CN108294380B - 一种组装式过滤口罩 - Google Patents

一种组装式过滤口罩 Download PDF

Info

Publication number
CN108294380B
CN108294380B CN201810110625.1A CN201810110625A CN108294380B CN 108294380 B CN108294380 B CN 108294380B CN 201810110625 A CN201810110625 A CN 201810110625A CN 108294380 B CN108294380 B CN 108294380B
Authority
CN
China
Prior art keywords
mask
solution
added
under
mentioned steps
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201810110625.1A
Other languages
English (en)
Other versions
CN108294380A (zh
Inventor
魏成江
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hainan Yishang health protection products Co., Ltd
Original Assignee
Quanzhou Taishang Investment Zone Tiantai Industrial Design Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Quanzhou Taishang Investment Zone Tiantai Industrial Design Co Ltd filed Critical Quanzhou Taishang Investment Zone Tiantai Industrial Design Co Ltd
Priority to CN201810110625.1A priority Critical patent/CN108294380B/zh
Publication of CN108294380A publication Critical patent/CN108294380A/zh
Application granted granted Critical
Publication of CN108294380B publication Critical patent/CN108294380B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本分案申请公开了一种组装式过滤口罩，包括主口罩、固定带和主口罩两侧的副口罩，所述的主口罩两侧具有固定耳，所述的副口罩，一侧具有固定耳，另一侧具有弹性卡脚，所述的弹性卡脚能够与主口罩的固定耳固定连接，所述的主口罩包括主体框架，主体框架内部安装有空气净化滤料。

