CN108716061A - A kind of preparation process of anti-bacterial fibre base hydro-entangled composite non-woven fabric - Google Patents
A kind of preparation process of anti-bacterial fibre base hydro-entangled composite non-woven fabric Download PDFInfo
- Publication number
- CN108716061A CN108716061A CN201810584309.8A CN201810584309A CN108716061A CN 108716061 A CN108716061 A CN 108716061A CN 201810584309 A CN201810584309 A CN 201810584309A CN 108716061 A CN108716061 A CN 108716061A
- Authority
- CN
- China
- Prior art keywords
- bacterial fibre
- parts
- fiber
- net
- bacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation processes of anti-bacterial fibre base hydro-entangled composite non-woven fabric, include the following steps:(1)Raw material is configured, 50-55 parts of anti-bacterial fibres, 20-25 parts of chitin fibers, 5-10 parts of carbon fiber, 18-22 parts of polyester fiber are taken;(2)Shredding mixes;(3)Comb lapping;(4)Spun lacing;(5)Soaking paste;(6)Drying.By the above-mentioned means, present invention process is simple and easy to control, non-woven fabrics obtained has excellent antibacterial, bacteriostasis property and intensity.
Description
Technical field
The present invention relates to non-woven technology fields, more particularly to a kind of preparation work of anti-bacterial fibre base hydro-entangled composite non-woven fabric
Skill.
Background technology
With the development of science and technology, non-woven cloth processing technology is continuously improved, non-woven cloth manufacturing process and flow configuration
It is continuously improving and perfect.Non-woven cloth is increasingly deep into as a kind of low raw-material cost, the simple product of manufacturing process
In daily life.Non-woven cloth processing technology according to its at cloth technique can be divided into compound spun lacing, spun lacing, needle thorn, hot wind,
Hot rolling, melt-blown etc. are a variety of, and wherein spun lacing method is more commonly used one kind.Spun lacing method is also known as hydroentanglement processes, water-jet method, penetrates
Stream spray net method, is a kind of unique, novel non-woven cloth processing technology.But the preparation process of existing spun lacing non-woven material
Complexity, it is of high cost, and that there are intensity is low, does not have the defects of anti-microbial property for spun lacing non-woven material obtained.
Invention content
The invention mainly solves the technical problem of providing a kind of preparation process of highly hygroscopic spun lacing non-woven material, technique letters
Single easily-controllable, spun lacing non-woven material obtained has excellent moisture pick-up properties.
In order to solve the above technical problems, one aspect of the present invention is:A kind of anti-bacterial fibre base spun lacing is provided
The preparation process of compound nonwoven cloth, includes the following steps:
(1)Configure raw material, take 50-55 parts of anti-bacterial fibres, 20-25 parts of chitin fibers, 5-10 parts of carbon fiber, 18-22 parts
Polyester fiber;
(2)Shredding mixes, and the anti-bacterial fibre of formula ratio and chitin fiber are mixed to get anti-bacterial fibre mixture through shredding, will
The carbon fiber and polyester fiber of formula ratio are mixed to get reinforcing fiber mixture through shredding;
(3)Lapping is combed, above-mentioned anti-bacterial fibre mixture, reinforcing fiber mixture are passed through to carding machine respectively and comb networking, is obtained
To anti-bacterial fibre net and reinforcing fiber net, anti-bacterial fibre net and reinforcing fiber net are then passed through into drafting machine drawing-off, drafting machine
Draft ratio is 2.8-3.2 times;
(4)Spun lacing, above-mentioned anti-bacterial fibre net and reinforcing fiber net progress spun lacing is compound, obtain the compound fibre of anti-bacterial fibre base spun lacing
Tie up net;
(5)Then soaking paste carries out roller by the infiltration to antibacterial slurry of above-mentioned anti-bacterial fibre base spun lacing composite fiber web through pressure roller
It rolls;
(6)Drying, the anti-bacterial fibre base spun lacing composite fiber web after soaking paste rolling is dried, anti-bacterial fibre base spun lacing is obtained
Compound nonwoven cloth.
In a preferred embodiment of the present invention, the anti-bacterial fibre is nano silver-supported antibacterial fiber.
In a preferred embodiment of the present invention, the step(1)Raw material include:54 parts of anti-bacterial fibres, 22 parts of crusts
Cellulose fiber, 7 parts of carbon fiber, 17 parts of polyester fiber.
The beneficial effects of the invention are as follows:The present invention uses the fibrous raw material of rational formula amount, is spread successively through shredding, combing
Net, spun lacing are compound, antimicrobial treatment obtains anti-bacterial fibre base hydro-entangled composite non-woven fabric, simple for process easily-controllable, non-woven fabrics tool obtained
There are excellent antibacterial, bacteriostasis property and intensity.
Specific implementation mode
The preferred embodiments of the present invention will be described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that so as to make a clearer definition of the protection scope of the present invention.
