CN108405288A - A kind of construction method of water proof type garden landscape roof coatings - Google Patents

A kind of construction method of water proof type garden landscape roof coatings Download PDF

Info

Publication number
CN108405288A
CN108405288A CN201810067283.XA CN201810067283A CN108405288A CN 108405288 A CN108405288 A CN 108405288A CN 201810067283 A CN201810067283 A CN 201810067283A CN 108405288 A CN108405288 A CN 108405288A
Authority
CN
China
Prior art keywords
parts
coating
product
spraying
hang plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810067283.XA
Other languages
Chinese (zh)
Inventor
张�杰
李运生
李海英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henan Institute of Engineering
Original Assignee
Henan Institute of Engineering
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Henan Institute of Engineering filed Critical Henan Institute of Engineering
Priority to CN201810067283.XA priority Critical patent/CN108405288A/en
Publication of CN108405288A publication Critical patent/CN108405288A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of construction methods of water proof type garden landscape roof coatings, the longitudinal section on the roof is in reverse V-shaped structure, the roof is by the first hang plate, second hang plate and the central shaft composition being arranged between first hang plate and second hang plate, first hang plate, second hang plate and the central shaft are timber, coating adhesion using the dope layer on the log cabin top of this construction method is strong, good waterproof performance, antiseptic property is strong, and water conservancy diversion can be played to rainwater, it can be long-term in high temperature, it is placed in the case of rainwater, it can be good at meeting outdoor use environment.

Description

A kind of construction method of water proof type garden landscape roof coatings
Technical field
The present invention relates to material processing technical field more particularly to a kind of constructions of water proof type garden landscape roof coatings Method.
Background technology
Timber is exactly the main raw material(s) that human survival is relied on from ancient times, with other derived from resources such as mineral products, petrochemical industries Material compare, timber is unique reproducible natural polymer material in timber, four big construction material of steel, cement and plastics Material, remains consequence, the annual wood consumption in China has been over 400,000,000 m at present in Material Field3. Basic material of the timber as gardens roof is often used when Landscape Design, but timber is wooden as a kind of porous natural height Molecular composite material has the characteristics such as moisture absorption desorption, often because of the influence of environment mesoclimate and biological factor, wood surface Many chemical changes and physical change can occur, such as because of the drying shrinkage of climate change generation, bulking, cracking, distortion, in hot conditions Going mouldy for lower generation is rotten, is generated by worm, bacterium moth erosion rotten etc..These change procedures can allow wood surface to lose script Natural colored and texture, in order to make timber that there is more preferable environmental suitability, durability, the usually surface of wood materials It needs to coat a coating, it is mouldy to prevent timber from making moist.But the coating of existing timber on the market, poor waterproof properties, It is difficult to the environment requirement such as meet outdoor wind, solarization, drench with rain.
Invention content
The object of the present invention is to provide a kind of construction methods of water proof type garden landscape roof coatings, using this construction party The coating adhesion of the dope layer on the log cabin top of method is strong, good waterproof performance, antiseptic property are strong, and the work of water conservancy diversion can be played to rainwater With can be placed in the case of high temperature, rainwater long-term, can be good at meeting outdoor use environment.
The present invention to solve above-mentioned technical problem the technical solution adopted is that：A kind of water proof type garden landscape roof coatings Construction method, the longitudinal section on the roof is in reverse V-shaped structure, and the roof is existed by the first hang plate, the second hang plate and setting Central shaft composition between first hang plate and second hang plate, first hang plate, the second hang plate and described Central shaft is timber, and the construction method on the roof includes the following steps：
1）It is dry：The roof is put into drying machine and is dried, the moisture content on the roof after drying is 8 ~ 12%, obtains material Substrate；
2）Material processing：By step 1）Material after drying is first along the grain sanded with 250 ~ 400# sand paper, and material table is removed The oil in face, pollution, burr；Material surface is subjected to wear smooth with 400 ~ 600# sand paper again, then by dust removal machine to material table Face is dusted；
3）It sprays for the first time：Using coating I to step 2）Treated, and material surface carries out completely enclosed spraying, obtains with The product of one sprayed coating；
4）It is dry：Using ultraviolet light drying machine to step 3）Product after middle first time spraying is dried；
5）Sanding：Using 500 ~ 600# sand paper to step 4）The product after first time spraying after drying is sanded；
6）Second of spraying：Using flush coater to step 5）The surface spraying coating of the product after first time spraying after middle sand milling II, obtain the product with the second sprayed coating；
7）It is dry：Using ultraviolet light drying machine to step 6）In second spray after product be dried；
8）Sanding：With 500 ~ 600# sand paper to step 7）The product after second of spraying after drying is sanded；
9）Third time sprays：Using flush coater to step 8）It is sprayed on the surface of the product after second of spraying after middle sand milling It applies, obtains the product with third sprayed coating；The third sprayed coating includes the base being arranged in second sprayed coating outer surface And the stiffener in the base layer exterior surface is set, the stiffener is arranged at intervals in the base；
10）It is dry：Using ultraviolet light drying machine to step 9）Product after middle third time spraying is dried, and obtains finished product.
