CN108373718A - A kind of fire-retardant coating composition - Google Patents
A kind of fire-retardant coating composition Download PDFInfo
- Publication number
- CN108373718A CN108373718A CN201610989955.3A CN201610989955A CN108373718A CN 108373718 A CN108373718 A CN 108373718A CN 201610989955 A CN201610989955 A CN 201610989955A CN 108373718 A CN108373718 A CN 108373718A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire
- retardant coating
- coating composition
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fire-retardant coating compositions, are made of the raw material of following mass fraction：11 13 parts of silicate glass, 12 14 parts of expanded perlite, 68 parts of titanate coupling agent, 7 11 parts of chlorinated paraffin, 56 parts of titanium dioxide, 30 42 parts of acrylic ester elastic emulsion, 34 parts of sodium metasilicate, 15 17 parts of isobutyl ketone, 20 23 parts of epoxy resin, 11 14 parts of antimony oxide, 20 24 parts of water.The feature of environmental protection of the present invention is good, not will produce toxic gas during fire-retardant, and thermal insulation is good, and fire resistance property is strong, increases the fire prevention time, and the attachment period is long, not easily to fall off.
Description
Technical field
The present invention relates to fireproof material technology field more particularly to a kind of fire-retardant coating compositions.
Background technology
Fireproof coating is to be used for flammable substrates surface, can reduce by the combustibility of painting material surface, block the fast of fire
Speed sprawling, to improve by a kind of sapecial coating of painting material fire endurance, is applied to flammable substrates surface, to change
Material surface combustion characteristics, retardance fire are spread rapidly；Or be applied on building element, to improve the fire endurance of component,
Slow down propagation of flame spread speed, or can prevent to burn within a certain period of time.Mostly there is melamine in existing fire proofing material
Etc. harmful substances, when a fire, the heat of generation decomposes noxious material, pollutes, and the time of preventing fires is shorter, thermal insulation
It is poor, it is easy to fall off.
Invention content
Above-mentioned to solve the problems, such as, a kind of feature of environmental protection of present invention offer is good, and thermal insulation is good, and fire resistance property is strong, attachment
The fire-retardant coating composition of period length.
The present invention solve the technical solution that uses of above-mentioned technical problem for：A kind of fire-retardant coating composition, by following quality
The raw material of number is made：
11-13 parts of silicate glass, 12-14 parts of expanded perlite, 6-8 parts of titanate coupling agent, 7-11 parts of chlorinated paraffin, titanium white
5-6 parts of powder, 30-42 parts of acrylic ester elastic emulsion, 3-4 parts of sodium metasilicate, 15-17 parts of isobutyl ketone, 20-23 parts of epoxy resin, three
Aoxidize 11-14 parts of two antimony, 20-24 parts of water.
Further, above-mentioned fire-retardant coating composition is made of the raw material of following mass fraction：
12 parts of silicate glass, 13 parts of expanded perlite, 7 parts of titanate coupling agent, 9 parts of chlorinated paraffin, 5.6 parts of titanium dioxide, third
36 parts of olefin(e) acid ester elastomer lotion, 3.4 parts of sodium metasilicate, 16 parts of isobutyl ketone, 21 parts of epoxy resin, 12 parts of antimony oxide, 22 parts of water.
The present invention solves advantageous effect caused by technical problem and is：The feature of environmental protection of the present invention is good, will not during fire-retardant
Toxic gas is generated, thermal insulation is good, and fire resistance property is strong, increases the fire prevention time, and the attachment period is long, not easily to fall off.
Specific implementation mode
The present invention is described in further details with reference to specific embodiment.
Embodiment 1
A kind of fire-retardant coating composition is made of the raw material of following mass fraction：
11 parts of silicate glass, 12 parts of expanded perlite, 6 parts of titanate coupling agent, 7 parts of chlorinated paraffin, 5 parts of titanium dioxide, propylene
30 parts of acid esters elastic emulsion, 3 parts of sodium metasilicate, 15 parts of isobutyl ketone, 20 parts of epoxy resin, 11 parts of antimony oxide, 20 parts of water.
Embodiment 2
A kind of fire-retardant coating composition is made of the raw material of following mass fraction：
12 parts of silicate glass, 13 parts of expanded perlite, 7 parts of titanate coupling agent, 9 parts of chlorinated paraffin, 5.6 parts of titanium dioxide, third
36 parts of olefin(e) acid ester elastomer lotion, 3.4 parts of sodium metasilicate, 16 parts of isobutyl ketone, 21 parts of epoxy resin, 12 parts of antimony oxide, 22 parts of water.
Embodiment 3
A kind of fire-retardant coating composition is made of the raw material of following mass fraction：
13 parts of silicate glass, 14 parts of expanded perlite, 8 parts of titanate coupling agent, 11 parts of chlorinated paraffin, 6 parts of titanium dioxide, propylene
42 parts of acid esters elastic emulsion, 4 parts of sodium metasilicate, 17 parts of isobutyl ketone, 23 parts of epoxy resin, 14 parts of antimony oxide, 24 parts of water.
Although the above-mentioned specific implementation mode to the present invention is described, not to the limit of the scope of the present invention
System, those skilled in the art should understand that, based on the technical solutions of the present invention, those skilled in the art need not pay
Go out various modifications or changes that creative work can be made still within protection scope of the present invention.
Claims (2)
1. a kind of fire-retardant coating composition, it is characterised in that：It is made of the raw material of following mass fraction：
11-13 parts of silicate glass, 12-14 parts of expanded perlite, 6-8 parts of titanate coupling agent, 7-11 parts of chlorinated paraffin, titanium white
5-6 parts of powder, 30-42 parts of acrylic ester elastic emulsion, 3-4 parts of sodium metasilicate, 15-17 parts of isobutyl ketone, 20-23 parts of epoxy resin, three
Aoxidize 11-14 parts of two antimony, 20-24 parts of water.
2. fire-retardant coating composition according to claim 1, it is characterised in that：It is made of the raw material of following mass fraction：
12 parts of silicate glass, 13 parts of expanded perlite, 7 parts of titanate coupling agent, 9 parts of chlorinated paraffin, 5.6 parts of titanium dioxide, third
36 parts of olefin(e) acid ester elastomer lotion, 3.4 parts of sodium metasilicate, 16 parts of isobutyl ketone, 21 parts of epoxy resin, 12 parts of antimony oxide, 22 parts of water.