CN108659726A - A kind of height for CNC cuttings glues PE protective films and preparation method thereof - Google Patents
A kind of height for CNC cuttings glues PE protective films and preparation method thereof Download PDFInfo
- Publication number
- CN108659726A CN108659726A CN201810358681.7A CN201810358681A CN108659726A CN 108659726 A CN108659726 A CN 108659726A CN 201810358681 A CN201810358681 A CN 201810358681A CN 108659726 A CN108659726 A CN 108659726A
- Authority
- CN
- China
- Prior art keywords
- height
- protective films
- glues
- material layer
- base material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of height for CNC cuttings to glue PE protective films; it is made of composite base material layer and acrylic pressure sensitive glue-line; the composite base material layer melts co-extrusions by three layers of PE base materials and blows, the PE base materials include according to the weight percentage of raw materials 35~70% low density polyethylene (LDPE), 20~40% high density polyethylene (HDPE) and 5~10% metallocene linear-low density polyethylene.The present invention is used as composite base material layer by the way that three layers of PE base materials are compound; effectively increase brittleness and deflection that the height glues PE protective film entirety; the processing performances such as excellent cutting, punching are made it have, common protective film is solved and is easy to warp in CNC cutting process, bursts and scrap and other issues.The invention also discloses the preparation methods that the height glues PE protective films; it prepares composite base material layer by the way of melting coextrusion film blowing using three layers; acrylate pressure-sensitive adhesive is coated with by the recessed coating methods of V simultaneously so that the finished product being prepared into has both excellent flatness and winding performance.
Description
Technical field
The present invention relates to protective film field, more particularly to a kind of high viscous PE protective films.
Background technology
Protective film is a kind of to film material of the other materials with defencive function and a kind of pressure sensitive adhesive product.PE is protected
Cuticula biggest advantage is that protected product is made to produce and process, transport, not contaminated during storage and use, corrosion,
It scratches, original bright and clean glossy surface is protected, to improve the quality and the market competitiveness of product.
In the protective film cut for CNC, PE protective films are most widely used at present.It was used in CNC cutting processings
Cheng Zhongxu passes through the process such as various cutting fluids are rinsed, pickle impregnates, therefore film is not only claimed with centainly crisp
Degree and deflection are easy to cut punching, and require it with excellent anti-permeability to prevent from cutting during CNC cutting processings
It cuts liquid or cleaning solution osmotic protection film destroys affixed object, while also requiring it with suitable initial bonding strength and holding power to meet
Requirement during CNC cutting processings, after avoiding it from causing in process because viscous force deficiency causes to warp or viscosity is excessive
The problem of continuous hardly possible dyestripping.And the PE protective films for being used for CNC cuttings in the prior art are difficult to have both above-mentioned a variety of excellent performances, quilt
The yields of patch object still needs to be further increased.
Invention content
It is an object of the invention in view of the above shortcomings of the prior art, provide a kind of viscous PE guarantors of the height for CNC cuttings
Cuticula, while the preparation method that the height glues PE protective films being provided.
The technical solution used in the present invention is:A kind of height for CNC cuttings glues PE protective films, by composite base material layer
It is formed with acrylic pressure sensitive glue-line, the composite base material layer melts co-extrusion by three layers of PE base materials and blows, and the PE base materials are pressed
Raw material weight percentages include 35~70% low density polyethylene (LDPE), 20~40% high density polyethylene (HDPE) and 5~10%
Metallocene linear-low density polyethylene.
As being further improved for said program, the acrylic pressure sensitive glue-line includes by parts by weight of raw materials:Oiliness poly- third
100 parts of olefin(e) acid resin, 200~230 parts of ethyl acetate, 20~30 parts of organic solvent, 4~6 parts of composite curing agent.Specifically, originally
The acrylate pressure sensitive adhesive of invention has excellent flow leveling, it is ensured that and planarization is good after follow-up drying winding, while its formation
Glue-line does not reduce the brittleness of composite base material layer, and has excellent adhesive force with composite base material layer.The acrylic pressure sensitive of the present invention
Glue-line and affixed object viscous force are moderate, remove without residue glue.
As being further improved for said program, the composite curing agent is by 3~4 parts of Isocyanates curing agent and 1
~2 parts of epoxy curing agent is combined.Specifically, which can further improve the viscous PE protective films of the height
Anti-permeability and resistance to acid and alkali.
As being further improved for said program, the organic solvent is toluene.
As being further improved for said program, the thickness which glues PE protective films is 50~100 μm.
