CN108864810A - A kind of hidden magnetic card water-soluble silk screen ink and preparation method thereof - Google Patents
A kind of hidden magnetic card water-soluble silk screen ink and preparation method thereof Download PDFInfo
- Publication number
- CN108864810A CN108864810A CN201810851557.4A CN201810851557A CN108864810A CN 108864810 A CN108864810 A CN 108864810A CN 201810851557 A CN201810851557 A CN 201810851557A CN 108864810 A CN108864810 A CN 108864810A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- silk screen
- magnetic card
- soluble
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of hidden magnetic card water-soluble silk screen ink and preparation method thereof, belongs to technical field of ink, by weight, including following components：40-70 parts of waterborne polyurethane resin, 1-10 parts of water-soluble diluent, 0.1-1 parts of wetting agent, 0.1-2 parts of levelling agent, 0.5-5 parts of thickener, 0.1-0.5 parts of defoaming agent, 1-5 parts of filler, 0.1-1 parts of PH regulator, 1-10 parts of deionized water, 15-50 parts of aqueous pigment.Hidden magnetic card produced by the present invention is not precipitated with water-soluble silk screen ink in storage, and covering power is high；Scumming, not viscous version, modest viscosity do not flow good leveling property, and printing performance is excellent；And nontoxic, free from extraneous odour, it is real environment-friendly health type water-soluble silk screen ink, solvent ink for screen printing can be replaced to be applied to hidden magnetic card manufacture craft.
Description
Technical field
The present invention relates to a kind of hidden magnetic card water-soluble silk screen inks and preparation method thereof, belong to technical field of ink.
Background technique
IC card has just obtained rapid proliferation since popularization, and the issued volume of IC card has broken through 1,000,000,000 so far, accounts for
Add Card total volume of issuing most probably more than.With the development of science and technology and social progress, production work of the people to IC card
More stringent requirements are proposed for skill, and hidden magnetic card is born therewith.Hidden magnetic card is increased on the basis of original magnetic card manufacture craft
The magnetic card that hidden operation is produced is carried out to magnetic stripe, magnetic stripe is set to inside the card body of magnetic card by hidden magnetic card, rather than is blocked
Body surface face allows magnetic card surface to print other corresponding patterns, not only greatly improves the aesthetic measure of magnetic card, enhancing
The experience of user, and since magnetic stripe is hidden in inside magnetic card, it the safety of magnetic card itself is also improved, can preferably protect
The personal information of user is protected, thus is had a vast market foreground.
It is increasingly complex for the relatively common magnetic card of the manufacturing process of hidden magnetic card.It needs that magnetic stripe is first bonded in PVC plastic
Expect then to be covered with one layer of silver grey color ink on magnetic stripe in base, then white ink is covered on silver grey color ink again, white
Four-color process can be carried out on color ink again and adds print surface gloss oil to protect ink, improves the property of surface damage resistant and corrosion
Energy.Hidden magnetic card is very stringent to craft precision requirement, and the thickness of every layer of ink has specific requirement, and printed ink is not
It is preferably too thick or too thin, if ink is too thick, it is easy to become useless card so that the magnetism of magnetic card dies down；It, cannot if ink is excessively thin
Play good hidden effect.
The silver inks and chalk of concealed magnetic stripe card are one kind for fabrication ink for screen printing.It is used in card manufacturing industry at present
Ink for screen printing be all solvent-based ink, be with aliphatic, aromatic series, ketones solvent is as diluent, for adjusting ink
Viscosity and mobility, have reached best use effect.However ink is printing, and in drying process, due to a large amount of volatilizations of solvent,
A large amount of harmful substance is caused, the health of operator is not only influenced, but also periphery is polluted, it is hidden to there is safety
Suffer from.
Summary of the invention
In view of the above existing problems in the prior art, the present invention provides a kind of hidden magnetic card water-soluble silk screen ink, the oil
Black strong covering power, richness is high, traditional oiliness ink for screen printing can be replaced to be used for hidden magnetic card production technology.
The present invention goes back while providing the preparation method of above-mentioned water-soluble silk screen ink.
To achieve the goals above, a kind of hidden magnetic card water-soluble silk screen ink that the present invention uses, by weight, packet
Include following components：40-70 parts of waterborne polyurethane resin, 1-10 parts of water-soluble diluent, 0.1-1 parts of wetting agent, levelling agent 0.1-2
Part, 0.5-5 parts of thickener, 0.1-0.5 parts of defoaming agent, 1-5 parts of filler, 0.1-1 parts of PH regulator, 1-10 parts of deionized water, water
15-50 parts of pigment of property.
