CN108587470A - A kind of ordor removing degerming emulsion paint - Google Patents
A kind of ordor removing degerming emulsion paint Download PDFInfo
- Publication number
- CN108587470A CN108587470A CN201810567930.3A CN201810567930A CN108587470A CN 108587470 A CN108587470 A CN 108587470A CN 201810567930 A CN201810567930 A CN 201810567930A CN 108587470 A CN108587470 A CN 108587470A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- ordor removing
- emulsion paint
- degerming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ordor removing degerming emulsion paints, include the raw material of following parts by weight：50 100 parts of 200 350 parts of lotion, 150 300 parts of rutile type titanium white, 150 300 parts of packing agent, 25 parts of thickener, 10 20 parts of coalescents, 10 20 parts of mildewproof bacteria remover, 1 10 parts of mildew-resistant algae-resistant agent and nano-negative ion additive.Ordor removing degerming emulsion paint disclosed by the invention, coating exquisiteness is plentiful, with water-fast, resistance to mould, weatherability and it is easy to brushing, drying rapidly, smell dissipates fast, the effect of same day brushing is moved in every other day can be reached, in addition also there is killing and inhibiting effect to common microbiological, staphylococcus aureus, Escherichia coli, Candida albicans and saccharomycete, mould etc., to better people's living environment to a certain extent.
Description
Technical field
The present invention relates to the technical fields of chemistry painting industry, more particularly to a kind of ordor removing degerming emulsion paint.
Background technology
Internal wall emulsion coating is a kind of important revolution product in modern age interior decoration field, convenient with surface construction,
Color selection is abundant, smooth surface and it is easy to maintain the advantages that, dominate in inner wall decoration at home, the market share
More than 80%, but conventional latex paint does not have ordor removing and antibacterial action.Wherein in modern compact life step, to living
The requirement in room also enters in fast pace, and it is new with the characteristics of it can quickly move in have expedited the emergence of a series of such as wedding room, fast house
Type house form, but the ideal effect moved in rapidly required by oneself is often not achieved in house.Its basic reason is exactly
House needs the ventilation of a very long time after fitting up again, is distributed including emulsion paint, household to blow away indoor just fitted up
Peculiar smell out.
In addition, in hospital, children room is easy because bacterial adsorption is on wall, and people is accidentally easy for wall contact
Contaminated with bacteria, to generate harm to body.Common antibiotic emulsion paint on the market generally uses organic antibacterial agent at present
The compound of CMIT/MIT/ organic bromines or inorganic silver ion antimicrobial agent, organic antibacterial agent CMIT/MIT/ organic bromines are answered
Conjunction object is sensitive to PH, and additive amount is big, and toxicity is relatively significantly, irritant to people and animals, and adds inorganic silver ion antimicrobial agent
Price is high, but activity is low, to environmental requirement harshness.
People are more and more stronger to the pursuit of healthy clean ecology living environment, to antibacterial and ordor removing function
Latex paint product is also increasingly paid attention to.But existing emulsion paint is there are less varieties, effect is poor, smell is heavy, cannot effectively remove
The features such as bacterium.
Therefore, a kind of ordor removing degerming emulsion paint is invented, coating exquisiteness is plentiful, has water-fast, resistance to mould, weatherability and is easy to apply
Brush, drying are rapid, and smell dissipates soon, and also antibacterial functions are art technologies to better people's living environment to a certain extent
The problem of personnel's urgent need to resolve.
Invention content
In view of this, the present invention provides a kind of ordor removing degerming emulsion paint, coating exquisiteness is plentiful, has water-fast, resistance to mould, resistance to
Time property and being easy to brushes, is dry rapid, and smell dissipates fast, and can reach the same day brushes the effect of moving in every other day, in addition to common
Microorganism, staphylococcus aureus, Escherichia coli, Candida albicans and saccharomycete, mould etc. also have killing and inhibiting effect,
To better people's living environment to a certain extent.
To achieve the goals above, the present invention adopts the following technical scheme that：
A kind of ordor removing degerming emulsion paint, includes the raw material of following parts by weight：200-350 parts of lotion, rutile type titanium white 150-
300 parts, 150-300 parts of packing agent, 2-5 parts of thickener, 10-20 parts of coalescents, 10-20 parts of mildewproof bacteria remover, mildew-resistant algae-resistant
50-100 parts of 1-10 parts of agent and nano-negative ion additive.
Further, lotion 200-300 parts, 150-250 parts of rutile type titanium white, 150-250 parts of packing agent, thickener
3-5 parts, 15-20 parts of coalescents, 10-15 parts of mildewproof bacteria remover, 5-10 parts of mildew-resistant algae-resistant agent, nano-negative ion additive 50-
75 parts.
