CN108695012B - 用于形成太阳能电池电极的组合物及使用其制备的电极 - Google Patents
用于形成太阳能电池电极的组合物及使用其制备的电极 Download PDFInfo
- Publication number
- CN108695012B CN108695012B CN201810293273.8A CN201810293273A CN108695012B CN 108695012 B CN108695012 B CN 108695012B CN 201810293273 A CN201810293273 A CN 201810293273A CN 108695012 B CN108695012 B CN 108695012B
- Authority
- CN
- China
- Prior art keywords
- composition
- solar cell
- frit
- glass frit
- cell electrode
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种用于太阳能电池电极的组合物及一种使用所述组合物制作的电极。用于太阳能电池电极的组合物包含:导电粉;玻璃料;以及有机媒剂,其中所述玻璃料包含熔融温度(Tm)为400℃到600℃的第一玻璃料与熔融温度为650℃到800℃的第二玻璃料的混合物。
Description
技术领域
本发明涉及一种用于太阳能电池电极的组合物及一种使用所述组合物制作的电极。更具体来说,本发明涉及一种用于太阳能电池电极的组合物及一种使用所述组合物制作的电极,所述组合物包含熔融温度分别处于特定范围内的第一玻璃料与第二玻璃料的掺合物,且因此可在提供高抗张强度(拉拔强度)及因此提供高可靠性的同时在接触电阻及线电阻方面表现出良好的性质。
背景技术
太阳能电池利用将日光的光子转换成电力的p-n结(p-njunction)的光生伏打效应(photovoltaic effect)来产生电力。在太阳能电池中,分别在具有p-n结的半导体晶片或衬底的上表面及下表面上形成前电极及后电极。然后,由进入半导体晶片的日光诱发p-n结处的光生伏打效应,且通过p-n结处的光生伏打效应而产生的电子经由电极向外部提供电流。太阳能电池的电极是通过施用电极组合物、对所述电极组合物进行图案化及烘烤而形成在晶片上。
为提高太阳能电池的效率而持续减小射极(emitter)厚度可造成分流(shunting),而分流可使太阳能电池的性能劣化。此外,太阳能电池的面积已逐渐增大来实现更高的效率。然而,在这种情形中,可存在因太阳能电池的接触电阻增大而造成效率劣化的问题。
因此,需要一种可在给定不同的表面电阻情况下使对p-n结的不利影响最小化且提高晶片与电极之间的界面处的导电性以降低接触电阻(contact resistance)及线电阻(line resistance)、从而提高太阳能电池效率的用于太阳能电池电极的组合物。
本发明的背景技术公开在未经审查的日本专利公开第2015-144162号中。
发明内容
本发明的一个方面是提供一种可在改善抗张强度(tensile strength)及因此提高可靠性的同时减小接触电阻及线电阻以提供改善的电性质的用于太阳能电池电极的组合物。
本发明的另一方面是提供一种在表现出高抗张强度(拉拔强度(pull strength))及因此表现出高可靠性的同时因低的接触电阻及线电阻而具有良好电性质的太阳能电池电极。
