CN108610996A - 轻质隔音型塑料蜂窝板材料 - Google Patents
轻质隔音型塑料蜂窝板材料 Download PDFInfo
- Publication number
- CN108610996A CN108610996A CN201810266800.6A CN201810266800A CN108610996A CN 108610996 A CN108610996 A CN 108610996A CN 201810266800 A CN201810266800 A CN 201810266800A CN 108610996 A CN108610996 A CN 108610996A
- Authority
- CN
- China
- Prior art keywords
- parts
- cellular board
- hot melt
- proof plastic
- board material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种轻质隔音型塑料蜂窝板材料,包括面层、底层和设置于面层和底层之间的聚丙烯蜂窝芯层以及将面层、聚丙烯蜂窝芯层和底层粘接为一体的双面贴合复合热熔胶膜层,热熔胶膜层原料包括聚酯多元醇、苯酚树脂、1,4—丁二醇、一缩二乙二醇、2,6‑二叔丁基对甲酚、填料、(2、3‑二甲基)二亚丁基三胺等,通过提高热熔胶膜的粘接强度和剥离强度以及耐高低温、耐化学、耐老化性能,进而提高塑料蜂窝板的复合性能,各组分的相容性好,组分中含有的苯环可提高产品的强度,叔胺上的孤对电子能改善蜂窝板的力学性能、工艺性能及粘接性能等多种功能,与该蜂窝板的结构相结合,使蜂窝板成型所需压力小,成型效果好,促进结构的能量吸收、热塑再变型和受冲击减震吸震效果。
Description
技术领域
本发明涉及一种蜂窝板,特别涉及一种轻质隔音型塑料蜂窝板材料。
背景技术
PP蜂窝板是由两块较薄的面板,牢固地粘结在一层较厚的蜂窝状芯材两面而制成的板材,亦称蜂窝夹层结构。此结构由于轻质高刚、无毒环保、减震耐寒、隔音保温、防潮隔热等优点,广泛应用于中高档乘用车的行李箱盖板、行李箱隔板、行李箱地毯基板、侧围装饰板、顶棚等内饰部位、发动机周转箱等。例如,目前汽车零部件用周转箱主要由德国、日本生产,国内企业虽已起步,但两年多来仍没有市场化。PP蜂窝板制备的一大技术难题便是复合。使用传统的胶水,虽然能够复合,但一方面由于不符合环保的理念;一方面胶水多为固化型体系,低温发脆比较严重,性能无法保证。而热熔胶类型的产品目前仍没有适合五层复合工艺的胶。改性EVA类型的热熔胶膜,虽然粘结强度与复合工艺适合客户,但由于EVA致命的低软化点而无法推广。包胶类型的TPE虽然可以用于包覆PP材质,但该工艺主要采用注塑包胶的方法,包胶温度高,是在PP软化状态下包覆的,不适合覆膜机的连续化工艺。此外,TPE类型材料成膜性差,即使充油性的TPE,流延膜的速度依然很慢,无法市场化。
发明内容
有鉴于此,本发明的目的在于提供一种轻质隔音型塑料蜂窝板材料,通过提高热熔胶膜的粘接强度和剥离强度以及耐高低温、耐化学、耐老化性能,进而提高塑料蜂窝板的复合性能,与该蜂窝板的结构相结合,使蜂窝板成型所需压力小,成型效果好,促进结构的能量吸收、热塑再变型和受冲击减震吸震效果,同时具有更好的减重、隔音效果,防水防潮,耐腐蚀性好,有效提高车内的舒适性以及车辆的安全性。
