CN108659712A - 一种新能源汽车用漆面抛光剂 - Google Patents
一种新能源汽车用漆面抛光剂 Download PDFInfo
- Publication number
- CN108659712A CN108659712A CN201810412430.2A CN201810412430A CN108659712A CN 108659712 A CN108659712 A CN 108659712A CN 201810412430 A CN201810412430 A CN 201810412430A CN 108659712 A CN108659712 A CN 108659712A
- Authority
- CN
- China
- Prior art keywords
- parts
- polishing agent
- new
- energy automobile
- finish polishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种新能源汽车用漆面抛光剂。包括如下重量份数的组分：微晶蜡5‑10份,月桂蜡5‑10份，溶剂10‑30份，表面活性剂1‑5份，二甲基硅油3‑8份，无机磨料3‑5份，水30‑60份。本发明制备的新能源汽车用漆面抛光剂，用于新能源汽车漆面的抛光，抛光后，光泽度高，防腐蚀性能好，抛光剂采用涂抹擦拭的方式使用，使用方法简单，抛光剂在高温条件下性能稳定，保存时间长，该抛光剂的制备方法简单，适合大规模工业化生产。
Description
技术领域
本发明属于汽车美容技术领域，具体涉及一种新能源汽车用漆面抛光剂。
背景技术
汽车车身表面的涂层赋予了汽车漂亮的外观和优良的防护性能，可以提高汽车的使用价值，延长其使用寿命。汽车作为交通工具使用环境十分复杂，既要经受酷暑、严寒、风吹、日晒、雨淋的考验，又要承受尘埃、废气、燃料、公路沥青、泥浆以及机械蹭擦的侵害，一般来说，汽车涂层的寿命在良好的保养和正常维护之下是可以与汽车的使用寿命相近的，车身涂层可以达到长期的装饰效果。
汽车表面涂层受到诸多因索的影响，需要科学地加以保护，而漆面抛光是汽车涂层保养中最为重要的部分，汽车涂层在去除顽固硬膜时，可以通过摩擦加速顽固硬膜的去除，同时使漆而平整光洁或在彻底清洁后根据漆面的损伤程度以抛光剂做抛光处理，使划痕、表面破破、漆面橘皮和流挂等缺陷得到修复，恢复均匀、平整光亮的表观效果。抛光剂及抛光技术直接关系到漆面保养的最终效果。
专利201410507004.9公开了一种高性能汽车抛光剂。由以下重量份的成份组成：乙基溶纤剂3-7份，羧甲基纤维素3-10份，甘油4-6份，三氟乙醇6-11份，缓蚀剂4-8份，环烷烃2-6份，地蜡7-11份，烷基糖苷4-9份，三乙醇胺5-10份，十二醇醚硫酸钠4-10份，溶剂汽油2-4份，水15份。该抛光剂虽然耐腐蚀，但是，抛光的光泽度不高，抛光过程较复杂，需要反复抛光好几次。
专利201310481932.8公开了一种乳化型车用抛光剂及其制备方法。按照重量百分比，其包括：一种乳化型车用抛光剂，按照重量百分比，其包括：蜂蜡10-20％、氧化微晶蜡6-8％、乳化硅油1-4％、甘遂1-2％、二烷基苯磺酸钠2-4％、柠檬酸钠4-8％、昆布3-6％、清香剂1-2％，芳樟醇5-8％、二氧化铈1-2％、氧化锑4-6％、白砒1-2％、丙二酸2-6％、叠氮化钠3-8％、焦磷酸二氢钠4-6％、其余为去离子水。该抛光剂使用比较方便快捷，节约资源，但是其不耐腐蚀，形成的保护膜容易被物理刮伤，也容易被酸性物质氧化而褪色。