根据本发明的一个方面,一种用于太阳能电池电极的组合物包含:导电粉;玻璃料;以及有机媒剂,其中所述玻璃料包含熔融温度(Tm)为400℃到600℃的第一玻璃料与熔融温度为650℃到800℃的第二玻璃料的掺合物。
所述第一玻璃料可为包含元素碲(Te)及铋(Bi)的碲-铋系玻璃料。
所述第一玻璃料还可包含选自由以下组成的群组的至少一者:锌(Zn)、铅(Pb)、磷(P)、锗(Ge)、镓(Ga)、铈(Ce)、铁(Fe)、锂(Li)、硅(Si)、钨(W)、镁(Mg)、铯(Cs)、锶(Sr)、钼(Mo)、钛(Ti)、锡(Sn)、铟(In)、钒(V)、钡(Ba)、镍(Ni)、铜(Cu)、钠(Na)、钾(K)、砷(As)、钴(Co)、锆(Zr)、锰(Mn)、铝(Al)、及其氧化物。
所述第二玻璃料可为包含元素碲(Te)及铋(Bi)的碲-铋系玻璃料。
所述第一玻璃料对所述第二玻璃料的重量比可介于6∶1到1∶1的范围内。
以所述组合物的总重量计,可存在0.5重量%到10重量%的量的所述第一玻璃料,且以所述组合物的总重量计,可存在0.1重量%到5重量%的量的所述第二玻璃料。
所述组合物可包含:60重量%到95重量%的所述导电粉;1重量%到20重量%的所述玻璃料;以及剩余量为所述有机媒剂。
所述组合物还可包含分散剂、触变剂、塑化剂、粘度稳定剂、消泡剂、颜料、紫外线(ultraviolet,UV)稳定剂、抗氧化剂及偶合剂中的至少一种添加剂。
根据本发明的另一方面,一种太阳能电池电极是使用根据本发明的用于太阳能电池电极的组合物来制作。
本发明提供一种可在改善抗张强度及因此提高可靠性的同时减小接触电阻及线电阻以提供改善的电性质的用于太阳能电池电极的组合物。
另外,本发明提供一种在表现出高抗张强度及因此表现出高可靠性的同时因低的接触电阻及线电阻而具有良好电性质的太阳能电池电极。
附图说明
图1是根据本发明的一个实施例的太阳能电池的示意图。
附图标号说明
10:晶片或衬底;
11:p层或n层;
12:n层或p层;
21:后电极;
23:前电极;
100:太阳能电池。
具体实施方式
以下,将参照附图详细地阐述本发明的实施例。应理解,本发明可用不同的方式来实施而并非仅限于以下实施例。
本文中,玻璃料的“熔融温度”可通过热重法-差热分析(thermogravimetry-differential thermal analysis,TG-DTA)来测量。
本文中,包含在玻璃料中的每一元素金属的含量(mol%)可通过电感耦合等离子体-发射光谱法(inductively coupled plasma-optical emission spectrometry,ICP-OES)来测量。由于电感耦合等离子体-发射光谱法使用非常小的样本,因此可缩短样本制备时间,可减少因样本预处理而造成的误差,且可提高分析灵敏度。
具体来说,电感耦合等离子体-发射光谱法可包括:对样本(即,玻璃料)进行预处理、制备标准溶液以及通过对分析目标的浓度进行测量及转换来计算所述玻璃料中的每一元素金属的含量。
在样本的预处理操作中,可将预定量的样本溶解在酸性溶液中且接着进行加热以发生碳化。此处,酸性溶液可包括例如硫酸(H2SO4)溶液。
可用例如蒸馏水或过氧化氢(H2O2)等溶剂将经碳化样本稀释到使得能够对分析目标进行分析的适当程度。有鉴于电感耦合等离子体-发射光谱测定仪的元素检测能力,经碳化样本可被稀释约10,000倍。
在用电感耦合等离子体-发射光谱测定仪进行测量时,可利用标准溶液(例如用于测量元素的分析目标标准溶液)对经预处理样本进行校准。举例来说,可通过以下方式来计算玻璃料中每一元素的摩尔含量:将标准溶液引入到电感耦合等离子体-发射光谱测定仪中,且用外标法(external standard method)来绘制校准曲线,然后利用电感耦合等离子体-发射光谱测定仪对经预处理样本中的每一元素金属的浓度(ppm)进行测量及转换。
