CN108382030A - 一种透气沙发面料 - Google Patents
一种透气沙发面料 Download PDFInfo
- Publication number
- CN108382030A CN108382030A CN201810256544.2A CN201810256544A CN108382030A CN 108382030 A CN108382030 A CN 108382030A CN 201810256544 A CN201810256544 A CN 201810256544A CN 108382030 A CN108382030 A CN 108382030A
- Authority
- CN
- China
- Prior art keywords
- layer
- moisture absorption
- absorption filled
- base cloth
- filled layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提出了一种透气沙发面料,包括基布层、阻燃层、抗菌层、第一吸湿填充层、第二吸湿填充层和导湿表层,所述基布层由第一经纱和第一纬纱编织而成,所述基布层内均匀排列设置有透气孔,所述基布层的下表面设有阻燃层,所述基布层的上表面依次设有抗菌层、第一吸湿填充层、第二吸湿填充层和导湿表层,所述第一吸湿填充层与第二吸湿填充层之间设有热熔胶层,所述热熔胶层内均匀排布有导流纤维束,所述第二吸湿填充层上纵向均布有条形凸起,所述条形凸起上横向开设有若干个排气孔,所述排气孔横向贯穿第二吸湿填充层和导湿表层,吸湿填充层能够将面料表面的潮湿的汗液水分及时吸除,保证面料表面的干爽,面料具有良好的阻燃性、抗菌性。
Description
【技术领域】
本发明涉及面料的领域,特别是一种透气沙发面料。
【背景技术】
沙发布料是在沙发制造过程中所用到的各种主体覆盖物的统称或者简称,现在的沙发、靠垫等用布制作外层越来越成为一种新潮流。大多数面料采用单一的面料纤维进行编织,功能比较单一,存在透气性、阻燃性差的问题,人们生活水平不断提高,对沙发面料的要求也不断提高,现提出一种透气沙发面料。
【发明内容】
本发明的目的就是解决现有技术中的问题,提出一种透气沙发面料,解决现有技术中沙发装饰面料阻燃性、耐磨性、抗菌性较差的问题。
为实现上述目的,本发明提出了一种透气沙发面料,包括基布层、阻燃层、抗菌层、第一吸湿填充层、第二吸湿填充层和导湿表层,所述基布层由第一经纱和第一纬纱编织而成,所述基布层内均匀排列设置有透气孔,所述基布层的下表面设有阻燃层,所述基布层的上表面依次设有抗菌层、第一吸湿填充层、第二吸湿填充层和导湿表层,所述第一吸湿填充层与第二吸湿填充层之间设有热熔胶层,所述热熔胶层内均匀排布有导流纤维束,所述导流纤维束为超细纤维束,所述抗菌层与第一吸湿填充层之间设有防水透气膜,所述第二吸湿填充层上纵向均布有条形凸起,所述条形凸起上横向开设有若干个排气孔,所述排气孔横向贯穿第二吸湿填充层和导湿表层,所述导湿表层由第三经纱和第三纬纱编织而成,所述第三经纱为超细纤维、玻璃纤维混纺,所述第三纬纱为超细纤维、记忆纤维混纺。
作为优选,第二吸湿填充层和导湿表层之间均匀排布有第一支撑条,所述第一支撑条位于条形凸起的正上方,所述热熔胶层内均匀排布有第二支撑条,所述第一支撑条、第二支撑条均为聚酯防皱条。
