CN108609959A - A kind of formula of assembled architecture wood fibre closed pore wallboard - Google Patents
A kind of formula of assembled architecture wood fibre closed pore wallboard Download PDFInfo
- Publication number
- CN108609959A CN108609959A CN201810542188.0A CN201810542188A CN108609959A CN 108609959 A CN108609959 A CN 108609959A CN 201810542188 A CN201810542188 A CN 201810542188A CN 108609959 A CN108609959 A CN 108609959A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- wallboard
- fiber
- length
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of assembled architecture formulas of wood fibre closed pore wallboard, including following component:The degreasing fiber that the degreasing fiber that hydrophober is 0.9 parts by weight, part bamboo and woods fiber is 10 parts by weight, coconut fibre is 7 parts by weight, length is 4cm is 4.5 parts by weight, length is 6cm is 3.5 parts by weight, the common early strength silicate cement of 425R is 290 parts by weight, high-calcium powder is 9 parts by weight, water be 105 parts by weight, slag or building waste be 135 parts by weight, hydrogen peroxide catalyst is 0.5 parts by weight, gelling agent is 1 parts by weight, oxydol H 2O2 is 7 parts by weight.One aspect of the present invention improves secured intensity and space availability ratio in the case where reducing area and steel using amount;On the other hand, it is unlikely to deform while effectively raising water proofing property and fire line;In another aspect, sound insulation value is effectively raised, not easy-weathering, cracking, deliquescence and dusting;With the set-up time is short, advantageous effects simple for process and cost-effective etc..
Description
Technical field
The present invention relates to building fields, specifically, more particularly to a kind of assembled architecture wood fibre closed pore wallboard
Formula.
Background technology
Building wall board as used as exterior wall or interior wall and with the steel construction of assembled architecture be connected with each other, it is existing every
Wallboard generally has light weight gypsum wallboard, compound sawdust compacting wallboard or common cement board, though light weight gypsum wallboard produces
Period it is short, but water resistance is poor, and weight is also not light enough;Compound sawdust compacting wallboard fire protecting performance is poor, and temperature distortion is big;Commonly
Foam cement intensity is low, and sound insulation value is poor, easy-weathering, cracking, deliquescence, dusting;The condensation of sulphur aluminic acid quick hardening cement is fast but frangible.
The weight of sandwich foam sandwich wallboard is still heavier, and construction hoisting technological requirement is higher, and the performance for keeping the temperature noise reduction does not protrude.
In addition, in existing assembled architecture steel structure system, I-steel, quarter bend etc. is mainly used to be used as load-bearing pillar, separately applied with wallboard
Work can not be applied in combination, and wallboard is also used not as load load bearing unit;Also a kind of steel structure body using keel structure
System, steel using amount is huge, and acoustic resonance is with obvious effects, ineffective, the sound insulation of assembly, heat preservation, and water resistance is bad.
And the existing wallboard manufactured by the above several ways also all has that structural strength is not high, and the set-up time is long
The defects of higher with Master Cost.
Therefore those skilled in the art are dedicated to developing a kind of a kind of assembled architecture use that can effectively improve firmness
The formula of wood fibre closed pore wallboard.
Invention content
In view of the drawbacks described above of the prior art, technical problem to be solved by the invention is to provide a kind of assembled architectures
With the formula of wood fibre closed pore wallboard.