Description

一种组装式过滤口罩
本分案申请的原申请号为2016109252276 ，申请日为2016年10月30日，发明名称为“可组装式过滤口罩”。
技术领域
本发明涉及一种口罩，具体是一种组装式过滤口罩。
背景技术
近几年雾霾天气越来越严重，pm2.5严重超标，装修后的场所其甲醛含量也经常超标，给人们的健康带来了极大的威胁，目前的口罩还没有可组装式的结构。
发明内容
针对上述现有技术存在的问题，本发明提供一种组装式过滤口罩，能够组装搭配，并且过滤甲醛效果好，更换方便。
为了实现上述目的，本发明采用的技术方案是：一种组装式过滤口罩，包括主口罩、固定带和主口罩两侧的副口罩，所述的主口罩两侧具有固定耳，所述的副口罩，一侧具有固定耳，另一侧具有弹性卡脚，所述的弹性卡脚能够与主口罩的固定耳固定连接，所述的主口罩包括主体框架，主体框架内部安装有空气净化滤料。
所述的副口罩也具有主体框架，主体框架内部安装有空气净化滤料。
所述的主口罩的主体框架为弹性材料制备。
本发明的口罩具有主口罩、固定带和主口罩两侧的副口罩，所述的主口罩两侧具有固定耳，所述的副口罩，一侧具有固定耳，另一侧具有弹性卡脚，组装方便，而且两个副口罩可以拼装成一个口罩当做备用口罩，并且主口罩和副口罩均安装有空气滤料，空气净化效果好。
附图说明
图1是本发明的示意图。
图2是本发明的滤料。
1、主口罩，2、副口罩，3、固定带，4、滤料。
具体实施方式
下面结合附图1-2和实施例对本发明作进一步说明。
一种组装式过滤口罩，包括主口罩1、固定带3和主口罩两侧的副口罩2，所述的主口罩两侧具有固定耳，所述的副口罩，一侧具有固定耳，另一侧具有弹性卡脚，所述的弹性卡脚能够与主口罩的固定耳固定连接，所述的主口罩包括主体框架，主体框架内部安装有空气净化滤料。
如图2，滤料装载包装袋上，包装袋两侧具有均匀的通孔。
所述的副口罩也具有主体框架，主体框架内部安装有空气净化滤料。
所述的主口罩的主体框架为弹性材料制备。
本发明的口罩具有主口罩、固定带和主口罩两侧的副口罩，所述的主口罩两侧具有固定耳，所述的副口罩，一侧具有固定耳，另一侧具有弹性卡脚，组装方便，而且两个副口罩可以拼装成一个口罩当做备用口罩，并且主口罩和副口罩均安装有空气滤料，空气净化效果好。
所述的空气滤料为改性纳米滤料，用于吸附甲醛，改性纳米滤料具体制备方法如下：
实施例1
制备氯化胆碱、十六烷基三甲基溴化铵这两种有机模板剂摩尔比1:3的样。
0.02mol氯化胆碱、0.06mol十六烷基三甲基溴化铵,5ml硅溶胶，0.06mol偏铝酸钠，2mol/L12ml的氢氧化钠溶液，24ml98%硫酸，0.01mol二氧化硅粉，0.001mol硝酸镨，0.001mol硝酸铈，300ml去离子水。
步骤1、首先将NaAlO2，NaOH，去离子水在氖气氛围下超声波震荡3h;
步骤2、将0.06molNaAlO2，2mol/L12mlNaOH溶液在磁力搅拌下90℃油浴加热完全溶解于200ml去离子水中形成铝酸钠透明液；
步骤3、将硅溶胶，硫酸先在氖气氛围下超声波震荡3h，然后将5ml硅溶胶以每分钟40滴的速度滴加到铝酸钠透明液中磁力搅拌90℃油浴加热2h，然后将10ml98%硫酸以每分钟15滴的速度滴加到上述溶液里磁力搅拌油浴加热2h制成凝胶液；
步骤4、将0.02mol氯化胆碱、0.06mol十六烷基三甲基溴化铵有机模板剂在氩气氛围下超声波震荡3h，然后加入到上述溶液里；分4次加入，每次加入四分之一，每次加入后在磁力搅拌油浴加热90℃2h；
步骤5、将上述溶液通过引流器倒入聚四氟乙烯为内衬的反应釜中，然后将反应釜放入到微波反应器中以15kap/min的速度升压到250kpa,温度以25℃/min的速度升至180℃，在氦气氛围下晶化48h；
步骤6、然后将0.01mol二氧化硅粉末加入到上述晶化液中磁力搅拌油浴加热90℃6h;
步骤7、然后用98%硫酸调节上述溶液ph值成弱酸性（ph值大约为6-7）；
步骤8、将0.001mol硝酸镨，0.001mol硝酸铈先经过20%Ar+50%CO2+30%CO氛围下超声波震荡3h，然后分别滴加到上述溶液里边滴加边磁力搅拌油浴加热90℃2h;
步骤9、将上述溶液通过引流器倒入聚四氟乙烯为内衬的反应釜中,然后将反应釜放入到微波反应器中以20kap/min的速度升压到550kpa,温度以25℃/min的速度升至450℃，在30%Ar+70%CO2氛围下晶化12h;
步骤10、然后在真空泵下过滤，在真空旋转蒸发器下除去水分，鼓风干燥箱110℃干燥，得到纳米级晶体Pr,Ce-Y/Beta改性滤料。
实施例2制备氯化胆碱、十六烷基三甲基溴化铵这两种有机模板剂摩尔比1:1，即0.02mol氯化胆碱、0.02mol十六烷基三甲基溴化铵，其余原料与实施例1相同，制备方法业与实施例1相同。
实施例3制备氯化胆碱、十六烷基三甲基溴化铵这两种有机模板剂摩尔比1:2，即0.02mol氯化胆碱、0.04mol十六烷基三甲基溴化铵，其余原料与实施例1相同，制备方法业与实施例1相同。
实施例4制备氯化胆碱、十六烷基三甲基溴化铵这两种有机模板剂摩尔比1:5，即0.02mol氯化胆碱、0.1mol十六烷基三甲基溴化铵，其余原料与实施例1相同，制备方法业与实施例1相同。
实施例5制备氯化胆碱、十六烷基三甲基溴化铵这两种有机模板剂摩尔比2:1，即0.04mol氯化胆碱、0.02mol十六烷基三甲基溴化铵，其余原料与实施例1相同，制备方法业与实施例1相同。
实施例6制备氯化胆碱、十六烷基三甲基溴化铵这两种有机模板剂摩尔比3:1，即0.06mol氯化胆碱、0.02mol十六烷基三甲基溴化铵，其余原料与实施例1相同，制备方法业与实施例1相同。
对比例1，制备方法与实施1均相同，不同在于，所有的步骤均不含有磁性搅拌。
对比例2，制备方法与实施1均相同，不同在于，有机模板剂只含有单一氯化胆碱0.02mol。
对比例3，制备方法与实施1均相同，不同在于，有机模板剂只含有单一十六烷基三甲基溴化铵0.02mol。
对比例4，制备方法与实施1均相同，不同在于，步骤8、将0.001mol硝酸镨，0.001mol硝酸铈先经过氦气氛围下超声波震荡3h，然后分别滴加到上述溶液里边滴加边磁力搅拌油浴加热90℃2h。
对比例5，制备方法与实施1均相同，不同在于，步骤9、将上述溶液通过引流器倒入聚四氟乙烯为内衬的反应釜中,然后将反应釜放入到微波反应器中以20kap/min的速度升压到550kpa,温度以25℃/min的速度升至450℃，在氧气氛围下晶化12h。
吸附甲醇效果评价，
在2m3密封箱中，量取0.6ml体积的甲醛溶液，放于表面皿中，置于密封箱中1米处两个托盘其中一个上，使甲醛自然挥发，静置24小时，用甲醛速测灵测量甲醛浓度。24h后将制备的各种比例的滤料放在表面皿中，置于密封中间两个托盘的另一个上米处托盘中，滤料暴露于含有甲醛的空气中，一周后测量甲醛浓度，然后量取0.4ml甲醛添加到1m处表面皿中。一共做12个这种装置一起实验。
表一不同滤料吸附甲醛比较：
实验结果表明实施例1制备的纳米滤料吸附甲醛效果最好，而其他比例组吸附效果与实施例1的差距较大，可见“有机模板剂利用氯化胆碱、十六烷基三甲基溴化铵摩尔比1:3，将0.001mol硝酸镨，0.001mol硝酸铈先经过20%Ar+50%CO2+30%CO氛围下超声波震荡3h，然后分别滴加到上述溶液里边滴加边磁力搅拌油浴加热90℃2h、将上述溶液通过引流器倒入聚四氟乙烯为内衬的反应釜中,然后将反应釜放入到微波反应器中以20kap/min的速度升压到550kpa,温度以25℃/min的速度升至450℃，在30%Ar+70%CO2氛围下晶化12h”这些改性的因素对于滤料吸附甲醛具有很好的效果。其纳米级晶体Pr,Ce-Y/Beta改性滤料非常优异的吸甲醛性能，而且其过滤雾霾的效果也非常的出色，实施例1中的滤料对于直径在5微米的雾霾颗粒能达到98%阻挡率。

