CN108866779A - A kind of tussah knitting fabric and its production technology - Google Patents
A kind of tussah knitting fabric and its production technology Download PDFInfo
- Publication number
- CN108866779A CN108866779A CN201810784865.XA CN201810784865A CN108866779A CN 108866779 A CN108866779 A CN 108866779A CN 201810784865 A CN201810784865 A CN 201810784865A CN 108866779 A CN108866779 A CN 108866779A
- Authority
- CN
- China
- Prior art keywords
- tussah
- fabric
- mixed yarn
- dye
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to textile technology fields, fabric and its production technology are knitted more particularly to a kind of tussah, the tussah is knitted fabric, it is made of mixed yarn and spandex filament, wherein, mixed yarn is formed by acrylic fiber, Modal fibre and tussah fiber blend, and spandex filament, acrylic fiber and Modal fibre can play good improvement result to wild silkworm silk fiber, and then substantially overcomes the disadvantage that tussah fabric lining in the prior art is at high price and washing nursing is troublesome.Through mixed yarn made of acrylic fiber, Modal fibre and tussah fiber blend, cooperateed with again with spandex filament tussah knitting fabric obtained have the advantages that washing nursing is convenient, feel it is fluffy it is soft it is glutinous, warmth retention property is excellent, moisture absorption is ventilative, it is comfortable and easy to wear to paste skin, and have effects that skin-protection and health-care.The production technology of the tussah has process simple, and production cost is low, and can be suitble to the characteristics of being mass produced.
Description
Technical field
The present invention relates to textile technology fields, and in particular to a kind of tussah knitting fabric and its production technology.
Background technique
Tussah is by getting in a kind of produced silk cocoon of tussah category wild silkworm, and this wild silkworm is mainly big in field by manually putting in a suitable place to breed
Among the toothed oak woods of mountain, it is food with toothed oak leaf.Due to the variability of weather, the anti-ultraviolet ability of tussah is significantly larger than silkworm,
And the protein of tussah and the content of amino acid are more than ten times of mulberry silk, tussah also contain water-wet side skirt amino acid,
Silk peptide, silk contracting amino acid etc. have the ingredient of skin-protection and health-care, wherein and water-wet side skirt amino acid can absorb the moisture in body surface, and
It is excluded, maintains human body dry and comfortable, keep comfortable, it is particularly useful to rheumatism, arthritis, skin disease；Silk peptide has extremely strong
Penetration can penetrate into skin matter layer, in conjunction with skin epidermal cells, and by cell as nutrient absorption, participate in and promote cell
Metabolism, provides required nutrient for its metabolism, moreover it is possible to repair the skin damaged；Silk contracting amino acid can inhibit junket in skin
The activity of propylhomoserin enzyme so that tyrosinase be inhibited to generate melanin, therefore has effects that whitening.But there is also not for tussah
Foot, low output and at high price, there are process complexity, washing nursing for tussah knitting fabric especially in the prior art
Defect very troublesome.
Summary of the invention
It is an object of the present invention in view of the deficiencies of the prior art, provide a kind of tussah knitting fabric, the wild silkworm
Silk knitting fabric have washing nursing is convenient, feel it is fluffy it is soft it is glutinous, that warmth retention property is excellent, moisture absorption is ventilative, to paste skin comfortable and easy to wear is excellent
Point, and have effects that skin-protection and health-care.
The second object of the present invention is to provide a kind of production work of tussah knitting fabric in view of the deficiencies of the prior art
The production technology of skill, tussah knitting fabric has the advantages that process is simple.
One of to achieve the goals above, the present invention adopts the following technical scheme that：
A kind of tussah knitting fabric is provided, is made of the raw material of following weight percent：
Mixed yarn 94%~98%
Spandex filament 2%~6%；
Wherein, the mixed yarn blended is made of the raw material of following weight percent：
Acrylic fiber 55%~65%
Modal fibre 25%~35%
Wild silkworm silk fiber 5%~15%.