As an improvement, the water-soluble diluent is one of ethylene glycol, propylene glycol, glycerol or above-mentioned with arbitrary proportion
Mixing.
As an improvement, the wetting agent is alkyl phenol polyoxyethylene ether, sodium dioctyl sulfosuccinate, polysiloxanes-are poly-
One of ether copolymer above-mentioned mixes in any proportion.
As an improvement, the levelling agent is that high-boiling point alcohol ether solvents, polyether-modified dimethyl silicone polymer, acrylate are total
One of polymers or mentioned component are mixed with arbitrary proportion.
As an improvement, the thickener is hydrophobically modified polyurethane thickener, the thickening of anion hydrophobically-modified alkali swelling type
One of agent or mentioned component are mixed with arbitrary proportion.
As an improvement, the defoaming agent be one of polyoxyethylene ether, modified siloxane, modified mineral oil or it is above-mentioned at
Divide and is mixed with arbitrary proportion.
As an improvement, the filler be one of precipitated calcium carbonate, fumed silica, silica flatting silica or on
Ingredient is stated to mix with arbitrary proportion.
As an improvement, the PH regulator is monoethanolamine, in diethanol amine, triethanolamine, AMP95, DEMA, ammonium hydroxide
A kind of or mentioned component is mixed with arbitrary proportion.
As an improvement, the aqueous pigment is one of water aluminum-silver slurry, aqueous white slurry or mentioned component with any
Ratio mixing.
In addition, specifically including following step the present invention provides the preparation method of above-mentioned hidden magnetic card water-soluble silk screen ink
Suddenly：Based on formulation weight part, deionized water, water-soluble diluent, filler are sequentially added in Scattered Kettle and are stirred evenly, then plus
Enter waterborne polyurethane resin to stir evenly, wetting agent, levelling agent, thickener, defoaming agent is added, with 700-1000 revs/min
20~30min of Rate Dispersion, be finally added with stirring PH regulator, aqueous pigment in the speed with 300-500 revs/min,
After mixing evenly, it filters and packages and obtains the water-soluble silk screen silver inks.
Compared with prior art, hidden magnetic card produced by the present invention is not precipitated with water-soluble silk screen ink in storage, is covered
Power is high；Scumming, not viscous version, modest viscosity do not flow good leveling property, and printing performance is excellent；And nontoxic, free from extraneous odour, it is real
Environment-friendly health type water-soluble silk screen ink can replace solvent ink for screen printing to be applied to hidden magnetic card manufacture craft.
Specific embodiment
In order to make the objectives, technical solutions and advantages of the present invention clearer, the present invention is carried out below further detailed
It describes in detail bright.However, it should be understood that the specific embodiments described herein are merely illustrative of the present invention, it is not limited to this hair
Bright range.
Unless otherwise defined, all technical terms and scientific terms used herein are led with technology of the invention is belonged to
The normally understood meaning of the technical staff in domain is identical, and term as used herein in the specification of the present invention is intended merely to retouch
State the purpose of specific embodiment, it is not intended that in the limitation present invention.
A kind of hidden magnetic card water-soluble silk screen ink, by weight, including following components：Waterborne polyurethane resin 40-
70 parts, 1-10 parts of water-soluble diluent, 0.1-1 parts of wetting agent, 0.1-2 parts of levelling agent, 0.5-5 parts of thickener, defoaming agent 0.1-
0.5 part, 1-5 parts of filler, 0.1-1 parts of PH regulator, 1-10 parts of deionized water, 15-50 parts of aqueous pigment.
As the improvement of embodiment, PU115, PU617, the PU303 of Guangdong silver dollar is can be used in the waterborne polyurethane resin,
Guangdong is with the 6754 of moral, 6717,6719, the 7360 of Yantai Wanhua, 3458, the MR712 that Dongguan rice people accounts for, one kind of MR875 or
It is above-mentioned to mix in any proportion.
As the improvement of embodiment, the water-soluble diluent be one of ethylene glycol, propylene glycol, glycerol or it is above-mentioned with
Arbitrary proportion mixing.
