CN108950834A - A kind of preparation method of high abrasion anti-pilling 4D air layer Q elasticity fabric - Google Patents
A kind of preparation method of high abrasion anti-pilling 4D air layer Q elasticity fabric Download PDFInfo
- Publication number
- CN108950834A CN108950834A CN201810938473.4A CN201810938473A CN108950834A CN 108950834 A CN108950834 A CN 108950834A CN 201810938473 A CN201810938473 A CN 201810938473A CN 108950834 A CN108950834 A CN 108950834A
- Authority
- CN
- China
- Prior art keywords
- fabric
- yarn
- flotation line
- pilling
- tunnels
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation method of high abrasion anti-pilling 4D air layer Q elasticity fabric is related to a kind of preparation method for being knitted fabric, and it further includes following steps, step A: weaving fabric that fabric, which includes surface layer yarn, intermediate yarn and bottom yarn,;Step B: fabric blank is subjected to pre-setting;Step C: rinsing fabric blank, and rinsing liquid includes 0.5 g/l ~ 1g/l hydrogen peroxide when rinsing;Step D: fabric blank is dyed;Step E: fabric blank is dried;Step F: multiple sizing is carried out to fabric blank.Compared with prior art, there is good warming effect by the woven fabric of this method, also has the characteristics that the good and certain tensile ductility of high abrasion, anti pilling, taking.
Description
Technical field
The present invention relates to a kind of preparation method for being knitted fabric, especially a kind of preparation methods of air layer face fabric.
Background technique
Air layer face fabric designs the fabric construction using inner, domestic and abroad three pieces by structure, to form air in the fabric
Interlayer plays warming effect.It can use double-layered structure in woven fabric, add a system again between table back warp, weft yarn
Warp thread or weft yarn, then in being formed, in, outer three layers of sandwich type structure, intermediate one layer it is using bulkiness good, elasticity is good
It fills yarn and reaches warming effect to form still air layer.Air layer face fabric will not generate fold, and liquid-sky can be absorbed
Gas-bearing formation fabric is using three-decker, and intermediate gaps are big, and surface is purified cotton cloth, also has effects that the water lock that absorbs water.It passes at present
Although system air layer face fabric have the advantages that keep warm, it is not wrinkled, as the improvement of people's living standards, to sportswear
The requirement of fabric is also higher and higher, has been unable to satisfy consumer demand only according to two above advantage.And conventional air level
Expect that wearability and anti pilling property can be poor, and thickness also has certain limitation, comfortable flexibility is also to be improved.
Summary of the invention
The present invention aiming at the shortcomings in the prior art, provides a kind of system of high abrasion anti-pilling 4D air layer Q elasticity fabric
Preparation Method has good warming effect by the woven fabric of this method, also has high abrasion, anti pilling, taking good
The characteristics of and certain tensile ductility.
In order to solve the above-mentioned technical problem, a kind of preparation method of high abrasion anti-pilling 4D air layer Q elasticity fabric, fabric packet
Surface layer yarn, intermediate yarn and bottom yarn are included, further includes following steps, step A: chooses terylene as bottom yarn raw material, choose
Terylene and spandex are blended as intermediate yarn raw material, choose cotton yarn and spandex is blended as surface layer yarn raw material, then set by weaving
The standby fabric blank knitted by surface layer yarn, intermediate yarn and bottom weaving yarns at air interlayer, wherein in the three-legged structure on 6 tunnels, 1,
4 tunnels are surface layer yarn, and the 1st tunnel is flotation line, tuck, tuck, flotation line weaving structure circulation, and the 4th tunnel is tuck, flotation line, flotation line, tuck
Weaving structure circulation, 2,5 tunnels be intermediate yarn, the 2nd tunnel be lopping, lopping, flotation line, flotation line weaving structure circulation, the 5th tunnel be at
Circle, lopping, flotation line, flotation line weaving structure circulation, 3,6 tunnels are bottom yarn, and the 3rd tunnel is flotation line, flotation line, lopping, lopping weaving
Structured loop, the 6th tunnel are flotation line, flotation line, lopping, lopping weaving structure circulation;Step B: fabric blank is subjected to pre-setting;Step
Rapid C: rinsing fabric blank, and rinsing liquid includes 0.5 g/l ~ 1g/l hydrogen peroxide when rinsing;Step D: to fabric blank
It is dyed;Step E: fabric blank is dried;Step F: multiple sizing is carried out to fabric blank, is obtained after multiple sizing
High abrasion anti-pilling 4D air layer Q elasticity fabric.