用于太阳能电池电极的组合物
根据本发明的一种用于太阳能电池电极的组合物包含导电粉、玻璃料以及有机媒剂,其中所述玻璃料包含熔融温度(Tm)为400℃到600℃的第一玻璃料与熔融温度为650℃到800℃的第二玻璃料的掺合物。本发明人发现了,包含第一玻璃料与第二玻璃料的掺合物的用于太阳能电池电极的组合物可在提供高抗张强度及因此提供高可靠性的同时因低的接触电阻及低的线电阻而表现出良好的电性质,且因此完成了本发明。
现在,将更详细地阐述根据本发明的用于太阳能电池电极的组合物的每一组分。
导电粉
根据本发明,导电粉可包括银(Ag)粉。银粉可具有纳米级粒度或微米级粒度。举例来说,银粉可具有数十纳米到数百纳米的粒度或数微米到数十微米的粒径。作为另外一种选择,银粉可为具有不同粒度的两种或更多种银粉的混合物。
导电粉可具有各种颗粒形状,例如球形颗粒形状、薄片形颗粒形状、或非晶形颗粒形状,对此并无限制。
优选地,导电粉具有0.1μm到10μm、更优选地0.5μm到5μm的平均粒径(D50)。在此平均粒径范围内,所述组合物可减小太阳能电池的接触电阻及线电阻。可在经由超声波作用在25℃下将导电粉分散在异丙醇(isopropy1 alcohol,IPA)中达3分钟之后,利用例如型号1064D(西莱斯有限公司(CILAS Co.,Ltd.))来测量平均粒径(D50)。
以组合物的总重量计,可存在60重量%到95重量%的量的导电粉。在此范围内,所述组合物可提高太阳能电池的转换效率且可易于制备成膏形式。优选地,以组合物的总重量计,存在70重量%到90重量%的量的导电粉。
玻璃料
玻璃料用于通过在用于太阳能电池电极的组合物的烘烤工艺期间对抗反射层进行刻蚀并对导电粉进行熔融而在射极区(emitter region)中形成银晶粒。此外,玻璃料会提高导电粉与晶片的粘合力,且在烘烤工艺期间被软化以降低烘烤温度。
根据本发明的用于太阳能电池电极的组合物包含具有不同的熔融温度且熔融温度分别处于特定范围内的第一玻璃料与第二玻璃料的掺合物。一般来说,为了降低接触电阻及线电阻且为了提高抗张强度,需要增大玻璃料的含量,从而造成开路电压减小。包含具有不同的熔融温度且熔融温度分别处于特定范围内的第一玻璃料与第二玻璃料的掺合物的根据本发明的用于太阳能电池电极的组合物可在使开路电压的减小最小化的同时表现出低的接触电阻及低的线电阻且提高抗张强度。
接下来,将详细地阐述第一玻璃料及第二玻璃料。
(A)第一玻璃料
第一玻璃料可具有400℃到600℃的熔融温度。在此范围内,第一玻璃料可减小接触电阻及线电阻。优选地,第一玻璃料具有450℃到500℃的熔融温度。
第一玻璃料可为包含元素碲(Te)及铋(Bi)的碲-铋系玻璃料。当第一玻璃料包含元素碲及铋时,可易于确保熔融温度处于上述范围内且第一玻璃料可稳定地刻蚀抗反射层,从而使接触电阻方面的性质得到改善。
第一玻璃料除碲及铋外还可包含金属和/或金属氧化物。举例来说,第一玻璃料还可包含选自由以下组成的群组的至少一者:锌(Zn)、铅(Pb)、磷(P)、锗(Ge)、镓(Ga)、铈(Ce)、铁(Fe)、锂(Li)、硅(Si)、钨(W)、镁(Mg)、铯(Cs)、锶(Sr)、钼(Mo)、钛(Ti)、锡(Sn)、铟(In)、钒(V)、钡(Ba)、镍(Ni)、铜(Cu)、钠(Na)、钾(K)、砷(As)、钴(Co)、锆(Zr)、锰(Mn)、铝(Al)、及其氧化物。
