CN108530008A - It is a kind of using ardealite as advanced composite material (ACM) of base material and preparation method thereof - Google Patents
It is a kind of using ardealite as advanced composite material (ACM) of base material and preparation method thereof Download PDFInfo
- Publication number
- CN108530008A CN108530008A CN201810628951.1A CN201810628951A CN108530008A CN 108530008 A CN108530008 A CN 108530008A CN 201810628951 A CN201810628951 A CN 201810628951A CN 108530008 A CN108530008 A CN 108530008A
- Authority
- CN
- China
- Prior art keywords
- ardealite
- composite material
- acm
- slag
- sodium hydroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to metal recovery technical fields, provide a kind of using ardealite as advanced composite material (ACM) of base material and preparation method thereof.The raw material of the advanced composite material (ACM) includes in parts by weight:0.03 0.05 parts of 1 part of ardealite, 0.85 0.95 parts of slag and sodium hydroxide.The composite material can be directed to Yunnan ardealite containing the high feature of silica, physical and mechanical properties of the enhancing ardealite in building products;The composite material can increase ardealite comprehensive Utilization Ways and a large amount of consumption ardealites;The composite material can correspondingly improve water resistance, reach outdoor municipal works requirement.The preparation method includes:By ardealite, mixture is formed after slag and sodium hydroxide mixing, water, the mass ratio 188 200 of mixture and water are added into mixture:120, it conserves 3 days.The preparation method design science, it is easy to operate, it is suitable for large-scale industrial production.
Description
Technical field
The invention belongs to technical field of composite materials, specifically, being related to a kind of using ardealite as the NEW TYPE OF COMPOSITE of base material
Material and preparation method thereof.
Background technology
The recycling emphasis of ardealite is conceived to production cement retarder and building gypsum cementitious material at present.In reality
In the extension process of border, the problems such as there are still transportation radius small, various regions ardealite ingredient and product quality variance are larger.Meanwhile
Since the α gypsum of traditional handicraft processing is of high cost, the physical and mechanical properties limitation of β gypsum itself generally all cannot be used for room
Outer municipal works.
Invention content
For deficiency above-mentioned in the prior art, the first object of the present invention is the provision of one kind using ardealite as base material
Advanced composite material (ACM);The composite material can be directed to Yunnan ardealite containing the high feature of silica, and enhancing ardealite is being built
The physical and mechanical properties in product are built, a kind of novel acid-resistant anti-corrosion material is formed;It is comprehensive that the composite material can increase ardealite
Close utilization ways and a large amount of consumption ardealites;The composite material can correspondingly improve water resistance, reach outdoor municipal works
Requirement.
For deficiency above-mentioned in the prior art, the second object of the present invention is the provision of one kind using ardealite as base material
Advanced composite material (ACM) preparation method;The preparation method design science, it is easy to operate, it is suitable for large-scale industrial production.
In order to achieve the above object, the solution that the present invention uses is:
It is a kind of using ardealite as the advanced composite material (ACM) of base material, raw material in parts by weight, including:1 part of ardealite,
0.03-0.05 parts of 0.85-0.95 parts of slag and sodium hydroxide.
It is a kind of such as above-mentioned using ardealite as the preparation method of the advanced composite material (ACM) of base material, including:By ardealite, slag with
And mixture is formed after sodium hydroxide mixing, water, the mass ratio 188-200 of mixture and water are added into mixture:120, it supports
Shield 3 days.