Further, the coating of the base of the third sprayed coating is coating I.
Further, the coating I is made of each component of following mass fraction：40 ~ 50 parts of epoxy acrylic resin, three 20 ~ 30 parts of poly cyanamid, 20 ~ 25 parts of ethylene glycol, 10 ~ 15 parts of dimethylethanolamine, 10 ~ 15 parts of ceresine, 10 ~ 15 parts of rosin, all scholars 5 ~ 10 parts of woods, 5 ~ 10 parts of tung oil, 5 ~ 10 parts of polyborosiloxane, 3 ~ 5 parts of hydroxypropyl methyl cellulose, polyoxyethylene polyoxy Propanolamine 2 ~ 4 parts of ether, 20 ~ 40 parts of water.
Further, the coating II is made of each component of following mass fraction：40 ~ 50 parts of epoxy acrylic resin, 10 ~ 20 parts of neopelex lotion, 10 ~ 20 parts of toluene di-isocyanate(TDI), 10 ~ 20 parts of titanium dioxide, methylethanolamine 8 ~ 16 parts, 8 ~ 12 parts of palm oil, 5 ~ 10 parts of hydroxyethyl cellulose, 5 ~ 8 parts of polypropylene glycerol aether, 3 ~ 8 parts of nano-calcium carbonate, silicon it is molten 2 ~ 6 parts of glue, 20 ~ 40 parts of water.
Further, the coating III of the stiffener is made of each component of following mass fraction：Epoxy acrylic resin 50 ~ 60 parts, 20 ~ 40 parts of hydroxyethyl cellulose, 15 ~ 35 parts of polyvinyl alcohol, 15 ~ 25 parts of attapulgite, polypropylene glycerol aether 5 ~ 10 parts, 5 ~ 10 parts of tung oil, 5 ~ 8 parts of nano silicon dioxide, nano-TiO24 ~ 6 parts, 3 ~ 5 parts of silane coupling agent, 2 ~ 4 parts of water-reducing agent.
Further, it is equipped with the stiffener on first hang plate and second hang plate, it is each described to add Strong item is arranged along perpendicular to the central axis direction.
Further, the thickness of the coating I of the product after the first time spraying is 0.3 ~ 0.8mm.
Further, the thickness of the coating II of the product after second of spraying is 0.4 ~ 0.8mm.
Further, the thickness of the coating I of the base of product is 0.1 ~ 0.6mm after third time sprays.
Further, the thickness of the coating III of the stiffener of product is 0.5 ~ 1mm after third time sprays.
Beneficial effects of the present invention mainly show as follows：The present invention regard waterproof and anticorrosion type coating I as the first sprayed coating, applies The completely enclosed surface coated in log cabin top of material I, the seamless one of formation homogeneous and waterproof after log cabin top surface film forming Sealant；The bonding force of the first sprayed coating and third sprayed coating is strengthened as the second sprayed coating using coating II so that log cabin The color of top on the whole is more plentiful fine and smooth and round and smooth, and third sprayed coating includes the base being arranged in second sprayed coating outer surface Layer and stiffener in the base layer exterior surface is set, the stiffener is arranged at intervals in the base；The coating of base is Water proof anti-corrosive paint I, the completely enclosed surface coated in log cabin top of coating I are formed equal after the surface filming on log cabin top The sealant of one that matter is seamless and waterproof；Stiffener uses waterproof heat-resisting anticorrosive paint III, on the one hand enhances roof On the other hand high temperature resistant waterproof corrosion resistance can also form the water conservancy diversion region of rainwater, avoid between spaced stiffener Rainwater, which is hoarded, damages roof on log cabin top.
Specific implementation mode
The present invention is described in detail in conjunction with the embodiments, the present embodiment based on the technical solution of the present invention, gives Detailed embodiment and specific operating process, but protection scope of the present invention is not limited to following embodiments.
Embodiment one
The longitudinal section of a kind of construction method of water proof type garden landscape roof coatings, the roof is in reverse V-shaped structure, the roof It is made of the first hang plate, the second hang plate and the central shaft that is arranged between first hang plate and second hang plate, First hang plate, the second hang plate and the central shaft are timber, and the construction method on the roof includes the following steps：
1）It is dry：The roof is put into drying machine and is dried, the moisture content on the roof after drying is 8 ~ 12%, obtains material Substrate；
2）Material processing：By step 1）Material after drying is first along the grain sanded with 250 ~ 400# sand paper, and material table is removed The oil in face, pollution, burr；Material surface is subjected to wear smooth with 400 ~ 600# sand paper again, then by dust removal machine to material table Face is dusted；
3）It sprays for the first time：Using coating I to step 2）Treated, and material surface carries out completely enclosed spraying, obtains with The product of one sprayed coating；
4）It is dry：Using ultraviolet light drying machine to step 3）Product after middle first time spraying is dried；
5）Sanding：Using 500 ~ 600# sand paper to step 4）The product after first time spraying after drying is sanded；
6）Second of spraying：Using flush coater to step 5）The surface spraying coating of the product after first time spraying after middle sand milling II, obtain the product with the second sprayed coating；
7）It is dry：Using ultraviolet light drying machine to step 6）In second spray after product be dried；
8）Sanding：With 500 ~ 600# sand paper to step 7）The product after second of spraying after drying is sanded；
9）Third time sprays：Using flush coater to step 8）It is sprayed on the surface of the product after second of spraying after middle sand milling It applies, obtains the product with third sprayed coating；The third sprayed coating includes the base being arranged in second sprayed coating outer surface And the stiffener in the base layer exterior surface is set, the stiffener is arranged at intervals in the base；
10）It is dry：Using ultraviolet light drying machine to step 9）Product after middle third time spraying is dried, and obtains finished product.