在一个实施例中,第一玻璃料可为包含元素碲及铋的Te-Bi-O玻璃料。优选地,Te-Bi-O玻璃料包含45mol%到75mol%的碲及5mol%到20mol%的铋。当元素金属的量落在此范围内时,第一玻璃料可在接触电阻及线电阻方面提供良好的性质。
在另一实施例中,第一玻璃料可为包含元素碲、铋及锌的Te-Bi-Zn-O玻璃料。优选地,Te-Bi-Zn-O玻璃料包含45mol%到75mol%的碲、5mol%到20mol%的铋及1mol%到20mol%的锌。当元素金属的量落在此范围内时,第一玻璃料可在接触电阻及线电阻方面提供良好的性质。
可通过所属领域中已知的任何典型方法由氧化碲、氧化铋及视需要金属和/或金属氧化物来制备第一玻璃料。举例来说,可通过以下方式来制备第一玻璃料:利用球磨机(ballmill)或行星式磨机(planetary mill)将氧化碲、氧化铋及视需要金属和/或金属氧化物进行混合,在800℃到1300℃下对此混合物进行熔融,并将经熔融混合物淬火到25℃,然后利用盘磨机(disk mill)、行星式磨机等将所获得的产物粉碎。
以用于太阳能电池电极的组合物的总重量计,可存在0.5重量%到10重量%的量的第一玻璃料。在此范围内,第一玻璃料可在提高抗张强度的同时在接触电阻及线电阻方面提供良好的性质。优选地,以用于太阳能电池电极的组合物的总重量计,存在1重量%到6重量%的量的第一玻璃料。
(B)第二玻璃料
第二玻璃料可具有650℃到800℃的熔融温度。在此范围内,第二玻璃料可在提高抗张强度的同时防止开路电压减小。优选地,第二玻璃料具有700℃到750℃的熔融温度。
第二玻璃料可为包含元素碲及铋的碲-铋系玻璃料。当第一玻璃料及第二玻璃料二者均包含元素碲时,此组合物可表现出进一步提高的抗张强度。
第二玻璃料除碲及铋外还可包含金属和/或金属氧化物。举例来说,第二玻璃料还可包含选自由以下组成的群组的至少一者:锌(Zn)、铅(Pb)、磷(P)、锗(Ge)、镓(Ga)、铈(Ce)、铁(Fe)、锂(Li)、硅(Si)、钨(W)、镁(Mg)、铯(Cs)、锶(Sr)、钼(Mo)、钛(Ti)、锡(Sn)、铟(In)、钒(V)、钡(Ba)、镍(Ni)、铜(Cu)、钠(Na)、钾(K)、砷(As)、钴(Co)、锆(Zr)、锰(Mn)、铝(A1)、及其氧化物。
在一个实施例中,第二玻璃料可为包含元素碲及铋的Te-Bi-O玻璃料。优选地,Te-Bi-O玻璃料包含5mol%到20mol%的碲及10mol%到30mol%的铋。当元素金属的量落在此范围内时,第二玻璃料可提供改善的抗张强度。
在另一实施例中,第二玻璃料可为包含元素碲、铋及钨的Te-Bi-W-O玻璃料。优选地,Te-Bi-W-O玻璃料包含5mol%到20mol%的碲、10mol%到30mol%的铋及5mol%到30mol%的钨。当元素金属的量落在此范围内时,第二玻璃料可提供改善的抗张强度。
可通过所属领域中已知的任何典型方法由氧化碲、氧化铋及视需要金属和/或金属氧化物来制备第二玻璃料。可利用与制备第一玻璃料相同的方式来制备第二玻璃料。
以用于太阳能电池电极的组合物的总重量计,可存在0.1重量%到5重量%的量的第二玻璃料。在此范围内,第二玻璃料可在提高抗张强度的同时减小接触电阻及线电阻。优选地,以用于太阳能电池电极的组合物的总重量计,存在0.5重量%到3重量%的量的第二玻璃料。
第一玻璃料和/或第二玻璃料的形状及大小无特别限制。举例来说,第一玻璃料和/或第二玻璃料可具有0.1μm到10μm的平均粒径(D50)。另外,第一玻璃料和/或第二玻璃料可具有球形形状或非晶形状。
可在经由超声波作用在25℃下将玻璃料粉分散在异丙醇(IPA)中达3分钟之后,利用例如型号1064D(西莱斯有限公司)来测量平均粒径(D50)。