A kind of height as described above for CNC cuttings glues the preparation method of PE protective films comprising following processing step:
1) it puts into and is come in the three-layer co-extruded inflation film manufacturing machine of dust pelletizing system after mixing each raw material component in PE base materials, passed through
The composite base material layer that three layers of melting co-extrusion, stainless steel filtering net group filter, blow to be combined by three layers of PE base materials;
2) based on parts by weight of raw materials by each component mixing preparation of acrylic pressure sensitive glue-line at after acrylate pressure sensitive adhesive use V
Recessed coating method is coated on composite base material layer upper surface obtained by step 1), through levelling, curing oven, obtain high viscous PE protective films at
Product.
As being further improved for said program, during step 1) three layers of melting co-extrusion controlled at 165~
185℃。
As being further improved for said program, step 1) the stainless steel filtering net group combined by five layer of 300 mesh filter screen and
At.
As being further improved for said program, the solidification temperature of the step 2) curing oven is 75~95 DEG C.
The beneficial effects of the invention are as follows:
The present invention is used as composite base material layer by the way that three layers of PE base materials are compound, effectively increases the height and glues PE protective film entirety
Brittleness and deflection make it have the processing performances such as excellent cutting, punching, solve common protective film in CNC cutting process
It is easy to warp, bursts and scrap and other issues.
The present invention prepares composite base material layer, simultaneously by improving preparation process by the way of melting coextrusion film blowing using three layers
It is coated with acrylate pressure-sensitive adhesive by the recessed coating methods of V so that the finished product being prepared into has both excellent flatness and winding performance.
Specific implementation mode
The present invention is specifically described with reference to embodiment, in order to technical field personnel to the present invention
Understand.It is necessary to it is emphasized that embodiment is only intended to, the present invention will be further described herein, should not be understood as to this
The limitation of invention protection domain, fields person skilled in the art, the non-intrinsically safe that the present invention is made according to foregoing invention content
The modifications and adaptations of property, should still fall within protection scope of the present invention.Mentioned raw materials following simultaneously are unspecified, are
Commercial product;The processing step or preparation method not referred in detail be processing step known to a person skilled in the art or
Preparation method.
Embodiment 1
A kind of height for CNC cuttings glues PE protective films, and the thickness which glues PE protective films is 50 μm, by composite base material
Layer and acrylic pressure sensitive glue-line composition, the composite base material layer melt co-extrusion by three layers of PE base materials and blow.
Wherein, the PE base materials include 35% low density polyethylene (LDPE), 40% high density according to the weight percentage of raw materials
Polyethylene, 5% metallocene linear-low density polyethylene and 20% PE;The acrylic pressure sensitive glue-line presses parts by weight of raw materials packet
It includes:100 parts of oiliness polyacrylic resin, 200 parts of ethyl acetate, 30 parts of toluene, 3 parts of Isocyanates curing agent and epoxy resin
2 parts of curing agent.
Preparation method:
1) it puts into and is come in the three-layer co-extruded inflation film manufacturing machine of dust pelletizing system after mixing each raw material component in PE base materials, passed through
The composite base material layer that three layers of melting co-extrusion, stainless steel filtering net group filter, blow to be combined by three layers of PE base materials, wherein described
Controlled at 165 DEG C during three layers of melting co-extrusion, the stainless steel filtering net group is composed of five layer of 300 mesh filter screen;
2) based on parts by weight of raw materials by each component mixing preparation of acrylic pressure sensitive glue-line at after acrylate pressure sensitive adhesive use V
Recessed coating method is coated on composite base material layer upper surface obtained by step 1), and through levelling, curing oven, solidification temperature is 75 DEG C, is obtained
1 finished product of embodiment.
Embodiment 2
A kind of height for CNC cuttings glues PE protective films, and the thickness which glues PE protective films is 100 μm, by composite base
Material layer and acrylic pressure sensitive glue-line composition, the composite base material layer melt co-extrusion by three layers of PE base materials and blow.
Wherein, the PE base materials include 70% low density polyethylene (LDPE), 20% high density according to the weight percentage of raw materials
Polyethylene and 10% metallocene linear-low density polyethylene;The acrylic pressure sensitive glue-line includes by parts by weight of raw materials:Oiliness
100 parts of polyacrylic resin, 230 parts of ethyl acetate, 20 parts of toluene, 4 parts of Isocyanates curing agent and epoxy curing agent 1
Part.
Preparation method:
1) it puts into and is come in the three-layer co-extruded inflation film manufacturing machine of dust pelletizing system after mixing each raw material component in PE base materials, passed through
The composite base material layer that three layers of melting co-extrusion, stainless steel filtering net group filter, blow to be combined by three layers of PE base materials, wherein described
Controlled at 185 DEG C during three layers of melting co-extrusion, the stainless steel filtering net group is composed of five layer of 300 mesh filter screen;
2) based on parts by weight of raw materials by each component mixing preparation of acrylic pressure sensitive glue-line at after acrylate pressure sensitive adhesive use V
Recessed coating method is coated on composite base material layer upper surface obtained by step 1), and through levelling, curing oven, solidification temperature is 95 DEG C, is obtained
2 finished product of embodiment.
