CN107022212A - High ferro fastener equipment fire-retardant fireproof anticorrosive paint - Google Patents
High ferro fastener equipment fire-retardant fireproof anticorrosive paint Download PDFInfo
- Publication number
- CN107022212A CN107022212A CN201710082125.7A CN201710082125A CN107022212A CN 107022212 A CN107022212 A CN 107022212A CN 201710082125 A CN201710082125 A CN 201710082125A CN 107022212 A CN107022212 A CN 107022212A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- fire
- anticorrosive paint
- retardant fireproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high ferro fastener equipment fire-retardant fireproof anticorrosive paint, it is made up of following component:Polyvinyl alcohol resin, acrylic resin, fluorine silicon resin, zinc powder, tung oil, n-butanol, hydroxy-ethyl acrylate, DPG, diethylene glycol (DEG), N-phenylsalicylamide, tetraethyl orthosilicate, antimony oxide, carborundum, calcium aluminate, sodium Diacetate, copper powder, manganese oxide, aluminium chloride, methylcellulose, magnesium stearate, the double great proficiency resin acid phthalein amine of ethylene, diatomite, aerosil, barium sulfate.The fire-retardant fireproof anticorrosive paint of the present invention has stability high, and impact-resistant abrasion-proof, hardness high adhesion force are good, flame resistant is not fallen off, high temperature resistant, anti-corrosion are anti-oxidation, can be used in long-term fire resisting environment.
Description
Technical field
The invention belongs to technical field of coatings, a kind of high ferro fastener equipment with fire retardant, anticorrosive performance is related in particular to
Use coating.
Background technology
Anti-flaming dope is brushed on protected object surface(Such as steel construction)Fireproofing passiveness material, by thickness be divided into thicker,
Slim and ultrathin and facing type.Fireproof coating is exactly that protected object has the limiting value for bearing big fire test, and fire prevention is applied
Material is to play a part of isolation in protected object body surface face, delays the time of building collapse, to succour and fire extinguishing wins preciousness
Time.
Fire-retardant fireproof anti-corrosion, which is applied, to be needed, with long-term heatproof, flame resistant, not falling off, anti-oxidation with high temperature resistant and anti-corrosion
Effect, can be used in long-term fire resisting environment.In face of high-temp combustion flame, high-temperature anticorrosion paint is also wanted can be in high temperature corrosion ring
In border, flame impingement under oxygen, the corrosion of sulphur and high temperature under resistance high temperature, current fire-retardant fireproof anticorrosive paint cannot concurrently reach
The effect above.
The content of the invention
The purpose of the present invention is that there is provided a kind of coating with fire retardant, anticorrosive performance on the basis of existing technology.
It is a further object of the present invention to provide a kind of preparation method of above-mentioned coating.
The purpose of the present invention can be reached by following measures:
A kind of high ferro fastener equipment fire-retardant fireproof anticorrosive paint, it is made up of the component of following mass parts:Polyvinyl alcohol resin
20~30 parts, 20~30 parts of acrylic resin, 25~35 parts of fluorine silicon resin, 15~20 parts of zinc powder, 45~60 parts of tung oil, n-butanol
15~20 parts, 15~20 parts of hydroxy-ethyl acrylate, 18~22 parts of DPG, 10~15 parts of diethylene glycol (DEG), N-phenylsalicylamide 10~
15 parts, 5~10 parts of tetraethyl orthosilicate, 5~10 parts of antimony oxide, 5~10 parts of carborundum, 10~20 parts of calcium aluminate, diacetic acid
5~10 parts of sodium, 5~10 parts of copper powder, 7~15 parts of manganese oxide, 8~12 parts of aluminium chloride, 5~10 parts of methylcellulose, magnesium stearate
10~20 parts, double 5~10 parts of the great proficiency resin acid phthalein amine of ethylene, 5~10 parts of diatomite, 5~10 parts of aerosil, barium sulfate
5~10 parts.
