CN108975878A - heat resisting porcelain and preparation method thereof - Google Patents
heat resisting porcelain and preparation method thereof Download PDFInfo
- Publication number
- CN108975878A CN108975878A CN201811040502.1A CN201811040502A CN108975878A CN 108975878 A CN108975878 A CN 108975878A CN 201811040502 A CN201811040502 A CN 201811040502A CN 108975878 A CN108975878 A CN 108975878A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- heat resisting
- porcelain
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heat resisting porcelain and preparation method thereof, the component and each component mass parts contained in porcelain used in heat resisting porcelain is as follows: 30~35 parts of kaolin;50~55 parts of petalite;20~25 parts of spodumene;Quartz: 4~5 parts.Inventive formulation is scientific and reasonable, interacts between each component, improves product quality, can will not generate and burst at 400 DEG C or so, improve its service life.
Description
Technical field
The present invention relates to a kind of heat resisting porcelains and preparation method thereof.
Background technique
Currently, high-temperature heat-resistance porcelain is a kind of porcelain, it is placed on electromagnetic oven and boils water, can be used for steeping kung fu tea, it is easy,
Fast, but general porcelain is unable to high temperature resistant, and reaching 200 DEG C will burst.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of heat resisting porcelain is provided, its formula section
It learns rationally, interacts between each component, improve product quality, can will not generate and burst at 400 DEG C or so, improve
Its service life.
In order to solve the above-mentioned technical problem, the technical scheme is that a kind of heat resisting porcelain, contain in porcelain used in it
Some components and each component mass parts are as follows:
30~35 parts of kaolin;
50~55 parts of petalite;
20~25 parts of spodumene;
Quartz: 4~5 parts.
The present invention also provides a kind of preparation method of heat resisting porcelain, the step of method in contain:
S1: it stocks up according to each component and each component mass parts;
S2: by material: ball: mass ratio=1:1.2:1 of water, wet ball grinding 15 hours~20 hours, then by except iron and
After sieving, slurry is obtained;
S3: it is formed using slurry;
S4: and then firing finished product.
Further, in step s 2, slurry fineness is that 10000-hole sieve tails between 1~1.5%.
After above-mentioned technical proposal, formula is scientific and reasonable for heat resisting porcelain of the invention, interacts between each component, mentions
Product quality has been risen, can will not generate and burst at 400 DEG C or so, improve its service life.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one
A kind of heat resisting porcelain, the component and each component mass parts contained in porcelain used in it are as follows:
30 parts of kaolin;
50 parts of petalite;
20 parts of spodumene;
Quartz: 4 parts.
Contain in the step of preparation method of the heat resisting porcelain, method:
S1: it stocks up according to each component and each component mass parts;
S2: by material: ball: mass ratio=1:1.2:1 of water wet ball grinding 15 hours, then after except iron and sieving, is obtained
To slurry;
S3: it is formed using slurry;
S4: and then firing finished product.
In step s 2, slurry fineness is that 10000-hole sieve tails between 1%~1.5%.
Embodiment two
A kind of heat resisting porcelain, the component and each component mass parts contained in porcelain used in it are as follows:
35 parts of kaolin;
55 parts of petalite;
25 parts of spodumene;
Quartz: 5 parts.
Contain in the step of preparation method of the heat resisting porcelain, method:
S1: it stocks up according to each component and each component mass parts;
S2: by material: ball: mass ratio=1:1.2:1 of water wet ball grinding 20 hours, then after except iron and sieving, is obtained
To slurry;
S3: it is formed using slurry;
S4: and then firing finished product.
In step s 2, slurry fineness is that 10000-hole sieve tails between 1~1.5%.
Embodiment three
A kind of heat resisting porcelain, the component and each component mass parts contained in porcelain used in it are as follows:
32 parts of kaolin;
52 parts of petalite;
22 parts of spodumene;
Quartz: 4 parts.
Contain in the step of preparation method of the heat resisting porcelain, method:
S1: it stocks up according to each component and each component mass parts;
S2: by material: ball: mass ratio=1:1.2:1 of water wet ball grinding 18 hours, then after except iron and sieving, is obtained
To slurry;
S3: it is formed using slurry;
S4: and then firing finished product.
In step s 2, slurry fineness is that 10000-hole sieve tails between 1~1.5%.
The heat resisting porcelain that three above embodiment is prepared is placed on electromagnetic oven in use, when temperature reaches 500 DEG C
When, it does not burst, high temperature resistance is good, meets design requirement.
Particular embodiments described above, pair present invention solves the technical problem that, technical scheme and beneficial effects carry out
It is further described, it should be understood that the above is only a specific embodiment of the present invention, is not limited to this
Invention, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should be included in this hair
Within bright protection scope.
Claims (3)
1. a kind of heat resisting porcelain, it is characterised in that the component and each component mass parts contained in porcelain used in it is as follows:
30~35 parts of kaolin;
50~55 parts of petalite;
20~25 parts of spodumene;
Quartz: 4~5 parts.
2. a kind of preparation method of heat resisting porcelain as described in claim 1, it is characterised in that contain in the step of method:
S1: it stocks up according to each component and each component mass parts;
S2: by material: ball: mass ratio=1:1.2:1 of water, wet ball grinding 15 hours~20 hours, then by removing iron and sieving
Afterwards, slurry is obtained;
S3: it is formed using slurry;
S4: and then firing finished product.
3. preparation method according to claim 2, it is characterised in that: in step s 2, slurry fineness tails over for 10000-hole sieve
Between 1~1.5%.