Preferably, a kind of tussah is knitted fabric, is made of the raw material of following weight percent：
Mixed yarn 95%~97%
Spandex filament 3%~5%；
Wherein, the mixed yarn blended is made of the raw material of following weight percent：
Acrylic fiber 57%~62%
Modal fibre 26%~33%
Wild silkworm silk fiber 7%~12%.
More preferably, a kind of tussah is knitted fabric, is made of the raw material of following weight percent：
Mixed yarn 96%
Spandex filament 4%；
Wherein, the mixed yarn blended is made of the raw material of following weight percent：
Acrylic fiber 60%
Modal fibre 30%
Wild silkworm silk fiber 10%.
The count of yarn of the mixed yarn is 30S~50S.
The fineness of the spandex filament is 10D~30D.
To achieve the goals above two, the present invention adopts the following technical scheme that：
A kind of production technology of tussah knitting fabric is provided, it includes the following steps：
Step 1, spinning：The progress of the acrylic fiber of formula ratio, Modal fibre and wild silkworm silk fiber is blended, it is made mixed
Spinning；
Step 2, weaving：Mixed yarn made from step 1 and spandex filament are weaved using circular knitting machine, obtained
Weave fabric；
Step 3, the predetermined embryo of open-width：Open-width is carried out to the weaving fabric that step 2 obtains, and uses high temperature open width dryer
Carry out predetermined embryo；
Step 4, dyeing：Step 3 dyes fabric after completing predetermined embryo, obtains dyed shell fabrics；
Step 5, dry cloth：The dry cloth of tentering is carried out using high temperature open width dryer to the dyed shell fabrics that step 4 obtains；
Step 6, sanding：Sanding is carried out using patch skin face of the diamond dust roller roughing-up machine to the fabric after dry cloth；
Step 7, cropping：Cropping processing is carried out to the face for completing sanding using rotary knife shearing machine；
Step 8, finished product of being formed：High temperature open width dryer is used to carry out tentering with finished product of being formed, with the side padded when sizing
Formula adds antistatic agent into fabric, after completing sizing, obtains the tussah knitting fabric.
In above-mentioned technical proposal, in the step 1, the blended mode is match network compact spinning.
In above-mentioned technical proposal, in the step 4, the dyeing is to carry out double dyes with amido colours and the dye of positive ion
Or single dye is carried out with the dye of positive ion；
The processes for carrying out double dyes with amido colours and the dye of positive ion are：
A, wild silkworm silk fiber is first contaminated at 90 DEG C with amido colours, then be cooled to 80 DEG C of dye Modal fibres, then carry out
Pickling and active soap washing；
B, acrylic fiber is contaminated at 98 DEG C with the dye of positive ion again, is then soaped, makes soft wash water and go out cylinder process；
It is described to be with the process that the dye of positive ion is singly contaminated：Acrylic fiber is contaminated at 98 DEG C using the dye of positive ion, so
After soaped, make soft wash water and go out cylinder process.
In above-mentioned technical proposal, in the step 8, when sizing, which is added with the mode padded into fabric, accounts for fabric weight
The antistatic agent that percentage is 0.5%~1.5%.
In above-mentioned technical proposal, in the step 8, the setting temperature is 150 DEG C~170 DEG C.
Beneficial effects of the present invention：
(1) a kind of tussah of the invention is knitted fabric, is made of mixed yarn and spandex filament, wherein mixed yarn is
It is formed by acrylic fiber, Modal fibre and tussah fiber blend, spandex filament, acrylic fiber and Modal fibre can be right
Wild silkworm silk fiber plays good improvement result, so substantially overcome tussah fabric lining in the prior art it is at high price and
The disadvantage of washing nursing trouble.Through mixed yarn made of acrylic fiber, Modal fibre and tussah fiber blend, then with spandex
Long filament cooperate with tussah knitting fabric obtained have washing nursing is convenient, feel it is fluffy it is soft it is glutinous, warmth retention property is excellent, moisture absorption is saturating
Gas, patch skin advantage comfortable and easy to wear, and have effects that skin-protection and health-care.