Further, the coating of the base of the third sprayed coating is coating I.
Further, the coating I is made of each component of following mass fraction：40 parts of epoxy acrylic resin, trimerization 20 parts of cyanamide, 20 parts of ethylene glycol, 10 parts of dimethylethanolamine, 10 parts of ceresine, 10 parts of rosin, 5 parts of vaseline, 5 parts of tung oil, poly- boron 5 parts of siloxanes, 3 parts of hydroxypropyl methyl cellulose, 2 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 20 parts of water.
Further, the coating II is made of each component of following mass fraction：40 parts of epoxy acrylic resin, 12 10 parts of sodium alkyl benzene sulfonate lotion, 10 parts of toluene di-isocyanate(TDI), 10 parts of titanium dioxide, 8 parts of methylethanolamine, 8 parts of palm oil, hydroxyl 5 parts of ethyl cellulose, 5 parts of polypropylene glycerol aether, 3 parts of nano-calcium carbonate, 2 parts of Ludox, 20 parts of water.
Further, the coating III of the stiffener is made of each component of following mass fraction：Epoxy acrylic resin 50 parts, 20 parts of hydroxyethyl cellulose, 15 parts of polyvinyl alcohol, 15 parts of attapulgite, 5 parts of polypropylene glycerol aether, 5 parts of tung oil, receive 5 parts of silica of rice, nano-TiO24 parts, 3 parts of silane coupling agent, 2 parts of water-reducing agent.
Further, it is equipped with the stiffener on first hang plate and second hang plate, it is each described to add Strong item is arranged along perpendicular to the central axis direction.
Further, the thickness of the coating I of the product after the first time spraying is 0.3 ~ 0.8mm.
Further, the thickness of the coating II of the product after second of spraying is 0.4 ~ 0.8mm.
Further, the thickness of the coating I of the base of product is 0.1 ~ 0.6mm after third time sprays.
Further, the thickness of the coating III of the stiffener of product is 0.5 ~ 1mm after third time sprays.
Embodiment two
The longitudinal section of a kind of construction method of water proof type garden landscape roof coatings, the roof is in reverse V-shaped structure, the roof It is made of the first hang plate, the second hang plate and the central shaft that is arranged between first hang plate and second hang plate, First hang plate, the second hang plate and the central shaft are timber, and the construction method on the roof includes the following steps：
1）It is dry：The roof is put into drying machine and is dried, the moisture content on the roof after drying is 8 ~ 12%, obtains material Substrate；
2）Material processing：By step 1）Material after drying is first along the grain sanded with 250 ~ 400# sand paper, and material table is removed The oil in face, pollution, burr；Material surface is subjected to wear smooth with 400 ~ 600# sand paper again, then by dust removal machine to material table Face is dusted；
3）It sprays for the first time：Using coating I to step 2）Treated, and material surface carries out completely enclosed spraying, obtains with The product of one sprayed coating；
4）It is dry：Using ultraviolet light drying machine to step 3）Product after middle first time spraying is dried；
5）Sanding：Using 500 ~ 600# sand paper to step 4）The product after first time spraying after drying is sanded；
6）Second of spraying：Using flush coater to step 5）The surface spraying coating of the product after first time spraying after middle sand milling II, obtain the product with the second sprayed coating；
7）It is dry：Using ultraviolet light drying machine to step 6）In second spray after product be dried；
8）Sanding：With 500 ~ 600# sand paper to step 7）The product after second of spraying after drying is sanded；
9）Third time sprays：Using flush coater to step 8）It is sprayed on the surface of the product after second of spraying after middle sand milling It applies, obtains the product with third sprayed coating；The third sprayed coating includes the base being arranged in second sprayed coating outer surface And the stiffener in the base layer exterior surface is set, the stiffener is arranged at intervals in the base；
10）It is dry：Using ultraviolet light drying machine to step 9）Product after middle third time spraying is dried, and obtains finished product.
Further, the coating of the base of the third sprayed coating is coating I.