The present invention provides a kind of ordor removing degerming emulsion paints, and coating exquisiteness is plentiful, are easy to brushing, drying rapidly, smell disappears
It dissipates soon, the effect of same day brushing is moved in every other day can be reached；Meanwhile the rutile type titanium white in the present invention can be used as pigment
But also as titanium dioxide, compared to anatase thpe white powder, its elementary cell of rutile type titanium white is smaller and close, so having
Larger stability and relative density has higher refractive index and dielectric constant and lower heat conductivity；In addition, of the invention
In ordor removing degerming emulsion paint to common microbiological, staphylococcus aureus, Escherichia coli, Candida albicans and saccharomycete, mould
Bacterium etc. has killing and inhibiting effect.
Further, further include 2-5 parts of environment friendly corrosion protection agent, environmentally friendly 10-20 parts of antifreezing agent, environmentally friendly 1-5 parts of antifoaming agent, environmental protection
200-300 parts of 0.2-2 parts of wetting agent, 1-10 parts of ordor removing dispersant, 4-10 parts of auxiliary rheological agents, 1-5 parts of function additive and water.
Further, further include 2-3 parts of environment friendly corrosion protection agent, environmentally friendly 10-15 parts of antifreezing agent, environmentally friendly 3-5 parts of antifoaming agent, environmental protection
200-250 parts of 0.2-1 parts of wetting agent, 5-10 parts of ordor removing dispersant, 4-8 parts of auxiliary rheological agents, 3-5 parts of function additive and water.
Ordor removing degerming emulsion paint disclosed by the invention is water soluble latex paints, using water as decentralized medium, good permeability,
Avoid the film blistering disadvantage caused by film internal and external temperature pressure difference；And with it is pollution-free, nontoxic, without fire hazard,
It is easy to brush, is dry rapid, the advantages that paint film is water-fast, scrub resistance is good and color is soft.
Further, the lotion includes except 50-100 parts of 150-250 parts of aldehyde lotion and degerming lotion.
Further, the packing agent includes 50-100 parts of calcined kaolin and active 100-200 parts of coarse whiting.
Preferably, the packing agent is further selected from diatomite, talcum powder.
Further, the thickener includes 0.5-2 parts of 1-5 parts of cellulose and bentonite.
Preferably, the cellulose is 35000 celluloses.
Further, the auxiliary rheological agents include 1-5 parts of L60 auxiliary rheological agents, 1-5 parts of 6050 auxiliary rheological agents and U601 rheologies
1-5 parts of auxiliary agent.
Further, the function additive is AMP 95.
The production method of the ordor removing degerming emulsion paint, includes the following steps：
（1）Blender is cleaned, and water is added and is stirred, the blender is put into successively under 200-500 revs/min of rotating speed
Environment friendly corrosion protection agent, environmentally friendly antifreezing agent, ordor removing dispersant, environmentally friendly wetting agent, environmentally friendly antifoaming agent and coalescents；
（2）Under 500-1000 revs/min of rotating speed, calcined kaolin, rutile type titanium white, cellulose, swelling are put into successively
Soil, active coarse whiting, nano-negative ion additive；
（3）The powder at blender edge is scraped, using the mildewproof bacteria remover cleaning blender edge of 20-30%, and adjusts stirring
The rotating speed of machine is to 1000-1500 revs/min；Dispersion 30-60 minutes, until powder fineness is less than 40 μm in blender；By blender
Rotating speed to 500-1000 revs/min, after will remaining mildewproof bacteria remover be added blender in；
（4）It successively will be described except aldehyde lotion, degerming lotion, mildew-resistant algae-resistant agent, AMP 95, L60 auxiliary rheological agents, 6050 auxiliary rheological agents
It is added in blender, stirs evenly with U601 auxiliary rheological agents.
Wherein, it is preferred that the coating process of the ordor removing degerming emulsion paint is brushing, roller coating or spraying.
It can be seen via above technical scheme that compared with prior art, the present invention provides a kind of ordor removing degerming emulsion paint,
With following technological merit：
（1）Ordor removing degerming emulsion paint disclosed by the invention is water soluble latex paints, and using water as decentralized medium, good permeability is kept away
The film blistering disadvantage caused by film internal and external temperature pressure difference is exempted from；And with it is pollution-free, nontoxic, without fire hazard, easily
Rapidly in brushing, drying, the advantages that paint film is water-fast, scrub resistance is good and color is soft.
（2）Ordor removing degerming emulsion paint provided by the invention, coating exquisiteness is plentiful, is easy to brushing, dry rapid, smell dissipation
Soon, the effect of same day brushing is moved in every other day can be reached；Meanwhile with larger stability and relative density and higher
Refractive index and dielectric constant and lower heat conductivity.