(2) production technology of a kind of tussah provided by the invention has process simple, and production cost is low, and energy
The characteristics of being suitble to large-scale production.
Specific embodiment
Below in conjunction with specific embodiment, the present invention is described in detail.
Embodiment 1.
A kind of tussah of the present embodiment is knitted fabric, is made of the raw material of following weight percent：
Mixed yarn 96%
Spandex filament 4%；
Wherein, the mixed yarn blended is made of the raw material of following weight percent：
Acrylic fiber 60%
Modal fibre 30%
Wild silkworm silk fiber 10%.
In the present embodiment, the count of yarn of mixed yarn is 40S.
In the present embodiment, the fineness of spandex filament is 20D.
A kind of production technology of above-mentioned tussah knitting fabric, it includes the following steps：
Step 1, spinning：The progress of the acrylic fiber of formula ratio, Modal fibre and wild silkworm silk fiber is blended, it is made mixed
Spinning；Wherein, blended mode is match network compact spinning；
Step 2, weaving：Mixed yarn made from step 1 and spandex filament are weaved using circular knitting machine, obtained
Weave fabric；
Step 3, the predetermined embryo of open-width：Open-width is carried out to the weaving fabric that step 2 obtains, and uses high temperature open width dryer
Carry out predetermined embryo；
Step 4, dyeing：Step 3 dyes fabric after completing predetermined embryo, obtains dyed shell fabrics；
Wherein, it dyes to carry out double dyes with amido colours and the dye of positive ion；
It is with the process that amido colours and the dye of positive ion carry out double dyes：
A, wild silkworm silk fiber is first contaminated at 90 DEG C with amido colours, then be cooled to 80 DEG C of dye Modal fibres, then carry out
Pickling and active soap washing；
B, acrylic fiber is contaminated at 98 DEG C with the dye of positive ion again, is then soaped, makes soft wash water and go out cylinder process；
Step 5, dry cloth：The dry cloth of tentering is carried out using high temperature open width dryer to the dyed shell fabrics that step 4 obtains；
Step 6, sanding：Sanding is carried out using patch skin face of the diamond dust roller roughing-up machine to the fabric after dry cloth；
Step 7, cropping：Cropping processing is carried out to the face for completing sanding using rotary knife shearing machine；
Step 8, finished product of being formed：High temperature open width dryer is used to carry out tentering with finished product of being formed, with the side padded when sizing
Formula is added into fabric accounts for the antistatic agent that fabric weight percent is 1%, after completing sizing, obtains the tussah knitting
Fabric.In the present embodiment, setting temperature is 160 DEG C.
Embodiment 2.
A kind of tussah of the present embodiment is knitted fabric, is made of the raw material of following weight percent：
Mixed yarn 94%
Spandex filament 6%；
Wherein, mixed yarn blended is made of the raw material of following weight percent：
Acrylic fiber 55%
Modal fibre 35%
Wild silkworm silk fiber 10%.
In the present embodiment, the count of yarn of mixed yarn is 30S.
In the present embodiment, the fineness of spandex filament is 10D.
A kind of production technology of above-mentioned tussah knitting fabric, it includes the following steps：
Step 1, spinning：The progress of the acrylic fiber of formula ratio, Modal fibre and wild silkworm silk fiber is blended, it is made mixed
Spinning；Wherein, blended mode is match network compact spinning；
Step 2, weaving：Mixed yarn made from step 1 and spandex filament are weaved using circular knitting machine, obtained
Weave fabric；
Step 3, the predetermined embryo of open-width：Open-width is carried out to the weaving fabric that step 2 obtains, and uses high temperature open width dryer
Carry out predetermined embryo；
Step 4, dyeing：Step 3 dyes fabric after completing predetermined embryo, obtains dyed shell fabrics；
Wherein, it dyes to carry out single dye with the dye of positive ion；
It is with the process that the dye of positive ion is singly contaminated：Acrylic fiber is contaminated at 98 DEG C using the dye of positive ion, then into
Row is soaped, makes soft wash water and go out cylinder process；
Step 5, dry cloth：The dry cloth of tentering is carried out using high temperature open width dryer to the dyed shell fabrics that step 4 obtains；
Step 6, sanding：Sanding is carried out using patch skin face of the diamond dust roller roughing-up machine to the fabric after dry cloth；
Step 7, cropping：Cropping processing is carried out to the face for completing sanding using rotary knife shearing machine；
Step 8, finished product of being formed：High temperature open width dryer is used to carry out tentering with finished product of being formed, with the side padded when sizing
Formula is added into fabric accounts for the antistatic agent that fabric weight percent is 0.5%, after completing sizing, obtains the tussah needle
Knitted fabric.In the present embodiment, setting temperature is 150 DEG C.
