CN108783676A - 一种触屏导电浸胶手套及其制备工艺 - Google Patents

一种触屏导电浸胶手套及其制备工艺 Download PDF

Info

Publication number
CN108783676A
CN108783676A CN201810758774.9A CN201810758774A CN108783676A CN 108783676 A CN108783676 A CN 108783676A CN 201810758774 A CN201810758774 A CN 201810758774A CN 108783676 A CN108783676 A CN 108783676A
Authority
CN
China
Prior art keywords
latex
dipped
swt
touch screen
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810758774.9A
Other languages
English (en)
Inventor
赵磊
雷传洲
宿希来
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Rising Security Technology Co Ltd
Original Assignee
Shandong Rising Security Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Rising Security Technology Co Ltd filed Critical Shandong Rising Security Technology Co Ltd
Priority to CN201810758774.9A priority Critical patent/CN108783676A/zh
Publication of CN108783676A publication Critical patent/CN108783676A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种触屏导电浸胶手套及其制备工艺，属于浸胶手套技术领域，该触屏导电浸胶手套的浸渍胶乳由以下重量份数的原料制成：胶乳100份、硫磺0.8‑1.5份、氧化锌1.5‑2份、促进剂0.7‑1.2份、SWT水性分散体7‑12份。通过在浸渍胶乳中掺加分散均匀的多壁碳纳米管(SWT)，得到具有触屏导电功能的胶乳手套。

