CN108752053A - A kind of high temperature color glaze and blue and white porcelain mixing burn and make new process - Google Patents
A kind of high temperature color glaze and blue and white porcelain mixing burn and make new process Download PDFInfo
- Publication number
- CN108752053A CN108752053A CN201810581342.5A CN201810581342A CN108752053A CN 108752053 A CN108752053 A CN 108752053A CN 201810581342 A CN201810581342 A CN 201810581342A CN 108752053 A CN108752053 A CN 108752053A
- Authority
- CN
- China
- Prior art keywords
- blue
- white
- high temperature
- glaze
- contours
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high temperature color glazes and blue and white porcelain mixing to burn and make new process, including：Ceramic component embryo, high temperature color glaze color block, rejecting face, blue and white porcelain sketch the contours figure, it is characterised in that：Upper high temperature color glaze color block is applied on ceramic component embryo；On the high white clay in the rejecting face of ceramic component embryo, upper cobalt bluepigment photoghraphic coupler is dipped in paintbrush, required blue and white porcelain is sketched the contours of and sketches the contours figure；It burns and makes at a temperature of 1300 DEG C ± 5 DEG C, burn the finished product after making, the color block combination for blurring, being abstracted of high temperature color glaze and blue and white porcelain clearly white background indigo plant line pattern, the different artistic style of the two is perfectly combined embodiment on same ceramic art works, brings a kind of pleasing visual impression of audience, while the present invention, a kind of blank of new process of ceramic works is filled up, and embodiment is simple, easy to learn, has pushed the ceramic development burnt and make technique.
Description
Technical field
The invention belongs to ceramic making burnings to make technology field, more particularly to be embodied simultaneously on same ceramic articles
The making burning of two kinds of different-styles of high temperature color glaze and blue and white porcelain makes new process.
Background technology
Glaze is the glassy thin layer for the colorless or colored for being covered in ceramic surface, is with raw mineral materials such as kaolin etc.
Coordinate by a certain percentage with industrial chemicals and glaze slip is made by grinding, impose on billet surface, calcined through certain temperature, can be increased
Mechanical strength, thermal stability and the dielectric strength of product are added, also beautifies implements, washed, not by dirty erosion of dust raw meat etc. convenient for wiping
Feature.The development for making technique is burnt with making, in the past 10 years, single colour glaze gradually develops to colorful glaze；
High temperature color glaze is that the color glaze by fusing point in 1300 DEG C of various different colours is applied according to that need to burn the ceramic works made
On ceramic embryo, after 1300 DEG C of high-temperature firing, abstract, the void being made of color block are showed on ceramic works
Artistic effect unreal, great waves are gorgeous, whole glaze colours is deep serious, sparkling and crystal-clear to moisten, and is other unapproachable skills of ceramic works
The individual style of art effect and high temperature color glaze colored drawing, but be no body of laws burning the ceramic product for the high temperature color glaze color block made
Existing careful polish such as word or fine and smooth stroke such as personage or decorative pattern；
Blue and white porcelain is that painting decoration is carried out on high white clay with natural cobalt material, white clear glaze is being applied, then at 1300 DEG C
At a high temperature of burn and make, finished product white background orchid line shows the figure image or each of is green and luxuriant blue decorative pattern or exquisiteness
Kind word, it appears peaceful beauty, it is bright and clean plain, but the blue and white porcelain products that burning is made can not embody a variety of colors；
At present in technology, high temperature color glaze and blue and white porcelain belong to entirely different artistic style, are individually embodied in ceramic works,
The color block of high temperature color glaze is abstract, it is illusory and blue and white porcelain it is fine and smooth, plain cannot jointly be embodied in same works, it is therefore, right
High temperature color glaze and blue and white porcelain burning are made and propose new requirement.
Invention content
The purpose of the present invention is to provide a kind of high temperature color glazes and blue and white porcelain mixing to burn and make new process, makees in the same ceramics
On product, while high temperature color glaze is embodied and two kinds of blue and white porcelain completes different styles, to meet people to the one of ceramic art works
The new pursuit of kind.
A kind of high temperature color glaze of the present invention and blue and white porcelain mixing burn and make new process, including：Ceramic component embryo, high temperature color glaze face
Color lump, rejecting face, blue and white porcelain sketch the contours figure.
To solve the problems in background technology, the technical solution adopted by the present invention is.
Step（1）, make ceramic component embryo, place room temperature in parch.
Step（2）, according to the design of artistic work, as required on ceramic component embryo apply different proportion it is various
The high temperature coloured glaze color block of color（Wherein the methods such as spray can be used, applies, dip in, putting in manner of application）, place and parched in room temperature.