作为优选,所述第一支撑条呈纵向排布,所述第二支撑条呈横向排布,所述导流纤维束呈横向排布。
作为优选,所述条形凸起的截面形状近似为等腰梯形,所述条形凸起上横向相邻的排气孔之间呈交错分布。
作为优选,所述阻燃层由第二经纱和第二纬纱相互交织而成,所述第二经纱采用涤纶阻燃纤维,所述第二纬纱采用阻燃氨纶、玻璃纤维混纺纱。
作为优选,所述热熔胶层内均匀分布有活性炭颗粒,所述导流纤维束与第一吸湿填充层、第二吸湿填充层相接触。
作为优选,所述抗菌层由包芯纤维与亚麻纤维编织而成,所述包芯纤维为抗菌纤维缠绕在导电纤维上制成。
作为优选,所述第一经纱为阻燃涤纶长丝,所述第一纬纱为中空涤纶纤维、麦尔登纤维混纺,所述基布层的经向密度为40-60根/厘米,纬向密度为30-40根/厘米。
本发明的有益效果:本发明通过提出一种透气沙发面料,两个吸湿填充层能够将面料表面的潮湿的汗液水分及时吸除,保证面料表面的干爽,两层支撑条具有记忆功能,能够保证面料表面的条形凸起不塌陷,条形凸起之间形成通气槽,增加面料表面积,加快水分蒸发,排气孔能够保证内部空气流通,及时将水分排除,阻燃层使面料具有阻燃的效果,玻璃纤维同时具有能够提高面料的耐磨性和阻燃性的效果,避免出现面料起球现象,抗菌纤维缠绕在导电纤维上的包芯纤维能够抑制面料表面滋生细菌,导电纤维进一步的提高面料的抗静电性,活性炭颗粒能够吸除面料产生的异味。
本发明的特征及优点将通过实施例结合附图进行详细说明。
【附图说明】
图1是本发明一种透气沙发面料第一实施例的截面结构示意图;
图2是本发明一种透气沙发面料第二实施例的截面结构示意图。
【具体实施方式】
参阅图1至图2本发明一种透气沙发面料,包括基布层1、阻燃层2、抗菌层3、第一吸湿填充层4、第二吸湿填充层5和导湿表层6,所述基布层1由第一经纱和第一纬纱编织而成,所述基布层1内均匀排列设置有透气孔,所述基布层1的下表面设有阻燃层2,所述基布层1的上表面依次设有抗菌层3、第一吸湿填充层4、第二吸湿填充层5和导湿表层6,所述第一吸湿填充层4与第二吸湿填充层5之间设有热熔胶层11,所述热熔胶层11内均匀排布有导流纤维束12,所述导流纤维束12为超细纤维束,所述抗菌层3与第一吸湿填充层4之间设有防水透气膜40,所述第二吸湿填充层5上纵向均布有条形凸起51,所述条形凸起51上横向开设有若干个排气孔52,所述排气孔52横向贯穿第二吸湿填充层5和导湿表层6,所述导湿表层6由第三经纱和第三纬纱编织而成,所述第三经纱为超细纤维、玻璃纤维混纺,所述第三纬纱为超细纤维、记忆纤维混纺。第二吸湿填充层5和导湿表层6之间均匀排布有第一支撑条60,所述第一支撑条60位于条形凸起51的正上方,所述热熔胶层11内均匀排布有第二支撑条13,所述第一支撑条60、第二支撑条13均为聚酯防皱条。所述第一支撑条60呈纵向排布,所述第二支撑条13呈横向排布,所述导流纤维束12呈横向排布。所述条形凸起51的截面形状近似为等腰梯形,所述条形凸起51上横向相邻的排气孔52之间呈交错分布。所述阻燃层2由第二经纱和第二纬纱相互交织而成,所述第二经纱采用涤纶阻燃纤维,所述第二纬纱采用阻燃氨纶、玻璃纤维混纺纱。所述热熔胶层11内均匀分布有活性炭颗粒,所述导流纤维束12与第一吸湿填充层4、第二吸湿填充层5相接触。所述抗菌层3由包芯纤维与亚麻纤维编织而成,所述包芯纤维为抗菌纤维缠绕在导电纤维上制成。所述第一经纱为阻燃涤纶长丝,所述第一纬纱为中空涤纶纤维、麦尔登纤维混纺,所述基布层1的经向密度为40-60根/厘米,纬向密度为30-40根/厘米。
