剂进行回流反应4小时，其中反应釜温度控制在80℃，待反应完全后，将得到物质进行干燥除去酒精溶剂，得到干燥的棉花，此棉花就是改性棉；(2)消毒棉的制备
将步骤(1)中制备的改性棉，称取质量份数为110加入反应釜中，然后加入18份双氧水、3份的抗菌剂进行浸泡16小时后，取出，进行干燥得到的物质就是抗菌消毒棉；
(3)产品消毒性能检测
将得到的产品进行检测，测试其细菌含量，抗菌性能检测以及安全性能是否符合国家标准的要求；
(4)产品包装处理
将步骤(2)得到的抗菌消毒棉，进行包装，密封保存，该产品就是抗菌消毒棉，其可以用来制备棉签或者直接使用。
作为优选，所述的漂洗液为，将质量份数为18份的次氯酸钠、5份的亚硫酸氢钠、10份的次氯酸钾、250份的蒸馏水进行混合均匀后制备而得到的物质。
作为优选，所述的催化剂为，将18份的对甲基苯磺酸、2份盐酸、4份的硫酸进行混合制备得到的物质。
作为优选，所述的抗菌剂为，将1份的碘、1份的碘化钾、40份的乙醇溶液进行混合均匀后而制备得到的物质。
作为优选，所述步骤(2)中反应的温度为，50℃，且在反应过程中远离火源。
作为优选，所述的十二烷基磺酸钠溶剂为，在60℃的反应釜中将质量份数为12份十二烷基磺酸钠、10份的酒精、30份的蒸馏水进行混合均匀后制备得到的物质。
实施例4
一种抗菌消毒棉的制备方法包括以下步骤：
(1)改性棉花的制备
将市场购买的棉花进行清理，除去杂质，然后将棉花浸泡在浓度为6％的漂洗液中进行漂洗5小时，除去漂洗液，用清水进行清洗3次后将棉花进行烘干得到干燥的棉花，然后将该棉花放置在紫外光照射发生器中进行紫外线杀菌18小时后取出棉花，称取质量份数为120份的棉花，加入反应釜中，然后加入350份的工业酒精、1.2份的2,4-二甲醛苯甲酸、0.15份的催化剂、1份的十二烷基磺酸钠溶剂进行回流反应3小时，其中反应釜温度控制在80℃，待反应完全后，将得到物质进行干燥除去酒精溶剂，得到干燥的棉花，此棉花就是改性棉；(2)消毒棉的制备
将步骤(1)中制备的改性棉，称取质量份数为100加入反应釜中，然后加入16份双氧水、5份的抗菌剂进行浸泡20小时后，取出，进行干燥得到的物质就是抗菌消毒棉；
(3)产品消毒性能检测
将得到的产品进行检测，测试其细菌含量，抗菌性能检测以及安全性能是否符合国家标准的要求；
(4)产品包装处理
将步骤(2)得到的抗菌消毒棉，进行包装，密封保存，该产品就是抗菌消毒棉，其可以用来制备棉签或者直接使用。
作为优选，所述的漂洗液为，将质量份数为10份的次氯酸钠、5份的亚硫酸氢钠、12份的次氯酸钾、180份的蒸馏水进行混合均匀后制备而得到的物质。
作为优选，所述的催化剂为，将12份的对甲基苯磺酸、2份盐酸、4份的硫酸进行混合制备得到的物质。
作为优选，所述的抗菌剂为，将2份的碘、3份的碘化钾、50份的乙醇溶液进行混合均匀后而制备得到的物质。
作为优选，所述步骤(2)中反应的温度为，40℃，且在反应过程中远离火源。
作为优选，所述的十二烷基磺酸钠溶剂为，在50℃的反应釜中将质量份数为12份十二烷基磺酸钠、20份的酒精、30份的蒸馏水进行混合均匀后制备得到的物质。
实验分析：
1、抗菌消毒棉无菌检测
将本发明制备的产品和市场购买的抗菌棉，按照国标GB/T4789.12和GB/T4789.28-2003的检测标准进行无菌检测，其检测结果如下：