In a kind of scheme, fire-retardant fireproof anticorrosive paint of the invention can be made up of the component of following mass parts:Polyethylene
21~28 parts of alcohol resin, 21~28 parts of acrylic resin, 26~33 parts of fluorine silicon resin, 15~20 parts of zinc powder, 45~55 parts of tung oil,
15~20 parts of n-butanol, 17~20 parts of hydroxy-ethyl acrylate, 18~22 parts of DPG, 10~15 parts of diethylene glycol (DEG), salicylic acid benzene
12~15 parts of amine, 5~10 parts of tetraethyl orthosilicate, 5~10 parts of antimony oxide, 5~10 parts of carborundum, 10~17 parts of calcium aluminate,
5~10 parts of sodium Diacetate, 5~10 parts of copper powder, 7~10 parts of manganese oxide, 8~12 parts of aluminium chloride, 5~10 parts of methylcellulose, firmly
10~18 parts of fatty acid magnesium, double 5~10 parts of the great proficiency resin acid phthalein amine of ethylene, 5~10 parts of diatomite, 5~8 parts of aerosil,
5~8 parts of barium sulfate.
In another scheme, fire-retardant fireproof anticorrosive paint of the invention can be made up of the component of following mass parts:Poly- second
21~28 parts of enol resin, 22~26 parts of acrylic resin, 26~32 parts of fluorine silicon resin, 15~20 parts of zinc powder, tung oil 50~55
Part, 15~20 parts of n-butanol, 17~20 parts of hydroxy-ethyl acrylate, 18~22 parts of DPG, 10~15 parts of diethylene glycol (DEG), salicylic acid
12~15 parts of aniline, 5~10 parts of tetraethyl orthosilicate, 5~10 parts of antimony oxide, 5~10 parts of carborundum, calcium aluminate 10~17
Part, 5~10 parts of sodium Diacetate, 5~10 parts of copper powder, 7~10 parts of manganese oxide, 8~12 parts of aluminium chloride, 5~10 parts of methylcellulose,
10~18 parts of magnesium stearate, double 5~10 parts of the great proficiency resin acid phthalein amine of ethylene, 5~10 parts of diatomite, aerosil 5~8
Part, 5~8 parts of barium sulfate.
In a kind of preferred scheme, fire-retardant fireproof anticorrosive paint of the invention can be made up of the component of following mass parts:It is poly-
25 parts of vinyl alcohol resin, 24 parts of acrylic resin, 30 parts of fluorine silicon resin, 17 parts of zinc powder, 53 parts of tung oil, 17 parts of n-butanol, propylene
Sour 18 parts of hydroxyl ethyl ester, 20 parts of DPG, 13 parts of diethylene glycol (DEG), 14 parts of N-phenylsalicylamide, 7 parts of tetraethyl orthosilicate, antimony oxide 6
Part, 8 parts of carborundum, 13 parts of calcium aluminate, 7 parts of sodium Diacetate, 7 parts of copper powder, 8 parts of manganese oxide, 10 parts of aluminium chloride, methylcellulose 7
Part, 15 parts of magnesium stearate, double 6 parts of the great proficiency resin acid phthalein amine of ethylene, 7 parts of diatomite, 7 parts of aerosil, 6 parts of barium sulfate.
A kind of preparation method of fire-retardant fireproof anticorrosive paint of the invention, it comprises the following steps:
(A)By polyvinyl alcohol resin, acrylic resin, fluorine silicon resin, zinc powder, tung oil, n-butanol, hydroxy-ethyl acrylate, three oxygen
Disperse at a high speed after changing two antimony, carborundum, calcium aluminate, sodium Diacetate, copper powder, manganese oxide and aluminium chloride mixing, then carried out with ultrasound
It is scattered;
(B)Continuously add the double great proficiency resin acid phthalein amine of methylcellulose, magnesium stearate, ethylene, diatomite, aerosil and
Disperse at a high speed after barium sulfate mixing, be then ground to fineness≤40 μm of slurry;
(C)DPG, diethylene glycol (DEG), N-phenylsalicylamide and tetraethyl orthosilicate are added, is uniformly dispersed at a high speed, is produced.