Further, the coating I is made of each component of following mass fraction：50 parts of epoxy acrylic resin, trimerization 30 parts of cyanamide, 15 parts of dimethylethanolamine, 15 parts of ceresine, 15 parts of rosin, 10 parts of vaseline, 10 parts of tung oil, gathers 25 parts of ethylene glycol 10 parts of Borosiloxane, 5 parts of hydroxypropyl methyl cellulose, 4 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 40 parts of water.
Further, the coating II is made of each component of following mass fraction：50 parts of epoxy acrylic resin, 12 20 parts of sodium alkyl benzene sulfonate lotion, 20 parts of toluene di-isocyanate(TDI), 20 parts of titanium dioxide, 16 parts of methylethanolamine, 12 parts of palm oil, 10 parts of hydroxyethyl cellulose, 8 parts of polypropylene glycerol aether, 8 parts of nano-calcium carbonate, 6 parts of Ludox, 40 parts of water.
Further, the coating III of the stiffener is made of each component of following mass fraction：Epoxy acrylic resin 60 parts, 40 parts of hydroxyethyl cellulose, 35 parts of polyvinyl alcohol, 25 parts of attapulgite, 10 parts of polypropylene glycerol aether, 10 parts of tung oil, 8 parts of nano silicon dioxide, nano-TiO26 parts, 5 parts of silane coupling agent, 4 parts of water-reducing agent.
Further, it is equipped with the stiffener on first hang plate and second hang plate, it is each described to add Strong item is arranged along perpendicular to the central axis direction.
Further, the thickness of the coating I of the product after the first time spraying is 0.3 ~ 0.8mm.
Further, the thickness of the coating II of the product after second of spraying is 0.4 ~ 0.8mm.
Further, the thickness of the coating I of the base of product is 0.1 ~ 0.6mm after third time sprays.
Further, the thickness of the coating III of the stiffener of product is 0.5 ~ 1mm after third time sprays.
Embodiment three
The longitudinal section of a kind of construction method of water proof type garden landscape roof coatings, the roof is in reverse V-shaped structure, the roof It is made of the first hang plate, the second hang plate and the central shaft that is arranged between first hang plate and second hang plate, First hang plate, the second hang plate and the central shaft are timber, and the construction method on the roof includes the following steps：
1）It is dry：The roof is put into drying machine and is dried, the moisture content on the roof after drying is 10%, obtains material base Bottom；
2）Material processing：By step 1）Material after drying is first along the grain sanded with 250 ~ 400# sand paper, and material table is removed The oil in face, pollution, burr；Material surface is subjected to wear smooth with 400 ~ 600# sand paper again, then by dust removal machine to material table Face is dusted；
3）It sprays for the first time：Using coating I to step 2）Treated, and material surface carries out completely enclosed spraying, obtains with The product of one sprayed coating；
4）It is dry：Using ultraviolet light drying machine to step 3）Product after middle first time spraying is dried；
5）Sanding：Using 500 ~ 600# sand paper to step 4）The product after first time spraying after drying is sanded；
6）Second of spraying：Using flush coater to step 5）The surface spraying coating of the product after first time spraying after middle sand milling II, obtain the product with the second sprayed coating；
7）It is dry：Using ultraviolet light drying machine to step 6）In second spray after product be dried；
8）Sanding：With 500 ~ 600# sand paper to step 7）The product after second of spraying after drying is sanded；
9）Third time sprays：Using flush coater to step 8）It is sprayed on the surface of the product after second of spraying after middle sand milling It applies, obtains the product with third sprayed coating；The third sprayed coating includes the base being arranged in second sprayed coating outer surface And the stiffener in the base layer exterior surface is set, the stiffener is arranged at intervals in the base；
10）It is dry：Using ultraviolet light drying machine to step 9）Product after middle third time spraying is dried, and obtains finished product.
Further, the coating of the base of the third sprayed coating is coating I.
Further, the coating I is made of each component of following mass fraction：45 parts of epoxy acrylic resin, trimerization 25 parts of cyanamide, 22.5 parts of ethylene glycol, 12.5 parts of dimethylethanolamine, 12.5 parts of ceresine, 12.5 parts of rosin, 7.5 parts of vaseline, paulownia 7.5 parts of oil, 7.5 parts of polyborosiloxane, 4 parts of hydroxypropyl methyl cellulose, 3 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 30 parts of water.
Further, the coating II is made of each component of following mass fraction：45 parts of epoxy acrylic resin, 12 15 parts of sodium alkyl benzene sulfonate lotion, 15 parts of toluene di-isocyanate(TDI), 15 parts of titanium dioxide, 12 parts of methylethanolamine, 10 parts of palm oil, 7.5 parts of hydroxyethyl cellulose, 6.5 parts of polypropylene glycerol aether, 5.5 parts of nano-calcium carbonate, 4 parts of Ludox, 30 parts of water.