本发明的轻质隔音型塑料蜂窝板材料,包括面层、底层和设置于面层和底层之间的聚丙烯蜂窝芯层以及将面层、聚丙烯蜂窝芯层和底层粘接为一体的双面贴合复合热熔胶膜层,所述双面贴合复合热熔胶膜层之间填充玻璃纤维增强段,所述面层和底层均为玻璃纤维材料,所述双面贴合复合热熔胶膜层原料按重量份包括:
30-40份聚酯多元醇、6-12份苯酚树脂、5-10份1,4—丁二醇、5-10份一缩二乙二醇、10-20份2,6-二叔丁基对甲酚、3-8份填料、5-10份(2、3-二甲基)二亚丁基三胺、5-10份低聚苯乙烯树脂、5-10份二苯基甲烷二异氰酸酯、3-8份聚合松香、4-12份N-羟甲基丙烯酰胺、1-3份N.N—二羟基(二异丙基)苯胺、1-3份复配抗老化剂、1-3份阻燃剂、1-5份的抗氧剂、1-3份增塑剂;
进一步,所述填料为碳酸钙、硫酸钡、高岭土、滑石粉、凹凸棒土、空心微珠、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑中一种或两种以上的混合物;
进一步,所述N.N—二羟基(二异丙基)苯胺的结构式为:
其中n=1、2、3;
进一步,所述增塑剂为2,5-二甲基-2,5-双-(叔丁基过氧基)己烷、2,5-二甲基-2,5-双-(叔丁基过氧基)己炔的混合物;
进一步,所述复配抗老化剂为质量比为2∶2∶1的紫外线吸收剂、受阻酚型抗氧剂和受阻胺型光稳定剂组成;
进一步,所述抗氧剂为为四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯、4,6-双(十二基硫甲基)-O-甲酚中的一种或两种。。
本发明的有益效果:本发明的轻质隔音型塑料蜂窝板材料,通过提高热熔胶膜的粘接强度和剥离强度以及耐高低温、耐化学、耐老化性能,进而提高塑料蜂窝板的复合性能,热熔胶膜的耐热性和内聚强度高,热熔胶粘结性好,稳定性强,具有干燥速度快、消耗量小、热稳定性高的特点,各组分的相容性好,组分中含有的苯环可提高产品的强度,叔胺上的孤对电子能改善蜂窝板的力学性能、工艺性能及粘接性能等多种功能,与该蜂窝板的结构相结合,使蜂窝板成型所需压力小,成型效果好,促进结构的能量吸收、热塑再变型和受冲击减震吸震效果,蜂窝板的尺寸稳定性好,收缩率小,同时具有更好的减重、隔音效果,防水防潮,耐腐蚀性好,有效提高车内的舒适性以及车辆的安全性。
附图说明
下面结合附图和实施例对本发明作进一步描述:
图1为本发明的结构示意图。
具体实施方式
图1为本发明的结构示意图,如图所示:本发明的轻质隔音型塑料蜂窝板材料,其特征在于:包括面层1、底层4和设置于面层1和底层4之间的聚丙烯蜂窝芯层3以及将面层1、聚丙烯蜂窝芯层3和底层4粘接为一体的双面贴合复合热熔胶膜层2,所述双面贴合复合热熔胶膜层2之间填充玻璃纤维增强段,所述面层1和底层4均为玻璃纤维材料,所述双面贴合复合热熔胶膜层2原料按重量份包括:
30-40份聚酯多元醇、6-12份苯酚树脂、5-10份1,4—丁二醇、5-10份一缩二乙二醇、10-20份2,6-二叔丁基对甲酚、3-8份填料、5-10份(2、3-二甲基)二亚丁基三胺、5-10份低聚苯乙烯树脂、5-10份二苯基甲烷二异氰酸酯、3-8份聚合松香、4-12份N-羟甲基丙烯酰胺、1-3份N.N—二羟基(二异丙基)苯胺、1-3份复配抗老化剂、1-3份阻燃剂、1-5份的抗氧剂、1-3份增塑剂;通过提高热熔胶膜的粘接强度和剥离强度以及耐高低温、耐化学、耐老化性能,进而提高塑料蜂窝板的复合性能,热熔胶膜的耐热性和内聚强度高,热熔胶粘结性好,稳定性强,具有干燥速度快、消耗量小、热稳定性高的特点。