从图表中，我们可以看出本产品达到商用无菌状态的物质。
2、抗菌消毒棉抗菌时间
将本发明制备的产品和市场购买的抗菌棉，分别取适量的放置于相同的环境中，然后使其暴露在空气中，然后每天采集一次样，检测其是否有微生物的生长，查到其有微生物时停止实验，通过利用显微镜观察，其测试结果如下表：
从图表中可以看出，本发明制备的抗菌棉较市场购买的抗菌棉具有很好的抗菌效果。
最后说明的是，以上优选实施例仅用于说明本发明的技术方案而非限制，尽管通过上述优选实施例已经对本发明进行了详细的描述，但本领域技术人员应当理解，可以在形式上和细节上对其作出各种各样的改变，而不偏离本发明权利要求书所限定的。
Claims (8)
1.一种抗菌消毒棉的制备方法，其特征在于,所述抗菌消毒棉的制备方法如下：
(1)改性棉花的制备
将市场购买的棉花进行清理，除去杂质，然后将棉花浸泡在浓度为5-10％的漂洗液中进行漂洗1-5小时，除去漂洗液，用清水进行清洗2-3次后将棉花进行烘干得到干燥的棉花，然后将该棉花放置在紫外光照射发生器中进行紫外线杀菌10-20小时后取出棉花，称取质量份数为100-120份的棉花，加入反应釜中，然后加入300-400份的工业酒精、1-2份的2,4-二甲醛苯甲酸、0.1-0.2份的催化剂、1-2份的十二烷基磺酸钠溶剂进行回流反应2-4小时，其中反应釜温度控制在80-100℃，待反应完全后，将得到物质进行干燥除去酒精溶剂，得到干燥的棉花，此棉花就是改性棉；
(2)消毒棉的制备
将步骤(1)中制备的改性棉，称取质量份数为100-120加入反应釜中，然后加入10-20份双氧水、1-5份的抗菌剂进行浸泡10-20小时后，取出，进行干燥得到的物质就是抗菌消毒棉；
(3)产品消毒性能检测
将得到的产品进行检测，测试其细菌含量，抗菌性能检测以及安全性能是否符合国家标准的要求；
(4)产品包装处理
将步骤(2)得到的抗菌消毒棉，进行包装，密封保存，该产品就是抗菌消毒棉，其可以用来制备棉签或者直接使用。
2.根据权利要求1所述的一种抗菌消毒棉的制备方法，其特征在于，所述的漂洗液为，将质量份数为10-20份的次氯酸钠、1-5份的亚硫酸氢钠、8-12份的次氯酸钾、100-300份的蒸馏水进行混合均匀后制备而得到的物质。
3.根据权利要求1所述的一种抗菌消毒棉的制备方法，其特征在于，所述的催化剂为，将10-20份的对甲基苯磺酸、1-2份盐酸、4-6份的硫酸进行混合制备得到的物质。
4.根据权利要求1所述的一种抗菌消毒棉的制备方法，其特征在于，所述的抗菌剂为，将1-2份的碘、1-3份的碘化钾、30-50份的乙醇溶液进行混合均匀后而制备得到的物质。
5.根据权利要求1所述的一种抗菌消毒棉的制备方法，其特征在于，所述步骤(2)中反应的温度为，40-60℃，且在反应过程中远离火源。
6.根据权利要求1所述的一种抗菌消毒棉的制备方法，其特征在于，所述的十二烷基磺酸钠溶剂为，在50-60℃的反应釜中将质量份数为10-20份十二烷基磺酸钠、10-20份的酒精、20-30份的蒸馏水进行混合均匀后制备得到的物质。
7.根据权利要求1所述的一种抗菌消毒棉的制备方法，其特征在于，所述的双氧水为质量分数在20-30％的双氧水。
8.根据权利要求1所述的一种抗菌消毒棉的制备方法，其特征在于，所述的抗菌消毒棉的制备过程是在干净无菌的室内进行生产制备的。