Embodiment 3.
A kind of tussah of the present embodiment is knitted fabric, is made of the raw material of following weight percent：
Mixed yarn 98%
Spandex filament 2%；
Wherein, mixed yarn blended is made of the raw material of following weight percent：
Acrylic fiber 65%
Modal fibre 25%
Wild silkworm silk fiber 10%.
In the present embodiment, the count of yarn of mixed yarn is 50S.
In the present embodiment, the fineness of spandex filament is 30D.
A kind of production technology of above-mentioned tussah knitting fabric, it includes the following steps：
Step 1, spinning：The progress of the acrylic fiber of formula ratio, Modal fibre and wild silkworm silk fiber is blended, it is made mixed
Spinning；Wherein, blended mode is match network compact spinning；
Step 2, weaving：Mixed yarn made from step 1 and spandex filament are weaved using circular knitting machine, obtained
Weave fabric；
Step 3, the predetermined embryo of open-width：Open-width is carried out to the weaving fabric that step 2 obtains, and uses high temperature open width dryer
Carry out predetermined embryo；
Step 4, dyeing：Step 3 dyes fabric after completing predetermined embryo, obtains dyed shell fabrics；
Wherein, it dyes to carry out double dyes with amido colours and the dye of positive ion；
It is with the process that amido colours and the dye of positive ion carry out double dyes：
A, wild silkworm silk fiber is first contaminated at 90 DEG C with amido colours, then be cooled to 80 DEG C of dye Modal fibres, then carry out
Pickling and active soap washing；
B, acrylic fiber is contaminated at 98 DEG C with the dye of positive ion again, is then soaped, makes soft wash water and go out cylinder process；
Step 5, dry cloth：The dry cloth of tentering is carried out using high temperature open width dryer to the dyed shell fabrics that step 4 obtains；
Step 6, sanding：Sanding is carried out using patch skin face of the diamond dust roller roughing-up machine to the fabric after dry cloth；
Step 7, cropping：Cropping processing is carried out to the face for completing sanding using rotary knife shearing machine；
Step 8, finished product of being formed：High temperature open width dryer is used to carry out tentering with finished product of being formed, with the side padded when sizing
Formula is added into fabric accounts for the antistatic agent that fabric weight percent is 1.5%, after completing sizing, obtains the tussah needle
Knitted fabric.In the present embodiment, setting temperature is 170 DEG C.
Embodiment 4.
A kind of tussah of the present embodiment is knitted fabric, is made of the raw material of following weight percent：
Mixed yarn 95%
Spandex filament 5%；
Wherein, mixed yarn blended is made of the raw material of following weight percent：
Acrylic fiber 62%
Modal fibre 33%
Wild silkworm silk fiber 5%.
In the present embodiment, the count of yarn of mixed yarn is 35S.
In the present embodiment, the fineness of spandex filament is 15D.