Further, the coating III of the stiffener is made of each component of following mass fraction：Epoxy acrylic resin 55 parts, 30 parts of hydroxyethyl cellulose, 20 parts of polyvinyl alcohol, 20 parts of attapulgite, 7.5 parts of polypropylene glycerol aether, tung oil 7.5 Part, 5.6 parts of nano silicon dioxide, nano-TiO25 parts, 4 parts of silane coupling agent, 3 parts of water-reducing agent.
Further, it is equipped with the stiffener on first hang plate and second hang plate, it is each described to add Strong item is arranged along perpendicular to the central axis direction.
Further, the thickness of the coating I of the product after the first time spraying is 0.55mm.
Further, the thickness of the coating II of the product after second of spraying is 0.6mm.
Further, the thickness of the coating I of the base of product is 0.35mm after third time sprays.
Further, the thickness of the coating III of the stiffener of product is 0.75mm after third time sprays.
Example IV
The longitudinal section of a kind of construction method of water proof type garden landscape roof coatings, the roof is in reverse V-shaped structure, the roof It is made of the first hang plate, the second hang plate and the central shaft that is arranged between first hang plate and second hang plate, First hang plate, the second hang plate and the central shaft are timber, and the construction method on the roof includes the following steps：
1）It is dry：The roof is put into drying machine and is dried, the moisture content on the roof after drying is 9%, obtains material base Bottom；
2）Material processing：By step 1）Material after drying is first along the grain sanded with 250 ~ 400# sand paper, and material table is removed The oil in face, pollution, burr；Material surface is subjected to wear smooth with 400 ~ 600# sand paper again, then by dust removal machine to material table Face is dusted；
3）It sprays for the first time：Using coating I to step 2）Treated, and material surface carries out completely enclosed spraying, obtains with The product of one sprayed coating；
4）It is dry：Using ultraviolet light drying machine to step 3）Product after middle first time spraying is dried；
5）Sanding：Using 500 ~ 600# sand paper to step 4）The product after first time spraying after drying is sanded；
6）Second of spraying：Using flush coater to step 5）The surface spraying coating of the product after first time spraying after middle sand milling II, obtain the product with the second sprayed coating；
7）It is dry：Using ultraviolet light drying machine to step 6）In second spray after product be dried；
8）Sanding：With 500 ~ 600# sand paper to step 7）The product after second of spraying after drying is sanded；
9）Third time sprays：Using flush coater to step 8）It is sprayed on the surface of the product after second of spraying after middle sand milling It applies, obtains the product with third sprayed coating；The third sprayed coating includes the base being arranged in second sprayed coating outer surface And the stiffener in the base layer exterior surface is set, the stiffener is arranged at intervals in the base；
10）It is dry：Using ultraviolet light drying machine to step 9）Product after middle third time spraying is dried, and obtains finished product.
Further, the coating of the base of the third sprayed coating is coating I.
Further, the coating I is made of each component of following mass fraction：40 parts of epoxy acrylic resin, trimerization 20 parts of cyanamide, 20 parts of ethylene glycol, 10 parts of dimethylethanolamine, 10 parts of ceresine, 10 parts of rosin, 5 parts of vaseline, 5 parts of tung oil, poly- boron 5 parts of siloxanes, 3 parts of hydroxypropyl methyl cellulose, 2 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 20 parts of water.
Further, the coating II is made of each component of following mass fraction：50 parts of epoxy acrylic resin, 12 20 parts of sodium alkyl benzene sulfonate lotion, 20 parts of toluene di-isocyanate(TDI), 20 parts of titanium dioxide, 16 parts of methylethanolamine, 12 parts of palm oil, 10 parts of hydroxyethyl cellulose, 8 parts of polypropylene glycerol aether, 8 parts of nano-calcium carbonate, 6 parts of Ludox, 40 parts of water.
Further, the coating III of the stiffener is made of each component of following mass fraction：Epoxy acrylic resin 60 parts, 40 parts of hydroxyethyl cellulose, 35 parts of polyvinyl alcohol, 25 parts of attapulgite, 10 parts of polypropylene glycerol aether, 10 parts of tung oil, 8 parts of nano silicon dioxide, nano-TiO26 parts, 5 parts of silane coupling agent, 4 parts of water-reducing agent.
Further, it is equipped with the stiffener on first hang plate and second hang plate, it is each described to add Strong item is arranged along perpendicular to the central axis direction.
Further, the thickness of the coating I of the product after the first time spraying is 0.3mm.
Further, the thickness of the coating II of the product after second of spraying is 0.4mm.
Further, the thickness of the coating I of the base of product is 0.1mm after third time sprays.
Further, the thickness of the coating III of the stiffener of product is 0.5mm after third time sprays.