In step(A)In, scattered speed can be 3000~4000r/min at a high speed, and the frequency of ultrasonic disperse can be
20~40KHz, the time of scattered or ultrasonic disperse is 10~50min at a high speed.
In step(B)In, preferably it is ground to fineness≤30 μm of slurry.
Pass through the mutually coordinated effect of multiple components in the fire-retardant fireproof anticorrosive paint of the present invention so that coating has stable
Property it is high, impact-resistant abrasion-proof, hardness high adhesion force are good, flame resistant is not fallen off, high temperature resistant, anti-corrosion are anti-oxidation, can be in long-term fire resisting
Used in environment.
Embodiment
Present disclosure is described further with reference to embodiments.But protection scope of the present invention is not limited to following
Each embodiment.
Embodiment 1
Constituent mass part is constituted:25 parts of polyvinyl alcohol resin, 24 parts of acrylic resin, 30 parts of fluorine silicon resin, 17 parts of zinc powder, paulownia
53 parts of oil, 17 parts of n-butanol, 18 parts of hydroxy-ethyl acrylate, 20 parts of DPG, 13 parts of diethylene glycol (DEG), 14 parts of N-phenylsalicylamide, just
7 parts of silester, 6 parts of antimony oxide, 8 parts of carborundum, 13 parts of calcium aluminate, 7 parts of sodium Diacetate, 7 parts of copper powder, 8 parts of manganese oxide,
10 parts of aluminium chloride, 7 parts of methylcellulose, 15 parts of magnesium stearate, double 6 parts of the great proficiency resin acid phthalein amine of ethylene, 7 parts of diatomite, gas phase
7 parts of silica, 6 parts of barium sulfate.
Preparation method is:By polyvinyl alcohol resin, acrylic resin, fluorine silicon resin, zinc powder, tung oil, n-butanol, acrylic acid
Hydroxyl ethyl ester, antimony oxide, carborundum, calcium aluminate, sodium Diacetate, copper powder, manganese oxide and aluminium chloride mixing after 3000~
4000r/min scattered 30 min, then scattered 30 min are carried out with 20~40KHz ultrasounds at a high speed;Continuously add methylcellulose, it is hard
Disperse at a high speed after the double great proficiency resin acid phthalein amine of fatty acid magnesium, ethylene, diatomite, aerosil and barium sulfate mixing, Ran Houjin
Row is ground to fineness≤30 μm of slurry;DPG, diethylene glycol (DEG), N-phenylsalicylamide and tetraethyl orthosilicate are added, is divided at a high speed
Dissipate uniform, produce.
Embodiment 2
Constituent mass part is constituted:27 parts of polyvinyl alcohol resin, 25 parts of acrylic resin, 29 parts of fluorine silicon resin, 18 parts of zinc powder, paulownia
50 parts of oil, 19 parts of n-butanol, 18 parts of hydroxy-ethyl acrylate, 21 parts of DPG, 17 parts of diethylene glycol (DEG), 12 parts of N-phenylsalicylamide, just
6 parts of silester, 7 parts of antimony oxide, 8 parts of carborundum, 13 parts of calcium aluminate, 7 parts of sodium Diacetate, 8 parts of copper powder, 9 parts of manganese oxide,
9 parts of aluminium chloride, 8 parts of methylcellulose, 13 parts of magnesium stearate, double 8 parts of the great proficiency resin acid phthalein amine of ethylene, 9 parts of diatomite, gas phase two
5 parts of silica, 5 parts of barium sulfate.Preparation method be the same as Example 1.
Embodiment 3
Constituent mass part is constituted:29 parts of polyvinyl alcohol resin, 24 parts of acrylic resin, 32 parts of fluorine silicon resin, 16 parts of zinc powder, paulownia
52 parts of oil, 17 parts of n-butanol, 18 parts of hydroxy-ethyl acrylate, 20 parts of DPG, 13 parts of diethylene glycol (DEG), 14 parts of N-phenylsalicylamide, just
7 parts of silester, 6 parts of antimony oxide, 8 parts of carborundum, 13 parts of calcium aluminate, 7 parts of sodium Diacetate, 7 parts of copper powder, 8 parts of manganese oxide,
10 parts of aluminium chloride, 7 parts of methylcellulose, 15 parts of magnesium stearate, double 6 parts of the great proficiency resin acid phthalein amine of ethylene, 7 parts of diatomite, gas phase
7 parts of silica, 6 parts of barium sulfate.Preparation method be the same as Example 1.