第一玻璃料对第二玻璃料的重量比(第一玻璃料:第二玻璃料)可介于6∶1到1∶1的范围内。在此重量比范围内,组合物可在具有提高的抗张强度的同时表现出减小的接触电阻及线电阻。优选地,第一玻璃料对第二玻璃料的重量比介于4∶1到1∶1的范围内。
以用于太阳能电池电极的组合物的总重量计,可存在1重量%到20重量%、具体来说2重量%到15重量%的量的包含第一玻璃料及第二玻璃料的玻璃料。在此范围内,玻璃料可确保在各种片电阻下p-n结的稳定性,使线电阻最小化,且最终提高太阳能电池的效率。
有机媒剂
有机媒剂通过与用于太阳能电池电极的组合物的无机组分进行机械混合而对所述组合物赋予适合于印刷的合适的粘度及流变特性。
有机媒剂可为用于太阳能电池电极的组合物中所使用的任何典型有机媒剂,且可包含粘合剂树脂、溶剂等。
粘合剂树脂可选自丙烯酸酯树脂或纤维素树脂。一般使用乙基纤维素作为所述粘合剂树脂。另外,可使用以下中的粘合剂树脂:乙基羟乙基纤维素、硝基纤维素、乙基纤维素与酚树脂的掺合物、醇酸树脂、酚树脂、丙烯酸酯树脂、二甲苯树脂、聚丁烷树脂(polybutane resin)、聚酯树脂、脲树脂、三聚氰胺树脂、乙酸乙烯酯树脂、木松香、醇的聚甲基丙烯酸酯等。
溶剂可选自由例如以下组成的群组:己烷、甲苯、乙基溶纤剂、环己酮、丁基溶纤剂、丁基卡必醇(二乙二醇单丁醚)、二丁基卡必醇(二乙二醇二丁醚)、丁基卡必醇乙酸酯(二乙二醇单丁醚乙酸酯)、丙二醇单甲醚、己二醇、萜品醇、甲基乙基酮、苯甲醇、γ-丁内酯、及乳酸乙酯。这些溶剂可单独使用或以其混合物形式使用。
用于太阳能电池电极的组合物可包含剩余量的有机媒剂。优选地,以组合物的总重量计,存在1重量%到30重量%的量的有机媒剂。在此范围内,有机媒剂可对所述组合物提供足够的粘合强度及良好的可印刷性。
添加剂
根据本发明的用于太阳能电池电极的组合物根据需要还可包含任何典型添加剂以增强流动性、工艺性质及稳定性。添加剂可包括分散剂、触变剂、塑化剂、粘度稳定剂、消泡剂、颜料、紫外线稳定剂、抗氧化剂、偶合剂等。这些添加剂可单独使用或以其混合物形式使用。以用于太阳能电池电极的组合物的总重量计,可存在0.1重量%到5重量%的量的添加剂,但所述添加剂的含量可根据需要进行改变。
太阳能电池电极及包括所述太阳能电池电极的太阳能电池
本发明的其他方面涉及一种由用于太阳能电池电极的组合物形成的电极以及一种包括所述太阳能电池电极的太阳能电池。图1示出根据本发明的一个实施例的太阳能电池100。
参照图1,可通过以下方式来形成后电极21及前电极23:将用于电极的组合物印刷在包括p层(或n层)11及n层(或p层)12作为射极的晶片或衬底10上,然后进行烘烤。举例来说,通过以下方式来执行制备后电极的初步工艺:将组合物印刷在晶片10的背面上且在约200℃到约400℃下将经印刷组合物干燥约10秒到60秒。此外,可通过将组合物印刷在晶片10的前表面上且对经印刷组合物进行干燥来执行用于制备前电极23的初步工艺。接着,可通过在约400℃到约950℃下、优选地在约700℃到约950℃下将晶片10烘烤约30秒到210秒来形成前电极23及后电极21。
接下来,将参照实例更详细地阐述本发明。然而,应注意,提供这些实例仅用于说明,且不应理解为以任何方式限制本发明。
在实例及比较例中使用的玻璃料的细节示于表1及表2中。表1示出第一玻璃料的细节,且表2示出第二玻璃料的细节。第一玻璃料及第二玻璃料中所包含的每一元素金属的含量是通过上述电感耦合等离子体-发射光谱法来测量。第一玻璃料及第二玻璃料中的每一者的熔融温度是通过上述热重法-差热分析来测量。