（3）Ordor removing degerming emulsion paint provided by the invention, also to common microbiological such as staphylococcus aureus, large intestine bar
Bacterium, Candida albicans and saccharomycete, mould etc. have killing and inhibiting effect, to better people's living environment to a certain extent.
（4）Ordor removing degerming emulsion paint provided by the invention, not only can brushing wall can also brushing timber, the paint of formation
Film is nontoxic, smell is light, adhesive force is good, resistance to shampooing, and application property is good and has sustainability in effect.
Specific implementation mode
Below in conjunction with the embodiment in the present invention, technical solution in the embodiment of the present invention carries out clearly and completely
Description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on this hair
Embodiment in bright, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
Embodiment 1
The embodiment of the invention discloses a kind of ordor removing degerming emulsion paint, ordor removing degerming emulsion paint by following parts by weight raw material group
At：
According to the following steps, ordor removing degerming emulsion paint is made：
（1）Blender is cleaned, and the water of 250Kg is added in blender, the rotating speed that blender is arranged is 300 revs/min, works as stirring
When the rotating speed of the rotating speed of machine reaches set rotating speed, the environment friendly corrosion protection agent of 3Kg, environmentally friendly antifreezing agent, the 5Kg of 15Kg are put into successively
Ordor removing dispersant, 1Kg environmentally friendly wetting agent, the environmentally friendly antifoaming agent of 5Kg and the coalescents of 15Kg；
（2）The rotating speed that blender is arranged is 800 revs/min, puts into the calcined kaolin of 50Kg, the rutile type titanium of 250Kg successively
The nano-negative ion additive of white powder, 35000 celluloses of 2Kg, the bentonite of 1Kg, the active coarse whiting of 200Kg and 75Kg；
（3）The powder at blender edge is scraped, using the mildewproof bacteria remover cleaning blender edge of 3Kg, and adjusts blender
Rotating speed to 1200 revs/min；Dispersion 30 minutes, until powder fineness is less than 40 μm in blender；By the rotating speed of blender to 800
Rev/min, after will 7Kg mildewproof bacteria remover be added blender in；
（4）Successively by 200Kg except aldehyde lotion, the degerming lotion of 100Kg, the mildew-resistant algae-resistant agent of 5Kg, 3Kg AMP 95,5Kg
L60 auxiliary rheological agents, 2Kg 6050 auxiliary rheological agents and 1Kg U601 auxiliary rheological agents be added blender in, stir evenly.
Embodiment 2
The embodiment of the invention discloses a kind of ordor removing degerming emulsion paints, and the embodiment of the invention discloses a kind of ordor removing degerming latexes
Paint, ordor removing degerming emulsion paint are made of the raw material of following parts by weight：
The preparation method of taste degerming emulsion paint is in the same manner as in Example 1 in the present embodiment, and this is no longer going to repeat them.
Embodiment 3
The embodiment of the invention discloses a kind of ordor removing degerming emulsion paint, ordor removing degerming emulsion paint by following parts by weight raw material group
At：
。
Comparative example 1
The embodiment of the invention discloses a kind of ordor removing degerming emulsion paints, and the embodiment of the invention discloses a kind of ordor removing degerming latexes
Paint, ordor removing degerming emulsion paint are made of the raw material of following parts by weight：
。
Embodiment 4
The generic latex paint that the present embodiment buys ordor removing degerming emulsion paint made of embodiment 1-3 and comparative example 1 and market
Carry out quality technology measurement, measurement at film outward appearance, drying time, state, application property and low-temperature stability as a result, such as table 1：
1 emulsion paint presentation quality of table measures
According to table 1 it is found that ordor removing degerming emulsion paint provided by the invention, have it is good at film outward appearance, state and application property, and
Drying time is no more than for 24 hours, same day painting is fully meet, the effect of moving in every other day.The tasteless pollution free green environment protection, envelope
The contact with room air inside wall is closed, and prevents wall from generating mould, or the mould generated is killed, to prevent
Mould grows the indoor a large amount of oxygen of consumption while destroying wall and causes indoor anoxic and prevent mould from being discharged in growth course
A large amount of pernicious gas, so using to all kinds of moulds there is specific aim to remove and inhibit.
Embodiment 4
The generic latex paint that the present embodiment buys ordor removing degerming emulsion paint made of embodiment 1-3 and comparative example 1 and market
Carry out quality technology measurement, free formaldehyde content, volatile organic matter, benezene material, soluble heavy metal and the antibacterial of measurement
Performance, such as table 2：
2 emulsion paint harmful components of table measure
By the present embodiment it can be seen that free formaldehyde, volatile organic compounds, benzene class in odorless emulsion paint provided by the invention
Substance and soluble heavy metal equal size are well below national standard.