In above-mentioned technical proposal, it is preferred that in step B pre-setting, at 180 DEG C ~ 200 DEG C, speed exists pre-setting temperature
The m/min of 10m/min ~ 30, overfeeding is than 10% ~ 40%.
In above-mentioned technical proposal, it is preferred that in step C rinsing, rinsing liquid further includes the defoaming of 0.1g/L ~ 1g/L non-silicon
Agent, 1g/L ~ 2g/L refining dye one-bath deoiling agent, 0.1g/L ~ 1g/L glacial acetic acid, 0.1g/L ~ 1g/L piece alkali.
In above-mentioned technical proposal, it is preferred that when step D dyes fabric blank, fabric fabric needs are immersed in
In dyeing liquor, 1 ~ 8:10 of bath raio of fabric fabric and dyeing liquor, dyeing temperature is 90 DEG C ~ 100 DEG C, and the processing time is 50min ~ 70
Min further includes 1g/L ~ 3g/L chelating agent, 2 g/L ~ 4g/L Disperse Leveler, 2% (owf) ~ 4% (owf) soft in dyeing
Agent and 1% (owf) ~ 7% (owf) KY dye of positive ion.
In above-mentioned technical proposal, it is preferred that when step E dries fabric blank, opposite material base cloth is vibrated
Drying, 100 DEG C ~ 120 DEG C of drying temperature, 15 m/min -20m/min of speed.
In above-mentioned technical proposal, it is preferred that when step F carries out multiple sizing to fabric blank, setting temperature 110 DEG C ~ 130
DEG C, speed 10m/min ~ 30m/min, overfeeding ratio 25%-35%,
In above-mentioned technical proposal, it is preferred that in step, 40SJCF (C)+40D spandex silk blend, the choosing of 2,5 tunnels are selected in 1,4 tunnels
With 100D/144F (DTY) (A)+40D spandex silk blend, 30D/1F (FDY) (B) terylene is selected on 3,6 tunnels.
Fabric of the present invention by structure design using it is inner, in, outer three layers of fabric construction, using paraphysis by upper and lower two
Surface layer is joined together to form sandwich structure.Air interlayer is formed in the fabric, using the smallest principle of air conduction coefficient,
Human body and extraneous insulating effect are played, to reach superior warming effect, while spandex is added in fabric, so that fabric has
Certain tensile ductility.
Compared with prior art, there is good warming effect by the woven fabric of this method, also there is high abrasion, resist
The good feature of pilling, taking and certain tensile ductility.
Detailed description of the invention
Fig. 1 is the cam chart of the embodiment of the present invention 1, embodiment 2 and embodiment 3.
Fig. 2 is the knitting arrangement figure of the embodiment of the present invention 1, embodiment 2 and embodiment 3.
Specific embodiment
Present invention is further described in detail with specific embodiment with reference to the accompanying drawing.