Description

一种触屏导电浸胶手套及其制备工艺
技术领域
本发明涉及浸胶手套技术领域，具体涉及一种触屏导电浸胶手套及其制备工艺。
背景技术
碳纳米管作为一维纳米材料，重量轻，六边形结构连接完美，其径向尺寸较小，管的外径一般在几纳米到几十纳米，管的内径更小，有的只有1nm左右，而其长度一般在微米级，长度和直径比非常大，可达103-106。碳纳米管的独特结构决定了它具有许多特殊的物理和化学性质，具有极高的强度和极大的韧性，既具有碳素材料的固有本性，又具有金属材料的导电和导热性，陶瓷材料的耐热和耐腐蚀性，纺织纤维的可编织性，以及高分子材料的轻质、易加工性。而且，由于碳纳米管中碳原子采取SP2杂化，相比SP3杂化，SP2杂化中S轨道成分比较大，使碳纳米管具有高模量和高强度，碳纳米管上碳原子的P电子形成大范围的离域π键，由于共轭效应显著，碳纳米管具有一些特殊的电学性质，具有良好的导电性能。
随着科技的发展，越来越多的带有触屏显示器的设备出现在我们的生活中，我们在戴上手套后发现对触屏显示器的使用会带来不便，由于碳纳米管的各种优异的性能，可以把碳纳米管添加到高分子胶乳基体中，得到具有触屏导电功能的胶乳手套。
发明内容
本发明提供一种触屏导电浸胶手套及其制备工艺，通过在浸渍胶乳中掺加分散均匀的多壁碳纳米管(SWT)，得到具有触屏导电功能的胶乳手套。
为实现上述目的，本发明采用以下技术方案：
一种触屏导电浸胶手套，浸渍胶乳由以下重量份数的原料制成：胶乳100份、硫磺0.8-1.5份、氧化锌1.5-2份、促进剂0.7-1.2份、SWT水性分散体7-12份。
优选的，所述SWT水性分散体是由3wt％的SWT与97wt％的水组成。
优选的，所述胶乳为丁腈胶乳。
优选的，所述促进剂由二丁基二硫代氨基甲酸锌(BZ)与二乙基二硫代氨基甲酸锌(ZDC)共同组成。
本发明还提供一种触屏导电浸胶手套的制备工艺，包括以下步骤：
(1)将手模先进行清洗和预热，再将手套芯戴到手模；
(2)浸渍凝固剂，在室温条件下放置挥发至六成干；
(3)浸入浸渍胶乳；
(4)室温条件下自然放置，固化成膜；
(5)用水清洗掉未凝固的多余胶料；
(6)硫化；
(7)脱模。
优选的，所述步骤(2)中，浸渍凝固剂10s。
优选的，所述步骤(3)中浸渍胶乳的具体制备方法是:首先将SWT进行研磨，然后分散到水溶液中得到SWT水性分散体，最后将SWT水性分散体加入到胶乳中，与胶乳充分混合。
优选的，所述步骤(3)中，浸入浸渍胶乳2-5s，
优选的，所述步骤(4)中在室温下自然放置固化成膜，放置时间2.5-5min。
其中，SWT的性能指标为：pH7.5-7.9，粘度200-300Cps，表面电阻＜300ohm/sq。
本发明的有益技术效果为：
在手套浸渍胶乳中加入SWT，由于SWT的优异导电性能，使得手套整体本身具有触屏效果；由于SWT的特殊性能，手套不仅具有良好的导电性，耐磨损性能也提高；采用共混的方法将SWT水性分散体掺加到胶乳中，该方法简单易行，不需要严苛的条件。
具体实施方式
下面结合具体实施例对本发明作进一步说明。
实施例1
一种触屏导电浸胶手套，浸渍胶乳由以下重量份数的原料制成：胶乳100份、硫磺0.8份、氧化锌1.5份、促进剂0.7份、SWT水性分散体10份。
所述SWT水性分散体是由3wt％的SWT与97wt％的水组成。所述胶乳为丁腈胶乳。
所述促进剂由二丁基二硫代氨基甲酸锌(BZ)与二乙基二硫代氨基甲酸锌(ZDC)共同组成。
上述触屏导电浸胶手套的制备工艺，包括以下步骤：
(1)将手模先进行清洗和预热，再将手套芯戴到手模；
(2)浸渍凝固剂10s，在室温条件下放置挥发至六成干；
(3)浸入浸渍胶乳2-5s，所述浸渍胶乳的具体制备方法：将SWT进行研磨，然后分散到水溶液中得到SWT水性分散体，最后将SWT水性分散体加入到胶乳中，与胶乳充分混合得到浸渍胶乳；
(4)在室温下自然放置固化成膜，放置时间2.5-5min；
(5)用水清洗掉未凝固的多余胶料；
(6)硫化；
(7)脱模。
对比例1-1:本对比例是实施例1的对比例，浸渍胶乳中不掺加SWT水性分散体，其它组分完全相同，具体制备工艺步骤除了步骤(3)中，不掺加SWT水性分散体，直接浸渍胶乳外，其它工艺步骤完全相同。
对比例1-2：本对比例是实施例1的对比例，浸渍胶乳中掺加SWT水性分散体5份，其它组分及手套制备工艺和实施例1完全相同。
性能测试：
对上述实施例1、对比例1-1、对比例1-2制得的手套产品进行性能测试，其中，实施例1为SWT 10％(以SWT在胶乳中的质量百分含量)，对比例1-1为SWT 0％、对比例1-2为SWT5％，结果如下：
表1手套导电性能测试
实验次数 SWT 0％ SWT 5％ SWT 10％
1 11.5 5.9 5.4
2 11.2 5.9 5.4
3 11.2 5.95 5.4
4 11.0 5.9 5.5
5 11.0 6.0 5.4
平均值 11.14 5.93 5.42
上述导电性能测试，采用SIMCO ST-4设备，检测手套的表面阻抗(单位10^X ohm/sq)，表面阻抗值越小，导电性能越好，由检测数据说明，通过在胶乳中掺加SWT，手套导电性能提高，且随着SWT量的增加，导电性能也提高。
表2手套耐磨性能测试
组别 SWT 0％ SWT 5％ SWT 10％
圈数 1800-2000 8500 10000
上述耐磨性能测试，采用EN388标准，将手套材料样本在已知的压力下(9kPa)被摩擦，耐摩擦圈数越高则耐磨性越好，由检测数据说明，通过在胶乳中掺加SWT，手套耐磨性能提高，且随着SWT量的增加，耐磨性能也提高。
实施例2
一种触屏导电浸胶手套，浸渍胶乳由以下重量份数的原料制成：胶乳100份、硫磺1.5份、氧化锌2份、促进剂1.2份、SWT水性分散体10份。
所述SWT水性分散体是由3wt％的SWT与97wt％的水组成。所述胶乳为丁腈胶乳。
所述促进剂由二丁基二硫代氨基甲酸锌(BZ)与二乙基二硫代氨基甲酸锌(ZDC)共同组成。
上述触屏导电浸胶手套的制备工艺，包括以下步骤：
(1)将手模先进行清洗和预热，再将手套芯戴到手模；
(2)浸渍凝固剂10s，在室温条件下放置挥发至六成干；
(3)浸入浸渍胶乳2-5s，所述浸渍胶乳的具体制备方法：将SWT进行研磨，然后分散到水溶液中得到SWT水性分散体，最后将SWT水性分散体加入到胶乳中，与胶乳充分混合得到浸渍胶乳；
(4)在室温下自然放置固化成膜，放置时间2.5-5min；
(5)用水清洗掉未凝固的多余胶料；
(6)硫化；
(7)脱模。
对比例2-1：本对比例是实施例2的对比例，浸渍胶乳中不掺加SWT水性分散体，其它组分完全相同，具体制备工艺步骤除了步骤(3)中，不掺加SWT水性分散体，直接浸渍胶乳外，其它工艺步骤完全相同。
对比例2-2：本对比例是实施例2的对比例，浸渍胶乳中掺加SWT水性分散体5份，其它组分及手套制备工艺完全相同。
对比例2-3：本对比例是实施例2的对比例，浸渍胶乳中掺加SWT水性分散体15份，其它组分及手套制备工艺完全相同。
性能测试：
对上述实施例2、对比例2-1、对比例2-2、对比例2-3制得的手套产品进行性能测试，其中，实施例2为SWT 10％(以SWT在胶乳中的质量百分含量)，对比例2-1为SWT 0％、对比例2-2为SWT 5％、对比例2-3为SWT 15％结果如下：
表3手套导电性能测试
上述导电性能测试，采用SIMCO ST-4设备，检测手套的表面阻抗(单位10^X ohm/sq)，表面阻抗值越小，导电性能越好，由检测数据说明，通过在胶乳中掺加SWT，手套导电性能提高，且随着SWT量的增加，导电性能也提高。
结论：通过在胶乳中掺加SWT，得到导电性能及耐磨性能良好的触屏导电手套，综合考虑成本，选择SWT的最佳掺加量为7-12％(以SWT在胶乳中的质量百分含量)。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的技术方案的基础上，本领域技术人员不需要付出创造性劳动即可做出的各种修改或变形仍在本发明的保护范围内。