To achieve the above object, the present invention provides a kind of assembled architecture formula of wood fibre closed pore wallboard, packets
Include following component:
0.6-1.2 parts by weight hydrophober, 8-12 parts by weight bamboo and woods fiber, 6-8 parts by weight coconut fibre, 3-6 parts by weight are long
The common early strong silicon of 425R of degreasing fiber, the degreasing fiber that 2-5 parts by weight length is 6cm, 280-300 parts by weight that degree is 4cm
Acid salt cement, 6-12 parts by weight high-calcium powder, the water of 80-130 parts by weight, the slag of 120-150 parts by weight or building waste, 0.5
The oxydol H 2O2 of part hydrogen peroxide catalyst, the gelling agent of 0.8-1.2 parts by weight, 4-10 parts by weight;
Wherein, the temperature of water is 40 DEG C -45 DEG C;Hydrogen peroxide catalyst is MnO2,Fecl3。
Preferably, the hydrophober is 0.6 parts by weight, part bamboo and woods fiber is 8 parts by weight, coconut fibre be 6 parts by weight,
The degreasing fiber that the degreasing fiber that length is 4cm is 3 parts by weight, length is 6cm is 2 parts by weight, the common early strength silicates of 425R
Cement is 280 parts by weight, high-calcium powder is 6 parts by weight, water is that 80 parts by weight, slag or building waste are 120 parts by weight, hydrogen peroxide
Catalyst is 0.5 parts by weight, gelling agent is 0.8 parts by weight, oxydol H 2O2 is 4 parts by weight.
Further, the hydrophober is 0.9 parts by weight, part bamboo and woods fiber is 10 parts by weight, coconut fibre be 7 parts by weight,
The degreasing fiber that the degreasing fiber that length is 4cm is 4.5 parts by weight, length is 6cm is 3.5 parts by weight, the common early strong silicon of 425R
Acid salt cement is 290 parts by weight, high-calcium powder is 9 parts by weight, water be 105 parts by weight, slag or building waste be 135 parts by weight,
Hydrogen peroxide catalyst is 0.5 parts by weight, gelling agent is 1 parts by weight, oxydol H 2O2 is 7 parts by weight.
Further, the hydrophober is 1.2 parts by weight, part bamboo and woods fiber is 12 parts by weight, coconut fibre be 8 parts by weight,
The degreasing fiber that the degreasing fiber that length is 4cm is 6 parts by weight, length is 6cm is 5 parts by weight, the common early strength silicates of 425R
Cement is 300 parts by weight, high-calcium powder is 12 parts by weight, water is that 130 parts by weight, slag or building waste are 150 parts by weight, dioxygen
Water catalyst is 0.5 parts by weight, gelling agent is 1.2 parts by weight, oxydol H 2O2 is 10 parts by weight.
The beneficial effects of the invention are as follows:The wallboard manufactured by this formula is suitble to three layers or less low layer assembleds to build
It builds, on the one hand, steel pipe and wallboard can be combined use, and wallboard is made to mitigate Steel Structural Design load, be used reducing steel construction
Secured intensity and space availability ratio are improved in the case of amount;On the other hand, acoustic resonance is reduced, and is effectively being improved
It is unlikely to deform while water proofing property and fire line;In another aspect, improve structural strength and sound insulation value, and not easy-weathering,
Cracking, deliquescence and dusting;With the set-up time is short, advantageous effects simple for process and cost-effective etc..
Description of the drawings
Fig. 1 is the external wall panel structure schematic diagram of exterior wall Mold Making.
Fig. 2 is the overlooking structure diagram of Fig. 1.
Fig. 3 is the dimensional structure diagram of Fig. 1.
Fig. 4 is that two blocks of Side fascias splice the structural schematic diagram used.
Fig. 5 is the overlooking structure diagram of Fig. 4.
Fig. 6 is the dimensional structure diagram of Fig. 4.
Fig. 7 is the interior wall plate structure schematic diagram of interior wall Mold Making.
Fig. 8 is the overlooking structure diagram of Fig. 7.
Fig. 9 is the dimensional structure diagram of Fig. 7.
Figure 10 is that two pieces of linings splice the structural schematic diagram used.
Figure 11 is the overlooking structure diagram of Figure 10.
Figure 12 is the dimensional structure diagram of Figure 10.
Specific implementation mode
With reference to Fig. 1-12 and embodiment, the invention will be further described:
Weight in the present invention is with every part of 1kg.