It is provided by the invention a kind of to be by the advantageous effect of the advanced composite material (ACM) of base material and preparation method thereof of ardealite:
(1) present invention, by being compounded with slag and sodium hydroxide, is creatively researched and developed using ardealite as primary raw material
A kind of hydraulicity gelling composite material with higher-strength is gone out.The composite material can substitute common portland cement
Used as construction material, can not only consume a large amount of ardealites, and meet the energy saving, emission reduction of country's proposition, consumption reduction economy
Developing direction;The rational utilization of resource is of great significance to the sustainable development of China's phosphorus chemical industry and building materials industry.This
Ardealite is taken in invention:Slag:Sodium hydroxide is compounded according to above-mentioned parts by weight so that the coefficient of softing of gypsum base is by passing
The 0.6 of system is increased to 0.8, has correspondingly improved water resistance, has reached outdoor municipal works requirement.In addition, material of the present invention
Expect production cost at 150 yuan/ton hereinafter, nearly 200 yuan/ton or so of selling cost, market prospects are good.
(2) present invention is simple and efficient by the preparation method design science of the advanced composite material (ACM) of base material of ardealite, each anti-
Coordinated between condition is answered, physical property, mechanical property can be prepared and water resistance is excellent is with ardealite
The advanced composite material (ACM) of base material.
Specific implementation mode
It in order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below will be in the embodiment of the present invention
Technical solution be clearly and completely described.The person that is not specified actual conditions in embodiment, builds according to normal condition or manufacturer
The condition of view carries out.Reagents or instruments used without specified manufacturer is the conventional production that can be obtained by commercially available purchase
Product.
Below to provided in an embodiment of the present invention a kind of using ardealite as advanced composite material (ACM) of base material and preparation method thereof
It is specifically described.
It is a kind of using ardealite as the advanced composite material (ACM) of base material, raw material in parts by weight, including:1 part of ardealite,
0.03-0.05 parts of 0.85-0.95 parts of slag and sodium hydroxide.
The selection of above-mentioned each raw material and proportioning pass through scientific design, so that association can be played by cooperating between various raw materials
With the effect of synergy, using this proportioning, can greatly improve the physical property of the advanced composite material (ACM) of preparation, mechanical property and
Water resistance.
Further, inventor's creatively hair style, when in parts by weight, ardealite is 1 part, slag 0.85-
When 0.9 part and sodium hydroxide are 0.03-0.04 parts, the physical property of the advanced composite material (ACM) being prepared, mechanical property and
Water resistance is more excellent.When in parts by weight, ardealite is 1 part, and slag is 0.85 part and sodium hydroxide is 0.04
Part when, the physical property of the advanced composite material (ACM) being prepared, mechanical property and water resistance are the most excellent.
It should be noted that in the present embodiment, the phosphorus stone generated when ardealite is using production high-concentration phosphate compound fertilizers
Cream;The slag uses the Iron-ore Slag of steel plant's production, in favor of saving cost, refuse reclamation.Sodium hydroxide is using saturation
The supernatant of sodium hydroxide solution after precipitation.There is very strong water imbibition due to sodium hydroxide and easily absorb in air
CO2, therefore often contain Na in commercially available sodium hydroxide2CO3。Na2CO3It is affected to using, needs to remove.Due to Na2CO3
It is not almost dissolved in saturation sodium hydroxide solution, can slowly be precipitated out, therefore, in the present embodiment, first match sodium hydroxide
At saturated solution, Na is waited for2CO3After precipitation, then Aspirate supernatant.
In the present embodiment, the attached water of ardealite be less than 10% wet-milling, the pH=2-5 of ardealite, ardealite it is water-soluble
Property fluorine<0.5% and ardealite grain size be less than 50 μm;The control of the performance indicator of above-mentioned ardealite is conducive in ardealite
Active principle give full play to, in favor of carrying out sufficient compound synergic with other raw materials.
In the present embodiment, the detection moisture content of Iron-ore Slag is less than 2%, and the butt solid formation content of Iron-ore Slag is more than
95%.The active principle that the control of the performance indicator of above-mentioned Iron-ore Slag is conducive in Iron-ore Slag gives full play to, in favor of with other
Raw material carries out sufficient compound synergic.In the present embodiment, the size controlling of Iron-ore Slag is 0.04-0.06mm;Further subway
The size controlling of slag is 0.05mm, so that the active principle in Iron-ore Slag fully plays, and is conducive to Iron-ore Slag and its
He is adequately mixed raw material.