Embodiment 1, as depicted in figs. 1 and 2, a kind of preparation method of high abrasion anti-pilling 4D air layer Q elasticity fabric, face
Material includes surface layer yarn, intermediate yarn and bottom yarn, further includes following steps, step A: choose terylene as bottom yarn raw material,
It chooses terylene and spandex is blended as intermediate yarn raw material, choose cotton yarn and spandex is blended as surface layer yarn raw material, then by knitting
Manufacturing apparatus knits the fabric blank by surface layer yarn, intermediate yarn and bottom weaving yarns at air interlayer, wherein the three-legged structure on 6 tunnels
In, 1,4 tunnels are surface layer yarn, and the 1st tunnel is flotation line, tuck, tuck, flotation line weaving structure circulation, and the 4th tunnel is tuck, flotation line, floats
Line, tuck weaving structure circulation, 2,5 tunnels be intermediate yarn, the 2nd tunnel be lopping, lopping, flotation line, flotation line weaving structure circulation, the 5th
Road be lopping, lopping, flotation line, flotation line weaving structure circulation, 3,6 tunnels be bottom yarn, the 3rd tunnel be flotation line, flotation line, lopping, at
Weaving structure circulation is enclosed, the 6th tunnel is flotation line, flotation line, lopping, lopping weaving structure circulation;1,40SJCF (C)+40D is selected on 4 tunnels
100D/144F (DTY) (A)+40D spandex silk blend is selected on spandex silk blend, 2,5 tunnels, and 30D/1F (FDY) is selected on 3,6 tunnels
(B) terylene.
Step B: fabric blank is subjected to pre-setting;Pre-setting temperature is at 180 DEG C, and speed is in 10m/min, and overfeeding is than 10%.
Step C: rinsing fabric blank, when rinsing rinsing liquid include the hydrogen peroxide of 0.5 g/l, 0.1g/L non-silicon defoaming agent,
1g/L refining dye one-bath deoiling agent, 0.1g/L glacial acetic acid, 0.1g/L piece alkali.Step D: fabric blank is dyed;Fabric base
Cloth needs to be immersed in dyeing liquor, the bath raio 1 ~ 8 of fabric fabric and dyeing liquor, dyeing temperature be 90 DEG C, processing the time be
50min further includes 1g/L chelating agent, 2 g/L Disperse Levelers, 2% (owf) softening agent and 1% (owf) KY sun in dyeing from
Sub- dyestuff.Step E: fabric blank is dried;Opposite material base cloth progress vibration drying, 100 DEG C of drying temperature, speed 15
m/min.Step F: multiple sizing is carried out to fabric blank, 110 DEG C of setting temperature, speed 10m/min, overfeeding is than 25%.
Embodiment 2, as depicted in figs. 1 and 2, a kind of preparation method of high abrasion anti-pilling 4D air layer Q elasticity fabric, face
Material includes surface layer yarn, intermediate yarn and bottom yarn, further includes following steps, step A: choose terylene as bottom yarn raw material,
It chooses terylene and spandex is blended as intermediate yarn raw material, choose cotton yarn and spandex is blended as surface layer yarn raw material, then by knitting
Manufacturing apparatus knits the fabric blank by surface layer yarn, intermediate yarn and bottom weaving yarns at air interlayer, wherein the three-legged structure on 6 tunnels
In, 1,4 tunnels are surface layer yarn, and the 1st tunnel is flotation line, tuck, tuck, flotation line weaving structure circulation, and the 4th tunnel is tuck, flotation line, floats
Line, tuck weaving structure circulation, 2,5 tunnels be intermediate yarn, the 2nd tunnel be lopping, lopping, flotation line, flotation line weaving structure circulation, the 5th
Road be lopping, lopping, flotation line, flotation line weaving structure circulation, 3,6 tunnels be bottom yarn, the 3rd tunnel be flotation line, flotation line, lopping, at
Weaving structure circulation is enclosed, the 6th tunnel is flotation line, flotation line, lopping, lopping weaving structure circulation;1,40SJCF (C)+40D is selected on 4 tunnels
100D/144F (DTY) (A)+40D spandex silk blend is selected on spandex silk blend, 2,5 tunnels, and 30D/1F (FDY) is selected on 3,6 tunnels
(B) terylene.