Embodiment five
The longitudinal section of a kind of construction method of water proof type garden landscape roof coatings, the roof is in reverse V-shaped structure, the roof It is made of the first hang plate, the second hang plate and the central shaft that is arranged between first hang plate and second hang plate, First hang plate, the second hang plate and the central shaft are timber, and the construction method on the roof includes the following steps：
1）It is dry：The roof is put into drying machine and is dried, the moisture content on the roof after drying is 10%, obtains material base Bottom；
2）Material processing：By step 1）Material after drying is first along the grain sanded with 250 ~ 400# sand paper, and material table is removed The oil in face, pollution, burr；Material surface is subjected to wear smooth with 400 ~ 600# sand paper again, then by dust removal machine to material table Face is dusted；
3）It sprays for the first time：Using coating I to step 2）Treated, and material surface carries out completely enclosed spraying, obtains with The product of one sprayed coating；
4）It is dry：Using ultraviolet light drying machine to step 3）Product after middle first time spraying is dried；
5）Sanding：Using 500 ~ 600# sand paper to step 4）The product after first time spraying after drying is sanded；
6）Second of spraying：Using flush coater to step 5）The surface spraying coating of the product after first time spraying after middle sand milling II, obtain the product with the second sprayed coating；
7）It is dry：Using ultraviolet light drying machine to step 6）In second spray after product be dried；
8）Sanding：With 500 ~ 600# sand paper to step 7）The product after second of spraying after drying is sanded；
9）Third time sprays：Using flush coater to step 8）It is sprayed on the surface of the product after second of spraying after middle sand milling It applies, obtains the product with third sprayed coating；The third sprayed coating includes the base being arranged in second sprayed coating outer surface And the stiffener in the base layer exterior surface is set, the stiffener is arranged at intervals in the base；
10）It is dry：Using ultraviolet light drying machine to step 9）Product after middle third time spraying is dried, and obtains finished product.
Further, the coating of the base of the third sprayed coating is coating I.
Further, the coating I is made of each component of following mass fraction：43 parts of epoxy acrylic resin, trimerization 23 parts of cyanamide, 21 parts of ethylene glycol, 12 parts of dimethylethanolamine, 12 parts of ceresine, 12 parts of rosin, 6 parts of vaseline, 6 parts of tung oil, poly- boron 6 parts of siloxanes, 3.5 parts of hydroxypropyl methyl cellulose, 2.5 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 25 parts of water.
Further, the coating II is made of each component of following mass fraction：42 parts of epoxy acrylic resin, 12 12 parts of sodium alkyl benzene sulfonate lotion, 12 parts of toluene di-isocyanate(TDI), 12 parts of titanium dioxide, 10 parts of methylethanolamine, 9 parts of palm oil, 6 parts of hydroxyethyl cellulose, 6 parts of polypropylene glycerol aether, 5 parts of nano-calcium carbonate, 3 parts of Ludox, 25 parts of water.
Further, the coating III of the stiffener is made of each component of following mass fraction：Epoxy acrylic resin 52 parts, 25 parts of hydroxyethyl cellulose, 18 parts of polyvinyl alcohol, 18 parts of attapulgite, 6 parts of polypropylene glycerol aether, 6 parts of tung oil, receive 6 parts of silica of rice, nano-TiO24.5 parts, 3.5 parts of silane coupling agent, 2.5 parts of water-reducing agent.
Further, it is equipped with the stiffener on first hang plate and second hang plate, it is each described to add Strong item is arranged along perpendicular to the central axis direction.
Further, the thickness of the coating I of the product after the first time spraying is 0.4mm.
Further, the thickness of the coating II of the product after second of spraying is 0.5mm.
Further, the thickness of the coating I of the base of product is 0.3mm after third time sprays.
Further, the thickness of the coating III of the stiffener of product is 0.6mm after third time sprays.
Embodiment six
The longitudinal section of a kind of construction method of water proof type garden landscape roof coatings, the roof is in reverse V-shaped structure, the roof It is made of the first hang plate, the second hang plate and the central shaft that is arranged between first hang plate and second hang plate, First hang plate, the second hang plate and the central shaft are timber, and the construction method on the roof includes the following steps：
1）It is dry：The roof is put into drying machine and is dried, the moisture content on the roof after drying is 11%, obtains material base Bottom；
2）Material processing：By step 1）Material after drying is first along the grain sanded with 250 ~ 400# sand paper, and material table is removed The oil in face, pollution, burr；Material surface is subjected to wear smooth with 400 ~ 600# sand paper again, then by dust removal machine to material table Face is dusted；
3）It sprays for the first time：Using coating I to step 2）Treated, and material surface carries out completely enclosed spraying, obtains with The product of one sprayed coating；
4）It is dry：Using ultraviolet light drying machine to step 3）Product after middle first time spraying is dried；
5）Sanding：Using 500 ~ 600# sand paper to step 4）The product after first time spraying after drying is sanded；
6）Second of spraying：Using flush coater to step 5）The surface spraying coating of the product after first time spraying after middle sand milling II, obtain the product with the second sprayed coating；
7）It is dry：Using ultraviolet light drying machine to step 6）In second spray after product be dried；
8）Sanding：With 500 ~ 600# sand paper to step 7）The product after second of spraying after drying is sanded；
9）Third time sprays：Using flush coater to step 8）It is sprayed on the surface of the product after second of spraying after middle sand milling It applies, obtains the product with third sprayed coating；The third sprayed coating includes the base being arranged in second sprayed coating outer surface And the stiffener in the base layer exterior surface is set, the stiffener is arranged at intervals in the base；
10）It is dry：Using ultraviolet light drying machine to step 9）Product after middle third time spraying is dried, and obtains finished product.