As the improvement of embodiment, the wetting agent is alkyl phenol polyoxyethylene ether, sodium dioctyl sulfosuccinate, poly- silicon
One of oxygen alkane-copolyether above-mentioned mixes in any proportion.Illustrate as an example, the wetting agent can be used
The OT75 of Qing Te company wins the TEGO245, TEGO270, TEGO280 for creating Degussa, the BYK340 of Bi Ke chemistry, BYK346's
It is a kind of or above-mentioned mix in any proportion.
As the improvement of embodiment, the levelling agent is high-boiling point alcohol ether solvents, polyether-modified dimethyl silicone polymer, third
One of olefin(e) acid ester copolymer or mentioned component are mixed with arbitrary proportion.Illustrate as an example, the levelling agent can be adopted
With PPH, DPM and the DPNB of the Dow Chemical Company, the GLIDE410, GLIDE432, GLIDE450 of wound Degussa are won, Bi Ke chemistry
One kind of BYK333, BYK306 above-mentioned mix in any proportion.
As the improvement of embodiment, the thickener is hydrophobically modified polyurethane thickener, anion hydrophobically modified alkali soluble
One of the type that rises thickener or mentioned component are mixed with arbitrary proportion.Illustrate as an example, the thickener can be used
PUR50, PUR60, the PUR62 of the bright icepro of Germany, the PS166 of Italian Ning Baidi, PS167, the RM8 of U.S.'s ROHM AND HAAS,
RM2020, one kind of the TT935 of Dow Chemical or above-mentioned mixes in any proportion.
As the improvement of embodiment, the defoaming agent is one of polyoxyethylene ether, modified siloxane, modified mineral oil
Or mentioned component is mixed with arbitrary proportion.Illustrate as an example, the defoaming agent, which can be used, wins wound Degussa
BYK023, BYK024, the BYK028 of FOAMEX3062, FOAMEX845, AIREX 902W, Bi Ke chemistry, French Luo Diya's
One kind of DF690, DF693 above-mentioned mix in any proportion.
As the improvement of embodiment, the filler is precipitated calcium carbonate, in fumed silica, silica flatting silica
A kind of or mentioned component is mixed with arbitrary proportion.Illustrate as an example, the filler can be used moral mountain chemical industry QS-102,
QS-20, QS-30, QS-40, the M-5 of Cabot win the 0K520 of wound Degussa, OK412, one kind of the SY-350 of Japanese fuji
Or it above-mentioned mixes in any proportion.
As the improvement of embodiment, the PH regulator be monoethanolamine, diethanol amine, triethanolamine, AMP95, DEMA,
One of ammonium hydroxide or mentioned component are mixed with arbitrary proportion.
As the improvement of embodiment, the aqueous pigment be water aluminum-silver slurry, aqueous white starch one of or it is above-mentioned at
Divide and is mixed with arbitrary proportion.
In addition, being specifically included the present invention also provides a kind of preparation method of hidden magnetic card water-soluble silk screen ink
Following steps：Based on formulation weight part, deionized water, water-soluble diluent, filler are sequentially added in Scattered Kettle and are stirred evenly,
Then waterborne polyurethane resin is added to stir evenly, wetting agent, levelling agent, thickener, defoaming agent are added, with 700-1000
Rev/min 20~30min of Rate Dispersion, be finally added with stirring PH regulator, water in the speed with 300-500 revs/min
Property pigment filters and packages after mixing evenly and obtains the water-soluble silk screen silver inks.
Embodiment 1
A kind of hidden magnetic card water-soluble silk screen silver inks, by weight, including following components：Waterborne polyurethane resin 40
Part, 1 part of water-soluble diluent, 0.1 part of wetting agent, 0.1 part of levelling agent, 0.5 part of thickener, 0.1 part of defoaming agent, 1 part of filler, PH
0.1 part of regulator, 1 part of deionized water, 15 parts of aqueous pigment.
The waterborne polyurethane resin uses the PU115 waterborne polyurethane resin of Guangdong silver dollar.
The water-soluble diluent is ethylene glycol.
The wetting agent is the OT75 that alkyl phenol polyoxyethylene ether uses Qing Te company.
The levelling agent is the BYK333 of Bi Ke chemistry.The PUR50 of the bright icepro of Germany can be used in the thickener.
The FOAMEX 3062 for winning wound Degussa can be used in the defoaming agent.
Moral mountain chemical industry QS-102 can be used in the filler.
The PH regulator is monoethanolamine.
The aqueous pigment is water aluminum-silver slurry.