Step B: fabric blank is subjected to pre-setting;Pre-setting temperature is at 190 DEG C, and speed is in 20 m/min, overfeeding ratio
25%.Step C: rinsing fabric blank, and rinsing liquid includes the hydrogen peroxide of 0.7g/l, the defoaming of 0.5g/L non-silicon when rinsing
Agent, 1.5g/L refining dye one-bath deoiling agent, 0.5g/L glacial acetic acid, 0.5g/L piece alkali.
Step D: fabric blank is dyed;Fabric fabric needs to be immersed in dyeing liquor, fabric fabric and dyeing liquor
Bath raio 1 ~ 9, dyeing temperature is 95 DEG C, and the processing time is 60 min, further include in dyeing 2g/L chelating agent, 3g/L disperse it is even
Stain, 3% (owf) softening agent and 4% (owf) KY dye of positive ion.Step E: fabric blank is dried;Opposite material base
Cloth progress vibration drying, 120 DEG C of drying temperature, speed 17m/min.Step F: multiple sizing, setting temperature are carried out to fabric blank
120 DEG C, speed 20m/min, overfeeding is than 30%.
Embodiment 3, as depicted in figs. 1 and 2, a kind of preparation method of high abrasion anti-pilling 4D air layer Q elasticity fabric, face
Material includes surface layer yarn, intermediate yarn and bottom yarn, further includes following steps, step A: choose terylene as bottom yarn raw material,
It chooses terylene and spandex is blended as intermediate yarn raw material, choose cotton yarn and spandex is blended as surface layer yarn raw material, then by knitting
Manufacturing apparatus knits the fabric blank by surface layer yarn, intermediate yarn and bottom weaving yarns at air interlayer, wherein the three-legged structure on 6 tunnels
In, 1,4 tunnels are surface layer yarn, and the 1st tunnel is flotation line, tuck, tuck, flotation line weaving structure circulation, and the 4th tunnel is tuck, flotation line, floats
Line, tuck weaving structure circulation, 2,5 tunnels be intermediate yarn, the 2nd tunnel be lopping, lopping, flotation line, flotation line weaving structure circulation, the 5th
Road be lopping, lopping, flotation line, flotation line weaving structure circulation, 3,6 tunnels be bottom yarn, the 3rd tunnel be flotation line, flotation line, lopping, at
Weaving structure circulation is enclosed, the 6th tunnel is flotation line, flotation line, lopping, lopping weaving structure circulation;1,40SJCF (C)+40D is selected on 4 tunnels
100D/144F (DTY) (A)+40D spandex silk blend is selected on spandex silk blend, 2,5 tunnels, and 30D/1F (FDY) is selected on 3,6 tunnels
(B) terylene.
Step B: fabric blank is subjected to pre-setting;Pre-setting temperature is at 200 DEG C, and speed is in 30 m/min, overfeeding ratio
40%.Step C: rinsing fabric blank, and rinsing liquid includes the hydrogen peroxide of 1g/l, 1g/L non-silicon defoaming agent, 2g/ when rinsing
L refining dye one-bath deoiling agent, 1g/L glacial acetic acid, 1g/L piece alkali.Step D: fabric blank is dyed;Fabric fabric needs to immerse
Into dyeing liquor, the bath raio 1 ~ 10 of fabric fabric and dyeing liquor, dyeing temperature is 100 DEG C, and the processing time is 70 min, in dyeing
It further include 3g/L chelating agent, 4g/L Disperse Leveler, 4% (owf) softening agent and 7% (owf) KY dye of positive ion.Step E:
Fabric blank is dried;Opposite material base cloth progress vibration drying, 120 DEG C of drying temperature, speed 20m/min.Step F: right
Fabric blank carries out multiple sizing, and 130 DEG C of setting temperature, speed 30m/min, overfeeding is than 35%.