复合热熔胶膜层原料的用量对热胶胶膜的性能也有着至关重要的影响,也就是说该热熔胶膜的整体性能是由组分和组分的用量共同决定的,一个组分的用量多少直接影响热熔胶胶膜的性能,由于加入多种添加剂,添加剂或各种组分对最终组合物的性能影响往往不是唯一的,即可能对组合物的多种性质同时有影响,因此,需考虑各种添加剂的综合影响,因为各种添加剂的性能有时可能会呈现“此消彼长”的情况。在双面贴合复合热熔胶膜层2之间填充玻璃纤维增强段增强蜂窝板的整体结构强度和刚性强度。尽管热熔胶中都添加了抗氧剂,有一定的作用,但若长时间处于使用的高温下,即使加了抗氧剂也不能防止氧化和热分解,因此,添加了具有耐热性的组分,以削弱其氧化和热分解。
本实施例中,所述填料为碳酸钙、硫酸钡、高岭土、滑石粉、凹凸棒土、空心微珠、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑中一种或两种以上的混合物。
本实施例中,所述N.N—二羟基(二异丙基)苯胺的结构式为:
其中n=1、2、3;苯环可提高产品的强度,叔胺上的孤对电子能改善蜂窝板的力学性能、工艺性能及粘接性能等多种功能本实施例中,所述增塑剂为2,5-二甲基-2,5-双-(叔丁基过氧基)己烷、2,5-二甲基-2,5-双-(叔丁基过氧基)己炔的混合物;两者协同作用,与其他组分的相容性好,对热熔胶的性能有明显的提高。
本实施例中,所述复配抗老化剂为质量比为2∶2∶1的紫外线吸收剂、受阻酚型抗氧剂和受阻胺型光稳定剂组成;紫外线吸收剂为2-羟基-4-正辛氧基二苯甲酮等,受阻酚型抗氧剂为四[β-(3,5-二叔丁基-4-羟基苯基)丙酸酯]季戊四醇酯等,受阻胺型光稳定剂为2,4一二羟基二苯甲酮944、GW一3346等。
本实施例中,所述抗氧剂为为四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯、4,6-双(十二基硫甲基)-O-甲酚中的一种或两种。
上述增塑剂和复配抗老化剂除具有自身优异效果外,对于其他组分都有很好的协同和促进作用。
下面通过具体实施例对发明的轻质隔音型塑料蜂窝板材料作进一步的阐述。
实施例一
本实施例的轻质隔音型塑料蜂窝板材料,所采用的双面贴合复合热熔胶膜层2原料按重量份包括:
30份聚酯多元醇、6份苯酚树脂、5份1,4—丁二醇、5份一缩二乙二醇、10份2,6-二叔丁基对甲酚、3份填料、5份(2、3-二甲基)二亚丁基三胺、5份低聚苯乙烯树脂、5份二苯基甲烷二异氰酸酯、3份聚合松香、4份N-羟甲基丙烯酰胺、1份N.N—二羟基(二异丙基)苯胺、1份复配抗老化剂、1份阻燃剂、1份的抗氧剂、1份增塑剂;
本实施例中,所述填料为碳酸钙,本实施例中,将所述碳酸钙按照同等重量份替换为硫酸钡、高岭土、滑石粉、凹凸棒土、空心微珠、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑中的一种,或按照同等重量份替换为碳酸钙与硫酸钡、高岭土、滑石粉、凹凸棒土、空心微珠、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑的混合物,均能实现本发明的目的。
本实施例中,所述N.N—二羟基(二异丙基)苯胺的结构式为:
其中n=1。
本实施例中,所述增塑剂为2,5-二甲基-2,5-双-(叔丁基过氧基)己烷、2,5-二甲基-2,5-双-(叔丁基过氧基)己炔的混合物。
本实施例中,所述复配抗老化剂为质量比为2∶2∶1的紫外线吸收剂、受阻酚型抗氧剂和受阻胺型光稳定剂组成。
