CN108441974A - 一种超高强度锦纶66纤维的生产方法 - Google Patents
一种超高强度锦纶66纤维的生产方法 Download PDFInfo
- Publication number
- CN108441974A CN108441974A CN201810240403.1A CN201810240403A CN108441974A CN 108441974 A CN108441974 A CN 108441974A CN 201810240403 A CN201810240403 A CN 201810240403A CN 108441974 A CN108441974 A CN 108441974A
- Authority
- CN
- China
- Prior art keywords
- hot
- rolling
- tow
- production method
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
性能指标 | 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 |
断裂强度(g/d) | 10.0 | 10.2 | 10.4 | 10.1 | 10.3 |
断裂伸长率(%) | 22.0 | 20.0 | 16.0 | 19.0 | 18.5 |
定负荷伸长率(%) | 13.5 | 12.2 | 10.5 | 11.6 | 11.6 |
干热收缩率(%,177℃×2min,0.05g/d) | 4.7 | 5.9 | 7.7 | 6.4 | 6.8 |
Claims (7)