Further, the coating of the base of the third sprayed coating is coating I.
Further, the coating I is made of each component of following mass fraction：48 parts of epoxy acrylic resin, trimerization 28 parts of cyanamide, 24 parts of ethylene glycol, 14 parts of dimethylethanolamine, 14 parts of ceresine, 14 parts of rosin, 9 parts of vaseline, 9 parts of tung oil, poly- boron 9 parts of siloxanes, 4.5 parts of hydroxypropyl methyl cellulose, 3.5 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, 38 parts of water.
Further, the coating II is made of each component of following mass fraction：48 parts of epoxy acrylic resin, 12 18 parts of sodium alkyl benzene sulfonate lotion, 18 parts of toluene di-isocyanate(TDI), 18 parts of titanium dioxide, 14 parts of methylethanolamine, 11 parts of palm oil, 9 parts of hydroxyethyl cellulose, 7 parts of polypropylene glycerol aether, 7 parts of nano-calcium carbonate, 5 parts of Ludox, 35 parts of water.
Further, the coating III of the stiffener is made of each component of following mass fraction：Epoxy acrylic resin 58 parts, 38 parts of hydroxyethyl cellulose, 30 parts of polyvinyl alcohol, 23 parts of attapulgite, 8 parts of polypropylene glycerol aether, 8 parts of tung oil, receive 7 parts of silica of rice, nano-TiO25.5 parts, 4.5 parts of silane coupling agent, 3.5 parts of water-reducing agent.
Further, it is equipped with the stiffener on first hang plate and second hang plate, it is each described to add Strong item is arranged along perpendicular to the central axis direction.
Further, the thickness of the coating I of the product after the first time spraying is 0.7mm.
Further, the thickness of the coating II of the product after second of spraying is 0.7mm.
Further, the thickness of the coating I of the base of product is 0.5mm after third time sprays.
Further, the thickness of the coating III of the stiffener of product is 0.9mm after third time sprays.
The roof surface on roof and log cabin top currently on the market in the present invention is occurred with the growth of usage time Variation as a comparison, it is found that log cabin in the market is withstood on during outdoor use, using after 1 ~ 2 year often because of rain Being exposed to the sun plus the sun in water penetration to the internal interstices of timber, log cabin top often will appear more serious corrosion phenomenon；From And log cabin top is caused not use normally；
The surface coated in log cabin top that the present invention completely encloses waterproof and anticorrosion type coating I as the first sprayed coating, coating I, The sealant of the seamless one of homogeneous and waterproof is formed after log cabin top surface film forming；Added as the second sprayed coating using coating II The strong bonding force of first sprayed coating and third sprayed coating so that the color of log cabin top on the whole it is more plentiful it is fine and smooth with it is round and smooth, Third sprayed coating include be arranged second sprayed coating outer surface base and stiffener in the base layer exterior surface is set, The stiffener is arranged at intervals in the base；The coating of base is water proof anti-corrosive paint I, the completely enclosed coating of coating I Surface on log cabin top forms the sealant of the seamless one of homogeneous and waterproof after the surface filming on log cabin top；Stiffener is adopted With waterproof heat-resisting anticorrosive paint III, the high temperature resistant waterproof corrosion resistance on roof is on the one hand enhanced, on the other hand, interval The water conservancy diversion region that rainwater can also be formed between the stiffener of setting avoids rainwater from hoarding and is damaged to roof on log cabin top；
The log cabin of the present invention is withstood on using still preferable state is remain after 3 ~ 4 years, is not in the corrosion phenomenon of large area, Usage time can reach 5 ~ 6 years as long as.
It should also be noted that, herein, the relational terms such as I, II, III are used merely to an entity or behaviour Make with another entity or operate distinguish, without necessarily requiring or implying between these entities or operation there are it is any this The actual relationship of kind or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to nonexcludability Include so that including a series of elements process, method, article or equipment not only include those elements, but also Including other elements that are not explicitly listed, or further include for this process, method, article or equipment intrinsic want Element.In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that wanted including described There is also other identical elements in the process, method, article or equipment of element.
Each embodiment is described by the way of progressive in this specification, the highlights of each of the examples are with other The difference of embodiment, just to refer each other for identical similar portion between each embodiment.