本实施例中,所述抗氧剂为为四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯。
实施例二
本实施例的轻质隔音型塑料蜂窝板材料,所采用的双面贴合复合热熔胶膜层2原料按重量份包括:
40份聚酯多元醇、12份苯酚树脂、10份1,4—丁二醇、10份一缩二乙二醇、20份2,6-二叔丁基对甲酚、8份填料、10份(2、3-二甲基)二亚丁基三胺、10份低聚苯乙烯树脂、10份二苯基甲烷二异氰酸酯、8份聚合松香、12份N-羟甲基丙烯酰胺、3份N.N—二羟基(二异丙基)苯胺、3份复配抗老化剂、3份阻燃剂、5份的抗氧剂、3份增塑剂;
本实施例中,所述填料为硫酸钡,本实施例中,将所述硫酸钡按照同等重量份替换为碳酸钙、高岭土、滑石粉、凹凸棒土、空心微珠、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑中的一种,或按照同等重量份替换为硫酸钡与碳酸钙、高岭土、滑石粉、凹凸棒土、空心微珠、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑的混合物,均能实现本发明的目的。
本实施例中,所述N.N—二羟基(二异丙基)苯胺的结构式为:
其中n=2。
本实施例中,所述增塑剂为2,5-二甲基-2,5-双-(叔丁基过氧基)己烷、2,5-二甲基-2,5-双-(叔丁基过氧基)己炔的混合物。
本实施例中,所述复配抗老化剂为质量比为2∶2∶1的紫外线吸收剂、受阻酚型抗氧剂和受阻胺型光稳定剂组成。
本实施例中,所述抗氧剂为4,6-双(十二基硫甲基)-O-甲酚。
实施例三
本实施例的轻质隔音型塑料蜂窝板材料,所采用的双面贴合复合热熔胶膜层2原料按重量份包括:
30份聚酯多元醇、12份苯酚树脂、5份1,4—丁二醇、10份一缩二乙二醇、10份2,6-二叔丁基对甲酚、8份填料、5份(2、3-二甲基)二亚丁基三胺、10份低聚苯乙烯树脂、5份二苯基甲烷二异氰酸酯、8份聚合松香、4份N-羟甲基丙烯酰胺、3份N.N—二羟基(二异丙基)苯胺、1份复配抗老化剂、3份阻燃剂、1份的抗氧剂、3份增塑剂;
本实施例中,所述填料为高岭土,本实施例中,将所述高岭土按照同等重量份替换为硫酸钡、碳酸钙、滑石粉、凹凸棒土、空心微珠、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑中的一种,或按照同等重量份替换为高岭土与硫酸钡、碳酸钙、滑石粉、凹凸棒土、空心微珠、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑的混合物,均能实现本发明的目的。
本实施例中,所述N.N—二羟基(二异丙基)苯胺的结构式为:
其中n=3。
本实施例中,所述增塑剂为2,5-二甲基-2,5-双-(叔丁基过氧基)己烷、2,5-二甲基-2,5-双-(叔丁基过氧基)己炔的混合物。
本实施例中,所述复配抗老化剂为质量比为2∶2∶1的紫外线吸收剂、受阻酚型抗氧剂和受阻胺型光稳定剂组成。
本实施例中,所述抗氧剂为四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯和4,6-双(十二基硫甲基)-O-甲酚中的混合物。
实施例四
本实施例的轻质隔音型塑料蜂窝板材料,所采用的双面贴合复合热熔胶膜层2原料按重量份包括:
40份聚酯多元醇、6份苯酚树脂、10份1,4—丁二醇、5份一缩二乙二醇、20份2,6-二叔丁基对甲酚、3份填料、10份(2、3-二甲基)二亚丁基三胺、5份低聚苯乙烯树脂、10份二苯基甲烷二异氰酸酯、3份聚合松香、12份N-羟甲基丙烯酰胺、1份N.N—二羟基(二异丙基)苯胺、3份复配抗老化剂、1份阻燃剂、5份的抗氧剂、1份增塑剂;
本实施例中,所述填料为滑石粉,本实施例中,将所述滑石粉按照同等重量份替换为硫酸钡、高岭土、碳酸钙、凹凸棒土、空心微珠、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑中的一种,或按照同等重量份替换为滑石粉与硫酸钡、高岭土、碳酸钙、凹凸棒土、空心微珠、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑的混合物,均能实现本发明的目的。
本实施例中,所述N.N—二羟基(二异丙基)苯胺的结构式为:
其中n=1。
本实施例中,所述增塑剂为2,5-二甲基-2,5-双-(叔丁基过氧基)己烷、2,5-二甲基-2,5-双-(叔丁基过氧基)己炔的混合物。
本实施例中,所述复配抗老化剂为质量比为2∶2∶1的紫外线吸收剂、受阻酚型抗氧剂和受阻胺型光稳定剂组成。
本实施例中,所述抗氧剂为为四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯。
实施例五
本实施例的轻质隔音型塑料蜂窝板材料,所采用的双面贴合复合热熔胶膜层2原料按重量份包括:
35份聚酯多元醇、8份苯酚树脂、8份1,4—丁二醇、8份一缩二乙二醇、15份2,6-二叔丁基对甲酚、6份填料、8份(2、3-二甲基)二亚丁基三胺、8份低聚苯乙烯树脂、8份二苯基甲烷二异氰酸酯、6份聚合松香、8份N-羟甲基丙烯酰胺、2份N.N—二羟基(二异丙基)苯胺、2份复配抗老化剂、2份阻燃剂、3份的抗氧剂、2份增塑剂。
本实施例中,所述填料为凹凸棒土,本实施例中,将所述凹凸棒土按照同等重量份替换为硫酸钡、高岭土、滑石粉、碳酸钙、空心微珠、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑中的一种,或按照同等重量份替换为凹凸棒土与硫酸钡、高岭土、滑石粉、碳酸钙、空心微珠、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑的混合物,均能实现本发明的目的。
本实施例中,所述N.N—二羟基(二异丙基)苯胺的结构式为:
其中n=2。
本实施例中,所述增塑剂为2,5-二甲基-2,5-双-(叔丁基过氧基)己烷、2,5-二甲基-2,5-双-(叔丁基过氧基)己炔的混合物。
本实施例中,所述复配抗老化剂为质量比为2∶2∶1的紫外线吸收剂、受阻酚型抗氧剂和受阻胺型光稳定剂组成。
本实施例中,所述抗氧剂为4,6-双(十二基硫甲基)-O-甲酚。
实施例六
本实施例的轻质隔音型塑料蜂窝板材料,所采用的双面贴合复合热熔胶膜层2原料按重量份包括:
35份聚酯多元醇、6份苯酚树脂、10份1,4—丁二醇、7份一缩二乙二醇、18份2,6-二叔丁基对甲酚、3份填料、10份(2、3-二甲基)二亚丁基三胺、6份低聚苯乙烯树脂、8份二苯基甲烷二异氰酸酯、3份聚合松香、12份N-羟甲基丙烯酰胺、2份N.N—二羟基(二异丙基)苯胺、1份复配抗老化剂、3份阻燃剂、2份的抗氧剂、1份增塑剂;
本实施例中,所述填料为空心微珠,本实施例中,将所述空心微珠按照同等重量份替换为硫酸钡、高岭土、滑石粉、凹凸棒土、碳酸钙、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑中的一种,或按照同等重量份替换为空心微珠与硫酸钡、高岭土、滑石粉、凹凸棒土、碳酸钙、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑的混合物,均能实现本发明的目的。