Embodiment 1
A kind of formula of assembled architecture wood fibre closed pore wallboard, including following component:
Hydrophober is 0.9 parts by weight, part bamboo and woods fiber is 10 parts by weight, coconut fibre is 7 parts by weight, length is 4cm's
The degreasing fiber that degreasing fiber is 4.5 parts by weight, length is 6cm is that common early strength silicate cement is by 3.5 parts by weight, 425R
290 parts by weight, high-calcium powder are 9 parts by weight, water is that 105 parts by weight, slag or building waste are 135 parts by weight, hydrogen peroxide catalysis
Agent is 0.5 parts by weight, gelling agent is 1 parts by weight, oxydol H 2O2 is 7 parts by weight.
Wherein, the temperature of water is 40 DEG C -45 DEG C;Hydrogen peroxide catalyst is MnO2,Fecl3。
The assembled architecture manufacturing method of wood fibre closed pore wallboard, includes the following steps:
S1:It is by 0.9 parts by weight hydrophober, 10 parts by weight bamboo and woods fibers, 7 parts by weight coconut fibres, 4.5 parts by weight length
The degreasing fiber of 4cm and the degreasing fiber that 3.5 parts by weight length are 6cm are put into agitator and are stirred to form mixture A;
S2:The common early strength silicate cement of the 425R of 290 parts by weight and 9 parts by weight high-calcium powders are put into agitator, and it is mixed
Material A is closed to be stirred to form mixture B;
S3:The water of 105 parts by weight, the slag of 135 parts by weight or building waste, 0.9 parts by weight hydrophober and 0.5 part is double
Oxygen water catalyst is put into agitator, and high-speed stirred is carried out 15 minutes with mixture B;
Wherein, the temperature of water is 43 DEG C;Hydrogen peroxide catalyst is MnO2,Fecl3;
S4:The gelling agent of 1 parts by weight is added in agitator and forms slurries;
S5:The oxydol H 2O2 of 7 parts by weight is put into agitator, the material in agitator is put into mould after 10 seconds
Tool;
S6:After 38 minutes, it is confirmed whether consolidation molding;
S7:It can depanning after placing four hours;
S8:It is completed the production after carrying out 7 days High Temperature Curings by steam, wherein vapor (steam) temperature is 43 DEG C -47 DEG C, this implementation
In example, vapor (steam) temperature is 45 DEG C.
In the present embodiment, in S5, mold is exterior wall mold, and the thickness of the wallboard 1 after completing is 20cm;Wallboard 1
Top offers two exhausting holes 6, and each through-hole 6 is through the bottom end of wallboard 1;
The diameter of each through-hole 6 is 6cm, and the spacing between adjacent two 6 central points of cross through hole is 13cm;It is each adjacent
Two 6 central points of longitudinal hole between spacing be 9cm;
It is both provided with steel pipe 2 in each through-hole 6, cement mortar is both provided between 2 hollow part of steel pipe and steel pipe 2 and through-hole 6
The first half of each steel pipe 2 extends through-hole 6, and the top of wallboard 1 is provided with link block 3, and four angles of link block 3 are set
It is equipped with connecting hole 5, link block 3 is set in the first half of each steel pipe 2;
The side setting of wallboard 1 is offered from top to bottom through limiting slot 7, so the other side of wallboard 1 is provided with limit
Fin 8.
In S5, mold is interior wall mold, including wallboard 1, and the thickness of wallboard 1 is 10cm;The top of wallboard 1 offers one
Exhausting hole 6, each through-hole 6 is through the bottom end of wallboard 1;
The diameter of each through-hole 6 is 6cm, and the spacing between adjacent two 6 central points of through-hole is 13cm;
It is both provided with steel pipe 2 in each through-hole 6, cement mortar is both provided between 2 hollow part of steel pipe and steel pipe 2 and through-hole 6;
The first half of each steel pipe 2 extends through-hole 6, and the top of wallboard 1 is provided with link block 3, and four angles of link block 3 are set
It is equipped with connecting hole 5, link block 3 is set in the first half of each steel pipe 2;
The side setting of wallboard 1 is offered from top to bottom through limiting slot 7, so the other side of wallboard 1 is provided with limit
Fin 8.