发明内容
本发明的目的在于提供一种新能源汽车用漆面抛光剂。
一种新能源汽车用漆面抛光剂，包括如下重量份数的组分：微晶蜡5-10份,月桂蜡5-10份，溶剂10-30份，表面活性剂1-5份，二甲基硅油3-8份，无机磨料3-5份，水30-60份。
所述溶剂为乙醇，液体石蜡，乙二醇，***中的一种或一种以上。
所述表面活性剂为十二烷基苯磺酸钠，月桂醇聚氧乙烯醚，烷基酚聚氧乙烯醚中的一种或一种以上。
所述无机磨料为高岭土，蒙脱石，氧化铝，氧化铁，硅藻土中的一种或一种以上。
所述抛光剂还包括紫花前胡苷1-3份。
所述抛光剂还包括4-氨基吡啶(2-氨基吡啶)1-3份。
上述新能源汽车用漆面抛光剂的制备方法，按照如下步骤进行：
(1)按照重量份数，取微晶蜡5-10份,月桂蜡5-10份，混合后在80-100℃条件下熔融；
(2)取溶剂10-30份，加入步骤(1)制备的熔融液中，搅拌均匀；
(3)取表面活性剂1-5份，二甲基硅油3-8份，无机磨料3-5份，加入步骤(2)制备的混合液中，搅拌均匀；
(4)降温至室温，加入水30-60份，搅拌均匀，制成。
所述步骤(3)中加入紫花前胡苷1-3份。
所述步骤(3)中加入4-氨基吡啶1-3份。
本发明的有益效果：本发明制备的新能源汽车用漆面抛光剂，用于新能源汽车漆面的抛光，抛光后，光泽度高，防腐蚀性能好，抛光剂采用涂抹擦拭的方式使用，使用方法简单，抛光剂在高温条件下性能稳定，保存时间长，该抛光剂的制备方法简单，适合大规模工业化生产。
具体实施方式
下面结合具体实施例对本发明做进一步说明。
实施例1
一种新能源汽车用漆面抛光剂，包括如下重量份数的组分：微晶蜡8份,月桂蜡7份，乙二醇20份，十二烷基苯磺酸钠3份，二甲基硅油6份，蒙脱石4份，水45份。
上述新能源汽车用漆面抛光剂的制备方法，按照如下步骤进行：
(1)按照重量份数，取微晶蜡8份,月桂蜡7份，混合后在90℃条件下熔融；
(2)取乙二醇20份，加入步骤(1)制备的熔融液中，搅拌均匀；
(3)取十二烷基苯磺酸钠3份，二甲基硅油6份，蒙脱石4份，加入步骤(2)制备的混合液中，搅拌均匀；
(4)降温至室温，加入水45份，搅拌均匀，制成。
实施例2
一种新能源汽车用漆面抛光剂，包括如下重量份数的组分：微晶蜡5份,月桂蜡5份，液体石蜡10份，月桂醇聚氧乙烯醚1份，二甲基硅油3份，氧化铁3份，水30份。
上述新能源汽车用漆面抛光剂的制备方法，按照如下步骤进行：
(1)按照重量份数，取微晶蜡5份,月桂蜡5份，混合后在80℃条件下熔融；
(2)取液体石蜡10份，加入步骤(1)制备的熔融液中，搅拌均匀；
(3)取月桂醇聚氧乙烯醚1份，二甲基硅油3份，氧化铁3份，加入步骤(2)制备的混合液中，搅拌均匀；
(4)降温至室温，加入水30份，搅拌均匀，制成。
实施例3
一种新能源汽车用漆面抛光剂，包括如下重量份数的组分：微晶蜡10份,月桂蜡10份，乙醇30份，烷基酚聚氧乙烯醚5份，二甲基硅油8份，高岭土5份，水60份。
上述新能源汽车用漆面抛光剂的制备方法，按照如下步骤进行：
(1)按照重量份数，取微晶蜡10份,月桂蜡10份，混合后在100℃条件下熔融；
(2)取乙醇30份，加入步骤(1)制备的熔融液中，搅拌均匀；
(3)取烷基酚聚氧乙烯醚5份，二甲基硅油8份，高岭土5份，加入步骤(2)制备的混合液中，搅拌均匀；
(4)降温至室温，加入水60份，搅拌均匀，制成。
实施例4
一种新能源汽车用漆面抛光剂，包括如下重量份数的组分：微晶蜡8份,月桂蜡7份，乙二醇20份，十二烷基苯磺酸钠3份，二甲基硅油6份，蒙脱石4份，紫花前胡苷2份，水45份。