Claims (9)

1.一种触屏导电浸胶手套，其特征在于，浸渍胶乳由以下重量份数的原料制成：胶乳100份、硫磺0.8-1.5份、氧化锌1.5-2份、促进剂0.7-1.2份、SWT水性分散体7-12份。
2.根据权利要求1所述的一种触屏导电浸胶手套，其特征在于，所述SWT水性分散体是由3wt％的SWT与97wt％的水组成。
3.根据权利要求1所述的一种触屏导电浸胶手套，其特征在于，所述胶乳为丁腈胶乳。
4.根据权利要求1所述的一种触屏导电浸胶手套，其特征在于，所述促进剂由二丁基二硫代氨基甲酸锌(BZ)与二乙基二硫代氨基甲酸锌(ZDC)共同组成。
5.权利要求1-4任一项所述的一种触屏导电浸胶手套的制备工艺，其特征在于，包括以下步骤：
(1)将手模先进行清洗和预热，再将手套芯戴到手模；
(2)浸渍凝固剂，在室温条件下放置挥发至六成干；
(3)浸入浸渍胶乳；
(4)室温条件下自然放置，固化成膜；
(5)用水清洗掉未凝固的多余胶料；
(6)硫化；
(7)脱模。
6.根据权利要求5所述的一种触屏导电浸胶手套的制备工艺，其特征在于，所述步骤(2)中，浸渍凝固剂10s。
7.根据权利要求5所述的一种触屏导电浸胶手套的制备工艺，其特征在于，所述步骤(3)中浸渍胶乳的具体制备方法是:首先将SWT进行研磨，然后分散到水溶液中得到SWT水性分散体，最后将SWT水性分散体加入到胶乳中，与胶乳充分混合。
8.根据权利要求5所述的一种触屏导电浸胶手套的制备工艺，其特征在于，所述步骤(3)中，浸入浸渍胶乳2-5s。
9.根据权利要求5所述的一种触屏导电浸胶手套的制备工艺，其特征在于，所述步骤(4)中在室温下自然放置固化成膜，放置时间2.5-5min。
CN201810758774.9A 2018-07-11 2018-07-11 一种触屏导电浸胶手套及其制备工艺 Pending CN108783676A (zh)