Claims (1)

1.一种组装式过滤口罩，其特征在于，包括主口罩、固定带和主口罩两侧的副口罩，所述的主口罩两侧具有固定耳，所述的副口罩，一侧具有固定耳，另一侧具有弹性卡脚，所述的弹性卡脚能够与主口罩的固定耳固定连接，所述的主口罩包括主体框架，主体框架内部安装有空气净化滤料；
所述的空气净化滤料制备方法如下：
步骤1、首先将NaAlO2，NaOH，去离子水在氖气氛围下超声波震荡3h；
步骤2、将0.06molNaAlO2，2mol/L，12ml的NaOH溶液在磁力搅拌下90℃油浴加热完全溶解于200ml去离子水中形成铝酸钠透明液；
步骤3、将硅溶胶，硫酸先在氖气氛围下超声波震荡3h，然后将5ml硅溶胶以每分钟40滴的速度滴加到铝酸钠透明液中磁力搅拌90℃油浴加热2h，然后将10ml的98%硫酸以每分钟15滴的速度滴加到上述步骤2溶液里磁力搅拌油浴加热2h制成凝胶液；
步骤4、将0.02mol氯化胆碱、0.06mol十六烷基三甲基溴化铵有机模板剂在氩气氛围下超声波震荡3h，然后加入到上述步骤3溶液里；分4次加入，每次加入四分之一，每次加入后在磁力搅拌90℃油浴加热2h；
步骤5、将上述步骤4溶液通过引流器倒入聚四氟乙烯为内衬的反应釜中，然后将反应釜放入到微波反应器中以15kPa/min的速度升压到250kPa,温度以25℃/min的速度升至180℃，在氦气氛围下晶化48h；
步骤6、然后将0.01mol二氧化硅粉末加入到上述步骤5晶化液中磁力搅拌90℃油浴加热6h；
步骤7、然后用98%硫酸将上述步骤6得到的溶液pH值调节成弱酸性；
步骤8、将0.001mol硝酸镨，0.001mol硝酸铈先经过20%Ar+50%CO2+30%CO氛围下超声波震荡3h，然后分别滴加到上述步骤7溶液里边滴加边磁力搅拌90℃油浴加热2h;
步骤9、将上述步骤8溶液通过引流器倒入聚四氟乙烯为内衬的反应釜中,然后将反应釜放入到微波反应器中以20kPa/min的速度升压到550kPa,温度以25℃/min的速度升至450℃，在30%Ar+70%CO2氛围下晶化12h；
步骤10、然后在真空泵下过滤，在真空旋转蒸发器下除去水分，鼓风干燥箱110℃干燥，得到纳米级晶体Pr,Ce-Y/Beta改性空气净化滤料。
CN201810110625.1A 2016-10-30 2016-10-30 一种组装式过滤口罩 Active CN108294380B (zh)