It is a kind of using ardealite as the preparation method of the advanced composite material (ACM) of base material, including:By the phosphorus stone of above-mentioned quality proportioning
Mixture is formed after cream, slag and sodium hydroxide mixing, water, the mass ratio 188- of mixture and water are added into mixture
200:120, it conserves 3 days.It is conserved, advanced composite material (ACM) obtained, is had using the quality proportioning of said mixture and water
There are excellent physical property, mechanical property and water resistance.
The feature and performance of the present invention are described in further detail with reference to embodiments.
Embodiment 1
Present embodiments provide it is a kind of using ardealite as the advanced composite material (ACM) of base material,
It prepares raw material:0.03 part of score meter by weight, 1 part of ardealite, 0.85 part of slag and sodium hydroxide.
Preparation method:By the ardealite, mixture is formed after the slag and sodium hydroxide mixing, to institute
It states and water is added in mixture, the mass ratio 188 of the mixture and the water:120, it conserves 3 days.
Embodiment 2
Present embodiments provide it is a kind of using ardealite as the advanced composite material (ACM) of base material,
It prepares raw material:0.05 part of score meter by weight, 1 part of ardealite, 0.95 part of slag and sodium hydroxide.
Preparation method:By the ardealite, mixture is formed after the slag and sodium hydroxide mixing, to institute
It states and water is added in mixture, the mass ratio 188 of the mixture and the water:120, it conserves 3 days.
Embodiment 3
Present embodiments provide it is a kind of using ardealite as the advanced composite material (ACM) of base material,
It prepares raw material:0.03 part of score meter by weight, 1 part of ardealite, 0.9 part of slag and sodium hydroxide.
Preparation method:By the ardealite, mixture is formed after the slag and sodium hydroxide mixing, to institute
It states and water is added in mixture, the mass ratio 188 of the mixture and the water:120, it conserves 3 days.
Embodiment 4
Present embodiments provide it is a kind of using ardealite as the advanced composite material (ACM) of base material,
It prepares raw material:0.04 part of score meter by weight, 1 part of ardealite, 0.9 part of slag and sodium hydroxide.
Preparation method:By the ardealite, mixture is formed after the slag and sodium hydroxide mixing, to institute
It states and water is added in mixture, the mass ratio 188 of the mixture and the water:120, it conserves 3 days.
Embodiment 5
Present embodiments provide it is a kind of using ardealite as the advanced composite material (ACM) of base material,
It prepares raw material:0.04 part of score meter by weight, 1 part of ardealite, 0.85 part of slag and sodium hydroxide.
Preparation method:By the ardealite, mixture is formed after the slag and sodium hydroxide mixing, to institute
It states and water is added in mixture, the mass ratio 188 of the mixture and the water:120, it conserves 3 days.
Embodiment 6
Present embodiments provide it is a kind of using ardealite as the advanced composite material (ACM) of base material,
It prepares raw material:0.04 part of score meter by weight, 1 part of ardealite, 0.85 part of slag and sodium hydroxide.
Preparation method:By the ardealite, mixture is formed after the slag and sodium hydroxide mixing, to institute
It states and water is added in mixture, the mass ratio 200 of the mixture and the water:120, it conserves 3 days.
Embodiment 7
Present embodiments provide it is a kind of using ardealite as the advanced composite material (ACM) of base material,
It prepares raw material:0.04 part of score meter by weight, 1 part of ardealite, 0.85 part of slag and sodium hydroxide.
Preparation method:By the ardealite, mixture is formed after the slag and sodium hydroxide mixing, to institute
It states and water is added in mixture, the mass ratio 189 of the mixture and the water:120, it conserves 3 days.
