CN108384449A - A kind of multifunctional coating - Google Patents
A kind of multifunctional coating Download PDFInfo
- Publication number
- CN108384449A CN108384449A CN201810202322.2A CN201810202322A CN108384449A CN 108384449 A CN108384449 A CN 108384449A CN 201810202322 A CN201810202322 A CN 201810202322A CN 108384449 A CN108384449 A CN 108384449A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- curing agent
- multifunctional coating
- filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of multifunctional coatings, are made of the raw material of following parts by weight：50 70 parts of organic siliconresin, 40 60 parts of diluent, S1O2For 6 10 parts, 46 parts of pigment, 57 parts of talcum powder, SI3N4For 57 parts, 48 parts of curing agent, 7-13 parts of levelling agent, 8-12 parts of antisettling agent, 40 50 parts of filler.A kind of main function of multifunctional coating of the present invention is protection and decorating objects surface, is prolonged the service life, beautifying articles appearance；With strong corrosion proof function, also there is the specific function that anti-sleet knot slips.Decorate and be not easy to fall dust for outdoor facility body surface simultaneously, service life is far above ten times of general coating or more, and the coating applications are extremely wide, and non-environmental-pollution problem, high temperature resistant is up to 300 DEG C or more and simple production process.
Description
Technical field
The present invention relates to a kind of coating, and in particular to a kind of multifunctional coating.
Background technology
95% or more the coating material of domestic construction, the industries such as the net such as anti-transformation, iron skill, ship, oil in old city at present
It is all made of coating, since people begin to use coating, the development of coatings industry can be described as advancing by leaps and bounds, and produce skill
Earth-shaking variation has occurred with the continuous improvement of human sciences' technology in art, technological level.But prior art coating is deposited
It is poor in antistatic property, anticorrosion, resistance tocrocking, do not have anti-sleet knot mostly and slips function, is easily stained with that fall dust and production technology complicated
The defects of.
Invention content
The purpose of the present invention provides a kind of multifunctional coating aiming at defect of the existing technology.
Its technical solution is：A kind of multifunctional coating is made of the raw material of following parts by weight：Organic siliconresin 50-70
Part, 40-60 parts of diluent, S1O2For 6-10 parts, 4-6 parts of pigment, 5-7 parts of talcum powder, SI3N4For 5-7 parts, 4-8 parts of curing agent,
7-13 parts of levelling agent, 8-12 parts of antisettling agent, 40-50 parts of filler；Wherein best composition is 60 parts of organic siliconresin, diluent
50 parts, S1O2For 8 parts, 5 parts of pigment, 6 parts of talcum powder, SI3N4For 6 parts, 5 parts of curing agent, 10 parts of levelling agent, 10 parts of antisettling agent,
47 parts of filler.
Wherein, the filler by the schmigel of 19-20 parts by weight, 6-10 parts of refined cement, 5-11 parts of mica powder and
9-12 parts of flake asbestos mixing composition；Wherein best composition is the schmigel, 8 parts of refined cement, 9 parts of cloud by 20 parts by weight
Female powder and 10 parts of flake asbestos mixing composition.
The organic siliconresin, S1O2, pigment, talcum powder, SI3N4, curing agent and filler be tiny of -300 purposes
Grain.
The curing agent is aliphatic amine or latent solidification amine curing agent.
The diluent is organosilicon coating diluent.
The levelling agent is silicone oil or end and modified organic silicon in organic silicon type levelling agent.
The antisettling agent is organobentonite or aerosil.
The present invention compared with prior art, has the advantages that：The main function of the coating is protection and decoration
Body surface prolongs the service life, beautifying articles appearance；With strong corrosion proof function, also there is the special work(that anti-sleet knot slips
Energy.Decorate and be not easy to fall dust for outdoor facility body surface simultaneously, service life is far above ten times of general coating or more,
The coating applications are extremely wide, and non-environmental-pollution problem, high temperature resistant is up to 300 DEG C or more and simple production process.
Specific implementation mode
A kind of multifunctional coating is made of the raw material of following parts by weight：50-70 parts of organic siliconresin, diluent 40-60
Part, S1O2For 6-10 parts, 4-6 parts of pigment, 5-7 parts of talcum powder, SI3N4For 5-7 parts, 4-8 parts of curing agent, 7-13 parts of levelling agent,
8-12 parts of antisettling agent, 40-50 parts of filler；Wherein best composition is 60 parts of organic siliconresin, 50 parts of diluent, S1O2For 8 parts,
5 parts of pigment, 6 parts of talcum powder, SI3N4For 6 parts, 5 parts of curing agent, 10 parts of levelling agent, 10 parts of antisettling agent, 47 parts of filler.
The filler is by the schmigel of 19-20 parts by weight, 6-10 parts of refined cement, 5-11 parts of mica powder and 9-12 parts
Flake asbestos mixing composition；Wherein best composition be by the schmigel of 20 parts by weight, 8 parts of refined cement, 9 parts of mica powder and
10 parts of flake asbestos mixing composition.The organic siliconresin, S1O2, pigment, talcum powder, SI3N4, curing agent and filler be-
The fine particle of 300 mesh.The curing agent is aliphatic amine or latent solidification amine curing agent.The diluent is organosilicon
Lacquer diluent.The levelling agent is silicone oil or end and modified organic silicon in organic silicon type levelling agent.The antisettling agent is to have
Machine bentonite or aerosil.