上述新能源汽车用漆面抛光剂的制备方法，按照如下步骤进行：
(1)按照重量份数，取微晶蜡8份,月桂蜡7份，混合后在90℃条件下熔融；
(2)取乙二醇20份，加入步骤(1)制备的熔融液中，搅拌均匀；
(3)取十二烷基苯磺酸钠3份，二甲基硅油6份，蒙脱石4份，紫花前胡苷2份，加入步骤(2)制备的混合液中，搅拌均匀；
(4)降温至室温，加入水45份，搅拌均匀，制成。
实施例5
一种新能源汽车用漆面抛光剂，包括如下重量份数的组分：微晶蜡8份,月桂蜡7份，乙二醇20份，十二烷基苯磺酸钠3份，二甲基硅油6份，蒙脱石4份，4-氨基吡啶2份，水45份。
上述新能源汽车用漆面抛光剂的制备方法，按照如下步骤进行：
(1)按照重量份数，取微晶蜡8份,月桂蜡7份，混合后在90℃条件下熔融；
(2)取乙二醇20份，加入步骤(1)制备的熔融液中，搅拌均匀；
(3)取十二烷基苯磺酸钠3份，二甲基硅油6份，蒙脱石4份，4-氨基吡啶2份，加入步骤(2)制备的混合液中，搅拌均匀；
(4)降温至室温，加入水45份，搅拌均匀，制成。
实施例6
一种新能源汽车用漆面抛光剂，包括如下重量份数的组分：微晶蜡8份,月桂蜡7份，乙二醇20份，十二烷基苯磺酸钠3份，二甲基硅油6份，蒙脱石4份，2-氨基吡啶2份，水45份。
上述新能源汽车用漆面抛光剂的制备方法，按照如下步骤进行：
(1)按照重量份数，取微晶蜡8份,月桂蜡7份，混合后在90℃条件下熔融；
(2)取乙二醇20份，加入步骤(1)制备的熔融液中，搅拌均匀；
(3)取十二烷基苯磺酸钠3份，二甲基硅油6份，蒙脱石4份，2-氨基吡啶2份，加入步骤(2)制备的混合液中，搅拌均匀；
(4)降温至室温，加入水45份，搅拌均匀，制成。
实施例7
一种新能源汽车用漆面抛光剂，包括如下重量份数的组分：微晶蜡8份,月桂蜡7份，乙二醇20份，十二烷基苯磺酸钠3份，二甲基硅油6份，蒙脱石4份，库尤樟桂(Ocoteacujumary Mart.)提取物2份，水45份。
所述库尤樟桂提取物的提取方法为：将库尤樟桂的叶片晒干，磨成粉末，加3-5倍重量份数的水回流提取3次，合并滤液，蒸干制成。
上述新能源汽车用漆面抛光剂的制备方法，按照如下步骤进行：
(1)按照重量份数，取微晶蜡8份,月桂蜡7份，混合后在90℃条件下熔融；
(2)取乙二醇20份，加入步骤(1)制备的熔融液中，搅拌均匀；
(3)取十二烷基苯磺酸钠3份，二甲基硅油6份，蒙脱石4份，库尤樟桂提取物2份，加入步骤(2)制备的混合液中，搅拌均匀；
(4)降温至室温，加入水45份，搅拌均匀，制成。
对比例1
一种新能源汽车用漆面抛光剂，包括如下重量份数的组分：月桂蜡7份，乙二醇20份，十二烷基苯磺酸钠3份，二甲基硅油6份，蒙脱石4份，水45份。
上述新能源汽车用漆面抛光剂的制备方法，按照如下步骤进行：
(1)按照重量份数，取月桂蜡7份，在90℃条件下熔融；
(2)取乙二醇20份，加入步骤(1)制备的熔融液中，搅拌均匀；
(3)取十二烷基苯磺酸钠3份，二甲基硅油6份，蒙脱石4份，加入步骤(2)制备的混合液中，搅拌均匀；
(4)降温至室温，加入水45份，搅拌均匀，制成。
对比例2
一种新能源汽车用漆面抛光剂，包括如下重量份数的组分：微晶蜡8份，乙二醇20份，十二烷基苯磺酸钠3份，二甲基硅油6份，蒙脱石4份，水45份。
上述新能源汽车用漆面抛光剂的制备方法，按照如下步骤进行：
(1)按照重量份数，取月桂蜡7份，在90℃条件下熔融；
(2)取乙二醇20份，加入步骤(1)制备的熔融液中，搅拌均匀；
(3)取十二烷基苯磺酸钠3份，二甲基硅油6份，蒙脱石4份，加入步骤(2)制备的混合液中，搅拌均匀；