In the present embodiment, limiting slot 7 and limit fin 8 are integrally formed with wallboard 1.
Embodiment 2
A kind of formula of assembled architecture wood fibre closed pore wallboard, including following component:
Hydrophober is 0.6 parts by weight, part bamboo and woods fiber is 8 parts by weight, coconut fibre is 6 parts by weight, length is the de- of 4cm
The degreasing fiber that fat fiber is 3 parts by weight, length is 6cm is 2 parts by weight, the common early strength silicate cement of 425R is 280 weight
Part, high-calcium powder be 6 parts by weight, water be 80 parts by weight, slag or building waste be 120 parts by weight, hydrogen peroxide catalyst is 0.5 weight
Measure part, gelling agent is 0.8 parts by weight, oxydol H 2O2 is 4 parts by weight.
Wherein, the temperature of water is 40 DEG C -45 DEG C;Hydrogen peroxide catalyst is MnO2,Fecl3。
A kind of assembled architecture manufacturing method of wood fibre closed pore wallboard, includes the following steps:
S1:It is 4cm by 0.6 parts by weight hydrophober, 8 parts by weight bamboo and woods fibers, 6 parts by weight coconut fibres, 3 parts by weight length
Degreasing fiber and degreasing fiber that 2 parts by weight length are 6cm be put into agitator and be stirred to form mixture A;
S2:The common early strength silicate cement of the 425R of 280 parts by weight and 6 parts by weight high-calcium powders are put into agitator, and it is mixed
Material A is closed to be stirred to form mixture B;
S3:The water of 80 parts by weight, the slag of 120 parts by weight or building waste, 0.6 parts by weight hydrophober and 0.5 part is double
Oxygen water catalyst is put into agitator, and high-speed stirred is carried out 23 minutes with mixture B;
Wherein, the temperature of water is 40 DEG C;Hydrogen peroxide catalyst is MnO2,Fecl3;
S4:The gelling agent of 0.8 parts by weight is added in agitator and forms slurries;
S5:The oxydol H 2O2 of 4 parts by weight is put into agitator, the material in agitator is put into mold after 9 seconds;
S6:After 30 minutes, it is confirmed whether consolidation molding;
S7:It can depanning after placing four hours;
S8:It is completed the production after carrying out 6 days High Temperature Curings by steam, wherein vapor (steam) temperature is 43 DEG C -47 DEG C, this implementation
In example, vapor (steam) temperature is 45 DEG C.
In the present embodiment, in S5, mold is exterior wall mold, and the thickness of the wallboard 1 after completing is 20cm;Wallboard 1
Top offers two exhausting holes 6, and each through-hole 6 is through the bottom end of wallboard 1;
The diameter of each through-hole 6 is 6cm, and the spacing between adjacent two 6 central points of cross through hole is 13cm;It is each adjacent
Two 6 central points of longitudinal hole between spacing be 9cm;
It is both provided with steel pipe 2 in each through-hole 6, cement mortar is both provided between 2 hollow part of steel pipe and steel pipe 2 and through-hole 6
The first half of each steel pipe 2 extends through-hole 6, and the top of wallboard 1 is provided with link block 3, and four angles of link block 3 are set
It is equipped with connecting hole 5, link block 3 is set in the first half of each steel pipe 2;
The side setting of wallboard 1 is offered from top to bottom through limiting slot 7, so the other side of wallboard 1 is provided with limit
Fin 8.