本发明工作过程:
本发明一种透气沙发面料,两个吸湿填充层能够将面料表面的潮湿的汗液水分及时吸除,保证面料表面的干爽,两层支撑条具有记忆功能,能够保证面料表面的条形凸起不塌陷,条形凸起之间形成通气槽,增加面料表面积,加快水分蒸发,排气孔能够保证内部空气流通,及时将水分排除,阻燃层使面料具有阻燃的效果,玻璃纤维同时具有能够提高面料的耐磨性和阻燃性的效果,避免出现面料起球现象,抗菌纤维缠绕在导电纤维上的包芯纤维能够抑制面料表面滋生细菌,导电纤维进一步的提高面料的抗静电性,活性炭颗粒能够吸除面料产生的异味。
上述实施例是对本发明的说明,不是对本发明的限定,任何对本发明简单变换后的方案均属于本发明的保护范围。
Claims (8)
1.一种透气沙发面料,其特征在于:包括基布层(1)、阻燃层(2)、抗菌层(3)、第一吸湿填充层(4)、第二吸湿填充层(5)和导湿表层(6),所述基布层(1)由第一经纱和第一纬纱编织而成,所述基布层(1)内均匀排列设置有透气孔,所述基布层(1)的下表面设有阻燃层(2),所述基布层(1)的上表面依次设有抗菌层(3)、第一吸湿填充层(4)、第二吸湿填充层(5)和导湿表层(6),所述第一吸湿填充层(4)与第二吸湿填充层(5)之间设有热熔胶层(11),所述热熔胶层(11)内均匀排布有导流纤维束(12),所述导流纤维束(12)为超细纤维束,所述抗菌层(3)与第一吸湿填充层(4)之间设有防水透气膜(40),所述第二吸湿填充层(5)上纵向均布有条形凸起(51),所述条形凸起(51)上横向开设有若干个排气孔(52),所述排气孔(52)横向贯穿第二吸湿填充层(5)和导湿表层(6),所述导湿表层(6)由第三经纱和第三纬纱编织而成,所述第三经纱为超细纤维、玻璃纤维混纺,所述第三纬纱为超细纤维、记忆纤维混纺。
2.如权利要求1所述的一种透气沙发面料,其特征在于:第二吸湿填充层(5)和导湿表层(6)之间均匀排布有第一支撑条(60),所述第一支撑条(60)位于条形凸起(51)的正上方,所述热熔胶层(11)内均匀排布有第二支撑条(13),所述第一支撑条(60)、第二支撑条(13)均为聚酯防皱条。
3.如权利要求2所述的一种透气沙发面料,其特征在于:所述第一支撑条(60)呈纵向排布,所述第二支撑条(13)呈横向排布,所述导流纤维束(12)呈横向排布。
4.如权利要求1所述的一种透气沙发面料,其特征在于:所述条形凸起(51)的截面形状近似为等腰梯形,所述条形凸起(51)上横向相邻的排气孔(52)之间呈交错分布。
5.如权利要求1所述的一种透气沙发面料,其特征在于:所述阻燃层(2)由第二经纱和第二纬纱相互交织而成,所述第二经纱采用涤纶阻燃纤维,所述第二纬纱采用阻燃氨纶、玻璃纤维混纺纱。
6.如权利要求1所述的一种透气沙发面料,其特征在于:所述热熔胶层(11)内均匀分布有活性炭颗粒,所述导流纤维束(12)与第一吸湿填充层(4)、第二吸湿填充层(5)相接触。
7.如权利要求1所述的一种透气沙发面料,其特征在于:所述抗菌层(3)由包芯纤维与亚麻纤维编织而成,所述包芯纤维为抗菌纤维缠绕在导电纤维上制成。
8.如权利要求1所述的一种透气沙发面料,其特征在于:所述第一经纱为阻燃涤纶长丝,所述第一纬纱为中空涤纶纤维、麦尔登纤维混纺,所述基布层(1)的经向密度为40-60根/厘米,纬向密度为30-40根/厘米。