Comparative example 1
This comparative example provide it is a kind of using ardealite as the advanced composite material (ACM) of base material,
It prepares raw material:0.06 part of score meter by weight, 1 part of ardealite, 0.84 part of slag and sodium hydroxide.
Preparation method:By the ardealite, mixture is formed after the slag and sodium hydroxide mixing, to institute
It states and water is added in mixture, the mass ratio 188 of the mixture and the water:120, it conserves 3 days.
Comparative example 2
This comparative example provide it is a kind of using ardealite as the advanced composite material (ACM) of base material,
It prepares raw material:0.02 part of score meter by weight, 1 part of ardealite, 0.96 part of slag and sodium hydroxide.
Preparation method:By the ardealite, mixture is formed after the slag and sodium hydroxide mixing, to institute
It states and water is added in mixture, the mass ratio 188 of the mixture and the water:120, it conserves 3 days.
Comparative example 3
This comparative example provide it is a kind of using ardealite as the advanced composite material (ACM) of base material,
It prepares raw material:0.04 part of score meter by weight, 1 part of ardealite, 0.85 part of slag and sodium hydroxide.
Preparation method:By the ardealite, mixture is formed after the slag and sodium hydroxide mixing, to institute
It states and water is added in mixture, the mass ratio 187 of the mixture and the water:120, it conserves 3 days.
Comparative example 4
This comparative example provide it is a kind of using ardealite as the advanced composite material (ACM) of base material,
It prepares raw material:0.04 part of score meter by weight, 1 part of ardealite, 0.85 part of slag and sodium hydroxide.
Preparation method:By the ardealite, mixture is formed after the slag and sodium hydroxide mixing, to institute
It states and water is added in mixture, the mass ratio 201 of the mixture and the water:120, it conserves 3 days.
Experimental example 1
Experimental method:Embodiment 1-7 and comparative example the 1-4 composite material provided are set to experimental group 1-11, by phosphorus stone
Cream is set as experimental group 12, as follows the coefficient of softing of test experiments group 1-12:
6 equal portions are taken to immerse in the water that temperature is (20 ± 5) DEG C the product that above-mentioned every group of experimental group provides, the water surface should be higher by
The product spacing of product 20mm, 6 equal portions should be greater than 5mm, are taken out from water after 48h, wipe and show adhesive water, by GB/T
The regulation of the 6th chapters of 5486-2008 carries out the measurement of compression strength, takes the arithmetic mean of instantaneous value of 6 equal portions product testing values as immersion
Compression strength value f1 afterwards;
Coefficient of softing is calculated by formula 1:
ψ=f1/f0…………………………………………………(1)
In formula:ψ-coefficient of softing;f0Compression strength under-absolute dry condition, kPa;f1Pressure resistance under-water-saturated state
Degree, kPa.
The coefficient of softing of experimental group 1-12 is shown in Table 1:
The coefficient of softing of 1 experimental group 1-12 of table
Group number | 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 | 12 |
Coefficient of softing | 0.76 | 0.76 | 0.77 | 0.77 | 0.78 | 0.79 | 0.8 | 0.7 | 0.7 | 0.71 | 0.73 | 0.6 |
From the data in table 1, it can be seen that compared to experimental group 12, the coefficient of softing of the product of the offer of experimental group 1-11 can reach
To 0.7 or more, illustrate using raw material provided by the invention preparation method according to the invention carry out compounding be prepared it is compound
The mechanical property and water resistance of material are improved.The raw material proportioning of experimental group 8 and 9 is not in model provided in an embodiment of the present invention
In enclosing, coefficient of softing is not up to 0.75, illustrates using the ratio range between each raw material proportioning provided in an embodiment of the present invention
The mechanical property and water resistance for the composite material being prepared are more excellent.In the preparation method of experimental group 10 and 11, mixing
For the proportioning of object and water not in range provided in an embodiment of the present invention, coefficient of softing is not up to 0.75, illustrates using the present invention
In the parameter area for the preparation method that embodiment provides, the mechanical property and water resistance for the composite material being prepared are more excellent
It is different.In experimental group 1-7, with the coefficient of softing highest of experimental group 7, should the result shows that, when ardealite, slag, sodium hydroxide and
The mass ratio of water is 1:0.85:4:When 1.2, the mechanical property and water resistance for the composite material being prepared are the most excellent.