A kind of production technology of above-mentioned tussah knitting fabric, it includes the following steps：
Step 1, spinning：The progress of the acrylic fiber of formula ratio, Modal fibre and wild silkworm silk fiber is blended, it is made mixed
Spinning；Wherein, blended mode is match network compact spinning；
Step 2, weaving：Mixed yarn made from step 1 and spandex filament are weaved using circular knitting machine, obtained
Weave fabric；
Step 3, the predetermined embryo of open-width：Open-width is carried out to the weaving fabric that step 2 obtains, and uses high temperature open width dryer
Carry out predetermined embryo；
Step 4, dyeing：Step 3 dyes fabric after completing predetermined embryo, obtains dyed shell fabrics；
Wherein, it dyes to carry out double dyes with amido colours and the dye of positive ion；
It is with the process that amido colours and the dye of positive ion carry out double dyes：
A, wild silkworm silk fiber is first contaminated at 90 DEG C with amido colours, then be cooled to 80 DEG C of dye Modal fibres, then carry out
Pickling and active soap washing；
B, acrylic fiber is contaminated at 98 DEG C with the dye of positive ion again, is then soaped, makes soft wash water and go out cylinder process；
Step 5, dry cloth：The dry cloth of tentering is carried out using high temperature open width dryer to the dyed shell fabrics that step 4 obtains；
Step 6, sanding：Sanding is carried out using patch skin face of the diamond dust roller roughing-up machine to the fabric after dry cloth；
Step 7, cropping：Cropping processing is carried out to the face for completing sanding using rotary knife shearing machine；
Step 8, finished product of being formed：High temperature open width dryer is used to carry out tentering with finished product of being formed, with the side padded when sizing
Formula is added into fabric accounts for the antistatic agent that fabric weight percent is 0.8%, after completing sizing, obtains the tussah needle
Knitted fabric.In the present embodiment, setting temperature is 155 DEG C.
Embodiment 5.
A kind of tussah of the present embodiment is knitted fabric, is made of the raw material of following weight percent：
Mixed yarn 94%~98%
Spandex filament 2%~6%；
Wherein, mixed yarn blended is made of the raw material of following weight percent：
Acrylic fiber 58%
Modal fibre 27%
Wild silkworm silk fiber 15%.
In the present embodiment, the count of yarn of mixed yarn is 45S.
In the present embodiment, the fineness of spandex filament is 25D.
A kind of production technology of above-mentioned tussah knitting fabric, it includes the following steps：
Step 1, spinning：The progress of the acrylic fiber of formula ratio, Modal fibre and wild silkworm silk fiber is blended, it is made mixed
Spinning；Wherein, blended mode is match network compact spinning；
Step 2, weaving：Mixed yarn made from step 1 and spandex filament are weaved using circular knitting machine, obtained
Weave fabric；
Step 3, the predetermined embryo of open-width：Open-width is carried out to the weaving fabric that step 2 obtains, and uses high temperature open width dryer
Carry out predetermined embryo；
Step 4, dyeing：Step 3 dyes fabric after completing predetermined embryo, obtains dyed shell fabrics；
Wherein, it dyes to carry out double dyes with amido colours and the dye of positive ion；
It is with the process that amido colours and the dye of positive ion carry out double dyes：
A, wild silkworm silk fiber is first contaminated at 90 DEG C with amido colours, then be cooled to 80 DEG C of dye Modal fibres, then carry out
Pickling and active soap washing；
B, acrylic fiber is contaminated at 98 DEG C with the dye of positive ion again, is then soaped, makes soft wash water and go out cylinder process；
Step 5, dry cloth：The dry cloth of tentering is carried out using high temperature open width dryer to the dyed shell fabrics that step 4 obtains；
Step 6, sanding：Sanding is carried out using patch skin face of the diamond dust roller roughing-up machine to the fabric after dry cloth；
Step 7, cropping：Cropping processing is carried out to the face for completing sanding using rotary knife shearing machine；
Step 8, finished product of being formed：High temperature open width dryer is used to carry out tentering with finished product of being formed, with the side padded when sizing
Formula is added into fabric accounts for the antistatic agent that fabric weight percent is 1.2%, after completing sizing, obtains the tussah needle
Knitted fabric.In the present embodiment, setting temperature is 165 DEG C.
Finally it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention, rather than the present invention is protected
The limitation of range is protected, although explaining in detail referring to preferred embodiment to the present invention, those skilled in the art are answered
Work as understanding, it can be with modification or equivalent replacement of the technical solution of the present invention are made, without departing from the reality of technical solution of the present invention
Matter and range.