In S5, mold is interior wall mold, including wallboard 1, and the thickness of wallboard 1 is 10cm;The top of wallboard 1 offers one
Exhausting hole 6, each through-hole 6 is through the bottom end of wallboard 1;
The diameter of each through-hole 6 is 6cm, and the spacing between adjacent two 6 central points of through-hole is 13cm;
It is both provided with steel pipe 2 in each through-hole 6, cement mortar is both provided between 2 hollow part of steel pipe and steel pipe 2 and through-hole 6;
The first half of each steel pipe 2 extends through-hole 6, and the top of wallboard 1 is provided with link block 3, and four angles of link block 3 are set
It is equipped with connecting hole 5, link block 3 is set in the first half of each steel pipe 2;
The side setting of wallboard 1 is offered from top to bottom through limiting slot 7, so the other side of wallboard 1 is provided with limit
Fin 8.
In the present embodiment, limiting slot 7 and limit fin 8 are integrally formed with wallboard 1.
Embodiment 3
A kind of formula of assembled architecture wood fibre closed pore wallboard, including following component:
Hydrophober is 1.2 parts by weight, part bamboo and woods fiber is 12 parts by weight, coconut fibre is 8 parts by weight, length is 4cm's
The degreasing fiber that degreasing fiber is 6 parts by weight, length is 6cm is 5 parts by weight, the common early strength silicate cement of 425R is 300 weights
Amount part, high-calcium powder are 12 parts by weight, water be 130 parts by weight, slag or building waste be 150 parts by weight, hydrogen peroxide catalyst is
0.5 parts by weight, gelling agent are 1.2 parts by weight, oxydol H 2O2 is 10 parts by weight.
Wherein, the temperature of water is 40 DEG C -45 DEG C;Hydrogen peroxide catalyst is MnO2,Fecl3。
After any embodiment molding in embodiment 1- embodiments 3, surface flawless and crack phenomenon, impervious effect
Good, overall weight is light, according to national Testing and appraisal standard GB/T23451-2009《Light partition board for building》Testing result
It shows, the wallboard that any embodiment produces in the present invention, compression strength 10.5Mpa, moisture content 5%, air-borne sound oise insulation factor
65dB;Fire-protection rating is A1 grades.
According to national Testing and appraisal standard GB/T13475-2008《The measurement of adiabatic steady state heat transfer property is demarcated and protective hot
Case method》Testing result shows that the heat transfer coefficient that any embodiment produces wallboard in the present invention is 0.192W/ (㎡ K).
In the present invention, embodiment 1 is most preferred embodiment.
A kind of assembled architecture manufacturing method of wood fibre closed pore wallboard, includes the following steps:
S1:It is by 1.2 parts by weight hydrophober, 12 parts by weight bamboo and woods fibers, 8 parts by weight coconut fibres, 6 parts by weight length
The degreasing fiber of 4cm and the degreasing fiber that 5 parts by weight length are 6cm are put into agitator and are stirred to form mixture A;
S2:The common early strength silicate cement of the 425R of 300 parts by weight and 12 parts by weight high-calcium powders are put into agitator, and it is mixed
Material A is closed to be stirred to form mixture B;
S3:The water of 130 parts by weight, the slag of 150 parts by weight or building waste, 1.2 parts by weight hydrophober and 0.5 part is double
Oxygen water catalyst is put into agitator, and high-speed stirred is carried out 30 minutes with mixture B;
Wherein, the temperature of water is 45 DEG C;Hydrogen peroxide catalyst is MnO2,Fecl3;
S4:The gelling agent of 1.2 parts by weight is added in agitator and forms slurries;
S5:The oxydol H 2O2 of 10 parts by weight is put into agitator, the material in agitator is put into mould after 11 seconds
Tool;
S6:After 45 minutes, it is confirmed whether consolidation molding;
S7:It can depanning after placing four hours;
S8:It is completed the production after carrying out 9 days High Temperature Curings by steam, wherein vapor (steam) temperature is 43 DEG C -47 DEG C, this implementation
In example, vapor (steam) temperature is 45 DEG C.