Claims (7)
1. a kind of preparation method of high abrasion anti-pilling 4D air layer Q elasticity fabric, it is characterized in that, fabric includes surface layer yarn, centre
Yarn and bottom yarn, further include following steps,
Step A: choose terylene be used as bottom yarn raw material, choose terylene and spandex it is blended be used as intermediate yarn raw material, choose cotton yarn with
Spandex is blended to be used as surface layer yarn raw material, is then knitted by fabric manufacture equipment and presss from both sides surface layer yarn, intermediate yarn and bottom weaving yarns at air
The fabric blank of layer, wherein in the three-legged structure on 6 tunnels, 1,4 tunnels are surface layer yarn, and the 1st tunnel is flotation line, tuck, tuck, flotation line
Weaving structure circulation, the 4th tunnel be tuck, flotation line, flotation line, tuck weaving structure circulation, 2,5 tunnels be intermediate yarn, the 2nd tunnel be at
Circle, lopping, flotation line, flotation line weaving structure circulation, the 5th tunnel are lopping, lopping, flotation line, flotation line weaving structure circulation, 3,6 tunnels
For bottom yarn, the 3rd tunnel is flotation line, flotation line, lopping, lopping weaving structure circulation, and the 6th tunnel is that flotation line, flotation line, lopping, lopping are knitted
Make structured loop;
Step B: fabric blank is subjected to pre-setting;
Step C: rinsing fabric blank, and rinsing liquid includes 0.5 g/l ~ 1g/l hydrogen peroxide when rinsing;
Step D: fabric blank is dyed;
Step E: fabric blank is dried;
Step F: multiple sizing is carried out to fabric blank, obtains high abrasion anti-pilling 4D air layer Q elasticity fabric after multiple sizing.
2. a kind of preparation method of high abrasion anti-pilling 4D air layer Q elasticity fabric according to claim 1, it is characterized in that,
In step B pre-setting, pre-setting temperature is at 180 DEG C ~ 200 DEG C, and speed is in the m/min of 10m/min ~ 30, and overfeeding is than 10% ~ 40%.
3. a kind of preparation method of high abrasion anti-pilling 4D air layer Q elasticity fabric according to claim 1, it is characterized in that,
Step C rinsing when, rinsing liquid further include 0.1g/L ~ 1g/L non-silicon defoaming agent, 1g/L ~ 2g/L refining dye one-bath deoiling agent,
0.1g/L ~ 1g/L glacial acetic acid, 0.1g/L ~ 1g/L piece alkali.
4. a kind of preparation method of high abrasion anti-pilling 4D air layer Q elasticity fabric according to claim 1, it is characterized in that,
When step D dyes fabric blank, fabric fabric needs to be immersed in dyeing liquor, the bath raio of fabric fabric and dyeing liquor
1 ~ 8:10, dyeing temperature are 90 DEG C ~ 100 DEG C, and the processing time is the min of 50min ~ 70, further include 1g/L ~ 3g/L chelating in dyeing
Agent, 2 g/L ~ 4g/L Disperse Leveler, 2% (owf) ~ 4% (owf) softening agent and 1% (owf) ~ 7% (owf) KY cation
Dyestuff.
5. a kind of preparation method of high abrasion anti-pilling 4D air layer Q elasticity fabric according to claim 1, it is characterized in that,
When step E dries fabric blank, opposite material base cloth progress vibration drying, 100 DEG C ~ 120 DEG C of drying temperature, speed 15
m/min -20m/min。
6. a kind of preparation method of high abrasion anti-pilling 4D air layer Q elasticity fabric according to claim 1, it is characterized in that,
When step F carries out multiple sizing to fabric blank, 110 DEG C ~ 130 DEG C of setting temperature, speed 10m/min ~ 30m/min, overfeeding ratio
25%-35%。
7. a kind of preparation method of high abrasion anti-pilling 4D air layer Q elasticity fabric according to claim 1, it is characterized in that,
It is characterized in that in step, 40SJCF (C)+40D spandex silk blend is selected on 1,4 tunnels, 100D/144F (DTY) is selected on 2,5 tunnels
(A) 30D/1F (FDY) (B) terylene is selected on+40D spandex silk blend, 3,6 tunnels.