Comparative example 1
In addition to polyvinyl alcohol resin is not used, other be the same as Examples 1.
Comparative example 2
In addition to acrylic resin is not used, other be the same as Examples 1.
Comparative example 3
In addition to fluorine silicon resin is not used, other be the same as Examples 1.
Embodiment 4
Performance test is carried out to various embodiments above and comparative example, it is as a result as follows:
Technological project | Embodiment 1 | Embodiment 2 | Embodiment 2 | Detection method |
Fineness(μm) | ≤30 | ≤30 | ≤30 | GB1724-89 |
Adhesive force(Scratch) | One-level | One-level | One-level | GB1720-89 |
Surface drying time(min) | ≤3 | ≤3 | ≤3 | GB1728 |
Do solid work the time(h) | ≤22 | ≤22 | ≤22 | GB1728 |
Thickness of dry film(μm) | ≥40 | ≥40 | ≥40 | GB1764-89 |
Pencil hardness | 8H | 7H | 7 H | GB/T6739 |
Impact resistance(kg/cm) | 91 | 90 | 89 | GB/T1732-93 |
Fire protection flame retarding rank | V-1 | V-1 | V-2 | UL94 |
Moisture-proof rate of corrosion(%) | 7.4 | 7.3 | 7.3 | The environment of humidity 50% |
Acid corrosion-resistant rate(%) | 7.8 | 7.7 | 8.0 | The sour environment of pH value 3.5 |
Alkali corrosion resistance rate(%) | 8.0 | 8.2 | 8.1 | The alkaline environment of pH value 85 |
Storage stability | Without caking | Without caking | Without caking | Range estimation, 30 DEG C of 10d |
Comparative example 1-3 is in addition to fineness and thickness of dry film, and other all technicals are below embodiment 1, particularly pencil hardness
In below 5H, impact resistance is less than V-3 in 60 below kg/cm, fire protection flame retarding rank, and moisture-proof, bronsted lowry acids and bases bronsted lowry rate of corrosion are all higher than
20%, there is caking in storage stability test.
Claims (7)
1. a kind of high ferro fastener equipment fire-retardant fireproof anticorrosive paint, it is characterised in that it is made up of the component of following mass parts:
20~30 parts of polyvinyl alcohol resin, 20~30 parts of acrylic resin, 25~35 parts of fluorine silicon resin, 15~20 parts of zinc powder, tung oil 45
~60 parts, 15~20 parts of n-butanol, 15~20 parts of hydroxy-ethyl acrylate, 18~22 parts of DPG, 10~15 parts of diethylene glycol (DEG), water
Poplar 10~15 parts of aniline of acid, 5~10 parts of tetraethyl orthosilicate, 5~10 parts of antimony oxide, 5~10 parts of carborundum, calcium aluminate 10~
20 parts, 5~10 parts of sodium Diacetate, 5~10 parts of copper powder, 7~15 parts of manganese oxide, 8~12 parts of aluminium chloride, methylcellulose 5~10
Part, 10~20 parts of magnesium stearate, double 5~10 parts of the great proficiency resin acid phthalein amine of ethylene, 5~10 parts of diatomite, aerosil 5~
10 parts, 5~10 parts of barium sulfate.