Claims (10)
1. a kind of tussah is knitted fabric, it is characterised in that：It is made of the raw material of following weight percent：
Mixed yarn 94%~98%
Spandex filament 2%~6%；
Wherein, the mixed yarn blended is made of the raw material of following weight percent：
Acrylic fiber 55%~65%
Modal fibre 25%~35%
Wild silkworm silk fiber 5%~15%.
2. a kind of tussah according to claim 1 is knitted fabric, it is characterised in that：It is by the original of following weight percent
Material is made：
Mixed yarn 95%~97%
Spandex filament 3%~5%；
Wherein, the mixed yarn blended is made of the raw material of following weight percent：
Acrylic fiber 57%~62%
Modal fibre 26%~33%
Wild silkworm silk fiber 7%~12%.
3. a kind of tussah according to claim 1 is knitted fabric, it is characterised in that：It is by the original of following weight percent
Material is made：
Mixed yarn 96%
Spandex filament 4%；
Wherein, the mixed yarn blended is made of the raw material of following weight percent：
Acrylic fiber 60%
Modal fibre 30%
Wild silkworm silk fiber 10%.
4. a kind of tussah according to claim 1 is knitted fabric, it is characterised in that：The count of yarn of the mixed yarn is
30S~50S.
5. a kind of tussah according to claim 1 is knitted fabric, it is characterised in that：The fineness of the spandex filament is
10D~30D.
6. a kind of production technology of tussah knitting fabric described in claim 1 to 5 any one, it is characterised in that：It is wrapped
Include following steps：
Step 1, spinning：The acrylic fiber of formula ratio, Modal fibre and wild silkworm silk fiber are carried out to blended, obtained mixed yarn；
Step 2, weaving：Mixed yarn made from step 1 and spandex filament are weaved using circular knitting machine, weaved
Fabric；
Step 3, the predetermined embryo of open-width：Open-width is carried out to the weaving fabric that step 2 obtains, and is carried out using high temperature open width dryer
Predetermined embryo；
Step 4, dyeing：Step 3 dyes fabric after completing predetermined embryo, obtains dyed shell fabrics；
Step 5, dry cloth：The dry cloth of tentering is carried out using high temperature open width dryer to the dyed shell fabrics that step 4 obtains；
Step 6, sanding：Sanding is carried out using patch skin face of the diamond dust roller roughing-up machine to the fabric after dry cloth；
Step 7, cropping：Cropping processing is carried out to the face for completing sanding using rotary knife shearing machine；
Step 8, finished product of being formed：High temperature open width dryer is used to carry out tentering with finished product of being formed, when sizing is past with the mode padded
Antistatic agent is added in fabric, after completing sizing, obtains the tussah knitting fabric.
7. a kind of production technology of tussah knitting fabric according to claim 6, it is characterised in that：The step 1
In, the blended mode is match network compact spinning.
8. a kind of production technology of tussah knitting fabric according to claim 6, it is characterised in that：The step 4
In, the dyeing to carry out double dyes with amido colours and the dye of positive ion or carries out single dye with the dye of positive ion；
The processes for carrying out double dyes with amido colours and the dye of positive ion are：
A, wild silkworm silk fiber is first contaminated at 90 DEG C with amido colours, then be cooled to 80 DEG C of dye Modal fibres, then carry out pickling
With active soap washing；
B, acrylic fiber is contaminated at 98 DEG C with the dye of positive ion again, is then soaped, makes soft wash water and go out cylinder process；
It is described to be with the process that the dye of positive ion is singly contaminated：Acrylic fiber is contaminated at 98 DEG C using the dye of positive ion, then into
Row is soaped, makes soft wash water and go out cylinder process.
9. a kind of production technology of tussah knitting fabric according to claim 6, it is characterised in that：The step 8
In, when sizing, which is added with the mode padded into fabric, accounts for the antistatic agent that fabric weight percent is 0.5%~1.5%.
10. a kind of production technology of tussah knitting fabric according to claim 6, it is characterised in that：The step 8
In, the setting temperature is 150 DEG C~170 DEG C.