Embodiment one：
By 60 parts of organic siliconresin, 50 parts of organosilicon coating diluent, 8 parts of S1O2, 5 parts pigment, 6 parts of talcum powder, 6
The SI of part3N4For 10 parts of, latent 5 parts of amine curing agent of solidification, end and modified organic silicon, 10 parts of organobentonite, 20 parts by weight
It is that -300 mesh are thin that all solids raw material, which crushes, in schmigel, 8 parts of refined cement, 9 parts of mica powder and 10 parts of flake asbestos
It is mixed and stirred for uniformly obtaining this product after little particle.
Embodiment two：
By 60 parts of organic siliconresin, 50 parts of organosilicon coating diluent, 8 parts of S1O2, 5 parts pigment, 6 parts of talcum powder, 6
The SI of part3N4For, 5 parts of aliphatic amine curing agent, 10 parts of silicone oil, 10 parts of aerosil, the schmigel of 20 parts by weight, 8 parts
Refined cement, all solids raw material crushes to be mixed after -300 mesh fine particles in 9 parts of mica powder and 10 parts of flake asbestos
Merging, which stirs evenly, obtains this product.
Embodiment three：
By 50 parts of organic siliconresin, 40 parts of organosilicon coating diluent, 6 parts of S1O2, 4 parts pigment, 5 parts of talcum powder, 5
The SI of part3N4For 4 parts of, latent 4 parts of amine curing agent of solidification, end and modified organic silicon, 8 parts of organobentonite, 19 parts by weight it is rigid
It is tiny of -300 mesh that all solids raw material, which crushes, in beautiful powder, 6 parts of refined cement, 5 parts of mica powder and 9 parts of flake asbestos
It is mixed and stirred for uniformly obtaining this product after grain.
Example IV：
By 69 parts of organic siliconresin, 58 parts of organosilicon coating diluent, 10 parts of S1O2, 6 parts pigment, 7 parts of talcum powder,
7 parts of SI3N4For, latent 8 parts of amine curing agent of solidification, end and 12 parts of modified organic silicon, 12 parts of organobentonite, 20 parts by weight
Schmigel, 10 parts of refined cement, all solids raw material crushes in 11 parts of mica powder and 12 parts of flake asbestos is -300
It is mixed and stirred for uniformly obtaining this product after mesh fine particle.
A kind of main function of multifunctional coating of the present invention is protection and decorating objects surface, is prolonged the service life, beautiful
Compound is seen in vitro；With strong corrosion proof function, also there is the specific function that anti-sleet knot slips.It is used for outdoor facility object table simultaneously
Dust is decorated and is not easy to fall in face, and service life is far above ten times of general coating or more, and the coating applications are extremely wide, non-environmental-pollution
Problem, high temperature resistant is up to 300 DEG C or more and simple production process.
Claims (7)
1. a kind of multifunctional coating, it is characterised in that：It is made of the raw material of following parts by weight：It is 50-70 parts of organic siliconresin, dilute
Release 40-60 parts of agent, S1O2For 6-10 parts, 4-6 parts of pigment, 5-7 parts of talcum powder, SI3N4For 5-7 parts, 4-8 parts of curing agent, levelling agent
7-13 parts, 8-12 parts of antisettling agent, 40-50 parts of filler；Wherein best composition be 60 parts of organic siliconresin, 50 parts of diluent,
S1O2For 8 parts, 5 parts of pigment, 6 parts of talcum powder, SI3N4For 6 parts, 5 parts of curing agent, 10 parts of levelling agent, 10 parts of antisettling agent, filler
47 parts.
2. a kind of multifunctional coating according to claim 1, it is characterised in that：The filler is rigid by 19-20 parts by weight
Beautiful powder, 6-10 parts of refined cement, 5-11 parts of mica powder and 9-12 parts of flake asbestos mixing composition；Wherein best composition is served as reasons
The schmigel of 20 parts by weight, 8 parts of refined cement, 9 parts of mica powder and 10 parts of flake asbestos mixing composition.
3. a kind of multifunctional coating according to claim 1, it is characterised in that：The organic siliconresin, S1O2, pigment,
Talcum powder, SI3N4, curing agent and filler be -300 mesh fine particle.
4. a kind of multifunctional coating according to claim 2, it is characterised in that：The curing agent is aliphatic amine or dives
Volt solidification amine curing agent.
5. a kind of multifunctional coating according to claim 1, it is characterised in that：The diluent dilutes for organosilicon coating
Agent.
6. a kind of multifunctional coating according to claim 1, it is characterised in that：The levelling agent is organic silicon type levelling agent
In silicone oil or end and modified organic silicon.
7. a kind of multifunctional coating according to claim 1, it is characterised in that：The antisettling agent be organobentonite or
Aerosil.