In the present embodiment, in S5, mold is exterior wall mold, and the thickness of the wallboard 1 after completing is 20cm;Wallboard 1
Top offers two exhausting holes 6, and each through-hole 6 is through the bottom end of wallboard 1;
The diameter of each through-hole 6 is 6cm, and the spacing between adjacent two 6 central points of cross through hole is 13cm;It is each adjacent
Two 6 central points of longitudinal hole between spacing be 9cm;
It is both provided with steel pipe 2 in each through-hole 6, cement mortar is both provided between 2 hollow part of steel pipe and steel pipe 2 and through-hole 6
The first half of each steel pipe 2 extends through-hole 6, and the top of wallboard 1 is provided with link block 3, and four angles of link block 3 are set
It is equipped with connecting hole 5, link block 3 is set in the first half of each steel pipe 2;
The side setting of wallboard 1 is offered from top to bottom through limiting slot 7, so the other side of wallboard 1 is provided with limit
Fin 8.
In S5, mold is interior wall mold, including wallboard 1, and the thickness of wallboard 1 is 10cm;The top of wallboard 1 offers one
Exhausting hole 6, each through-hole 6 is through the bottom end of wallboard 1;
The diameter of each through-hole 6 is 6cm, and the spacing between adjacent two 6 central points of through-hole is 13cm;
It is both provided with steel pipe 2 in each through-hole 6, cement mortar is both provided between 2 hollow part of steel pipe and steel pipe 2 and through-hole 6;
The first half of each steel pipe 2 extends through-hole 6, and the top of wallboard 1 is provided with link block 3, and four angles of link block 3 are set
It is equipped with connecting hole 5, link block 3 is set in the first half of each steel pipe 2;
The side setting of wallboard 1 is offered from top to bottom through limiting slot 7, so the other side of wallboard 1 is provided with limit
Fin 8.
In the present embodiment, limiting slot 7 and limit fin 8 are integrally formed with wallboard 1.
In addition, prestressed net piece system is added in a mold, after technological process consolidation molding according to the invention, can be used as
200mm floorboards use, and reduction hydrophobic agent content is minimum 0.6kg, reduces dioxygen water consumption, outstanding feature compression strength
Can be optimal, guarantee safety energy.According to national Testing and appraisal standard GB/T23451-2009《Light partition board for building》Inspection
Survey the integrated board compression strength 15Mpa the results show that the production of this example, moisture content 5.6%, air-borne sound oise insulation factor 60dB;Fire prevention
Grade is A1 grades.
According to national Testing and appraisal standard GB/T13475-2008《The measurement of adiabatic steady state heat transfer property is demarcated and protective hot
Case method》Testing result shows that the heat transfer coefficient of this serial wallboard is 0.195W/ (㎡ K).
Include the following steps when wallboard when in use:
S1:Each steel pipe 2 is plugged in respectively in each through-hole 6 of 1 one end of wallboard;
S2:2 both ends of steel pipe that would extend out through-hole 6 are arranged link block 3, and link block 3 is welded on steel pipe 2, respectively
Link block 3 is located at the top and bottom of wallboard 1;
S3:The bottom of wallboard 1 is attached with built-in fitting;
S4:Cement mortar is injected between 2 hollow part of steel pipe and steel pipe 2 and through-hole 6;
S5:It will be connected with steel construction positioned at the link block 3 at 1 top of wallboard.