Claims (10)

1. the longitudinal section of a kind of construction method of water proof type garden landscape roof coatings, the roof is in reverse V-shaped structure, feature It is：The roof is by the first hang plate, the second hang plate and is arranged between first hang plate and second hang plate Central shaft composition, first hang plate, the second hang plate and the central shaft are timber, the construction method packet on the roof Include following steps：
1）It is dry：The roof is put into drying machine and is dried, the moisture content on the roof after drying is 8 ~ 12%, obtains material Substrate；
2）Material processing：By step 1）Material after drying is first along the grain sanded with 250 ~ 400# sand paper, and material table is removed The oil in face, pollution, burr；Material surface is subjected to wear smooth with 400 ~ 600# sand paper again, then by dust removal machine to material table Face is dusted；
3）It sprays for the first time：Using coating I to step 2）Treated, and material surface carries out completely enclosed spraying, obtains with The product of one sprayed coating；
4）It is dry：Using ultraviolet light drying machine to step 3）Product after middle first time spraying is dried；
5）Sanding：Using 500 ~ 600# sand paper to step 4）The product after first time spraying after drying is sanded；
6）Second of spraying：Using flush coater to step 5）The surface spraying coating of the product after first time spraying after middle sand milling II, obtain the product with the second sprayed coating；
7）It is dry：Using ultraviolet light drying machine to step 6）In second spray after product be dried；
8）Sanding：With 500 ~ 600# sand paper to step 7）The product after second of spraying after drying is sanded；
9）Third time sprays：Using flush coater to step 8）It is sprayed on the surface of the product after second of spraying after middle sand milling It applies, obtains the product with third sprayed coating；The third sprayed coating includes the base being arranged in second sprayed coating outer surface And the stiffener in the base layer exterior surface is set, the stiffener is arranged at intervals in the base；
10）It is dry：Using ultraviolet light drying machine to step 9）Product after middle third time spraying is dried, and obtains finished product.
2. a kind of construction method of water proof type garden landscape roof coatings according to claim 1, it is characterised in that：Institute The coating for stating the base of third sprayed coating is coating I.
3. a kind of construction method of water proof type garden landscape roof coatings according to claim 1, it is characterised in that：Institute Coating I is stated to be made of each component of following mass fraction：40 ~ 50 parts of epoxy acrylic resin, 20 ~ 30 parts of melamine, second two 20 ~ 25 parts of alcohol, 10 ~ 15 parts of dimethylethanolamine, 10 ~ 15 parts of ceresine, 10 ~ 15 parts of rosin, 5 ~ 10 parts of vaseline, tung oil 5 ~ 10 Part, 5 ~ 10 parts of polyborosiloxane, 3 ~ 5 parts of hydroxypropyl methyl cellulose, 2 ~ 4 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, water 20 ~ 40 Part.
4. a kind of construction method of water proof type garden landscape roof coatings according to claim 1, it is characterised in that：Institute Coating II is stated to be made of each component of following mass fraction：40 ~ 50 parts of epoxy acrylic resin, neopelex lotion 10 ~ 20 parts, 10 ~ 20 parts of toluene di-isocyanate(TDI), 10 ~ 20 parts of titanium dioxide, 8 ~ 16 parts of methylethanolamine, 8 ~ 12 parts of palm oil, hydroxyl 5 ~ 10 parts of ethyl cellulose, 5 ~ 8 parts of polypropylene glycerol aether, 3 ~ 8 parts of nano-calcium carbonate, 2 ~ 6 parts of Ludox, 20 ~ 40 parts of water.
5. a kind of construction method of water proof type garden landscape roof coatings according to claim 1, it is characterised in that：Institute The coating III for stating stiffener is made of each component of following mass fraction：50 ~ 60 parts of epoxy acrylic resin, hydroxyethyl cellulose 20 ~ 40 parts, 15 ~ 35 parts of polyvinyl alcohol, 15 ~ 25 parts of attapulgite, 5 ~ 10 parts of polypropylene glycerol aether, tung oil 5 ~ 10 part, nanometer 5 ~ 8 parts of silica, nano-TiO24 ~ 6 parts, 3 ~ 5 parts of silane coupling agent, 2 ~ 4 parts of water-reducing agent.
6. a kind of construction method of water proof type garden landscape roof coatings according to claim 1, it is characterised in that：Institute It states and is equipped with the stiffener on the first hang plate and second hang plate, each stiffener is along in described Mandrel direction is arranged.
7. a kind of construction method of water proof type garden landscape roof coatings according to claim 1, it is characterised in that：Institute The thickness for stating the coating I of the product after spraying for the first time is 0.3 ~ 0.8mm.
8. a kind of construction method of water proof type garden landscape roof coatings according to claim 1, it is characterised in that：Institute The thickness for stating the coating II of the product after second of spraying is 0.4 ~ 0.8mm.
9. a kind of construction method of water proof type garden landscape roof coatings according to claim 1, it is characterised in that：The The thickness of the coating I of the base of product is 0.1 ~ 0.6mm after spraying three times.
10. a kind of construction method of water proof type garden landscape roof coatings according to claim 1, it is characterised in that： The thickness of the coating III of the stiffener of product is 0.5 ~ 1mm after third time sprays.
CN201810067283.XA 2018-01-24 2018-01-24 A kind of construction method of water proof type garden landscape roof coatings Pending CN108405288A (en)