The above-mentioned hidden magnetic card preparation method of water-soluble silk screen silver inks, specifically includes following steps：Based on formulation weight part,
Deionized water, water-soluble diluent, filler are sequentially added in Scattered Kettle and stirred evenly, waterborne polyurethane resin is then added and stirs
Mix uniformly, add wetting agent, levelling agent, thickener, defoaming agent, with 700 revs/min of Rate Dispersion 20min, finally with
300 revs/min of speed is added with stirring PH regulator, aqueous pigment, after mixing evenly, filter and package obtain it is described aqueous
Silk-screen silver inks.
Embodiment 2
A kind of hidden magnetic card water-soluble silk screen silver inks, by weight, including following components：Waterborne polyurethane resin 70
Part, 10 parts of water-soluble diluent, 1 part of wetting agent, 2 parts of levelling agent, 5 parts of thickener, 0.5 part of defoaming agent, 5 parts of filler, PH is adjusted
1 part of agent, 10 parts of deionized water, 50 parts of aqueous pigment.
As the improvement of embodiment, the waterborne polyurethane resin is using Guangdong with 6754 waterborne polyurethane resins of moral.
The water-soluble diluent is propylene glycol.
The wetting agent is alkyl phenol polyoxyethylene ether.
The levelling agent is polyether-modified dimethyl silicone polymer.
The thickener is hydrophobically modified polyurethane thickener.
The defoaming agent is polyoxyethylene ether.The filler is fumed silica.
The PH regulator is diethanol amine.
The aqueous pigment is water aluminum-silver slurry.
The above-mentioned hidden magnetic card preparation method of water-soluble silk screen silver inks, specifically includes following steps：Based on formulation weight part,
Deionized water, water-soluble diluent, filler are sequentially added in Scattered Kettle and stirred evenly, waterborne polyurethane resin is then added and stirs
Mix uniformly, add wetting agent, levelling agent, thickener, defoaming agent, with 800 revs/min of Rate Dispersion 25min, finally with
400 revs/min of speed is added with stirring PH regulator, aqueous pigment, after mixing evenly, filter and package obtain it is described aqueous
Silk-screen silver inks.
Embodiment 3,4,5
A kind of hidden magnetic card water-soluble silk screen silver inks, are prepared according to the component formula of the following table 1.
Table 1 prepares three embodiment component formulas (mass parts) of water-soluble silk screen silver inks
In addition, preparing above-mentioned water-soluble silk screen silver inks according to the preparation method in embodiment 1.
Performance such as the following table 2 of water-soluble silk screen silver inks is made by the various embodiments described above.
The hidden magnetic card of table 2 water-soluble silk screen silver inks the performance test results
In summary each embodiment is it is found that be made water-soluble silk screen silver inks, viscosity 5000- using the method for the present invention
1000cps (25 degree, NDJ-1 rotational viscometer)；Fineness≤20um；Surface drying time≤25min；Heat resistance be 150 degree 30 minutes,
Non yellowing；Peel strength 4.5-8N/CM；Shelf-life up to 6 months or more, at 7 degree of storage temperature or more.
Embodiment 6
A kind of hidden magnetic card water-soluble silk screen chalk, by weight, including following components：Waterborne polyurethane resin 50
Part, 6 parts of water-soluble diluent, 0.3 part of wetting agent, 0.3 part of levelling agent, 1.5 parts of thickener, 0.3 part of defoaming agent, 2 parts of filler, PH
0.3 part of regulator, 4 parts of deionized water, 25 parts of aqueous pigment.
The MR875 waterborne polyurethane resin that the waterborne polyurethane resin is accounted for using Dongguan rice people.
The water-soluble diluent is glycerol.The wetting agent is sodium dioctyl sulfosuccinate.
The levelling agent is acrylate copolymer.The thickener is anion hydrophobically-modified alkali swelling type thickener.
The defoaming agent is polyoxyethylene ether.The filler is precipitated calcium carbonate.
The PH regulator is monoethanolamine.The aqueous pigment is aqueous white slurry.
The above-mentioned hidden magnetic card preparation method of water-soluble silk screen chalk, specifically includes following steps：Based on formulation weight part,
Deionized water, water-soluble diluent, filler are sequentially added in Scattered Kettle and stirred evenly, waterborne polyurethane resin is then added and stirs
It mixes uniformly, adds wetting agent, levelling agent, thickener, defoaming agent, with 1000 revs/min of Rate Dispersion 30min, finally exist
It is added with stirring PH regulator, aqueous pigment with 500 revs/min of speed, after mixing evenly, filters and packages and obtains the water
Sex pilus printing chalk.