Step（3）, on ceramic component embryo with pencil it is light sketch the contours of setting blue and white porcelain position.
Step（4）, on the position sketched the contours of with cutter by the high temperature color glaze color block applied reject 1.0mm-
2.0mm thickness forms rejecting face, and it is smooth to be trimmed to rejecting face.
Step（5）, in the face of rejecting apply high white clay, high white clay is fine and smooth, clean, is suitable for the embryo bottom of blue and white porcelain, will reject
The high white clay finishing that face applies is smooth, and former ceramic component embryo is highly consistent.
Step（6）, with cobalt bluepigment do photoghraphic coupler, upper cobalt bluepigment photoghraphic coupler is dipped in paintbrush, on rejecting the high white clay in face
The careful description of progress stroke by stroke, sketches the contours of required blue and white porcelain and sketches the contours figure, place and parched in room temperature.
Step（7）, spray white clear glaze on high white clay, blue and white porcelain sketches the contours figure into color under glaze, places in room temperature and does
Thoroughly.
Step（8）, ceramic component embryo is placed in firing, setting temperature is at 1300 DEG C ± 5 DEG C, ceramic component embryo
Tire in firing, make by the burning of high temperature, and the thawing of high temperature color glaze color block is made to trickle down, forms illusory, abstract color block composition
Pattern；It is color under glaze that blue and white porcelain on high white clay, which sketches the contours figure, cobalt bluepigment photoghraphic coupler will not dizzy dye outward, formed fine and smooth, only
Beautiful white background orchid line pattern；By diel 1300 DEG C from low temperature to high temperature, wicket, natural slow cooling to room temperature shape are opened
State takes out finished product.
Step（9）, take out ceramic product on, high temperature color glaze and 2 kinds of entirely different artistic styles of blue and white porcelain are perfect
Fusion embodies.
The ceramic art works that novel technique of the present invention makes, when being fired in kiln, different colours and different proportion
Coloured glaze melts at high temperature, to flowing down, forms the pattern of virtualization, the combination of abstract color block, boundless air；Blue and white porcelain part
After burning is made, clearly is green and luxuriant blue decorative pattern or word or figure image remarkably true to life, elegant aestheticism, the two are showed
Different artistic styles is perfectly combined embodiment on same ceramic art works, brings a kind of pleasing vision of audience
Sense, while the present invention, have filled up a kind of blank of new process of ceramic works, and embodiment is simple, easy to learn, have pushed ceramics
Burn the development for making technique.
【Description of the drawings】
Fig. 1 is that the ceramic works of the present invention apply high temperature color glaze and blue and white porcelain schematic diagram.
Fig. 2 is ceramic component embryo schematic diagram of the present invention.
Fig. 3 is that bulk ceramics device embryo of the present invention applies high temperature color glaze completion schematic diagram.
Fig. 4 is that the present invention completes rejecting face schematic diagram on ceramic component embryo.
Fig. 5 is that blue and white porcelain sketches the contours schematic diagram on rejecting face of the present invention.
Wherein：A- ceramic components embryo, B- high temperature color glazes color block, C- rejects face, D- blue and white porcelains sketch the contours figure.
【Specific implementation mode】
Hereinafter, preferred embodiments of the present invention will be described, it should be understood that preferred embodiment described herein is only used for
The bright and explanation present invention, is not intended to limit the present invention.
Embodiment
- Fig. 5 refering to fig. 1, a kind of high temperature color glaze and blue and white porcelain mixing burn and make new process, the technical solution adopted by the present invention
It is.
Step（1）, make ceramic component embryo A, place room temperature in parch.
Step（2）, according to the design of artistic work, as required on ceramic component embryo A apply different proportion it is various
The high temperature coloured glaze color block B of color（Wherein the methods such as spray can be used, applies, dip in, putting in manner of application）, place and parched in room temperature.
Step（3）, on ceramic component embryo A with pencil it is light sketch the contours of setting blue and white porcelain position.
Step（4）, rejected with the high temperature coloured glaze color block B that cutter will apply on the position sketched the contours of
1.0mm-2.0mm thickness forms rejecting face C, and it is smooth to be trimmed to rejecting face C.
Step（5）, apply high white clay rejecting face C, high white clay is fine and smooth, clean, is suitable for the embryo bottom of blue and white porcelain, will pick
Except the high white clay finishing that face C is applied is smooth, and former ceramic component embryo A highly consistent.