表1
Te(mol%) | Bi(mo1%) | Zn(mol%) | Li(mol%) | W(mol%) | 熔融温度(℃) | |
Al | 75.0 | 10.5 | 7.0 | 4.5 | 3.0 | 400 |
A2 | 60.5 | 12.5 | 12.5 | 4.0 | 10.5 | 600 |
A3 | 70.0 | 10.0 | 5.0 | 12.0 | 3.0 | 380 |
A4 | 60.5 | 12.5 | 10.0 | 3.5 | 13.5 | 620 |
表2
Te(mol%) | Bi(mol%) | Zn(mo1%) | Li(mol%) | W(mol%) | Si(mol%) | 熔融温度(℃) | |
B1 | 15.0 | 15.0 | 14.5 | 13.5 | 7.0 | 35.0 | 650 |
B2 | 10.0 | 15.0 | 15.0 | 9.0 | 15.0 | 36.0 | 800 |
B3 | 20.0 | 10.0 | 14.5 | 15.5 | 5.0 | 35.0 | 630 |
B4 | 10.0 | 17.0 | 13.5 | 7.0 | 30.0 | 22.5 | 820 |
实例1
作为有机粘合剂,在60℃下将1.0重量%的乙基纤维素(STD4,陶氏化学公司(DowChemical Company))充分溶解在6.5重量%的丁基卡必醇中,且向此粘合剂溶液中添加了89.0重量%的平均粒径为1.0μm的球形银粉(AG-4-8,同和高级技术有限公司(DowaHightech Co.,Ltd.))、3.0重量%的玻璃料、0.2重量%的分散剂BYK 102(毕克化学公司(BYK-chemie))及0.3重量%的触变剂Thixatrol ST(海名斯有限公司(Elementis Co.,Ltd.)),然后在3辊捏合机中进行混合及捏合,从而制备用于太阳能电池电极的组合物。此处,作为玻璃料,表1及表2的第一玻璃料及第二玻璃料的用量如表3所列。
实例2到实例4
除了将第一玻璃料及第二玻璃料的种类及量变为如表3所列以外,以与实例1相同的方式制备了用于太阳能电池电极的组合物。
比较例1
除了不使用第二玻璃料以外,以与实例1相同的方式制备了用于太阳能电池电极的组合物。
比较例2
除了不使用第一玻璃料以外,以与实例1相同的方式制备了用于太阳能电池电极的组合物。
比较例3
除了使用A3替代A1作为第一玻璃料以外,以与实例1相同的方式制备了用于太阳能电池电极的组合物。
比较例4
除了使用A4替代A1作为第一玻璃料以外,以与实例1相同的方式制备了用于太阳能电池电极的组合物。
比较例5
除了使用B3替代B1作为第二玻璃料以外,以与实例1相同的方式制备了用于太阳能电池电极的组合物。
比较例6
除了使用B4替代B1作为第二玻璃料以外,以与实例1相同的方式制备了用于太阳能电池电极的组合物。
使用在实例及比较例中制备的用于太阳能电池电极的组合物中的每一者制作了太阳能电池,且接着关于接触电阻、线电阻及抗张强度进行了评估。结果示出于表3中。
太阳能电池的制作
通过以预定图案进行网版印刷、然后在红外线(infrared ray,IR)干燥炉中在300℃到400℃下干燥1分钟而将在实例及比较例中制备的用于太阳能电池电极的组合物中的每一者沉积在晶片(通过对掺杂有硼(B)的p型晶片的前表面进行纹理化、在纹理化表面上形成POCL3的n+层、并在n+层上形成由氮化硅(SiNx:H)形成的抗反射膜而制备的多晶晶片)的前表面之上。接着,将铝膏印刷在晶片的背面上并以与上述相同的方式进行了干燥。将根据此程序形成的电池在带型烘烤炉中在400℃到900℃的温度下烘烤50秒,从而制作太阳能电池。