Such as according to the size for using real area, when needing laterally or vertically to be connected polylith wallboard 1, concrete operations
Steps are as follows:
Lateral connection:
SA1:Width is measured, confirms the quantity for needing wallboard 1;
SA2:After the completion of S5 steps, it is coated with bonding agent on wallboard 1, by two blocks of wallboards 1 laterally connect by bonding agent
It connects, the bottom of each wallboard 1 is attached with built-in fitting, and the top of each wallboard 1 is connected by link block 3 with steel construction respectively
It connects;
It is longitudinally connected:
SC1:Height is measured, confirms the quantity for needing wallboard 1;
SC2:In S2 steps, by steel pipe 2 simultaneously be inserted into two blocks of wallboards 1 on through-hole 6, to by two blocks of wallboards 1 into
The vertical connection of row.Exhausting hole 6 in the present invention is six, but protection scope of the present invention is not limited to six.
The preferred embodiment of the present invention has been described in detail above.It should be appreciated that those skilled in the art without
It needs creative work according to the present invention can conceive and makes many modifications and variations.Therefore, all technologies in the art
Personnel are available by logical analysis, reasoning, or a limited experiment on the basis of existing technology under this invention's idea
Technical solution, all should be in the protection domain being defined in the patent claims.
Claims (4)
1. a kind of assembled architecture formula of wood fibre closed pore wallboard, it is characterized in that:Including following component:
0.6-1.2 parts by weight hydrophober, 8-12 parts by weight bamboo and woods fiber, 6-8 parts by weight coconut fibre, 3-6 parts by weight length are
The degreasing fiber of 4cm, 2-5 parts by weight length be the degreasing fiber of 6cm, 280-300 parts by weight the common early strength silicates of 425R
Cement, 6-12 parts by weight high-calcium powder, the water of 80-130 parts by weight, the slag of 120-150 parts by weight or building waste, 0.5 part it is double
The oxydol H 2O2 of oxygen water catalyst, the gelling agent of 0.8-1.2 parts by weight, 4-10 parts by weight;
Wherein, the temperature of water is 40 DEG C -45 DEG C;Hydrogen peroxide catalyst is MnO2,Fecl3。
2. the assembled architecture as described in claim 1 formula of wood fibre closed pore wallboard, it is characterized in that:The hydrophober
It is 3 weight for the degreasing fiber that 0.6 parts by weight, part bamboo and woods fiber are 8 parts by weight, coconut fibre is 6 parts by weight, length is 4cm
The degreasing fiber that part, length are 6cm is 2 parts by weight, the common early strength silicate cement of 425R is 280 parts by weight, high-calcium powder is 6 weights
Amount part, water be 80 parts by weight, slag or building waste be 120 parts by weight, hydrogen peroxide catalyst is 0.5 parts by weight, gelling agent is
0.8 parts by weight, oxydol H 2O2 are 4 parts by weight.
3. the assembled architecture as described in claim 1 formula of wood fibre closed pore wallboard, it is characterized in that:The hydrophober
It is 4.5 weights for the degreasing fiber that 0.9 parts by weight, part bamboo and woods fiber are 10 parts by weight, coconut fibre is 7 parts by weight, length is 4cm
Measure part, the degreasing fiber that length is 6cm is 3.5 parts by weight, the common early strength silicate cement of 425R is 290 parts by weight, high-calcium powder
For 9 parts by weight, water be 105 parts by weight, slag or building waste be 135 parts by weight, hydrogen peroxide catalyst is 0.5 parts by weight, glue
Solidifying agent is 1 parts by weight, oxydol H 2O2 is 7 parts by weight.
4. the assembled architecture as described in claim 1 formula of wood fibre closed pore wallboard, it is characterized in that:The hydrophober
It is 6 weight for the degreasing fiber that 1.2 parts by weight, part bamboo and woods fiber are 12 parts by weight, coconut fibre is 8 parts by weight, length is 4cm
The degreasing fiber that part, length are 6cm is 5 parts by weight, the common early strength silicate cement of 425R is 300 parts by weight, high-calcium powder 12
Parts by weight, water be 130 parts by weight, slag or building waste be 150 parts by weight, hydrogen peroxide catalyst is 0.5 parts by weight, gelling agent
It is 10 parts by weight for 1.2 parts by weight, oxydol H 2O2.