Step（6）, with cobalt bluepigment do photoghraphic coupler, dip in upper cobalt bluepigment photoghraphic coupler with paintbrush, rejecting face C high white clays
On the careful description of progress stroke by stroke, sketch the contours of required blue and white porcelain and sketch the contours figure D, place and parched in room temperature.
Step（7）, spray white clear glaze on high white clay, blue and white porcelain sketches the contours figure D-shaped into color under glaze, places in room temperature
It parches.
Step（8）, ceramic component embryo A is placed in firing, setting temperature is at 1300 DEG C ± 5 DEG C, ceramic component embryo
Tire A in firing, make by the burning of high temperature, so that high temperature color glaze color block B thawings is trickled down, forms illusory, abstract color block group
At pattern；It is color under glaze that blue and white porcelain on high white clay, which sketches the contours figure D, cobalt bluepigment photoghraphic coupler will not dizzy dye outward, formed it is fine and smooth,
The white background orchid line pattern of aestheticism；By diel from low temperature to high temperature 1300 DEG C ± 5 DEG C, open wicket, natural slow cooling is extremely
Normal temperature state takes out finished product.
Step（9）, take out finished product on, 2 kinds of entirely different artistic styles of high temperature color glaze and blue and white porcelain perfectly merge
It embodies.
The present invention makes experiment through repeatedly burning, because thickness itself is about 5-8mm in ceramic component embryo A；
Rejecting face C thickness is more than 2.0mm, and rejecting face C is too thick, ceramic component embryo's A slight impacts, the ceramic embryo under rejecting face
Wall is too thin broken, is unfavorable for preserving；
Rejecting face C thickness is less than 1.0mm, and high white clay and the ceramic component embryo A rejecting face peripheries C adhesive bond degree are inadequate, touch
After hitting stress, high white clay layer is fallen, and is equally unfavorable for preserving.
A kind of high temperature color glaze of the present invention and blue and white porcelain mixing burn and make new process, and technological process is simple, easy to learn, after the completion of burning is made
Works, it is color block virtualization that polychrome high temperature color glaze is formed, abstract, it is boundless and air, blue and white porcelain white background are blue and white, stroke is fine and smooth,
It is true to nature, elegant and aestheticism, the two kinds of tradition but entirely different art of style is perfectly combined embodiments on same works, be it is a kind of entirely
New ceramic art creation, which is burnt, makes new process, fills up the blank that ceramics burn the industry made, brings the completely new visual impression of audience.
Finally it should be noted that：The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
With technical scheme described in the above embodiments is modified or equivalent replacement of some of the technical features.
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in the present invention's
Within protection domain.
Claims (1)
1. a kind of high temperature color glaze and blue and white porcelain mixing burn and make new process, the technical solution adopted by the present invention is;
Step（1）, make ceramic component embryo, place room temperature in parch；
Step（2）, according to the design of artistic work, as required on ceramic component embryo apply different proportion a variety of colors
High temperature coloured glaze color block（Wherein the methods such as spray can be used, applies, dip in, putting in manner of application）, place and parched in room temperature；
Step（3）, on ceramic component embryo with pencil it is light sketch the contours of setting blue and white porcelain position；
Step（4）, on the position sketched the contours of with cutter by the high temperature color glaze color block applied reject 1.5mm-2.0mm
Thickness forms rejecting face, and it is smooth to be trimmed to rejecting face；
Step（5）, in the face of rejecting apply high white clay, high white clay is fine and smooth, clean, is suitable for the embryo bottom of blue and white porcelain, rejecting face is applied
The high white clay finishing applied is smooth, and former ceramic component embryo is highly consistent；
Step（6）, with cobalt bluepigment do photoghraphic coupler, upper cobalt bluepigment photoghraphic coupler is dipped in paintbrush, one on rejecting the high white clay in face
One careful description of progress, sketches the contours of required blue and white porcelain and sketches the contours figure, place and parched in room temperature；
Step（7）, spray white clear glaze on high white clay, blue and white porcelain sketches the contours figure into color under glaze, places and is parched in room temperature；
Step（8）, ceramic component embryo is placed in firing, setting temperature is at 1300 DEG C, and ceramic component embryo is in firing
In, the burning of high temperature is made, and the thawing of high temperature color glaze color block is made to trickle down, forms the pattern of illusory, abstract color block composition；It is high
It is color under glaze that blue and white porcelain on white clay, which sketches the contours figure, and cobalt bluepigment photoghraphic coupler will not dizzy dye, formation exquisiteness, the white background of aestheticism be blue outward
Line pattern；By diel 1300 DEG C from low temperature to high temperature, wicket is opened, natural slow cooling to normal temperature state takes out finished product.