Embodiment 5
In one 30 square metres of closed room, it is respectively put into 61 cubic metre of wooden box, two are stayed in each box
A ventilation opening keeps ventilation state, wherein 1 box not mopping left blank standard sample, remaining box brush implementation respectively
Ordor removing degerming emulsion paint in example 1-3 and comparative example 1, and common emulsion paint purchased in market, are put into latter every four hours and are heard from ventilation opening
Once, until being asked in box and holding one's breath taste, judge its ordor removing effect by reaching the speed of smell resolution time.As a result
Such as table 3, as shown in Table 3, generic latex paint still has a taste after brushing 24 hours, and the breast in this patent embodiment 1-3
Shellac varnish equal tasteless after brushing 24 hours is fully able to reach the effect of same day brushing is moved in every other day.
3 each emulsion paint smell dissipation effect of table compares
The present disclosure provides a kind of ordor removing degerming emulsion paints, and coating exquisiteness is plentiful, with water-fast, resistance to mould, weatherability and easily
In brushing, dry smell dissipates soon rapidly, the effect of moving in every other day is brushed on the day of capable of reaching, in addition to common microbiological, gold
Staphylococcus aureus, Escherichia coli, Candida albicans and saccharomycete, mould etc. also have killing and inhibiting effect, to one
Determine to better people's living environment in degree.
Each embodiment is described by the way of progressive in this specification, the highlights of each of the examples are with other
The difference of embodiment, just to refer each other for identical similar portion between each embodiment.For device disclosed in embodiment
For, since it is corresponded to the methods disclosed in the examples, so description is fairly simple, related place is said referring to method part
It is bright.
The foregoing description of the disclosed embodiments enables those skilled in the art to implement or use the present invention.
Various modifications to these embodiments will be apparent to those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, of the invention
It is not intended to be limited to the embodiments shown herein, and is to fit to and the principles and novel features disclosed herein phase one
The widest range caused.
Claims (9)
1. a kind of ordor removing degerming emulsion paint, which is characterized in that include the raw material of following parts by weight：200-350 parts of lotion, rutile
150-300 parts of type titanium dioxide, 150-300 parts of packing agent, 2-5 parts of thickener, 10-20 parts of coalescents, mildewproof bacteria remover 10-20
50-100 parts of part, 1-10 parts of mildew-resistant algae-resistant agent and nano-negative ion additive.
2. a kind of ordor removing degerming emulsion paint according to claim 1, which is characterized in that include the raw material of following parts by weight：
200-300 parts of lotion, 150-250 parts of rutile type titanium white, 150-250 parts of packing agent, 3-5 parts of thickener, coalescents 15-
20 parts, 10-15 parts of mildewproof bacteria remover, 5-10 parts of mildew-resistant algae-resistant agent, 50-75 parts of nano-negative ion additive.
3. a kind of ordor removing degerming emulsion paint according to claim 1 or 2, which is characterized in that further include environment friendly corrosion protection agent 2-5
Part, environmentally friendly 10-20 parts of antifreezing agent, environmentally friendly 1-5 parts of antifoaming agent, environmentally friendly 0.2-2 parts of wetting agent, 1-10 parts of ordor removing dispersant, rheology
200-300 parts of 4-10 parts of auxiliary agent, 1-5 parts of function additive and water.
4. a kind of ordor removing degerming emulsion paint according to claim 1 or 2, which is characterized in that further include environment friendly corrosion protection agent 2-3
Part, environmentally friendly 10-15 parts of antifreezing agent, environmentally friendly 3-5 parts of antifoaming agent, environmentally friendly 0.2-1 parts of wetting agent, 5-10 parts of ordor removing dispersant, rheology
200-250 parts of 4-8 parts of auxiliary agent, 3-5 parts of function additive and water.
5. a kind of ordor removing degerming emulsion paint according to claim 2, which is characterized in that the lotion includes removing aldehyde lotion
150-250 parts and 50-100 parts of degerming lotion.
6. a kind of ordor removing degerming emulsion paint according to claim 2, which is characterized in that the packing agent includes calcining kaolinite
Native 50-100 parts and active 100-200 parts of coarse whiting.
7. a kind of ordor removing degerming emulsion paint according to claim 2, which is characterized in that the thickener includes cellulose 1-
5 parts and 0.5-2 parts of bentonite.
8. a kind of ordor removing degerming emulsion paint according to claim 4, which is characterized in that the auxiliary rheological agents include L60 streams
Become 1-5 parts of 1-5 parts of auxiliary agent, 1-5 parts of 6050 auxiliary rheological agents and U601 auxiliary rheological agents.
9. a kind of ordor removing degerming emulsion paint according to claim 4, which is characterized in that the function additive is AMP 95.