2. fire-retardant fireproof anticorrosive paint according to claim 1, it is characterised in that it is made up of the component of following mass parts:
21~28 parts of polyvinyl alcohol resin, 21~28 parts of acrylic resin, 26~33 parts of fluorine silicon resin, 15~20 parts of zinc powder, tung oil 45
~55 parts, 15~20 parts of n-butanol, 17~20 parts of hydroxy-ethyl acrylate, 18~22 parts of DPG, 10~15 parts of diethylene glycol (DEG), water
Poplar 12~15 parts of aniline of acid, 5~10 parts of tetraethyl orthosilicate, 5~10 parts of antimony oxide, 5~10 parts of carborundum, calcium aluminate 10~
17 parts, 5~10 parts of sodium Diacetate, 5~10 parts of copper powder, 7~10 parts of manganese oxide, 8~12 parts of aluminium chloride, methylcellulose 5~10
Part, 10~18 parts of magnesium stearate, double 5~10 parts of the great proficiency resin acid phthalein amine of ethylene, 5~10 parts of diatomite, aerosil 5~
8 parts, 5~8 parts of barium sulfate.
3. fire-retardant fireproof anticorrosive paint according to claim 2, it is characterised in that it is made up of the component of following mass parts:
21~28 parts of polyvinyl alcohol resin, 22~26 parts of acrylic resin, 26~32 parts of fluorine silicon resin, 15~20 parts of zinc powder, tung oil 50
~55 parts, 15~20 parts of n-butanol, 17~20 parts of hydroxy-ethyl acrylate, 18~22 parts of DPG, 10~15 parts of diethylene glycol (DEG), water
Poplar 12~15 parts of aniline of acid, 5~10 parts of tetraethyl orthosilicate, 5~10 parts of antimony oxide, 5~10 parts of carborundum, calcium aluminate 10~
17 parts, 5~10 parts of sodium Diacetate, 5~10 parts of copper powder, 7~10 parts of manganese oxide, 8~12 parts of aluminium chloride, methylcellulose 5~10
Part, 10~18 parts of magnesium stearate, double 5~10 parts of the great proficiency resin acid phthalein amine of ethylene, 5~10 parts of diatomite, aerosil 5~
8 parts, 5~8 parts of barium sulfate.
4. fire-retardant fireproof anticorrosive paint according to claim 3, it is characterised in that it is made up of the component of following mass parts:
25 parts of polyvinyl alcohol resin, 24 parts of acrylic resin, 30 parts of fluorine silicon resin, 17 parts of zinc powder, 53 parts of tung oil, 17 parts of n-butanol, third
18 parts of olefin(e) acid hydroxyl ethyl ester, 20 parts of DPG, 13 parts of diethylene glycol (DEG), 14 parts of N-phenylsalicylamide, 7 parts of tetraethyl orthosilicate, three oxidations two
6 parts of antimony, 8 parts of carborundum, 13 parts of calcium aluminate, 7 parts of sodium Diacetate, 7 parts of copper powder, 8 parts of manganese oxide, 10 parts of aluminium chloride, Methyl cellulose
7 parts of element, 15 parts of magnesium stearate, double 6 parts of the great proficiency resin acid phthalein amine of ethylene, 7 parts of diatomite, 7 parts of aerosil, barium sulfate 6
Part.
5. a kind of preparation method of fire-retardant fireproof anticorrosive paint according to any one in Claims 1 to 4, its feature exists
In comprising the following steps:
(A)By polyvinyl alcohol resin, acrylic resin, fluorine silicon resin, zinc powder, tung oil, n-butanol, hydroxy-ethyl acrylate, three oxygen
Disperse at a high speed after changing two antimony, carborundum, calcium aluminate, sodium Diacetate, copper powder, manganese oxide and aluminium chloride mixing, then carried out with ultrasound
It is scattered;
(B)Continuously add the double great proficiency resin acid phthalein amine of methylcellulose, magnesium stearate, ethylene, diatomite, aerosil and
Disperse at a high speed after barium sulfate mixing, be then ground to fineness≤40 μm of slurry;
(C)DPG, diethylene glycol (DEG), N-phenylsalicylamide and tetraethyl orthosilicate are added, is uniformly dispersed at a high speed, is produced.
6. method according to claim 5, it is characterised in that step(A)In, the scattered speed of the high speed for 3000~
4000r/min, the frequency of ultrasonic disperse is 20~40KHz, and the time of scattered or ultrasonic disperse is 10~50min at a high speed.
7. method according to claim 5, it is characterised in that step(B)In, it is ground to fineness≤30 μm of slurry.