CN108947338A - 一种蒸压加气混凝土砌块脱硫石膏 - Google Patents
一种蒸压加气混凝土砌块脱硫石膏 Download PDFInfo
- Publication number
- CN108947338A CN108947338A CN201810537746.4A CN201810537746A CN108947338A CN 108947338 A CN108947338 A CN 108947338A CN 201810537746 A CN201810537746 A CN 201810537746A CN 108947338 A CN108947338 A CN 108947338A
- Authority
- CN
- China
- Prior art keywords
- gypsum
- building block
- desulfurized gypsum
- concrete building
- aerated concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明专利公开了一种蒸压加气混凝土砌块脱硫石膏,包括按100%重量百分比计的以下原料:砂为51‑55%;废为6‑8%;废浆为9‑11%;石灰为7‑9%;水泥为12‑14%;石膏为6‑8%,其脱硫石膏的价格低于天然石膏的价格,但其对于蒸压加气混凝土生产所需要的化学数据指标要求并没有降低。虽然在产品制作过程中添加比列稍微有所提高,但还是降低了生产成本。
Description
技术领域
本发明涉及一种建筑材料,特别是一种蒸压加气混凝土砌块脱硫 石膏。
背景技术
石膏是蒸压加气混凝土砌块生产的主要原材料之一,但使用天然 石膏粉极大地增加了生产成本,用电厂的脱硫石膏来代替天然石膏其 好处在于:一、降低生产成本,其价格明显低于天然石膏;二、解决 电厂的固废问题。
发明专利内容
本发明专利所要解决的问题是提供一种降低生产成本和解决电 厂固废问题的一种蒸压加气混凝土砌块脱硫石膏。
为达到上述目的,本发明专利解决上述技术问题所采用的技术方 案是:一种蒸压加气混凝土砌块脱硫石膏,包括按100%重量百分比 计的以下原料:
砂为 51-55%;
废为 6-8%;
废浆为 9-11%;
石灰为 7-9%;
水泥为 12-14%;
石膏为 6-8%。
进一步,所述砂为 53.7%;
固废为 7%;
废浆为 10.1%;
石灰为 8.5%;
水泥为 13.7%;
石膏为 7%。
与现有技术相比,本发明专利的技术方案具有如下优点:
本发明专利所提供的一种蒸压加气混凝土砌块脱硫石膏,其脱硫 石膏的价格低于天然石膏的价格,但其对于蒸压加气混凝土生产所需 要的化学数据指标要求并没有降低。虽然在产品制作过程中添加比列 稍微有所提高,但还是降低了生产成本。
具体实施方式
下面结合实施例,对本发明专利的具体实施方式作进一步详细描 述。以下实施例用于说明本发明专利,但不用来限制本发明专利的范 围。
实施例1
本实施例所提供的一种蒸压加气混凝土砌块脱硫石膏,包括按 100%重量百分比计的以下原料:
砂为 51-55%;
废为 6-8%;
废浆为 9-11%;
石灰为 7-9%;
水泥为 12-14%;
石膏为 6-8%。
本实施例所提供的一种蒸压加气混凝土砌块脱硫石膏,其脱硫石 膏的价格低于天然石膏的价格,但其对于蒸压加气混凝土生产所需要 的化学数据指标要求并没有降低,虽然在产品制作过程中添加比列稍 微有所提高,但还是降低了生产成本。
实施例2
所述砂为 53.7%;
固废为 7%;
废浆为 10.1%;
石灰为 8.5%;
水泥为 13.7%;
石膏为 7%。
本实施例所提供的一种蒸压加气混凝土砌块脱硫石膏,其脱硫石 膏的价格低于天然石膏的价格,但其对于蒸压加气混凝土生产所需要 的化学数据指标要求并没有降低。虽然在产品制作过程中添加比列稍 微有所提高,但还是降低了生产成本。
以上所述仅是本发明专利的优选实施方式,应当指出,对于本技 术领域的普通技术人员来说,在不脱离本发明专利技术原理的前提 下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明专 利的保护范围。
Claims (2)
1.一种蒸压加气混凝土砌块脱硫石膏,其特征在于,包括按100%重量百分比计的以下原料:
砂为 51-55%;
废为 6-8%;
废浆为 9-11%;
石灰为 7-9%;
水泥为 12-14%;
石膏为 6-8%。
2.根据权利要求1所述的一种蒸压加气混凝土砌块脱硫石膏,其特征在于,
所述砂为 53.7%;
固废为 7%;
废浆为 10.1%;
石灰为 8.5%;
水泥为 13.7%;
石膏为 7%。