本实施例中,所述N.N—二羟基(二异丙基)苯胺的结构式为:
其中n=3。
本实施例中,所述增塑剂为2,5-二甲基-2,5-双-(叔丁基过氧基)己烷、2,5-二甲基-2,5-双-(叔丁基过氧基)己炔的混合物。
本实施例中,所述复配抗老化剂为质量比为2∶2∶1的紫外线吸收剂、受阻酚型抗氧剂和受阻胺型光稳定剂组成。
本实施例中,所述抗氧剂为为四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯和4,6-双(十二基硫甲基)-O-甲酚的混合物。
最后说明的是,以上实施例仅用以说明本发明的技术方案而非限制,尽管参照较佳实施例对本发明进行了详细说明,本领域的普通技术人员应当理解,可以对本发明的技术方案进行修改或者等同替换,而不脱离本发明技术方案的宗旨和范围,其均应涵盖在本发明的权利要求范围当中。
Claims (7)
1.一种轻质隔音型塑料蜂窝板材料,其特征在于:包括面层、底层和设置于面层和底层之间的聚丙烯蜂窝芯层以及将面层、聚丙烯蜂窝芯层和底层粘接为一体的双面贴合复合热熔胶膜层,所述双面贴合复合热熔胶膜层之间填充玻璃纤维增强段,所述面层和底层均为玻璃纤维材料,所述双面贴合复合热熔胶膜层原料按重量份包括:
30-40份聚酯多元醇、6-12份苯酚树脂、5-10份1,4—丁二醇、5-10份一缩二乙二醇、10-20份2,6-二叔丁基对甲酚、3-8份填料、5-10份(2、3-二甲基)二亚丁基三胺、5-10份低聚苯乙烯树脂、5-10份二苯基甲烷二异氰酸酯、3-8份聚合松香、4-12份N-羟甲基丙烯酰胺、1-3份N.N—二羟基(二异丙基)苯胺、1-3份复配抗老化剂、1-3份阻燃剂、1-5份的抗氧剂、1-3份增塑剂。
2.根据权利要求1所述的轻质隔音型塑料蜂窝板材料,其特征在于:所述双面贴合复合热熔胶膜层原料按重量份包括:
35份聚酯多元醇、8份苯酚树脂、8份1,4—丁二醇、8份一缩二乙二醇、15份2,6-二叔丁基对甲酚、6份填料、8份(2、3-二甲基)二亚丁基三胺、8份低聚苯乙烯树脂、8份二苯基甲烷二异氰酸酯、6份聚合松香、8份N-羟甲基丙烯酰胺、2份N.N—二羟基(二异丙基)苯胺、2份复配抗老化剂、2份阻燃剂、3份的抗氧剂、2份增塑剂。
3.根据权利要求1所述的轻质隔音型塑料蜂窝板材料,其特征在于:所述填料为碳酸钙、硫酸钡、高岭土、滑石粉、凹凸棒土、空心微珠、玻璃纤维、云母粉、二氧化钛、石墨粉、白炭黑、炭黑中一种或两种以上的混合物。
4.根据权利要求3所述的轻质隔音型塑料蜂窝板材料,其特征在于:所述N.N—二羟基(二异丙基)苯胺的结构式为:
其中n=1、2、3。
5.根据权利要求4所述的轻质隔音型塑料蜂窝板材料,其特征在于:所述增塑剂为2,5-二甲基-2,5-双-(叔丁基过氧基)己烷、2,5-二甲基-2,5-双-(叔丁基过氧基)己炔的混合物。
6.根据权利要求5所述的轻质隔音型塑料蜂窝板材料,其特征在于:所述复配抗老化剂为质量比为2∶2∶1的紫外线吸收剂、受阻酚型抗氧剂和受阻胺型光稳定剂组成。
7.根据权利要求6所述的轻质隔音型塑料蜂窝板材料,其特征在于:所述抗氧剂为为四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯、4,6-双(十二基硫甲基)-O-甲酚中的一种或两种。