Embodiment 7,8,9
A kind of hidden magnetic card water-soluble silk screen chalk, is prepared according to the component formula of the following table 3.
Table 3 prepares three embodiment component formulas (mass parts) of water-soluble silk screen chalk
In addition, preparing above-mentioned water-soluble silk screen chalk according to the preparation method in embodiment 6.
Performance such as the following table 4 of water-soluble silk screen chalk is made by the various embodiments described above.
4 water-soluble silk screen chalk the performance test results of table
In summary each embodiment is it is found that be made water-soluble silk screen chalk, viscosity 5000- using the method for the present invention
1000cps (25 degree, NDJ-1 rotational viscometer)；Fineness≤20um；Surface drying time≤25min；Heat resistance be 150 degree 30 minutes,
Non yellowing；Peel strength 4.5-8N/CM；Shelf-life up to 6 months or more, at 7 degree of storage temperature or more.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Made any modification, equivalent replacement or improvement etc., should all be included in the protection scope of the present invention within mind and principle.
Claims (10)
1. a kind of hidden magnetic card water-soluble silk screen ink, which is characterized in that by weight, including following components：Aqueous poly- ammonia
40-70 parts of ester resin, 1-10 parts of water-soluble diluent, 0.1-1 parts of wetting agent, 0.1-2 parts of levelling agent, 0.5-5 parts of thickener, disappear
0.1-0.5 parts of infusion, 1-5 parts of filler, 0.1-1 parts of PH regulator, 1-10 parts of deionized water, 15-50 parts of aqueous pigment.
2. hidden magnetic card water-soluble silk screen ink according to claim 1, which is characterized in that the water-soluble diluent is
One of ethylene glycol, propylene glycol, glycerol above-mentioned are mixed with arbitrary proportion.
3. hidden magnetic card water-soluble silk screen ink according to claim 1, which is characterized in that the wetting agent is alkyl phenol
One of polyoxyethylene ether, sodium dioctyl sulfosuccinate, polysiloxane-polyether copolymer above-mentioned mix in any proportion
It closes.
4. hidden magnetic card water-soluble silk screen ink according to claim 1, which is characterized in that the levelling agent is higher boiling
One of alcohol ether solvents, polyether-modified dimethyl silicone polymer, acrylate copolymer or mentioned component are mixed with arbitrary proportion
It closes.
5. hidden magnetic card water-soluble silk screen ink according to claim 1, which is characterized in that the thickener is hydrophobic changes
One of property polyurethane thickener, anion hydrophobically-modified alkali swelling type thickener or mentioned component are mixed with arbitrary proportion.
6. hidden magnetic card water-soluble silk screen ink according to claim 1, which is characterized in that the defoaming agent is polyoxy second
One of alkene ether, modified siloxane, modified mineral oil or mentioned component are mixed with arbitrary proportion.
7. hidden magnetic card water-soluble silk screen ink according to claim 1, which is characterized in that the filler is lightweight carbonic acid
One of calcium, fumed silica, silica flatting silica or mentioned component are mixed with arbitrary proportion.
8. hidden magnetic card water-soluble silk screen ink according to claim 1, which is characterized in that the PH regulator is a second
One of hydramine, diethanol amine, triethanolamine, AMP95, DEMA, ammonium hydroxide or mentioned component are mixed with arbitrary proportion.
9. hidden magnetic card water-soluble silk screen ink according to claim 1, which is characterized in that the aqueous pigment is aqueous
One of aluminum paste, aqueous white slurry or mentioned component are mixed with arbitrary proportion.
10. a kind of preparation method of any one of claim 1-9 hidden magnetic card water-soluble silk screen ink, which is characterized in that
Specifically include following steps：Based on formulation weight part, deionized water, water-soluble diluent, filler are sequentially added in Scattered Kettle
It stirs evenly, waterborne polyurethane resin is then added and stirs evenly, adds wetting agent, levelling agent, thickener, defoaming agent, with
700-1000 revs/min of 20~30min of Rate Dispersion is finally added with stirring PH tune in the speed with 300-500 revs/min
Section agent, aqueous pigment filter and package after mixing evenly and obtain the water-soluble silk screen silver inks.