(4)降温至室温，加入水45份，搅拌均匀，制成。
实验例1：光亮度测试
采用JKGZ-60型光泽度仪，每次实验，选取30cmX30cm的汽车车体面样板，在每个样板上任取个点测量，计算其平均值以作为它们的原始光亮度；将样板平分为左右两部分，左边涂覆试样，右边未涂覆，测量其光亮度。用毛巾轻轻的擦拭后静置，再暴露于室外自然状态下天测量其左右光亮度，进行对比。
实验结果如表1和表2所示：
表1各实验组擦拭后光亮度的增加值
注：*代表P<0.05；**代表P<0.01。
由表1可以看出，实施例4，实施例5和实施例7的光亮度增加值明显高于实施例1，实施例6与实施例1相当；对比例1和对比例2的光亮度增加值明显低于实施例1。
表2各实验组暴露10天后光亮度的减少值
注：*代表P<0.05；**代表P<0.01。
由表2可以看出，实施例4，实施例5和实施例7的光亮度减少值明显低于实施例1，实施例6与实施例1相当；对比例1和对比例2的光亮度增加值与实施例1相当。
实验例2：防锈性测试
将试样滴加在汽车车体面板样板上，放入湿润的干燥器内，置于士40℃下8h，观察有无锈性痕迹或变色。按4级评定判断结果：一级光亮、二级失光、三级轻锈、四级重锈。测试结果见表3：
表3各实验组防锈性检测
由表3可以看出，实施例1-4，对比例1和对比例2的防锈等级相同，实施例5-7明显优于实施例1。
实验例3：消泡性测试
在带塞量筒中装入试样100mL，上下剧烈摇晃1min，上下摇动距离大约为30cm，速度约为120次/min，完毕后静置10min，测量液面上残留泡沫体积(体积在2mL以内为合格)。测试结果见表4：
表4各实验组消泡性检测
注：*代表P<0.05；**代表P<0.01。
由表4可以看出，各实验组的消泡性能都合格，其中实施例7的残留泡沫体积明显低于其他实验组，其他实验组的残留泡沫体积相当，证明实施例7组的抛光剂消泡性最好。
Claims (9)
1.一种新能源汽车用漆面抛光剂，其特征在于，包括如下重量份数的组分：微晶蜡5-10份,月桂蜡5-10份，溶剂10-30份，表面活性剂1-5份，二甲基硅油3-8份，无机磨料3-5份，水30-60份。
2.根据权利要求1所述新能源汽车用漆面抛光剂，其特征在于，所述溶剂为乙醇，液体石蜡，乙二醇，***中的一种或一种以上。
3.根据权利要求1所述新能源汽车用漆面抛光剂，其特征在于，所述表面活性剂为十二烷基苯磺酸钠，月桂醇聚氧乙烯醚，烷基酚聚氧乙烯醚中的一种或一种以上。
4.根据权利要求1所述新能源汽车用漆面抛光剂，其特征在于，所述无机磨料为高岭土，蒙脱石，氧化铝，氧化铁，硅藻土中的一种或一种以上。
5.根据权利要求1所述新能源汽车用漆面抛光剂，其特征在于，所述抛光剂还包括紫花前胡苷1-3份。
6.根据权利要求1所述新能源汽车用漆面抛光剂，其特征在于，所述抛光剂还包括4-氨基吡啶1-3份。
7.权利要求1所述新能源汽车用漆面抛光剂的制备方法，其特征在于，按照如下步骤进行：
(1)按照重量份数，取微晶蜡5-10份,月桂蜡5-10份，混合后在80-100℃条件下熔融；
(2)取溶剂10-30份，加入步骤(1)制备的熔融液中，搅拌均匀；
(3)取表面活性剂1-5份，二甲基硅油3-8份，无机磨料3-5份，加入步骤(2)制备的混合液中，搅拌均匀；
(4)降温至室温，加入水30-60份，搅拌均匀，制成。
8.根据权利要求1所述新能源汽车用漆面抛光剂的制备方法，其特征在于，所述步骤(3)中加入紫花前胡苷1-3份。
9.根据权利要求1所述新能源汽车用漆面抛光剂的制备方法，其特征在于，所述步骤(3)中加入4-氨基吡啶1-3份。