Embodiment 3
A kind of height for CNC cuttings glues PE protective films, and the thickness which glues PE protective films is 70 μm, by composite base material
Layer and acrylic pressure sensitive glue-line composition, the composite base material layer melt co-extrusion by three layers of PE base materials and blow.
Wherein, the PE base materials include 50% low density polyethylene (LDPE), 30% high density according to the weight percentage of raw materials
Polyethylene, 8% metallocene linear-low density polyethylene and 12% PE;The acrylic pressure sensitive glue-line presses parts by weight of raw materials packet
It includes:100 parts of oiliness polyacrylic resin, 210 parts of ethyl acetate, 25 parts of toluene, 3 parts of Isocyanates curing agent and epoxy resin
1 part of curing agent.
Preparation method:
1) it puts into and is come in the three-layer co-extruded inflation film manufacturing machine of dust pelletizing system after mixing each raw material component in PE base materials, passed through
The composite base material layer that three layers of melting co-extrusion, stainless steel filtering net group filter, blow to be combined by three layers of PE base materials, wherein described
Controlled at 175 DEG C during three layers of melting co-extrusion, the stainless steel filtering net group is composed of five layer of 300 mesh filter screen;
2) based on parts by weight of raw materials by each component mixing preparation of acrylic pressure sensitive glue-line at after acrylate pressure sensitive adhesive use V
Recessed coating method is coated on composite base material layer upper surface obtained by step 1), and through levelling, curing oven, solidification temperature is 85 DEG C, is obtained
3 finished product of embodiment.
Embodiment 4
1~3 gained finished product of above-described embodiment is subjected to correlated performance test respectively, test result is as follows shown in table 1:
1 Examples 1 to 3 of table forms a film and correlated performance test result
Above-described embodiment is the preferred embodiment of the present invention, it is all with similar technique of the invention and made by equivalence changes,
The protection category of the present invention should all be belonged to.
Claims (9)
1. a kind of height for CNC cuttings glues PE protective films, it is characterised in that:By composite base material layer and acrylic pressure sensitive glue-line group
At the composite base material layer melts co-extrusion by three layers of PE base materials and blows, and the PE base materials wrap according to the weight percentage of raw materials
Include 35~70% low density polyethylene (LDPE), 20~40% high density polyethylene (HDPE) and 5~10% metallocene linear low density it is poly-
Ethylene.
2. a kind of height for CNC cuttings according to claim 1 glues PE protective films, it is characterised in that:The acrylic acid
Pressure-sensitive adhesive layer includes by parts by weight of raw materials:100 parts of oiliness polyacrylic resin, 200~230 parts of ethyl acetate, organic solvent 20
~30 parts, 4~6 parts of composite curing agent.
3. a kind of height for CNC cuttings according to claim 2 glues PE protective films, it is characterised in that:The composite solid
Agent is combined by 3~4 parts of Isocyanates curing agent and 1~2 part of epoxy curing agent.
4. a kind of height for CNC cuttings according to claim 2 glues PE protective films, it is characterised in that:It is described organic molten
Agent is toluene.
5. a kind of height for CNC cuttings according to claim 1 glues PE protective films, it is characterised in that:The height, which glues PE, to be protected
The thickness of cuticula is 50~100 μm.
6. a kind of preparation method for gluing PE protective films for the height of CNC cuttings such as Claims 1 to 5 any one of them, special
Sign is to comprise the technical steps that:
1) it puts into and is come in the three-layer co-extruded inflation film manufacturing machine of dust pelletizing system after mixing each raw material component in PE base materials, through three layers
The composite base material layer that melting co-extrusion, stainless steel filtering net group filter, blow to be combined by three layers of PE base materials;
2) based on parts by weight of raw materials by each component mixing preparation of acrylic pressure sensitive glue-line at after acrylate pressure sensitive adhesive use the recessed paintings of V
Cloth method is coated on composite base material layer upper surface obtained by step 1) and obtains high viscous PE protective films finished product through levelling, curing oven.
7. a kind of height for CNC cuttings according to claim 6 glues the preparation method of PE protective films, it is characterised in that:
Controlled at 165~185 DEG C during step 1) three layers of melting co-extrusion.
8. a kind of height for CNC cuttings according to claim 6 glues the preparation method of PE protective films, it is characterised in that:
Step 1) the stainless steel filtering net group is composed of five layer of 300 mesh filter screen.
9. a kind of height for CNC cuttings according to claim 6 glues the preparation method of PE protective films, it is characterised in that:
The solidification temperature of the step 2) curing oven is 75~95 DEG C.