The embodiment of the present invention includes:
Embodiment one:
A kind of preparation process of anti-bacterial fibre base hydro-entangled composite non-woven fabric, includes the following steps:
(1)Raw material is configured, 53 parts of nano silver-supported antibacterial fibers, 23 parts of chitin fibers, 6 parts of carbon fiber, 18 parts of polyester are taken
Fiber;
(2)Shredding mixes, and the anti-bacterial fibre of formula ratio and chitin fiber are mixed to get anti-bacterial fibre mixture through shredding, will
The carbon fiber and polyester fiber of formula ratio are mixed to get reinforcing fiber mixture through shredding;
(3)Lapping is combed, above-mentioned anti-bacterial fibre mixture, reinforcing fiber mixture are passed through to carding machine respectively and comb networking, is obtained
To anti-bacterial fibre net and reinforcing fiber net, anti-bacterial fibre net and reinforcing fiber net are then passed through into drafting machine drawing-off, drafting machine
Draft ratio is 2.8 times;
(4)Spun lacing, above-mentioned anti-bacterial fibre net and reinforcing fiber net progress spun lacing is compound, obtain the compound fibre of anti-bacterial fibre base spun lacing
Tie up net;
(5)Then soaking paste carries out roller by the infiltration to antibacterial slurry of above-mentioned anti-bacterial fibre base spun lacing composite fiber web through pressure roller
It rolls;
(6)Drying, the anti-bacterial fibre base spun lacing composite fiber web after soaking paste rolling is dried, anti-bacterial fibre base spun lacing is obtained
Compound nonwoven cloth.
Embodiment two:
A kind of preparation process of anti-bacterial fibre base hydro-entangled composite non-woven fabric, includes the following steps:
(1)Raw material is configured, 54 parts of nano silver-supported antibacterial fibers, 22 parts of chitin fibers, 7 parts of carbon fiber, 17 parts of polyester are taken
Fiber;
(2)Shredding mixes, and the anti-bacterial fibre of formula ratio and chitin fiber are mixed to get anti-bacterial fibre mixture through shredding, will
The carbon fiber and polyester fiber of formula ratio are mixed to get reinforcing fiber mixture through shredding;
(3)Lapping is combed, above-mentioned anti-bacterial fibre mixture, reinforcing fiber mixture are passed through to carding machine respectively and comb networking, is obtained
To anti-bacterial fibre net and reinforcing fiber net, anti-bacterial fibre net and reinforcing fiber net are then passed through into drafting machine drawing-off, drafting machine
Draft ratio is 3 times;
(4)Spun lacing, above-mentioned anti-bacterial fibre net and reinforcing fiber net progress spun lacing is compound, obtain the compound fibre of anti-bacterial fibre base spun lacing
Tie up net;
(5)Then soaking paste carries out roller by the infiltration to antibacterial slurry of above-mentioned anti-bacterial fibre base spun lacing composite fiber web through pressure roller
It rolls;
(6)Drying, the anti-bacterial fibre base spun lacing composite fiber web after soaking paste rolling is dried, anti-bacterial fibre base spun lacing is obtained
Compound nonwoven cloth.
Present invention is disclosed a kind of preparation processes of anti-bacterial fibre base hydro-entangled composite non-woven fabric, using the fibre of rational formula amount
Tie up raw material, successively through shredding, comb that lapping, spun lacing be compound, antimicrobial treatment obtains anti-bacterial fibre base hydro-entangled composite non-woven fabric, technique
Simple and easy to control, non-woven fabrics obtained has excellent antibacterial, bacteriostasis property and intensity.
Example the above is only the implementation of the present invention is not intended to limit the scope of the invention, every to utilize this hair
Equivalent structure or equivalent flow shift made by bright description is applied directly or indirectly in other relevant technology necks
Domain is included within the scope of the present invention.
Claims (3)
1. a kind of preparation process of anti-bacterial fibre base hydro-entangled composite non-woven fabric, which is characterized in that include the following steps:
(1)Configure raw material, take 50-55 parts of anti-bacterial fibres, 20-25 parts of chitin fibers, 5-10 parts of carbon fiber, 18-22 parts
Polyester fiber;
(2)Shredding mixes, and the anti-bacterial fibre of formula ratio and chitin fiber are mixed to get anti-bacterial fibre mixture through shredding, will
The carbon fiber and polyester fiber of formula ratio are mixed to get reinforcing fiber mixture through shredding;
(3)Lapping is combed, above-mentioned anti-bacterial fibre mixture, reinforcing fiber mixture are passed through to carding machine respectively and comb networking, is obtained
To anti-bacterial fibre net and reinforcing fiber net, anti-bacterial fibre net and reinforcing fiber net are then passed through into drafting machine drawing-off, drafting machine
Draft ratio is 2.8-3.2 times;
(4)Spun lacing, above-mentioned anti-bacterial fibre net and reinforcing fiber net progress spun lacing is compound, obtain the compound fibre of anti-bacterial fibre base spun lacing
Tie up net;
(5)Then soaking paste carries out roller by the infiltration to antibacterial slurry of above-mentioned anti-bacterial fibre base spun lacing composite fiber web through pressure roller
It rolls;
(6)Drying, the anti-bacterial fibre base spun lacing composite fiber web after soaking paste rolling is dried, anti-bacterial fibre base spun lacing is obtained
Compound nonwoven cloth.
2. the preparation process of anti-bacterial fibre base hydro-entangled composite non-woven fabric according to claim 1, which is characterized in that described anti-
Bacterium fiber is nano silver-supported antibacterial fiber.
3. the preparation process of anti-bacterial fibre base hydro-entangled composite non-woven fabric according to claim 1, which is characterized in that the step
Suddenly(1)Raw material include:54 parts of anti-bacterial fibres, 22 parts of chitin fibers, 7 parts of carbon fiber, 17 parts of polyester fiber.