In conclusion using provided by the invention using ardealite as the advanced composite material (ACM) of base material:It is main with ardealite
Raw material, by being compounded with slag and sodium hydroxide, the advanced composite material (ACM) being prepared can substitute common Portland water
Mud is used as construction material, can not only consume a large amount of ardealites, and meet the energy saving, emission reduction of country's proposition, consumption reduction warp
Ji developing direction;The rational utilization of resource is of great significance to the sustainable development of China's phosphorus chemical industry and building materials industry.
The present invention takes ardealite:Slag:Sodium hydroxide is compounded according to above-mentioned parts by weight so that the coefficient of softing of gypsum base by
Traditional 0.6 is increased to 0.8, has correspondingly improved water resistance, reaches outdoor municipal works requirement.In addition, of the invention
Material production cost is at 150 yuan/ton hereinafter, nearly 200 yuan/ton or so of selling cost, market prospects are good.It is provided by the invention with phosphorus
Gypsum is the preparation method of the advanced composite material (ACM) of base material:Design science is simple and efficient, coordinated between each reaction condition, energy
It is excellent using ardealite as the advanced composite material (ACM) of base material that physical property, mechanical property and water resistance is enough prepared.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, any made by repair
Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (9)
1. a kind of using ardealite as the advanced composite material (ACM) of base material, it is characterised in that:Its raw material in parts by weight, including:
0.03-0.05 parts of 1 part of ardealite, 0.85-0.95 parts of slag and sodium hydroxide.
2. according to claim 1 using ardealite as the advanced composite material (ACM) of base material, it is characterised in that:According to parts by weight
Meter, the ardealite are 1 part, and the slag is 0.85-0.9 parts and the sodium hydroxide is 0.03-0.04 parts.
3. according to claim 2 using ardealite as the advanced composite material (ACM) of base material, it is characterised in that:According to parts by weight
Meter, the ardealite are 1 part, and the slag is 0.85 part and the sodium hydroxide is 0.04 part.
4. according to claim 1 using ardealite as the advanced composite material (ACM) of base material, it is characterised in that:The ardealite is adopted
The ardealite generated when with production high-concentration phosphate compound fertilizers;The slag uses the Iron-ore Slag of steel plant's production.
5. according to claim 4 using ardealite as the advanced composite material (ACM) of base material, it is characterised in that:The ardealite
Attached water is less than 10% wet-milling, the pH=2-5 of the ardealite, the water-soluble fluorine of the ardealite<0.5% and the phosphorus
The grain size of gypsum is less than 50 μm.
6. according to claim 4 using ardealite as the advanced composite material (ACM) of base material, it is characterised in that:The Iron-ore Slag
It detects moisture content and is less than 2%, the butt solid formation content of the Iron-ore Slag is more than 95%.
7. according to claim 6 using ardealite as the advanced composite material (ACM) of base material, it is characterised in that:The Iron-ore Slag
Size controlling is 0.04-0.06mm.
8. according to claim 4 using ardealite as the advanced composite material (ACM) of base material, it is characterised in that:The sodium hydroxide
Using the supernatant of saturation sodium hydroxide solution after precipitation.
9. it is a kind of as described in claim 1-8 any one using ardealite as the preparation method of the advanced composite material (ACM) of base material,
It is characterized in that:Including:By the ardealite, mixture is formed after the slag and sodium hydroxide mixing, to described
It is added water in mixture, the mass ratio of the mixture and the water is 188-200:120, it conserves 3 days.