(1)接触电阻
使用接触电阻测定仪(GP 4-TEST Pro.)在上面印刷有1cm*2.0cm的指状杆(finger bar)的电池上对接触电阻(Rc)进行了测量。
(2)线电阻
使用电阻测定仪(吉时利(Keithley)2200)在暗室中在上面印刷有3cm的指状杆的电池上对线电阻(RL)进行了测量。
(3)抗张强度
对所制作的太阳能电池中的每一者的电极施加助焊剂(Flux)并接着在300℃到400℃下使用焊铁(白光有限公司(Hakko Co.,Ltd.))结合到带。接着,使用张紧器(天氏欧森公司(Tinus Olsen))评估在180°的剥离角度及50mm/min的拉伸速率条件下所得产物的抗张强度(N/mm)。优选地,电极具有3.7N/mm或高于3.7N/mm、例如3.7N/mm到5.0N/mm的抗张强度。在此抗张强度范围内,电极可具有高可靠性。
(4)开路电压
使用太阳能电池效率测定仪CT-801(帕桑有限公司(Pasan Co.,Ltd.))对所制作的太阳能电池中的每一者的开路电压(Voc)进行了测量。
表3
如表3所示,可以看到,根据本发明的用于太阳能电池电极的组合物表现出低接触电阻及线电阻以及高开路电压,从而提供良好的电性质及高抗张强度。
相反地,仅使用第一玻璃料而不使用第二玻璃料的比较例1的组合物表现出低抗张强度及低开路电压,且仅使用第二玻璃料而不使用第一玻璃料的比较例2的组合物表现出高接触电阻。另外,与实例2的组合物相比,使用熔融温度处于本发明所规定的范围之外的玻璃料的比较例3到比较例6的组合物在接触电阻、线电阻、抗张强度及开路电压方面表现出更差的性质。
应理解,在不背离本发明的精神及范围的条件下,所属领域中的技术人员可做出各种修改、改变、变更及等效实施例。
Claims (9)
1.一种用于太阳能电池电极的组合物,其特征在于,包含:导电粉;玻璃料;以及有机媒剂,
其中所述玻璃料包含熔融温度为400℃到600℃的第一玻璃料与熔融温度为650℃到800℃的第二玻璃料的掺合物。
2.根据权利要求1所述的用于太阳能电池电极的组合物,其特征在于,所述第一玻璃料是包含元素碲及铋的碲-铋系玻璃料。
3.根据权利要求2所述的用于太阳能电池电极的组合物,其特征在于,所述第一玻璃料还包含选自由以下组成的群组的至少一者:锌、铅、磷、锗、镓、铈、铁、锂、硅、钨、镁、铯、锶、钼、钛、锡、铟、钒、钡、镍、铜、钠、钾、砷、钴、锆、锰、铝、及其氧化物。
4.根据权利要求1所述的用于太阳能电池电极的组合物,其特征在于,所述第二玻璃料是包含元素碲及铋的碲-铋系玻璃料。
5.根据权利要求1所述的用于太阳能电池电极的组合物,其特征在于,所述第一玻璃料对所述第二玻璃料的重量比介于6∶1到1∶1的范围内。
6.根据权利要求1所述的用于太阳能电池电极的组合物,其特征在于,以所述组合物的总重量计,存在0.5重量%到10重量%的量的所述第一玻璃料,且以所述组合物的总重量计,存在0.1重量%到5重量%的量的所述第二玻璃料。
7.根据权利要求1所述的用于太阳能电池电极的组合物,其特征在于,包含:
60重量%到95重量%的所述导电粉;
1重量%到20重量%的所述玻璃料;以及
剩余量为所述有机媒剂。
8.根据权利要求1所述的用于太阳能电池电极的组合物,其特征在于,还包含:分散剂、触变剂、塑化剂、粘度稳定剂、消泡剂、颜料、紫外线稳定剂、抗氧化剂及偶合剂中的至少一种添加剂。
9.一种太阳能电池电极,其特征在于,使用根据权利要求1到8中任一项所述的用于太阳能电池电极的组合物来制作。